The dyeability and fastness properties of super-hydrophobic navy dyes having different length of alkyl groups were investigated on ultra high molecular weight polyethylene fabrics. Those dyes exhibited strong color strength in the wavelength of mainly 550~650nm, which meant that they were navy color. From the results accomplished under various dyeing conditions, it can be concluded that those dyes have higher affinity on the fibers at $130^{\circ}C$ than at the lower dyeing temperature. Considering processing time and thermal damage of the fibers, one hour is good enough to obtain full strength of color. Maximum color strength was obtained at 2~3%owf of pure dyes. Except for the rub fastness under dry condition, all fastness such as to washing and light showed as good as of 4~5 ratings.

• Textile Coloration and Finishing
• /
• v.30 no.4
• /
• pp.237-244
• /
• 2018

Three super hydrophobic red fluorescence dyes were selected to dye high molecular weight polyethylene fiber. Their absorbance and emission spectra were obtained and Stokes' shift was measured. Fluorescence emission strength of the dyes on the fiber was investigated and therefore Fluoro Red 3 was determined as the best one among those three dyes in this experiment. Dyeing properties and fluorescence intensities were investigated using the Fluoro Red 3 on high molecular weight polyethylene fiber at various dyeing conditions. The optimum concentration of a dispersing agent was appeared at 10wt% in aqueous solution. The best dyeing was obtained at $125^{\circ}C$ for 1 hour. The color fastnesses to the washing and rubbing were as high as ratings 4~5, however, the fastness to light was exhibited ratings 2~3.

• Textile Coloration and Finishing
• /
• v.18 no.5 s.90
• /
• pp.30-34
• /
• 2006

Polypropylene fiber was dyed with 4 super hydrophobic dyes having different alkyl derivatives on the same chromophore. Double-tailed cationic surfactant, didodecyldimethylammonium bromide(DDAB), was used to make dye-dispersant complex to improve the dispersion of dyes. As the alkyl groups are longer and the hydrophobicity is increased, the dyeability onto polypropylene fiber was improved and deep coloration was obtained. As for the fastness properties, wash fastness was relatively good, while light fastness was bit low.

• Textile Coloration and Finishing
• /
• v.29 no.4
• /
• pp.223-230
• /
• 2017

Three super hydrophobic fluorescence dyes were selected to dye high molecular weight polyethylene fiber and their molar absorptivity, emission spectrum, and quantum yield were measured. From the results of color strength on the fiber, all the three dyes exhibited linear increase according to the dye concentration and Fluoro3 dye showed the highest color strength among them. Emission strength of the fluorescence dyes on the fiber was investigated according to the dye concentrations. The emission was increased with the increase of the dye concentration at relatively low dye concentration and then after showing the maximum emission strength the emission was decreased at higher dye concentrations. The highest emission was obtained in Fluoro2 dye. Color fastness to washing and rubbing was generally good enough, however, especially to light, only Fluoro3 dye exhibited rating 3 acceptable practically and Fluoro1 and 2 was ratings 1 which is unacceptable level.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2008.10a
• /
• pp.77-78
• /
• 2008

Affinity between alkyl substituted super hydrophobic dyes and polypropylene fiber has been analyzed by using the molecular descriptor as a method to predict chemical and physical characteristics of compounds. Hydrophobicity of synthesized dyes calculated by LogP which is one of molecular descriptors was increased continuously as the length of alkyl substituents increased.

• Textile Coloration and Finishing
• /
• v.6 no.3
• /
• pp.60-66
• /
• 1994

With the view of studying on the dual adsorption mechanism of acid dyes in connection with the structural difference of silk fibroin, silk fiber and silk fibroin memberane were used for equilibrium dyeing at $60^{\circ}C$, $70^{\circ}C$, $80^{\circ}C$ and pH 3.2, pH 5.0. The dyes used were C.I.Acid Orange 7 and C.I.Acid Red 88 introduced aromatic hydrocabon into Acid Orange 7. From the adsorption isotherm experiment, the total uptake of dyes can be described by Langmuir sorption and Nernst partition. Nernst partition. Nernst partition coefficient $K_1$ decrease of crystalline regions and orientation. The saturation value S of Acid Red 88 were large than total amino group contents and it was attributed it hydrophobic bond. On the other hand, the standard afficity and enthalpy were increased with the in crease of hydrophobic part of dyes. Both $k_1$ and $K_2$ were decreased with the increase of pH, but $k_2$ were more effected than $K_1$.

• Textile Coloration and Finishing
• /
• v.26 no.3
• /
• pp.165-172
• /
• 2014

Novel super hydrophobic orange dyes having maximum absorption band at 450-500nm were synthesized to dye polyolefin fibers such as polypropylene and ultra high molecular weight polyethylene fibers, using 4-alkylanilines and ${\beta}$-naphthol. Their absorption spectra at visible range showed almost the same, which meant that the alkyl substituents introduced to chromophore did not affect on color appearance of the dyes. Considering both color strength and wash fastness, the decyl-substituted dye was determined as the optimum one practically. From the dyeing results at various conditions, the optimum dyeing was $130^{\circ}C$ for 1 hour with 5% owf of dyes. The good fastness ratings to washing, rubbing were obtained showing 4-5 for both fibers. Light fastness was also acceptable giving rating 3-4 for polypropylene fibers and rating 3 for ultra high molecular weight polyethylene fibers.

• Textile Coloration and Finishing
• /
• v.19 no.6
• /
• pp.28-34
• /
• 2007

The optical and physical properties of alkyl-substituted anthraquinoid dyes were investigated in terms of dyeing of pure polypropylene fiber. The length of alkyl substituents of the dyes did not affect the molar extinction coefficient and maximum absorption wavelength of them. The use of a double-tailed cationic surfactant, didodecyldimethylammonium bromide(DDDMAB), could make the hydrophobic dyes dispersed in water effectively. As the amount of DDDMAB increased, the average particle size of dye dispersion decreased. Maximum color strength of the fabrics was shown in the case that 1.5 molar ratio of DDDMAB was used. As for the fastness properties, commercially acceptable result was obtained in general.

• Textile Coloration and Finishing
• /
• v.28 no.3
• /
• pp.156-163
• /
• 2016

The 6 novel super hydrophobic bluish-green dyes, showing the maximum absorption at 600~650nm, were synthesized to dye polyolefin fibers such as polypropylene and high strength polyethylene fibers. Their absorption spectra appeared almost the same at visible range, which meant the length of alkyl substituents did not affect on color appearance of the dyes. The optimum length of alkyl group was determined as hexyl substituents from the practical point of view. From the dyeing results, the optimum dyeing condition was $130^{\circ}C$ for 1 hour. The good fastness ratings to washing, rubbing were obtained showing 4-5 for both fibers. Light fastness was obtained also good rating 4 for both fibers.