• Transactions of the Korean hydrogen and new energy society
• /
• v.18 no.4
• /
• pp.399-405
• /
• 2007

The hyper-eutectic Mg-33.5%Ni alloy was rapidly solidified by melt spinning process. The melt-spun Mg-33.5%Ni has amorphous structure and crystallization occurred above $162^{\circ}C$. The hydriding and dehydriding rates of melt-spun Mg-33.5%Ni increased with cycle and high rate of hydrogen storage occurred at 3rd cycle. The maximum hydrogen amount absorbed in melt-spun Mg-33.5%Ni at $300^{\circ}C$ is about 4.5%.

• Transactions of the Korean hydrogen and new energy society
• /
• v.14 no.4
• /
• pp.321-326
• /
• 2003

We tried to improve the $H_2$-sorption properties of Mg by mechanical grinding under $H_2$ (reactive grinding) with CoO. The sample Mg+10wt.%CoO as prepared absorbs 1.25wt.% hydrogen and the activated sample absorbs 2.39wt.% hydrogen for 60min at 598K, $11.2barH_2$. The reactive grinding of Mg with CoO increases the $H_2$-sorption rates by facilitating nueleation(by creating defects on the surface of the Mg particles and by the additive), by making cracks on the surface of Mg particles and reducing the particle size of Mg and thus by shortening the diffusion distances of hydrogen atoms. Hydriding-dehydriding cycling increases the $H_2$-sorption rates by making cracks on the surface of Mg particles and reducing the particle size of Mg.

• Transactions of the Korean hydrogen and new energy society
• /
• v.1 no.1
• /
• pp.31-39
• /
• 1989

Although it has been well known that many metal hydrides are promising to use for hydrogen storage and other applications, some difficulties still remain. Metal hydrides, particularly in powder form, have very poor thermal conductivity. The hydrogen storage alloys degrade intrinsically or extrinsically during repeated hydriding and dehydriding. Elimination of these problems is very important in the practical applications. In order to prevent degradation and to improve the thermal conductivity, the hydrogen storage characteristics of rare-earth type alloy encapsulated with Cu or Ni by means of chemical plating have been investigated. No changes has occured in hydrogen absorption capacity and equilibrium pressure even though the alloy powder is microencapsulated. The first hydrogen absorption rate of the alloy encapsulated increased considerably comparing to uncapsulated sample. In the case of encapsulating the fine powder ($>10{\mu}m$) and subsequent compacting by $8ton/cm^2$, shape of compact is maintained regardless of hydriding and dehydriding. The degree of degradation of the alloy caused by impurity gas of CO or $O_2$ was decreased prominently by encapsulation.

• Korean Journal of Metals and Materials
• /
• v.50 no.10
• /
• pp.769-774
• /
• 2012

Mg-x wt% $Fe_2O_3-y$ wt% Ni samples were prepared by reactive mechanical grinding in a planetary ball mill, and their hydrogen-storage properties were investigated and compared. Activations of $Mg-5Fe_2O_3-5Ni$ was completed after one hydriding (under 12 bar $H_2$) - dehydriding (in vacuum) cycle at 593 K. At n = 2, $Mg-5Fe_2O_3-5Ni$ absorbed 3.43 wt% H for 5 min, 3.57 wt% H for 10 min, 3.76 wt% H for 20 min, and 3.98 wt% H for 60 min. Activated $Mg-10Fe_2O_3$ had the highest hydriding rate, absorbing 2.99 wt% H for 2.5 min, 4.86 wt% H for 10 min, and 5.54 wt% H for 60 min at 593 K under 12 bar $H_2$. Activated $Mg-10Fe_2O_3-5Ni$ had the highest dehydriding rate, desorbing 1.31 wt% H for 10 min, 2.91 wt% H for 30 min, and 3.83 wt% H for 60 min at 593 K under 1.0 bar $H_2$.

• Transactions of the Korean hydrogen and new energy society
• /
• v.15 no.3
• /
• pp.250-256
• /
• 2004

Magnesium and its alloys have the high potential as hydrogen storage materials because of their highest hydrogen storage capacity, low density and abundant resources. But poor kinetic properties of hydriding and dehydriding and high working temperature have limited their practical applications. In this study, the Mg-Ni binary alloys with different amount of Ni were produced by gravity casting and characterized in order to investigate the relationship between the microstructures and hydriding properties. The maximum hydrogen absorption capacity decreased, but the absorption kinetics increased with Ni content. The difference in the absorption kinetics was resulted from the differences in the sort and shape of primary solid phases and eutectic microstructure.

• Korean Journal of Materials Research
• /
• v.23 no.10
• /
• pp.562-567
• /
• 2013

A 90 wt% Mg-10 wt% $NbF_5$ sample was prepared by mechanical milling under $H_2$ (reactive mechanical grinding). Its hydriding and dehydriding properties were then examined. Activation of the 90 wt% Mg-10 wt% $NbF_5$ sample was not required. At n=1, the sample absorbed 3.11 wt% H for 2.5 min, 3.55 wt% H for 5 min, 3.86 wt% H for 10 min, and 4.23 wt% H for 30 min at 593K under 12 bar $H_2$. At n=1, the sample desorbed 0.17 wt% H for 5 min, 0.74 wt% H for 10 min, 2.03 wt% H for 30 min, and 2.81 wt% H for 60 min at 593K under 1.0 bar $H_2$. The XRD pattern of the 90 wt% Mg-10 wt% $NbF_5$ after reactive mechanical grinding showed Mg, ${\beta}-MgH_2$ and small amounts of ${\gamma}-MgH_2$, $NbH_2$, $MgF_2$ and $NbF_3$. The XRD pattern of the 90 wt% Mg-10 wt% $NbF_5$ dehydrided at n=3 revealed Mg, ${\beta}-MgH_2$, a small amount of MgO and very small amounts of $MgH_2$ and $NbH_2$. The 90 wt% Mg-10 wt% $NbF_5$ had a higher initial hydriding rate and a larger quantity of hydrogen absorbed for 60 min than the 90 wt% Mg-10 wt% MnO and the 90 wt% Mg-10 wt% $Fe_2O_3$, which were reported to have quite high hydriding rates and/or dehydriding rates. The 90 wt% Mg-10 wt% $NbF_5$ had a higher initial dehydriding rate (after an incubation period) and a larger quantity of hydrogen desorbed for 60 min than the 90 wt% Mg-10 wt% MnO and the 90 wt% Mg-10 wt% $Fe_2O_3$.

• Transactions of the Korean hydrogen and new energy society
• /
• v.10 no.2
• /
• pp.81-89
• /
• 1999

Various characteristics - mechanical propertis, thermal cyclic hydriding characteristics and resistance to degradation by $H_2O$, CO in hydrogen - of hydrogen storage alloy powder compacts using PTFE and silicon sealant as a polymer binder were studied. Diametral tensile strength of 10wt% PTFE and 5wt% silicon sealant added compacts showed relatively high value of $4kg/cm^2$ and $10kg/cm^2$, respectively. Compacts show a good resistance to degradation by $H_2O$ in hydrogen. But hydrogen absorption rate and capacity of compacts were decreased by CO in hydrogen with the number of cycles. Cu coated and PTFE bonded compacts showed very small decrease of capacity and a good strength even after 1000 cycles of thermal hydriding and dehydriding.

• Transactions of the Korean hydrogen and new energy society
• /
• v.23 no.5
• /
• pp.455-460
• /
• 2012

This work describes the hydriding chemical vapor synthesis (HCVS) of the $MgH_2$ in a hydrogen atmosphere and the product's hydriding-dehydridng properties. Mg powder was used as a starting material to synthesize $MgH_2$ and uniformly heated to a temperature of $600^{\circ}C$ for Mg vaporization. The effects of hydrogen pressure on the morphology and the composition of HCVS-$MgH_2$ were examined by using X-ray diffraction (XRD) and scanning electron microscopy (SEM). It is clearly seen that after the HCVS process, the particle size of synthesized $MgH_2$ was drastically reduced to the submicron or micrometer-scale and these showed different shapes (needle-like nanofibers and angulated plate) depending on the hydrogen pressure. It was found that after the HCVS process, the $H_2$ desorption temperature of HCVS-$MgH_2$ decreased from 380 to $410^{\circ}C$, and the minimum hydrogen desorption tempreature of HCVS-$MgH_2$ powder with needle-like shape can be obtained. In addition, the enhanced hydrogen storage performance for needle-like $MgH_2$ was achieved during subsequent hydriding-dehydriding cycles.

• Transactions of the Korean hydrogen and new energy society
• /
• v.26 no.6
• /
• pp.541-546
• /
• 2015

Global energy shortage problem is expected to increase driven by strong energy demand growth from developing countries. Nuclear fusion power offers the prospect of an almost infinite source of energy for future generations. Hydrogen isotope storage and delivery system is a important subsystem of a nuclear fusion fuel cycle. Metal hydride is a method of the high-density storage of hydrogen isotope. For the safety storage of hydrogen isotope, depleted uranium (DU) has been widely proposed. But DU needs a safe test because It is a radioactive substance. The authors studied a small-scale DU bed and a medium-scale DU bed for the safety test. And then we made a large-scale DU bed and stored hydrogen isotopes in the bed. Before the hydriding/dehydriding, we tested it's heating and cooling properties and carried out an activation procedure. As a result, Reaction rate of DU-$H_2$ is more rapid than the other metal hydride ZrCo. Through the successful storage result of our large bed, the development possibility of the hydrogen isotope storage technology seems promising.

• Korean Journal of Metals and Materials
• /
• v.47 no.7
• /
• pp.433-439
• /
• 2009

Ti and Ti based hydrogen storage alloys have been thought to be the third generation of alloys with a high hydrogen capacity, which makes it difficult to handle because of high reactivity. In order to solve the problem, the activation of a wide range of hysteresis of hydriding/dehydriding and without degradation of hydrogen capacity due to the hydriding/dehydriding cycle have to be improved in order to be aplied. Ti-Cr alloys have a high capacity about 0.8 wt.% in an ambient atmosphere. When the Ti-Cr alloys are added to Nb and Ta elements, they formed a laves phase in the alloy system. The Nb element was expected to make easy diffuse hydrogen in the Ti-Cr storage alloy, which was a catalytic element. In this study, the Ti-Nb-Cr ternary alloy was prepared by melt spinning. As-received specimens were characterized using XRD (X-ray Diffraction), SEM (Scanning Electron Microscopy) with EDX (Energy Dispersive X-ray) and TG/DSC (Thermo Gravimetric Analysis/Differential Scanning Calorimetry). In order to examine hydrogenation behavior, the PCI (Pressure-Composition-Isotherm) was performed at 293, 323, 373 and 423 K.