• Korean Journal of Materials Research
• /
• v.29 no.1
• /
• pp.43-51
• /
• 2019

Nacre of abalone shell features a "brick-and-mortar" microstructure, in which micro-plates of calcium carbonate are bonded by nanometers-thick layers of chitin and proteins. Due to the microstructure and its unique toughening mechanisms, nacre possesses an excellent combination of specific strength, stiffness and toughness. This study deals with the possibility of using nacre fragments obtained from abalone shell for making a bulletproof armor system. A composite plate laminated with abalone shell fragments is made and compression and bend tests are carried out. In addition, a bulletproof test is performed with hybrid armor systems which are composed of an alumina plate, a composite plate, and aramid woven fabric to verify the ballistic performance of nacre. The compressive strength of the composite plate is around 258.3 MPa. The bend strength and modulus of the composite plate decrease according to the plate thickness and are about 149.2 MPa and 50.3 GPa, respectively, for a 4.85 mm thick plate. The hybrid armor system with a planar density of $45.2kg/m^2$, which is composed of an 8 mm thick alumina plate, a 2.4 mm thick composite plate, and 18 layers of aramid woven fabric, satisfy the NIJ Standard 0101.06 : 2008 Armor Type IV. These results show that a composite plate laminated with abalone shell fragments can be used for a bulletproof armor system as an interlayer between ceramic and fabric to decrease the armor system's weight.

• The Journal of Advanced Prosthodontics
• /
• v.10 no.1
• /
• pp.32-42
• /
• 2018

PURPOSE. The purpose of this study was to derive and compare the inherent color (hue angle, chroma), translucency ($TP_{SCI}$), surface gloss (${\Delta}E^*_{SCE-SCI}$), and surface roughness ($R_a$) amongst selected shades and brands of three hybrid CAD/CAM blocks [GC Cerasmart (CS); Lava Ultimate (LU); Vita Enamic (VE)]. MATERIALS AND METHODS. The specimens (N = 225) were prepared into square-shaped ($12{\times}12mm^2$) with different thicknesses and shades. The measurements of color, translucency, and surface gloss were performed by a reflection spectrophotometer. The surface roughness and surface topography were assessed by white light interferometry. RESULTS. Results revealed that hue and chroma values were influenced by the material type, material shade, and material thickness (P < .001). The order of hue angle amongst the materials was LU > CS > VE, whereas the order of chroma was VE > CS > LU. $TP_{SCI}$ results demonstrated a significant difference in terms of material types and material thicknesses ($P{\leq}.001$). $TP_{SCI}$ values of the tested materials were ordered as LU > CS > VE. ${\Delta}E^*_{SCE-SCI}$ and $R_a$ results were significantly varied amongst the materials (P < .001) and amongst the shades (P < .05). The order of ${\Delta}E^*_{SCE-SCI}$ amongst the materials were as follows $LU>VE{\geq}CS$, whereas the order of $R_a$ was $CS{\geq}VE>LU$. CONCLUSION. Nano-ceramic and polymer-infiltrated-feldspathic ceramic-network CAD/CAM materials exhibited different optical, inherent color and surface parameters.

• The Journal of Advanced Prosthodontics
• /
• v.12 no.6
• /
• pp.344-350
• /
• 2020

PURPOSE. Recently introduced hybrid and reinforced glass ceramic computer-aided design/computer-aided manufacturing (CAD/CAM) materials have been used for full-coverage restorations. However; the effect of adjustment and type of materials on internal and marginal adaptation are unknown. This study aimed to evaluate and compare the marginal and internal adaptations of crowns made of three different CAD/CAM materials before and after adjustment. MATERIALS AND METHODS. One acrylic resin maxillary first molar was prepared and served as the master die. Thirty-six restorations were fabricated using CAD/CAM system (CEREC Omnicam, MCXL) with three materials including lithium disilicate (IPS e.max CAD), zirconia-reinforced lithium silicate (Suprinity), and hybrid ceramic (Enamic). Internal and marginal adaptations were evaluated with the reference point matching technique before and after adjustment. The data were analyzed using mixed ANOVA considering α=.05 as the significance level. RESULTS. The effect of adjustment and its interaction with the restoration material were significant for marginal, absolute marginal, and occlusal discrepancies (P<.05). Before adjustment, Suprinity had lower marginal discrepancies than IPS e.max CAD (P=.18) and Enamic (P=.021); though no significant differences existed after adjustment. CONCLUSION. Within the limitations of this study, crowns fabricated from IPS e.max CAD and Suprinity resulted in slightly better adaptation compared with Enamic crowns before adjustment. However, marginal, axial, and occlusal discrepancies were similar among all materials after the adjustment.

• Journal of the Microelectronics and Packaging Society
• /
• v.16 no.4
• /
• pp.17-22
• /
• 2009

Two different organic-inorganic hybrid thin film transistors (OITFTs) with the structures of glass/ITO/ZnO/PMMA/Al (staggered structure) and glass/ITO/PMMA/ZnO/Al (inverted staggered structure), were fabricated and their electrical and structural properties were compared. The ZnO thin films used as active channel layers were deposited by the atomic layer deposition (ALD) method at a temperature of $100^{\circ}C$. To investigate the effect of the substrates on their properties, the ZnO films were deposited on bare glass, PMMA/glass and ITO/glass substrates and their crystal properties and surface morphologies were analyzed. The structural properties of the ZnO films varied with the substrate conditions. The ZnO film deposited on the ITO/glass substrate showed better crystallinity and morphologies, such as a higher preferred c-axis orientation, lower FWHM value and larger particle size compared with the one deposited on the PMMA/glass substrate. The field effect mobility ($\mu$), threshold voltage ($V_T$) and $I_{on/off}$ switching ratio for the OITFT with the staggered structure were about $0.61\;cm^2/V{\cdot}s$, 5.5 V and $10^2$, whereas those of the OITFT with the inverted staggered structure were found to be $0.31\;cm^2/V{\cdot}s$, 6.8 V and 10, respectively. The improved electrical properties for the staggered OITFTs may originate from the improved crystal properties and larger particle size of the ZnO active layer.

• Plant Resources
• /
• v.7 no.2
• /
• pp.141-146
• /
• 2004

Frequent occurrence of off-type plants in a given cultivar has been a serious problem in both breeder's and farmer's fields. An experiment was designed to examine the differences in rate of occurrence of off-type plants among Tongil-type cultivars (high yielding cultivars derived from indica/japonica hybridization) from which the possible cause of higher occurrence of off-type plant in a specific cultivar was deduced. Among five Tongil-type cultivars examined for morphological variant in the field, only one cultivar, Dasanbyeo, had off-type plants. When analyzed with SSR markers, off-type plants showed different band patterns from original cultivar, having several extra bands in addition to cultivar-specific band, suggesting that off-type plants were originated from Dasanbyeo, rather than originated from mixing or mishandling of seed materials with other cultivars. The possible cause of off-type occurrence seems to be natural pollination with other cuItivars adjacent to the original cultivar during seed multiplication. This was supported from the observation that self-crossed progeny of the off type plants showed a wide range of variation of agronomic traits which could not be observed when there was a smaller introduction of genes to the fixed germplasm as happened in the case of cultivar mutation. Another evidence supported this idea that Dasanbyeo showed much of difference in floral organ and behavior to other cultivar to be subjected to higher out-crossing than other cultivars examined.

• Proceedings of the IEEK Conference
• /
• 2003.07b
• /
• pp.995-998
• /
• 2003

This paper reports the correlation between dielectric constant and degree of amorphism of the hybrid type Si-O-C thin films. Si-O-C thin films were deposited by high density plasma chemical vapor deposition using bistrimethyl- silylmethane(BTMSM, $H_{9}$C$_3$-Si-C $H_2$-Si-C$_3$ $H_{9}$) and oxygen precursors with various flow rate ratio. As-deposited film and annealed films at 40$0^{\circ}C$ were analyzed by XRD. The Si-O-C thin films were amorphous from XRD patterns. For quantitative analysis, the diffraction pattern of the samples was transformed to radial distribution function by Fourier analysis, and then compared with each other. The degree of amorphism of annealed films was higher than that of as-deposited ones. The dielectric constant varied in accordance with flow rate ratio of precursors. The lowest dielectric constant was obtained from the as-deposited film which has the highest degree of amorphism after annealing.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.325-328
• /
• 2005

Fiber Reinforced Polymers are recognized as the alternative materials for solving the problem due to the excellent corrosion-resistant property, light-weight and higher strength than steel. Glass fiber is superior to other fibers from the economical point of view but the mechanical property is not. For this reason, researches to improve the mechanical property of glass fiber reinforced polymer rebar has been conducted and it emerged as a solution to make the bar as a hybrid type with carbon fibers. This paper presents results of experimental program to investigate the scattering effectiveness of carbon fibers in glass FRP bar.

• Journal of the Korean Chemical Society
• /
• v.60 no.6
• /
• pp.402-409
• /
• 2016

Thin films of lead sulfide colloidal quantum dots (CQDs) of 2.8 nm in diameter are fabricated and their surfaces are passivated by 3-mercaptopropionic acid (MPA) ligand or hybrid type ($MPA+CdCl_2$) ligand, respectively. The changes in valence band electronic structure and atomic composition of each PbS CQD film upon post-treatment such as air, N2 annealing or UV/Ozone have been studied by photoelectron spectroscopy. The air annealing makes the CQD fermi level to move toward the valence band leading to "p-type doping" regardless of ligand type. The UV/Ozone post-treatment generates $Pb(OH)_2$, $PbSO_x$ and PbO on both CQD surfaces. But the amount of the PbO has been reduced in hybrid type ligand case, especially. That is probably because the extra Pb cations in (111) surface are additionally passivated by $Cl_2$ ligand, which limits the reaction between the Pb cation and ozone.

• Applied Chemistry for Engineering
• /
• v.20 no.5
• /
• pp.547-552
• /
• 2009

When fiber reinforced plastics (FRP) products are manufactured, dust and odor materials are inevitably generated in a workplace. To improve the bad condition of the workshop, we developed the Hybrid Bag Filter attached activated carbon fiber (ACF) and installed the system at two companies producing FRP goods. In order to raise the efficiency of dust collection, we set the ducts both on the ceiling and at the bottom of the wall and according to the circumstances of the workshop's space, moving dust collector also adopted as a different type of flexible duct. Pulse Jet Type Bag Filter is also equipped to operate the system more effectively, for the improved fine environment because of high dust removal efficiency. Finally, we investigated the removal tendency of the dust and odor when operating the System of Hybrid Bag Filter.

• Restorative Dentistry and Endodontics
• /
• v.19 no.1
• /
• pp.194-204
• /
• 1994

The purpose of this study was to evaluate the surface hardness of composite resins according to heat treatment. storage condition and storage time. In this study. two kinds of composite resin inlays and one kind of conventional posterior composite resin were used as experimental materials. One hundred eighty composite resin specimens were constructed from composite resin inlays and conventional posterior composite resin. The conditions of this study were heat treatment. storage condition and storage time. Hardness readings were taken from the top surface of each samples using the Vickers microhardness tester(MHT-l. Matsuzawa. Japan}. The following results from this study were obtained: 1. Regardless of storage condition. both composite resin inlay and conventional posterior composite resin have a higher surface hardness under heat treatment than not. 2. Composite resins with heat treatment have a higher surface hardness under dry storage than under water immersion. 3. In case of Clearfil Photo Posterior and Brilliant Enamel with heat treatment. there was no significant difference with time. but Clearfil CR Inlay with heat treatment. there was statistical difference after 24 hours. 4. Surface hardness of composite resins with coarse hybrid type was higher than that of composite resin with fine hybrid type.