• 대한건축학회논문집:구조계
• /
• 제34권5호
• /
• pp.27-34
• /
• 2018

Concrete placed under hot weather condition suffers from larger slump loss, rapid moisture evaporation due to high air temperature. Proper measures for material, transportation and curing should be taken to prevent the quality deterioration of the concrete under hot weather condition. In Korea, Although the period of hot weather concrete in Korea occupies only 2 months, there are a lot of quality problems including plastic, drying shrinkage and cold joint. Therefore, the objective of this paper is to investigate and compare the temperature history and crack occurrence of the concrete, which was placed in the actual apartment house construction field under hot weather condition, in response to the application of surface covered curing blankets including PE film, single layer clear bubble sheet, white colored bubble sheet and aluminum metalized bubble sheet. Test results indicated that the application of white colored bubble sheet and aluminum metalized bubble sheet showed most favorable results in terms of reduction in temperature rise and crack occurrence as well as easiness in handling. But, due to light reflection by aluminum metalized bubble sheet, it is believed that white colored bubble sheet is preferable.

• 한국건축시공학회지
• /
• 제5권3호
• /
• pp.91-99
• /
• 2005

It is required to study systematical on the concrete quality management to extend structure life because rebuilding effect is reducing under present condition of large sized and high stories structure. Concrete, which shows its intensity by hydrating action and a big change in quality according to hot weather and temperature, produces a lot of qualify problem under hot and cold weather Because of each specification and construction plan which does not have basic standard on site, concrete's quality is irregular and makes some defect. As a result, Daegu is turned out to be the longest area after investigating application period and days focused on 8 cities weather information about relationship between hot weather circumstance and construction environment. Therefore, we first surveyed the concrete material in the region and found out the problem of quality nanagement. Then figure out the way of solution. Moreover, we integrated concrete material quality management, which is applied differently to each site, to have equal quality and to reduce defect from construction site. And then, based on various test of construction condition and analysis of quality management item, we suggest effective concrete quality management to make concrete material construction standard guide and plan under hot weather.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2017년도 추계 학술논문 발표대회
• /
• pp.96-97
• /
• 2017

Performances such as retention, setting time and strength generation of mortar with phosphate-introduced chemical admixture, domestic and foreign admixtures are evaluated to find one that meets over 3 hours retention in extremly hot weather condition in this study.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2006년도 추계 학술논문 발표대회 논문집
• /
• pp.87-90
• /
• 2006

This study investigates the temperature history of slab mock-up specimens for hot weather concreting applying various surface insulating methods, in order to improve concrete quality at hot weather condition. Test showed that the use of insulating blanket or a bubble sheet on upper section of slab prevented from abrupt increase of temperature and vaporization of moisture during early curing at hot weather circumstance. In addition, it secured higher strength at early age. Therefore it is concluded that concrete construction insulating with the bubble sheet will reduce the plastic and drying shrinkage as well as improve strength at early age, thus securing concrete duality.

• 한국건축시공학회지
• /
• 제18권3호
• /
• pp.251-257
• /
• 2018

여름철 콘크리트는 수분증발에 의한 소성 및 건조수축균열, 슬럼프 저하, 콜드조인트 발생 등 다양한 문제가 발생한다. 이에 국내에서는 수분증발을 방지하고, 단열성능을 확보하기 위해 표면피복 양생을 위한 다양한 형태의 버블시트를 제작하여 사용하고 있으나, 여름철에는 적용사례가 없었다. 따라서 본 연구에서는 여름철 시공중인 아파트 현장에 1중의 투명, 백색 및 알루미늄 증착 버블시트와 PE필름 및 표면노출의 5가지 표면피복 양생재를 적용하여 콘크리트의 온도 및 균열특성 등 품질에 미치는 영향을 분석하였다. 실험결과 알루미늄 증착 버블시트가 온도저감, 균열저감 면에서 가장 뛰어난 것으로 나타났지만, 알루미늄 재질의 특성상 빛이 반사되어 시공자의 눈부심에 따른 시각공해가 발생하기 때문에 백색 버블시트의 사용이 가장 효과적인 것으로 밝혀졌다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2012년도 추계 학술논문 발표대회
• /
• pp.11-12
• /
• 2012

This study investigates the temperature rise of reinforcement bars located in the middle of the form (for reinforcement concrete) during hot weather condition. The temperature was measured for three consecutive days before placing concrete. Test results showed that the temperature started to increase at 7:00 AM before sun rised, and peaked at around 2:00 PM. It was found that the thinner the diameter of a reinforcement bar, the higher is the speed of temperature rise and drop of the bar. The peak level of temperature for D13, D19, D25 and D32 was 54.4℃, 55.2℃, 56.4℃ and 60.2℃, respectively.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 추계 학술발표회 논문집
• /
• pp.785-788
• /
• 2006

This paper investigates the temperature history of slab mock-up specimens with various surface curing sheets, in order to determine a favorable surface curing method in hot weather condition. Test showed that insulating double bubble sheets+aluminum foil simultaneously on the upper section of a specimen prevented an increase of sudden temperature and a decrease of vaporization when placed during the hot weather condition. It also secured the high strength in early age. Therefore it is found that using the double bubble sheets+aluminum foil on concrete surface declined the plastic and drying shrinkage and inclined the early strength, thus improving the concrete quality.

• 한국건설관리학회논문집
• /
• 제7권2호
• /
• pp.71-80
• /
• 2006

건축물이 대형화, 고층화되는 현 상황에서는 재건축의 효용성이 감소되므로 구조물의 수명연장을 위한 콘크리트 품질관리의 체계적인 연구가 필요하다. 콘크리트는 시멘트의 수화 반응에 의해 강도가 발휘되며 온도에 따른 품질변화가 매우 큰 재료로서 한중과 서중 같은 시공환경에서 품질문제가 많이 유발된다. 특히 서중환경에 대해서는 콘크리트 표준시방서와 현장별 특기시방서 및 시공계획서 등으로 현장을 관리하고 있으나, 이에 대한규정이 명확하지 않아 현장별로 뚜렷한 기준 없이 임의로 시공되어 품질이 일정하지 않고 각종 하자가 발생하는 실정이다. 이에 서중 환경이 콘크리트의 시공환경과 어떤 관련성이 있는지에 대해 전국 8개 대도시의 기상자료를 중심으로 적용기간과 일수를 조사하고 분석한 결과 대구가 가장 긴 지역으로 판명되었다. 따라서 이 지역의 콘크리트 양생공정에 대한 현장 품질관리 실태를 조사하여 품질관리상 문제점을 파악하고, 그 해결방안이 될 기초 자료를 도출하였다. 또한, 서중 콘크리트 시공에 있어 현장별로 상이하게 적용되고 있는 양생공정의 품질관리 기준을 통합하여 균일한 품질 확보와 하자발생을 줄이기 위해 현장에서 가장 시급히 보완되어야 할 부분에 대한 현장시험과 품질관리 항목의 분석을 통하여 서중 환경시 양생공정의 시공지침과 시공계획서 작성에 필요한 콘크리트 품질관리에 관하여 연구한 논문이다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제24권6호
• /
• pp.189-196
• /
• 2020

초고층 건축물과 같은 대형 건축물의 부재가 대형화 되면 수화발열로 인하여 내 외부 온도차가 커져 균열이 발생한다. 잠열재인 상전이 물질을 수화열저감재로써 사용하는 방법은 다른 방법들보다 접근성, 사용성, 효율성이 높다. 이에 따라 수화열저감재로 상전이 물질을 사용한 연구들이 많이 진행되고 있다. 하지만 상전이 물질은 상전이 반응온도가 다르기 때문에 외기온도, 콘크리트 비빔온도 같은 환경요인에 영향을 받을 수 있는데 이를 고려한 연구는 미미한 수준이다. 따라서 본 논문에서는 서중환경에서 수화열저감재를 사용한 콘크리트의 수화발열 특성과 품질을 평가하였다. 그 결과, 서중환경에서 스트론튬계 수화열저감재를 3wt.%, 5wt.%를 혼입했을 경우, OPC수준보다 수화발열은 8%, 21% 저감이 가능하고 발열속도는 약 75분, 85분 정도 지연할 수 있는 것으로 나타났다. 이는 온도가 높을 때 상전이 반응이 상대적으로 촉진되어 실험실환경보다 향상된 성능 나타난 것으로 판단된다. 향후 서중환경에서 다른 종류의 수화열저감재 효율과 비교하고, 장기 재령에서의 강도발현 등에 대한 세부적인 검토를 진행할 예정이다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2013년도 춘계 학술논문 발표대회
• /
• pp.51-52
• /
• 2013

Generally, Adiabatic temperature rise and temperature rise rate are reported to increases when placement temperature, W/B and the unit water content is fixed. In this study, properties of adiabatic temperature rise on placement temperature consider the hot weather environments from of W/B 0.29, 0.34, 0.40 was reviewed, the amount of cement on mixing condition of the same W/B and unit water content evaluated on the impact of the adiabatic temperature rise. As a results, the adiabatic temperature rise of concrete is proportionate to binder as well as the cement content under the same unit water content.