• Journal of the Korean Society for Heat Treatment
• /
• v.23 no.4
• /
• pp.198-204
• /
• 2010

Modified 9Cr-1Mo steels possess excellent high-temperature mechanical properties and are widely used in energy conversion industries. However, in-service materials degradation, such as softening, carbide-induced embrittlement, temper embrittlement, etc., can take place during long-term operation. Evolution of microstructure due to service exposure to high temperature has a strong effect on the performance of heat resistant steels. In case of modified 9Cr-1Mo steels, precipitation of $Fe_2Mo$-type laves phases and coarsening of $M_{23}C_6$-type carbides are the primary cause of degradation of mechanical properties such as toughness, hardness, tensile strength and creep resistance. This study was aimed at finding reliable parameter for assessing the integrity of modified 9Cr-1Mo steels. Characteristic parameters were attained between mechanical and ultrasonic properties.

• Journal of the Society of Disaster Information
• /
• v.13 no.3
• /
• pp.313-321
• /
• 2017

In order to investigate the basic performance of the high strength anchor for asphalt road subjected to tensile load, the static pullout test was carried out and the pullout strength of the asphalt anchor was analyzed. In the pullout test, the depth of anchor, depth of pavement, diameter of anchor, type of anchor, experimental temperature, epoxy type and amount of anchor were used as test variables. As a result, the steel strength of asphalt anchor was 1.08 times higher than that of conventional concrete anchor, therefore it is considered appropriate to use the steel strength formula of concrete anchor for asphalt anchor. Compared with the proposed formula, the pullout load obtained from the test of the asphalt anchor was within ${\pm}10%$. The ratio of the projected area of the asphalt anchor is similar as that of the concrete anchor.

• Design & Manufacturing
• /
• v.12 no.3
• /
• pp.25-30
• /
• 2018

Recently The automotive industry is trying to increase the energy efficiency by reducing the weight of the car body and engine components as a way to achieve high energy efficiency. In particular, the reduction of the weight of the vehicle through the weight reduction of the vehicle body has the advantage that the fuel consumption and the output can be improved. But at the same time, there is the disadvantage that the strength becomes weak due to the reduction of the material thickness. Therefore, in order to overcome these disadvantages, materials with high strength according to the unit thickness have been actively developed, and researches for applying them have also been increasing. In this study, we will investigate the application of cold rolled steel sheet, which is a lightweight material, to a horn bracket that secures a installed in an automobile engine room. The horn bracket secures the horn on the car engine and is bolted to the outer wall of the engine. The momentum is acted on the bracket due to the distance between the bolt fastening part and the car horn installed on the bracket end side. Therefore, the body part of the bracket is more likely to be destroyed by the influence of the continuous stress. In this paper, design optimization for weight reduction and strength enhancement was performed to solve this problem, and possibility of applying the rolled steel sheet material as lightweight material by tensile test and fabrication was confirmed.

• Korean Journal of Metals and Materials
• /
• v.50 no.4
• /
• pp.285-292
• /
• 2012

Hot ductility behavior of precipitation-hardened low-carbon iron alloys containing 0.02 wt% Ti and 0.05 wt% Nb was characterized by a hot tensile stress test. Carbon (0.05, 0.1, 0.25 wt%) and boron (0.002 wt%) contents were varied to study the effect of precipitates on the high-temperature embrittlement of the alloys in the temperature range of $600{\sim}800^{\circ}C$. Ductility loss was observed at $700^{\circ}C$ for the tested alloys. The cause of the ductility loss was mainly attributed to the carbides and ferrite films formed at the grain boundaries during deformation. Although the carbon content tended to raise the total fraction of Nb (C, N), the precipitates were formed mostly in the grain interior as the precipitation temperature was raised above the deformation temperature by the high carbon content. Hence, carbon in excess suppressed the hot ductility loss. Meanwhile, boron addition improved the hot ductility of the alloys. The improvement is likely due to the boron atoms capturing carbon atoms and thus retarding the carbide formation.

• Journal of Korean Society of Steel Construction
• /
• v.26 no.3
• /
• pp.231-240
• /
• 2014

The T-stub subjected to an axial tensile force shows various behavior characteristics according to the changes in the diameter and tightening force of the fastener, the geometric shape of the T-stub, and the material properties of the T-stub and fastener. Due to the influence of these changes, the T-stub shows three failure modes: plastic failure after the flexural yielding of the T-stub flange, flexural yielding of the T-stub fillet, and fracture of the fastener. In general, a T-stub with a thin flange and where the gauge distance of the fastener is long has a larger energy dissipation capacity than a T-stub with a thick flange and where the gauge distance of the fastener is short, due to the plastic deformation after flexural yielding. In this study, three-dimensional nonlinear finite element analysis was carried out to determine the effect of the fastener used for fastening the T-stub on the energy dissipation capacity of the T-stub. For the fastener of the T-stub analysis model, F10T-M20 high-tension bolts and ${\varnothing}19.05-mm$ (3/4-inch) SMA bars were modeled, and the geometric shape of the T-stub was selected to represent the flexural yielding of the T-stub fillet and the axial tensile failure of the fastener.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.5
• /
• pp.86-94
• /
• 2022

Replacement of FRP rod as steel reinforcement has been attracted significantly to prevent the degradation of the concrete structure due to corrosion. So, the technology development to extend the structure's service life by improving FRP properties has been proceeded worldwide. Accordingly, it is necessary to develop Korea's CFRP rod and CFRP grid, including the manufacturing techniques to improve the properties of high-strength and high-stiffness. Moreover, the research should be conducted to evaluate the structural behavior of the beams using the CFRP rod or grid. This study investigates the flexural and shear behavior of reinforced concrete beam using demonstrated CFRP rod as reinforcement according to the reinforcement ratio and shear span to depth ratio. From the results, when the reinforcement ratio is out of a specific range, it is seemed that the effect on performance improvement of the beam using CFRP rod is cancelled or not significant. Meanwhile, when the CFRP rod was used as reinforcement, the possibility of shear failure occurred, even steel stirrups were installed in the beam with CFRP rod as tensile reinforcement according to the Korean Design Standard. Therefore, when the CFRP rod is used as tensile reinforcement in a beam, it should be prepared that a specific limitation of reinforcement ratio and an investigation against shear failure. Also, the ductility of the beam using the CFRP rod is determined by the deformation energy evaluation method. So, the ductility should be investigated by applying the deformation energy evaluation method that reflects the structural behavior of the beam.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.27 no.1
• /
• pp.46-53
• /
• 2023

In this paper, we evaluated the flexural performance of three types of reinforced concrete beams (SHCC-RB, SHCC-SB, SHCC-FRP) strengthened with ordinary steel rebar, very high strength (super strength) rebar, and FRP bars together with strain-hardening cement composite (SHCC). For this purpose, a series of beam specimens were manufactured and four-point load bending experiments were performed. As a result of the experiment, all specimens strengthened with SHCC exhibited tightly controlled flexural microcrakcs with the crack width of less than 100 ㎛. This is mostly due to the material properties of SHCC showing tensile strain hardening properties with multiple microcracks under uniaxial tension. The specimen SHCC-FRP showed lower initial cracking moment and yield flexural strength than SHCC-RB, whereas the maximum flexural strength of SHCC-FRP was superior to that of SHCC-RC. This is because the tensile strength of FRP bars is higher than that of ordinary steel reabr. The initial cracking moment of the beam specimen SHCC-SB was similar to that of SHCC-RB, but the yield flexural strength and maximum flexural strength of SHCC-SB were evaluated to be the highest.

• Journal of Korea Foundry Society
• /
• v.18 no.6
• /
• pp.563-569
• /
• 1998

A Study on microstructure and elevated temperature strength of 18Cr-2Mo ferritic stainless steel castings strengthened by alloying small amounts of titanium and carbon, has been conducted. The morphology of titanium carbides showed spherical in shape and their distribution depended on the amount of alloying elements. Maximum density ($7{\times}10^5/cm^2$) of titanium carbides has been formed in the alloy containing 2.0 wt.% titanium and 0.5 wt.% carbon as alloying elements and the size of carbide particles is in the range of 0.5 to $3.0\;{\mu}m$. High temperature tensile and fatigue strength of this alloy were the highest among the alloys tested in this research. The fracture mode of the alloys containing alloying elements less that 2.0 wt.% titanium and 0.5 wt.% carbon showed intercrystalline fracture at room temperature, while the alloys containing higher amounts of alloying elements showed transcrystalline fracture. All of the alloys showed creep or ductile rupture mode at elevated temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.100-103
• /
• 2003

The primary insulation system used in an oil-filled transformer is kraft paper, wood, porcelain and oil. Modern transformers use paper that is chemically treated to improve its tensile strength properties and resistance to aging caused by immersion in oil. But these insulation papers are mainly aged to thermal stress. Over the course of the insulation paper and oil's life it is exposed to high temperatures, oxygen and water. Its interaction with the steel of the tank and core plus the copper and aluminium of the windings will eventually cause the chemical properties of the oil to decay. High temperature have an effect on mechanical strength of cellulous paper using the layer insulation. We made two aging cell in which thermal aging tests of insulation papers and mineral oil are conducted. It is measured dielectric strength, number of acid, moisture, etc. of insulation paper and oil aged in the aging cells.

• Journal of the Architectural Institute of Korea Structure & Construction
• /
• v.35 no.1
• /
• pp.21-28
• /
• 2019

This study investigates the applicability of composite polyurea to contain fiber reinforcement like fiber glass, steel fiber and carbon nanotube. Polyurea as elastomer is an excellent water-proofing material with many mechanical characteristics such as high tensile strength, ductility, high rate of expansion and contraction, and so on. The reinforcing fibers can be utilized for improving the load-carrying capacity of concrete structures. The polyurea plays a role to improve the ductility and toughness. Composite polyurea takes the mechanical advantages of the fibers and the polyurea. The test variables include the type of reinforcing fiber, its spraying thickness, and its weight ratio contained in the composite polyurea. It is observed that the load-carrying capacity, and the ductility and toughness are improved with the increase in the spraying thickness and the weight ratio contained in the composite polyurea. It is expected that the composite polyurea can be widely utilized in enhancing the structural and seismic performance.