• 열처리공학회지
• /
• 제21권5호
• /
• pp.244-250
• /
• 2008

This study has investigated the surface phase change, hardness variation, surface precipitates, nitrogen content and corrosion resistance in STS 431 (17Cr-2Ni-0.2C-0.01Nb) martensitic stainless steel after high temperature gas nitriding (HTGN) treatment at the temperature range between $1050^{\circ}C$ and $1150^{\circ}C$. The HTGN-treated surface layer appeared $Cr_2N$ of rod type, carbo-nitride of round type and fine precipitates in the austenite matrix. On the other hand the interior region where the nitrogen was not permeated, exhibited martensite phase. The surface hardness showed 250~590 HV, depending on the HTGN treatment conditions, while the interior martensitic phase represented 520 HV. The permeation depth of nitrogen increased with increasing the HTGN-treated temperature. The nitrogen concentration of the surface layer appeared approximately ~0.17% at $1100^{\circ}C$. On comparing the corrosion resistance between solution-annealed and HTGN-treated steels, the corrosion resistance of HTGN-treated steel was superior to that of solution-annealed specimens.

• 대한전자공학회논문지SP
• /
• 제45권5호
• /
• pp.95-102
• /
• 2008

이 논문은 고강도매질 CR(Computed Radiography) 영상의 잡음을 모델링하는 적절한 접근법을 제시한다. 잡음 유형의 통계적이고 비선형적 특성이 구체적으로 고안되었다. CR영상은 컴퓨터 처리에 의해 코드화되기 이전 이미 훼손된다. 다양한 형태의 잡음은 비록 디지털화된 상태로 검출된다 하더라도 통상 방사선 영상을 오염시킨다. 양자 방출시의 포아송 분포는 CR 영상판에서의 광자 분포에서 포아송 잡음 분포를 항상 유지하지 않는다. 그 통계적 특성은 재질 특성에 의해 상대적이며 경우의존적이다. 통계적 잡음모델링 과정에서 통상적인 포아송, 이항 내지는 가우스 통계분포의 가정이 고려되었으며 아울러 비선형 효과 또한 포함시켰다. 이는 잡음 영역의 고저 전 방사선량에 걸쳐 추정하는 해석적 모델을 구현한다. 그리고 이 분석적 접근은 고강도 강판튜브 스텝웨지의 방사선측정실험을 통해 관측한 CR 영상데이터에서 구현되었다. 그 결과는 매질의 두께변화에 따른 잡음의 일관성, 잡음분포특성, SNR 및 비선형 보간을 측정하는 상호비교의 파라미터연구에 유용하다.

• 대한기계학회논문집A
• /
• 제26권7호
• /
• pp.1453-1460
• /
• 2002

Creep-fatigue crack growth models have been proposed employing $(C_t)_{avg}$ as a crack tip parameter characterizing the time-dependent crack growth. The basic assumptions made in these previous models were ideal creep reversal conditions such as no creep reversal and complete creep reversal condition. Due to this assumption, the applicability of the models was limited since they did not consider partial creep reversal condition which is usually observed in many engineering metals at high temperature. In this paper the creep reversal parameter, Temperature;$C_R$, which was defined by Grover, is critically evaluated to quantity the extent of partial creep reversal at the crack tip. This approach does not rely on any simplifying assumptions regarding the extent of the amount of creep reversal during the unloading part of a trapezoidal fatigue cycles. It is shown that the $(C_t)_{avg}$ value calculated for 9Cr steel agrees well with the experimentally measured one. It is argued that the extent of improvement is not significant when the result is compared with that of the conventional model which has an assumption of full creep reversal behavior.

• 에너지공학
• /
• 제26권4호
• /
• pp.1-6
• /
• 2017

본 연구는 수소-천연가스 혼합연료 차량에 사용되는 금속 및 비금속재료에 대한 수소영향을 평가하였다. 수소가 30% 혼합된 HCNG연료의 사용 조건(25MPa)에서 34CrMo강은 겨울철 조건에서는 수소 침투량이 0.0018ppm, 여름철 조건에서 5.3ppm으로 측정되었다. 일정하중시험(CLT)에 의한 임계 수소량이 1.03ppm으로 평가되어, 34CrMo 강은 HCNG 사용 조건에서 수소 취화에 의한 취성 파괴를 일으킬 수 있는 것으로 평가된다. 비금속재료에 대한 평가에서는 모든 재료가 시험 기준을 만족하였으나, Fluorocarbon 고무 재질의 경우 체적 변화가 크게 발생하여 사용에 각별한 주의가 요구된다.

• 한국재료학회지
• /
• 제11권10호
• /
• pp.813-819
• /
• 2001

The microstructure and the distribution of hardness of Co and A1 alloy powder cladding layer in high carbon 9CrSi alloy steel for roll materials cladded by laser surface cladding were investigated. And, for the evaluation of soundness as the roll materials, we examined the wear resistance of the cladding materials with the wear appratus of pin on disc type. The experimental results showed that the microstructure of laser cladding layer was constituted with the clad surface layer, the alloy layer, the heat treatment layer with base metal. The wear resistance of Ni alloy Powder cladding material was superior to that of Co alloy powder cladding material both at the low speed (0.46m/s) and the high speed(0.92m/s). It seemed that the behavior of wear showed the abrasive wear at the early stage and the adhesive wear at the late stage.

• Corrosion Science and Technology
• /
• 제3권4호
• /
• pp.140-147
• /
• 2004

High temperature oxidation of Fe-19Cr and Fe-19Cr-0.2Ti alloys is studied at 1173-1373 K in 16.5 kPa $O_2$ - balances $N_2$ atmosphere aimed at clarifying the effect of titanium addition. Oxidation rate of Fe-19Cr alloy was accelerated with titanium. For both alloys chromium rich $(Fe,\;Cr)_2O_3$ was formed as a major oxidation product. On Fe-19Cr-0.2Ti alloy, a thin layer composed of spinel type oxide and titanium oxide was also formed and an internal oxidation of titanium was observed. Titanium was concentrated at the oxide surface and internal oxidation zone but a small amount of titanium was also found in the intermediate corundum type $(Fe,\;Cr)_2O_3$ layer. Crystals of corundum type $(Fe,\;Cr)_2O_3$ formed on Fe-19Cr alloy are coarse but that formed on Fe-19Cr -0.2Ti alloys were fine and columnar. Reason for the difference in oxidation kinetics and crystal structure will be discussed relating to the distribution of aliovalent titanium in corundum type $(Fe,\;Cr)_2O_3$ oxide layer.

• 한국표면공학회지
• /
• 제52권6호
• /
• pp.293-297
• /
• 2019

Quasi-nano-hardness and corrosion behaviors of neutron-irradiated reactor pressure vessel (RPV) steels such as 15Ch2MFA (Ni<0.4, 2.520 n/㎠ (En>1.0 MeV) for 32 days. Quasi-nano-hardnesses of the 15Ch2MFA and 15Cr2NHFA steels were 183.8 and 179.8 Hv, respectively. Their corrosion rates and corrosion potentials were 2.4×10^-4Acm^-2, -515.9 mV_SHE and 6.8×10^-4 Acm^-2, -523.6 mV_SHE in NACE standard TM0284-96 solution at room temperature, respectively. 15Ch2MFA steel showed better quasi-nano-hardness and corrosion resistance than 15Cr2NHFA steel in this test condition.

• 대한금속재료학회지
• /
• 제46권9호
• /
• pp.593-603
• /
• 2008

In this study, effects of alloying elements on the sticking occurring during hot rolling of five kinds of ferritic STS430J1L stainless steels were investigated by analyzing high-temperature hardness and oxidation behavior of the rolled steels. Hot-rolling simulation tests were conducted by a high-temperature wear tester which could simulate actual hot rolling. The simulation test results revealed that the sticking process proceeded with three stages, i.e., nucleation, growth, and saturation. Since the hardness continuously decreased as the test temperature increased, whereas the formation of Fe-Cr oxides in the rolled steel surface region increased, the sticking of five stainless steels was evaluated by considering both the high-temperature hardness and oxidation effects. The addition of Zr, Cu, or Si had a beneficial effect on the sticking resistance, while the Ni addition did not show any difference in the sticking. Particularly in the case of the Si addition, Si oxides formed first in the initial stage of high-temperature oxidation, worked as initiation sites for Fe-Cr oxides, accelerated the formation of Fe-Cr oxides, and thus raised the sticking resistance by about 10 times in comparison with the steel without Si content.

• 대한기계학회논문집A
• /
• 제26권1호
• /
• pp.55-60
• /
• 2002

For the development of a new creep test technique, the availability of SP-Creep test is discussed for 1Cr-0.5Mo boiler header material. And some results are also compared with those of 2.25Cr- 1Mo steel which widely uses as boiler superheater tube. The results can be summarized as follows. The load exponents(n) obtained by SP-Creep test for 1Cr-0.5Mo steel are decreased with increasing creep temperature and the values are 15.67, 13.89, and 17.13 at 550$^{circ}C$ ,575$^{circ}C$ and 600$^{circ}C$, respectively. The temperature dependence of the load exponent is given by n = 107.19 - 0.1108T. This reason that load exponents show the extensive range of 10∼16 is attributed to the fine carbide such as M$_{23}$C$_{6}$ in lath tempered martensitic structures. At the same creep condition, the secondary creep rate of 1Cr-0.5Mo steel is lower than the 2.25Cr-1Mo steel1 due to the strengthening microstructure composed by normalizing and tempering treatments. Through a SEM observation, it can be summarized that the primary, secondary, and tertiary creep regions of SP-Creep specimen are corresponding to plastic bending, plastic membrane stretching, and plastic instability regions among the deformation behavior of four steps in SP test, respectively.y.

• 대한금속재료학회지
• /
• 제46권11호
• /
• pp.708-712
• /
• 2008

The influence of high temperature gas nitriding (HTGN) in STS347 and STS310S steels was experimentally investigated. The HTGN was carried out at $1,050^{\circ}C{\sim}1,150^{\circ}C$ for 10 hrs in a gaseous atmosphere containing $1kg/mm^2$ of nitrogen. After HTGN, fine precipitates of $Cr_2N$ and NbN appeared in austenite on the surface of STS 347, while nitrogen pearlite, which was layeredof $Cr_2N$ and austenite alternatively, appeared in austenite on the surface of STS 310S. The surface hardness of HTGN-treated, STS 347 and STS 310S specimens was 250~360 Hv and 270~400 Hv, respectively, depending on the temperature of HTGN. The nitrogen content was analyzed 1.4 wt% and 1.6 wt% at the surface layer of STS 347 and STS 310S steels, respectively. In addition, an improvement in the corrosion resistance of HTGN treated specimens was observed.