Hydrogen Effect Assessment of Fuel Supply Systems for Hydrogen Blended Natural Gas Vehicle

수소-천연가스 혼합연료 차량 연료 공급시스템 수소영향 평가

  • 강승규 (한국가스안전공사 미래연구실) ;
  • 김상렬 (한국산업기술시험원)
  • Received : 2017.11.11
  • Accepted : 2017.12.05
  • Published : 2017.12.31
Download PDF
⟨ Previous Next ⟩

Abstract

This study evaluated hydrogen effect of metal and non-metallic materials used in the hydrogen blended natural gas vehicle. Hydrogen penetrated concentration of 34Cr-Mo steel(850MPa tensile strength) for winter driving conditions was measured 0.0018ppm and summer driving conditions was 5.3ppm. The critical hydrogen concentration of high strength metal used in this study was measured 1.03ppm by CLT. Therefore, 34CrMo steel cas cause problems in the 30% HCNG(25MPa) environment. In case of the test for non-metallic materials, all materials met the criteria of the gas resistance test, but Fluorocarbon Rubber material had a significant change in the volume. So if it is used, extra care is needed.

본 연구는 수소-천연가스 혼합연료 차량에 사용되는 금속 및 비금속재료에 대한 수소영향을 평가하였다. 수소가 30% 혼합된 HCNG연료의 사용 조건(25MPa)에서 34CrMo강은 겨울철 조건에서는 수소 침투량이 0.0018ppm, 여름철 조건에서 5.3ppm으로 측정되었다. 일정하중시험(CLT)에 의한 임계 수소량이 1.03ppm으로 평가되어, 34CrMo 강은 HCNG 사용 조건에서 수소 취화에 의한 취성 파괴를 일으킬 수 있는 것으로 평가된다. 비금속재료에 대한 평가에서는 모든 재료가 시험 기준을 만족하였으나, Fluorocarbon 고무 재질의 경우 체적 변화가 크게 발생하여 사용에 각별한 주의가 요구된다.

Keywords

References

  1. ASTM G142-98, 2004, Standard Test Method for Determination of Susceptibility of Metals to Embrittlement in Hydrogen Containing Environments at High Pressure, High Temperature, or Both, ASTM International.
  2. ISO 11114-4, 2005, Transportable gas cylinders -- Compatibility of cylinder and valve materials with gas contents -- Part4: Test methods for selecting metallic materials resistant to hydrogen embrittlement, ISO International.
  3. ISO/TR15916, 2004, Basic considerations for the safety of hydrogen systems, ISO International.
  4. ANSI NGV1, 2006, Compressed Natural Gas Vehicle Fueling Connection Devices, American National Standard/CSA Standard.
  5. C. San Marchi, B.P. Somerday, 2008, Technical Reference on Hydrogen Compatibility of Materials, Sandia National Lab., Sandia Report SAND 2008-1163.
  6. Kim, J. S., 2009, Effect of Microstructures on the Hydrogne Delayed Fracture Behavior of High Strength Steels, Ph.D. Thesis, Postech.
  7. Park, K. G., Kim, J. H., Jeong, J. H. and Bae, J. M., 2007, Study on hydrogen embrittlement of fuel line for PEMFC, Trans. of the KSME 2007 Spring Conference, pp.1992-1996.
  8. Lee, H. W., Yang, H. T. and Kim S. T., 2002, The Characteristics of the hydrogen embrittlement for the Cr-Mo steels in use of pressure vessel, Trans. of the KSME, Vol.26, No.6, pp.1107-1113.