• The Journal of Korean Academy of Prosthodontics
• /
• v.34 no.1
• /
• pp.143-150
• /
• 1996

The purpose of this study was to evaluate the tensile strength of solder joint between gold alloy and nickel-chromium alloy. The specimens were made with type III gold alloys and Ni-Cr-Be alloy and Degular Lot 2 solder. Eighteen paired specimens were made, and subdivided into three groups. Group I specimens were gold alloy-gold alloy combination, Group II specimens were gold alloy-Ni-Cr alloy combination, Group III specimens were Ni-Cr alloy-Ni-Cr alloy combination. Solder block were made with solder investment(Degussa A,G, Germany) and stored in room temperature for 24 hours. To reduce the formation of metallic oxide and increase wetting properties, flux was used before preheating and soldering procedure. The specimens were preheated at $650^{\circ}C$ and flux were applied again and gas-oxygen torch was used to solder the specimen. All soldered specimens were subjected to a tensile force in the Instron universal testing machine : the crosshead speed was 1 mm/mim. Tensile strength values of three soldered joint groups were 1. Gold alloy-Gold alloy solder joint : $$48.8kg/mm^2$$ 2. Gold alloy-Ni-Cr alloy solder joint : $$30.9kg/mm^2$$ 3. Ni-Cr alloy-Ni-Cr alloy solder joint : $$31.8kg/mm^2$$ The microscopic examination of fracture site showed cohesive and combination fracture modes in gold alloy specimens, but showed all adhesive fracture modes in Ni-Cr alloy containing specimens.

• The Journal of Korean Academy of Prosthodontics
• /
• v.33 no.4
• /
• pp.645-661
• /
• 1995

As the mechanical property of composite resin improved, composite resin has been widely used esthetic dentistry. In the field of esthetic dentistry, the color of prosthetic material is very important. The purpose of this study was to evaluate the color difference of specimens, by the types of alloys and gold electrodeposit. Experimental groups were as follows : Group Prec : Au-Pt alloy with no gold coating and no resin veneer. Group Semi : Pd-Ag alloy with no gold coating and no resin veneer. Group BAse : Ni-Cr alloy with no gold coating and no resin veneer. Group Gsem : Pd-Ag alloy with no gold coating and no resin veneer. Group Gbas : Ni-Cr alloy with no gold coating and no resin veneer. Group PreR : Resin veneer on the Pd-Ag alloy without gold coating. Group SemR : Resin veneer on the Pd-Ag alloy without gold coating. Group GbsR : Resin veneer on the Ni-Cr alloy with gold coating Group BasR : Resin veneer on the Ni-Cr alloy without gold coating. In this study, colors of metal surfaces and veneered resins were evaluated by the CIE $L^{*}a^{*}b$ system. The results obtained were as follows : 1. different alloy types and gold coating make the $L^{*}a^{*}b$ system. 2. The ${\Delta}E^*$ab value between groups semi and Base was less than 1.5 and there was no $a^*$ and $b^*$ value difference between groups Gsem and Gbas 3. The values of $L^*$ and $a^*$ ain groups GsemR and GbasR were so similar that the ${\Delta}E^*$ab value was as small as 0.58. 4. In resin specimens with gold coated semiprecious or base alloys showed yellower and redder deviation than the resin specimens with precious alloy. 5. The ${\Delta}E^*$ab values between goups PreR-GsemR and groups PreR-GbasR were as small as 2.68 and 2.22 respectively.

• Journal of Technologic Dentistry
• /
• v.2 no.1
• /
• pp.11-15
• /
• 1980

This study was aimed at obtaining an ideal gold alloy for dental prothetic. The experiment was on physical characteristics of gold alloy and mixing proportion for proper appliance to living tissues. The most frequently used material in the past for dental prothetic was gold, but recently used are mictures or precious metals and non-precious, which are proved to affect on oral tissues. The experiment was to examine gold alloy over its physical and chemical qualities and to make an ideal type of gold alloy by means of statistic and laboratory research.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.2
• /
• pp.277-295
• /
• 1997

After clinical adjustment of dental casting restoration, re-polishing procedure is recommanded because the smooth gold sureface is lost. But there is the possibility to get more loose contact than that intended by loss of gold alloy according to the kinds of polishing materials and polishing time. Therefore in this study I polished type II gold alloy with 390gm force, 20,000rpm speed, and 8 kinds of gold alloy polishing materials, fabricated by 4 companies and then measured the amount of loss of gold alloy with Surfcorder SEF-30D and observed alloy surfaces polished by 3 brown rubber points with SEM. The amount of loss of gold alloys polished with 8 kinds of polishing materials and the degree of smoothness of gold alloys according to polishing time and polishing materials were compared. The following results were obtained : 1. When the amount of loss of gold alloys polished with 3 kinds of brown rubber point was compared, Alphalex brown point had the most amount of alloy loss, followed in decreasing order by Shofu brown point and Eveflex brown point. There was statistically significant difference in the amount of alloy loss according to polishing materials. 2. When the amount of loss of gold alloys polished with 5 kinds of green rubber point was compared, Shofu green point had the most amount of alloy loss, followed in decreasing order by Alphaflex green point, Dedeco green clasp polisher, and Eveflex green point. There was statistically significant difference in the amount of alloy loss according to polishing materials except Alphaflex green point and Dedeco green clasp polisher. 3. When the amount of loss of gold alloys polished with all kinds of rubber point was compared, there was no significant difference in Eveflex brown point, Alphaflex green point, and Dedeco green clasp polisher. 4. When average amount of alloy loss per 1 revolution by polishing materials was compared, Alphalex brown point had the greatest value as $0.329{\mu}m$ and Shofu supergreen point had the lowest value as $0.022{\mu}m$. 5. When the degree of sureface smoothness of gold alloy polished with 3 kinds of brown rubber point was compared, In Alphalex brown point surface roughness was completely lost after 20 seconds polishing time, in Shofu brown point 30 seconds, in Eveflex brown point 40 seconds. But in every gold alloys fine scratch formed by rubber points was observed. Based on the results of this study, as rubber polishing materials used in polishing of dental casting restoration after clinical adjustment influenced on the tightness of occlusal or proximal contact, we should make dental casting restoration with minimum error through careful laboratory procedure and form very smooth surface of restoration with tripoli and rouge after use of silicone polishing materials.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.3
• /
• pp.297-305
• /
• 2001

Statement of problem. There have been previous studies about instability according to screw material by means of calculating preload in tightening screw or recording of the torque necessary to loosen screw after tightening screw. Purpose. The purpose of this study was to evaluate screw joint stability through the analysis of fitness at the mating thread surfaces between implant and screw after tightening screws made of different materials. Material and methods. In this study, screws were respectively used to secure a cemented abutment to a hexlock implant fixture; teflon coated titanium alloy screw and titanium alloy screw(Steri-Oss), gold-plated gold-palladium alloy screw and titanium alloy screw(Implant Innovation), gold screw and titanium screw(AVANA Dental Implant System). Each abutment screw was secured to the implant with recommended torque value using a digital torque controller. Each screw was again tightened after 10minutes. All samples were cross sectioned with sandpaper and polished. Then samples were evaluated with an scanning electron microscope analysis. Results. In titanium alloy screw, irregular contact and relatively large gap was present at mating thread surface. Also in teflon-coated titanium screw, incomplete seating and only partially contact was present at the mating thread surface. In gold-plated gold-palladium alloy screw, relatively close and tight contact without the presence of large gap was present by existing of gold coating at the mating thread surfaces. In gold alloy screw, relatively small gap between the mating components was seen. Conclusions. This result suggested that gold plated gold-palladium alloy screw and gold alloy screw achieved a greater degree of contact at the mating thread surfaces compared to titanium alloy screw and teflon-coated titanium alloy screw.

• Tribology and Lubricants
• /
• v.24 no.1
• /
• pp.44-48
• /
• 2008

The wear characteristics of the gold alloy dental prosthesis have been investigated. The wear tests were performed by using a pin-on-disk wear tester at room temperature. Vickers hardness and fracture toughness measurement of dental materials were preformed. Microscopic observations on worn surfaces of specimens were conducted by microscope. The friction coefficient of the gold alloy dental prosthesis was investigated according to weight and slinging velocity. The hardness of the gold alloy dental prosthesis were similar and a half of the enamel of natural teeth.

• The Journal of the Korean dental association
• /
• v.14 no.5
• /
• pp.425-427
• /
• 1976

The author observed the reaction of gingval tissues which were implanted with gold, Bosung alloy and copper, the constituents of gold alloy. Pure gold and bosung alloy strips produced slight inflammation but copper had sovere inflammation. Dense fibrous fascile were formed around the gold and Bosung alloy strips on 7th day. When gold and Bosung alloy strips were implanted, eptithelial memberane were occured on 14th day, but copper strips produced eplthelial memberane on 21th day.

• The Journal of the Korean dental association
• /
• v.13 no.11
• /
• pp.1021-1024
• /
• 1975

Bo-sung dental gold alloy was tested an physical properties, tarnish and corrosion restistance. The results were as follows : 1. No differences beween physical properties of Bo-Sung dental gold alloy and American Dental Association Specification No. 5. 2. Tarnish and Corrosion resistance of Bo-Sung dental gold alloy were favorable of dental uses. 3. Bo-Sung dental gold alloys showed equiaxed grain structure in microstructures.

• The Journal of Korean Academy of Prosthodontics
• /
• v.37 no.5
• /
• pp.672-686
• /
• 1999

The purpose of this study was to compare the casting problem and corrosion behavior in two types of HL Hexed abutments of the Steri-Oss system ; gold/plastic coping and gold coping. The anodic Polarization behavior, the galvanic corrosion between abutments and Type III gold alloys, before and after casting were analyzed, and the crevice corrosion of casting samples was analyzed with the CPPT test and the SEM. The results are as follows : 1. Anodic polarization behavior of samples ; Before casting, gold/plastic coping and gold coping was shown to have a similar corrosion pat-terns. Type III casting gold alloy was shown to have a lower corrosion potential and passivation film. Corrosion potential of the case of gold/plastic coping after casting was higher than that of gold coping, but the region of passivation film for gold/plastic coping was smaller than that of gold coping. 2. Galvanic corrosion behavior of samples ; Contact current density between casting gold alloys and gold/plastic before casting was higher than that between gold coping and casting gold alloy Galvanic corrosion of samples after casting was shown to have similar contact current density 3. Crevice corrosion behavior of samples ; Crevice corrosion resistance of casting sample using gold coping was lower than that of cast-ing sample using gold/plastic coping, and a severe corrosion pattern was observed at the abutment-casting gold alloy interface by the SEM.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.5
• /
• pp.372-378
• /
• 2014

PURPOSE. The porcelain fused to gold has been widely used as a restoration both with the natural esthetics of the porcelain and durability and marginal fit of metal casting. However, recently, due to the continuous rise in the price of gold, an interest towards materials to replace gold alloy is getting higher. This study compared the bond strength of porcelain to millingable palladium-silver (Pd-Ag) alloy, with that of 3 conventionally used metal-ceramic alloys. MATERIALS AND METHODS. Four types of metal-ceramic alloys, castable nonprecious nickel-chrome alloy, castable precious metal alloys containing 83% and 32% of gold, and millingable Pd-Ag alloy were used to make metal specimens (n=40). And porcelain was applied on the center area of metal specimen. Three-point bending test was performed with universal testing machine. The bond strength data were analyzed with a one-way ANOVA and post hoc Scheffe's tests (${\alpha}=.05$). RESULTS. The 3-point bending test showed the strongest ($40.42{\pm}5.72$ MPa) metal-ceramic bond in the nonprecious Ni-Cr alloy, followed by millingable Pd-Ag alloy ($37.71{\pm}2.46$ MPa), precious metal alloy containing 83% of gold ($35.89{\pm}1.93$ MPa), and precious metal alloy containing 32% of gold ($34.59{\pm}2.63$ MPa). Nonprecious Ni-Cr alloy and precious metal alloy containing 32% of gold showed significant difference (P<.05). CONCLUSION. The type of metal-ceramic alloys affects the bond strength of porcelain. Every metal-ceramic alloy used in this study showed clinically applicable bond strength with porcelain (25 MPa).