• 한국화재소방학회논문지
• /
• 제25권6호
• /
• pp.146-155
• /
• 2011

본 연구에서는 현장방염처리(방염후처리)가 적용되고 있는 MDF 목재에 국내에서 유통되는 5개사 제품을 MDF 목재에 부착한 방염필름과 MDF 목재(무처리, 비방염필름)에 수성 유성 방염도료로 도포된 시편을 대상으로 현재 시중에서 사용되고 있는 방염처리 방법에 따라 방염성능을 비교하는 실험을 실시하였다. MDF 목재에 5개사의 방염필름을 부착하여 연소 시험한 결과 2개사 제품은 4가지 기준 내에 적합한 값을 나타냈으나 나머지 3개사 제품은 10~40 %의 불합격률을 나타냈다. 방염도료의 특성별로는 유성방염도료가 수성방염도료보다 방염성능 기준 내에서는 더 우수한 것으로 나타났지만 유성방염도료를 도포한 MDF 목재에서 수성방염도료를 도포한 MDF 목재에서 보다 독성지수의 위험등급은 상대적으로 더 높은 위험도를 나타내었다.

• 대한안전경영과학회지
• /
• 제25권1호
• /
• pp.61-66
• /
• 2023

The purpose of this study is to compare and analyze the flame retardant performance of Japanese cypress(Chamaecyparis obtusa) plywood, commonly used in indoor decoration, furniture, and tableware, by treating it with three different fire retardants with different primary ingredients. The experiment was conducted in compliance with Article 31, Paragraph 2 of the Enforcement Decree of the Fire Facilities Installation and Management Act and Articles 4 and 7-2 of the Flame Retardant Performance Standards. After flame time, after glow time, char length, and char area were measured. As a result, first, after flame time was measured at 0 seconds regardless of whether the flame retardant treatment was applied. Second, after glow time was relatively long, measuring 22.7 seconds without treatment, which is likely due to the weak fire resistance and high concentration of carbon monoxide generated by the chemical characteristics of the Japanese cypress itself. Third, it was confirmed that the effects of the primary ingredient, phosphorus, in the flame retardant treatment varied depending on the technological development of the manufacturers of the same species of Japanese cypress plywood. In the future, it is expected that the results of this study will provide fundamental data to select flame retardant treatments that show high flame retardant performance according to the botanical characteristics of the wood.

• Journal of the Korean Wood Science and Technology
• /
• 제42권2호
• /
• pp.157-162
• /
• 2014

This study was conducted to examine the functionality of the fire retardant treated wood. The hygroscopic property, leaching resistance, metal corrosive efficacy and gas toxicity of retardant treated wood were analyzed. Sodium silicate was penetrated to the wood for making fire retardant treated wood. The subsequent treatment agents such as boric acid, ammonium borate, di-ammonium phosphate were treated after sodium silicate treatment due to fixation. As results for the test, the leaching resist was improved by subsequent treatment. The fire retardant combination such as sodium silicate, boric acid and di-ammonium phosphate showed high hygroscopic property, metal corrosive efficacy. The gas toxicity was also satisfied KS standard.

• 한국화재소방학회논문지
• /
• 제16권3호
• /
• pp.48-55
• /
• 2002

본 연구는 용접불티 차단막 개발을 위해 섬유류의 방염처리 후 화재성능 평가를 통해 적정한 방염 처리 방안을 제시하였다. 실험재료는 시중에서 유통되고 있는 섬유류이며, 방염처리는 난연제와 방화도료를 사용하였다. 화재성능 실험은 한국과 일본 기준에 따라 수행하였다. 실험결과 방염처리된 섬유류는 방염 및 난연성능이 충분하였으며, 그들의 난연등급은 A급에서 C급으로 나타났다. 최소산소지수는 방염제로 처리된 모든 시료가 국제기준을 만족하였다. 용접불티 차단막을 수평으로 설치하여 사용할 경우에는 작업대 높이에 관계없이 난연 A급에서 C급의 성능을 가진 제품을, 수직으로 설치할 경우 난연 C급 성능을 갖는 제품을 사용하는 것이 용접불티에 의한 화재확산을 예방할 수 있을 것으로 사료된다.

• Journal of the Korean Wood Science and Technology
• /
• 제36권2호
• /
• pp.1-8
• /
• 2008

This study was performed to evaluate the burning characteristics of wood-based materials and the effect of surface treatment of fire retardant using cone calorimeter. Four types of wood-based materials, such as Plywood, Oriented Strand Board (OSB), Particle Board (PB) and Medium Density Fiberboard (MDF), were tested at a constant heat flux of $50kW/m^2$ to investigate the time to ignition, mass loss rate, heat release rate, effective heat of combustion, etc. In addition, each type of wood-based material was tested at the same heat flux after fire retardant treatment on the surface to evaluate the effect of this treatment on the burning characteristics. The surface treatment of fire retardant, by the amount of $110g/m^2$, delayed the time to ignition almost twice. However, it was indicated that heat release rate, mass loss rate, and effective heat of combustion were not significantly affected by fire retardants treatment for all types of wood-based materials.

• Journal of the Korean Wood Science and Technology
• /
• 제40권5호
• /
• pp.335-342
• /
• 2012

To prepare the eco-friendly fire retardant wood, Japanese red pine (Pinus densiflora), Hemlock (Tsuga heterophylla), and Radiata pine (Pinus radiata) were treated with inorganic chemicals, such as sodium silicate, boric acid, ammonium phosphate, and ammonium borate. Different combination and concentration of those chemicals were impregnated by vacuum/pressure treatment methods. The electron-beam treatment was used to increase the chemical penetration into the wood. The fire performance of the fire retardant treated wood was investigated. The penetration of chemicals into the wood was enhanced after electron beam treatment. Ignition time of the treated wood was the most effectively retarded by sodium silicate, ammonium phosphate, and ammonium borate. The most effective chemical combination was found at 50% sodium silicate and 3% ammonium borate, which satisfied flammability criteria for a fire retardant material in the KS F ISO 5660-1 standards.

• Journal of the Korean Wood Science and Technology
• /
• 제10권3호
• /
• pp.180-188
• /
• 1982

경질섬유판(硬質纖維板)의 내화처리방법(耐火處理方法)의 개선(改善)으로 인한 내화성(耐火性) 및 섬유판(纖維板)의 물리(物理) 및 기계적 성질(性質)을 구명(究明)하고자 시차열분석(示差熱分析) thermogram을 이용(利用)하여 제(第)1 및 제(第)2 인산(燐酸)암모늄에 붕사 및 붕산의 네 가지 내화제(耐火劑)를 각각(各各) 단용 또는 혼합(混合)하여 열압에 의(依)해 내부침투 시켜 처리한 결과(結果)는 다음과 같다. 1) 내화처리(耐火處理) 경질섬유판(硬質纖維板)은 무처리(無處理) 섬유판(纖維板)보다 비중(比重), 흡수율(吸水率), 휨강도(强度)가 증가하였고 물리(物理) 및 기계적성질이 더 개선(改善)되었다. 특히 휨강도(强度)에 있어서 제(第)1 인산(燐酸) 암모늄이 타(他) 내화제(耐火劑)보다 휨강도가 높았고 혼합(混合) 내화제(耐火劑)의 처리 경우(제 1 인산암모늄, 제 2 인산암모늄, 붕사) 충진에 따른 휨강도(强度)는 $30{\times}30cm$에 10gr의 처리가 제일 높았으며 20gr, 30gr의 경우는 이보다 떨어지나 무처리에 비(比)해서는 높은 결과(結果)를 보였다. 2) 함수율(含水率)은 처리와 무처리 사이에 뚜렷한 차(差)가 없으나 30gr의 1충진시 함수율이 약간 높았다. 3) 시차열분석(示差熟分析) thermogram에 의(依)한 내화도(耐火度) 차(差)를 보면 제1인산(第1燐酸) 암모늄과 제2인산(第2燐酸) 암모늄 및 붕사(硼砂) 혼합(混合) 내화제(耐火劑)가 내화성능(耐火性能)이 제일 우수하였으며 충진에 따른 내화효능(耐火效能)은 증가하고 있음을 나타냈다.

• 한국화재소방학회논문지
• /
• 제23권5호
• /
• pp.66-71
• /
• 2009

본 연구에서는 방염처리 단청목재에 대한 방염성능 및 연소가스를 분석하여 그 독성지수에 근거한 유독성을 평가하였다. 시료에 대한 방염처리방법과 시료처리의 환경조건은 방염성능에 크게 영향을 미치지 않았다. 연소가스의 발생량은 방염액을 분무도포한 시료들에서 거의 비슷한 발생량을 보였고 독성지수는 위험등급 III에 해당하는 높은 위험도를 나타내었고, 방염액을 가압함침시킨 시료가 상대적으로 낮은 위험도인 위험등급 II를 나타내었다.

• 한국안전학회지
• /
• 제22권6호
• /
• pp.46-54
• /
• 2007

The purpose of this study was to examines the burning rate of fire retardant treated wood in the cone heater with a one-dimensional integral model. The wood samples used in this study were four species. The species of woods are Redwood, White oak, Douglas fir and Maple. Each sample was nominally 50mm thick and 100mm square. Samples were exposed to a range of incident heat fluxes 10 to $35kW/m^2$ using the cone heater. A one-dimension integral model has been used to predict burning rate, heat of gasification, flame heat fluxes, charring rate and char depth of samples. As a result measurement of mass loss rate, softwoods(Redwood and Douglas fir) has relatively low value than those for hardwoods(White oak and Maple). Average charring rate of woods in case of fire retardant treatment showed reduction effect of 41.29%, 50.00%, 48.18% and 60.82% for Redwood, Douglas fir, White fir and Maple, respectively. Almost all the predictions from integral model showed faster charring than those measured. Average difference between predictions and experimental data was 16%, 9.5% and 11.8% for N, F1 and F2 respectively. Water-soluble fire retardant used in this study find out more effect in hardwood than softwood from the result of measurement of mass loss rate and average charring rate.

• Journal of the Korean Wood Science and Technology
• /
• 제42권4호
• /
• pp.477-482
• /
• 2014

최근 목재이용에 대한 소비자의 요구가 다양화 되면서 목조 주택뿐만 아니라 공공건물 및 놀이시설 등에 고내구성 집성재에 대한 시장수요가 증가할 것으로 예상된다. 본 연구는 국산 낙엽송으로 제조한 구조용 집성재에 적합한 난연처리 기술개발 및 기준을 정립하기 위한 목적으로 수행되었다. 난연처리된 국산 낙엽송 제재목을 이용하여 구조용 집성재를 제조하고 제조 후 집성재에 미치는 영향을 조사하였다. 낙엽송 난연처리재의 경우 구조용 집성재의 강도조건에는 만족하였으나 난연제 처리에 의한 강도적인 감소와 박리 발생 등은 개선될 필요가 있었다. 집성재의 제조 후 주입식 난연처리 혹은 도포식 난연처리 기술 개발이 요구되었다.