• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.297.2-297.2
• /
• 2014

Strong exciton-photon coupling in microcavities have generated an intense research effort since quasiparticles called exciton polaritons are produced and shows interesting phenomena. Most of studies have been done with GaAs based microcavities at cryogenic temperature. Recently, GaN material which has large exciton binding energy and oscillator strength has much attention because strong coupling between photon and exciton could be realized at room temperature. However, fabrication of high quality microcavity using GaN is challengeable due to the large mismatch between the lattice and the thermal expansion coefficient in GaN based distributed Bragg mirror. Here, we observed strong coupling regime of exciton-photon in GaN micro-rods which were grown by metalorganic vapour phase epitaxy (MOCVD) on Si substrate. Owing to the hexagonal cross-section of micro-rod, whispering gallery modes of photon are naturally formed and could be coupled with exciton in GaN. Using angle-resolved micro-photoluminescence measurement, exciton polariton dispersion curves were directly observed from GaN micro-rod. We expect room temperature exciton polariton condensation could be realized in high quality GaN micro-rod.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.3
• /
• pp.127-131
• /
• 2003

High quality zincblende ZnTe(100) epilayers have been grown on semi-insulating $CaAs(100\pm2^{\circ})$substrate by hot-wall epitaxy. To grow high quality ZnTe epilayers, the growth temperature dependence of the surface topography, the growth rate, and the crystalline properties were investigated. From the photoluminescence measured at 10 K, the light hole and heavy hole free exciton emissions splitted by thermal tensile strain were observed and their first excited state emissions were also measured. The low temperature doublet of the heavy hole free exciton is because of the energy separation between longitudinal exciton and transverse exciton due to exciton-polariton coupling.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.2
• /
• pp.197-206
• /
• 1999

The stochiometric mixture of evaporating materials for the $AgInSe_2$single crystal thin films were prepared from horizontal furnace. Using extrapolation method of X-ray diffraction patterns for the $AgInSe_2$polycrystal, it was found tetragonal structure whose lattice constant $a_0$ and $C_0$ were 6.092 $\AA$ and 11.688 $\AA$, respectively. To obtain the single crystal thin films of AgInSe$_2$, the mixed crystal was deposited on thoroughly etched semi-insulator GaAs(100) substrate by HWE system. The source and substrate temperature were fixed to $610^{\circ}C$ and $450^{\circ}C$ respectively, and the thickness of the single thin films was obtained to 3.8 $\mu\textrm{m}$. The crystallization of single crystal thin films was investigated by the photoluminescence (PL) and double crystal X-ray dirrfaction (DCXD). The Hall effect was measured by the method of van der Pauw and carrier density and mobility dependence on temperature were studied. The carrier density and mobility of $AgInSe_2$single crystal thin films deduced from Hall data are $9.58{\times}10^{22} electron/m^3,\; 3.42{\times}10^{-2}m^2/V{\cdot}s$ at 293 K, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $AgInSe_2$single crystal thin film, the spin orbit coupling $\Delta$So and the crystal field splitting $\Delta$Cr were obtained to 0.29 eV and 0.12 eV at 20 K respectively. From PL peaks measured at 20 K, 881.1 nm (1.4071 eV) and 882.4 nm (1.4051 eV) mean $E_x^U$ the upper polariton and $E_x^L$ the lower polariton of the free exciton $(E_x)$, also 884.1 nm (1.402 eV) express $I_2 peak of donor-bound exciton emission and 885.9 nm (1.3995 Ev) emerges $I_1$ peak of acceptor-bound exciton emission. In addition, the peak observed at 887.5 nm (1.3970 eV) was analyzed to be PL peak due to DAP.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.378-378
• /
• 2010

The ZnSe epilayers were grown on the GaAs substrate by hot wall epitaxy. After the ZnSe epilayers treated in the vacuum-, Zn-, and Se-atmosphere, respectively, the defects of the epilayer were investigated by means of the low, temperature photoluminescence measurement. The dominant peaks at 2.7988 eV and 2.7937 eV obtained from the PL spectrum of the as-grown ZnSe epilayer were found to be consistent with the upper and the lower polariton peak of the exciton, $I_2$ ($D^{\circ}$, X), bounded to the neutral donor associated with the Se-vacancy. This donor-impurity binding energy was calculated to be 25.3 meV. The exciton peak, $I_l^d$, at 2.7812 eV was confirmed to be bound to the neutral acceptor corresponded with the Zn-vacancy.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.2
• /
• pp.96-99
• /
• 2000

The photoluminescened experiments at temperature of 10K were carride out for ZnSe epilayers grown by hot-wall epitaxy. The upper and lower polariton peaks of the neutral dound exciton $I_2$($D^{\circ}$,X) for as-grown epilayer have been dominantly observed.For the heat-treatment under Se ambient,the origin of $I_2$ emission is confirmed to be related to Se-vacancy.The extra neutral acceptor bound exciton $I_1$$^d$ is also observed.The ZnSe epilayer shows the self-compensation effect and it is hard to be converted into p-type ZnSe epilayer.However,the photoluminescence spectrum of the annealed sample in Se ambient shows the intense $I_1$$^d$ emission.This indicates that in the annealed ZnSe epilayer,there are many acceptor levels due to the opical p-type converstion. The binding energy of acceptor-impurity is ecaluated to the value of 268meV and the self-activated emission is disappeared by thermal annealing under Se ambient,which indicates the association with Se-vacancy.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.84-84
• /
• 2003

The ZnSe epilayers were grown on the GaAs substrate by hot wall epitaxy. After the ZnSe epilayers treated in the vacuum-, Zn-, and Se-atmosphere, respectively, the defects of the epilayer were investigated by means of the low-temperature photoluminescence measurement. The dominant peaks at 2.7988 eV and 2.7937 eV obtained from the PL spectrum of the as-grown ZnSe epilayer were found to be consistent with the upper and the lower polariton peak of the exciton, I$_2$ (D$^{\circ}$, X), bounded to the neutral donor associated with the Se-vacancy. This donor-impurity binding energy was calculated to be 25.3meV The exciton peak, lid, at 2.7812 eV was confirmed to be bound to the neutral acceptor corresponded with the Zn-vacancy. The I$_1$$\^$d/ peak was dominantly observed in the ZnSe/GaAs:Se epilayer treated in the Se-atmosphere. This Se-atmosphere treatment may convert the ZnSe/GaAs:Se epilayer into the p-type. The SA peak was found to be related to a complex donor like a (V$\sub$se/ - V$\sub$zn/) - V$\sub$zn-/

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.3
• /
• pp.105-110
• /
• 2003

The ZnSe epilayers were grown on the GaAs substrate by hot wall epitaxy. After the ZnSe epilayers treated in the vacuum-, Zn-, and Se-atmosphere, respectively, the defects of the epilayer were investigated by means of the low-temperature photoluminescence measurement. The dominant peaks at 2.7988 eV and 2.7937 eV obtained from the PL spectrum of the as-grown ZnSe epilayer were found to be consistent with the upper and the lower polariton peak of the exciton, $I_{2}$ ($D^{\circ}$, X), bounded to the neutral donor associated with the Se-vacancy. This donor-impurity binding energy was calculated to be 25.3 meV, The exciton peak, $I_{1}^{d}$ at 2.7812 eV was confirmed to be bound to the neutral acceptor corresponded with the Zn-vacancy. The $I_{1}^{d}$ peak was dominantly observed in the ZnSe/GaAs : Se epilayer treated in the Se-atmosphere. This Se-atmosphere treatment may convert the ZnSe/GaAs : Se epilayer into the p-type. The SA peak was found to be related to a complex donor like a $(V_{se}-V_{zn})-V_{zn}$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.11a
• /
• pp.120-123
• /
• 2003

The ZnSe epilayers were grown on the GaAs substrate by hot wall epitaxy. After the ZnSe epilayers treated in the vacuum-, Zn-, and Se-atmosphere, respectively, the defects of the epilayer were investigated by means of the low-temperature photoluminescence measurement. The dominant peaks at 2.7988 eV and 2.7937 eV obtained from the PL spectrum of the as-grown ZnSe epilayer were found to be consistent with the upper and the lower polariton peak of the exciton, $I_2$ ($D^{\circ}$, X), bounded to the neutral donor associated with the Se-vacancy. This donor-impurity binding energy was calculated to be 25.3 meV. The exciton peak, $I_1^d$, at 2.7812 eV was confirmed to be bound to the neutral acceptor corresponded with the Zn-vacancy. The $I_1^d$ peak was dominantly observed in the ZnSe/GaAs:Se epilayer treated in the Se-atmosphere. This Se-atmosphere treatment may convert the ZnSe/GaAs:Se epilayer into the p-type. The SA peak was found to be related to a complex donor like a $(V_{Se}-V_{Zn})-V_{Zn}$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.2
• /
• pp.211-220
• /
• 1998

The stochiometric composition of $AgGaS_2$polycrystal source materials for the single crystal thin films were prepared from horizontal furnace. From the extrapolation method of X-ray diffraction patterns, it was found that the polycrystal $AgGaS_2$has tetragonal structure of which lattice constant $a_0\;and \;c_0$ were 5.756 $\AA$ and 10.305 $\AA$, respectively. $AgGaS_2$single crystal thin film was deposited on throughly etched GaAs(100) substrate from mixed crystal $AgGaS_2$by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $590^{\circ}C$ and $440^{\circ}C$ respectively, and the growth rate of the single crystal thin films was about 0.5 $mu \textrm{m}$/h. The crystallinity of the grown single crystal thin films was investigated by the DCRC (double crystal X-ray diffraction rocking curve). The optical energy gaps were found to be 2.61 eV for $AgGaS_2$single crystal thin films at room temperature. The temperature dependence of the photocurrent peak energy is well explained by the Varshni equation, then the constants in the Varshni equation are given by${\Alpha};=;8.695{\times}10^{-4};eV/K,and;{\beta};=;332;K$. from the photocurrent spectra by illumination of polarized light of the $AgGaS_2$single crystal thin film, we have found that crystal field splitting $\Delta$Cr was 0.28 eV at 20 K. From the PL spectra at 20 K, the peaks corresponding to free and bound excitons and a broad emission band due to D-A pairs are identified. The binding energy of the free excitons are determined to be 0.2676 eV and 0.2430 eV and the dissociation energy of the bound excitons to be 0.4695 eV.