• Journal of the Korea Institute of Military Science and Technology
• /
• v.12 no.5
• /
• pp.660-666
• /
• 2009

Thermoplastic polyurethane elastomer(PU-TPE) and energetic thermoplastic polyurethane Elastomer(E-PU-TPE) were prepared from Hexamethylene diisocyanate(HDI), 1,4-BD/AA ester polyol and glycidyl azide polymer(GAP-2400) as an energetic material by the addition polymerization. The PU-TPE and E-PU-TPE were characterized by FT-IR and GPC. Viscometer, DSC and UTM were used to investigate the viscose behavior with a various solvent, thermal properties and mechanical properties of PU-TPE and E-PU-TPE, which are of potential interest for the development of high performance binder of energetic solid propellants. It was found that $M_w$ of PU-TPE and E-PU-TPEs are over 100,000 and decreased with increase of GAP-2400 contents. $T_m$ and ${\Delta}H$ as thermal properties decreased and also tensile strength and elongation at break as mechanical properties decreased with increase of GAP-2400 contents.

• Applied Chemistry for Engineering
• /
• v.24 no.3
• /
• pp.305-313
• /
• 2013

In this study, we investigated effects of thermal annealing on the thermal properties and microphase separation behaviors of glycidyl azide-based thermoplastic polyurethane elastomers (ETPE). The GAP-based ETPEs were characterized by attenuated total reflectance-fourier transform infrared spectroscopy (ATR-FTIR), differential scanning calorimeter (DSC), dynamic mechanical analysis (DMA), and gel permeation chromatography (GPC). The effects of annealing temperature conditions ($80{\sim}130^{\circ}C$, 1 h or 24 h) on the properties of the ETPEs were investigated. The intensity of azide group absorption peak of ATR-FTIR spectra and the solubility of ETPE for methylene chloride and dimethylformamide solvent decreased after the annealing at $130^{\circ}C$ for 1 h and at $105^{\circ}C$ for 24 h. With increasing the annealing temperature from $80^{\circ}C$ to $110^{\circ}C$, the high temperature rubbery plateau region of storage modulus curves from DMA thermogram for GAP-based ETPEs was extended to the higher temperature.

• Applied Chemistry for Engineering
• /
• v.30 no.6
• /
• pp.673-680
• /
• 2019

GAP or GAP-co-BO based energetic thermoplastic elastomers (ETPEs) were synthesized by changing the hard segment content percent in the range of 30~45% by 5% difference. Thermal and mechanical properties of GAP-co-BO based ETPEs were compared to those of GAP based ETPEs. FT-IR results showed that the capability of forming hydrogen bond increases with increasing the hard segment content in GAP/GAP-co-BO based ETPE, and also the GAP-co-BO based ETPEs are stronger than GAP based ETPEs in the hydrogen bond formation. DSC and DMA results showed that the glass transition temperature (T_g) of GAP based ETPEs increased with the increment of the hard segment content, while the T_g of GAP-co-BO based ETPEs was maintained even the hard segment content increased. The storage modulus at room temperature of the GAP-co-BO based ETPEs was higher than that of the GAP based ETPEs. This was due to the strong phase separation behavior of the hard and soft segment of GAP-co-BO based ETPEs, which further resulted in the stronger breaking strength and lower tensile elongation at break point for GAP-co-BO based ETPE than the GAP based one.