• Journal of the Korean Wood Science and Technology
• /
• v.44 no.5
• /
• pp.750-759
• /
• 2016

The $MnO_2$ electrodeposited on the surface of the carbon nanofiber mats ($MnO_2$-LCNFM) were prepared from electrospun lignin-g-PAN copolymer via heat treatments and subsequent $MnO_2$ electrodeposition method. The resulting $MnO_2$-LCNFM was evaluateed for its potential use in a supercapicitor electrode. The increase of $MnO_2$ electric deposition time was revealed to increase diameter of carbon nanofibers as well as $MnO_2$ content on the surface of carbon nanofiber mats as confirmed by scanning electon microscope (SEM) analysis. The electrochemical properties of $MnO_2$-LCNFM electrodes are evaluated through cyclic voltammetry test. It was shown that $MnO_2$-LCNFM electrode exhibited good electrochemical performance with specific capacitance of $168.0mF{\cdot}cm^{-2}$. The $MnO_2$-LCNFM supercapacitor successfully fabricated using the gel electrolyte ($H_3PO_4$/Polyvinyl alcohol) showed to have the capacitance efficiency of ~90%, and stable behavior during 1,000 charging/discharging cycles.

• Proceedings of the Korean Fiber Society Conference
• /
• 2007.11a
• /
• pp.543-544
• /
• 2007

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.13 no.2
• /
• pp.21-27
• /
• 2014

Recently, various biochip environments have been presented. In this study, a novel transparent film with porous membrane windows, which is an essential component in a co-cultured biochip environment, is fabricated using spin-coating, 3D printing, and electrospinning processes. In detail, a transparent polystyrene film was fabricated by means of the spin-coating process followed bywindow cutting, after which apolycaprolactone-chloroform solution was deposited along the window edge to introduce an adhesion layer between the PS film and the PCL nanofibers. Nanofibers were electrospun into the window region using a direct-write electrospinning method. Consequently, it was demonstrated that the fabricated window film could be used in a co-culture biochip environment.

• Laser Solutions
• /
• v.11 no.4
• /
• pp.1-6
• /
• 2008

This paper describes microscale laser structuring of electrospun(ES) PCL and PET nanofiber meshes. Electrospinning produces non-woven meshes of synthetic or natural materials fibers with diameters ranging from micron down to the nanometer scales that are advantageous for the supporting the growth of the small scale structures. Ultrashort laser found to be effective on the fabrication of engineeredtissue scaffold with minimum heat affect and ultra precision ablation patterns. The affect of energy range for ablation quality was analyzed and ablation characteristics of PCL and PET were compared.

• Journal of the Korean Ceramic Society
• /
• v.43 no.4 s.287
• /
• pp.203-206
• /
• 2006

Polyacrylonitrile (PAN) nanofibers, which are pH-sensitive and exhibit soft actuation as a linear actuator and artificial muscles, were prepared by electrospinning to investigate the effect of viscosity on the morphology of PAN fibers. Experimental results revealed that higher viscosity is critical for the formation of unbeaded nanofibers because surface tension is almost constant throughout the experiment. Uniform, smooth, and continuous fibers with diameters of about 700 nm were achieved for the 10 wt% PAN fibers at a flow rate of 0.5 mL/h and an electric field of 0.875 kV/cm.

• Carbon letters
• /
• v.23
• /
• pp.17-21
• /
• 2017

Polyurethane (PU) nanofibers containing graphene oxide (GO) and Ag doped functionalized reduced graphene oxide (Ag-RGO) were successfully prepared via the electrospinning technique. The uniform distribution of GO sheets along with Ag nanoparticle in the nanofibers was investigated by scanning electron microscopy and the elemental mapping technique. X-ray diffraction and thermal gravimetric analysis verified the presence of GO and Ag in the bicomposite nanofibrous mats. Antibacterial tests against Escherichia coli demonstrated that the addition of GO and Ag-RGO to the PU nanofiber greatly enhanced bactericidal efficiency. Overall, these features of the synthesized nanofibers make them a promising candidate material in the biomedical field for applications such as tissue engineering, wound healing, and drug delivery systems.

• Clean Technology
• /
• v.28 no.3
• /
• pp.210-217
• /
• 2022

Boron(B) is a rare resource used for various purposes such as glass, semiconductor materials, gunpowder, rocket fuel, etc. However, Korea depends entirely on imports for boron. Considering the global boron reserves and its current production rate, boron will be depleted on earth in 50 years. Thus, a process including proper adsorbent materials recovering boron from seawater is demanded. This research proposed carbonized nanofibers prepared from electrospun PAN(polyacrylonitrile) mats as promising materials to adsorb boron in aqueous solution. First, the mechanism of boron adsorption on carbonized nanofibers was investigated by DFT(density functional method)-based molecular modeling and the calculated energetics demonstrated that the boron chemisorption on the nitrogen-doped graphene surface by a two-step dehydration is possible with viable activation energies. Then, the electrospun PAN mats were stabilized in air and then carbonized in an argon atmosphere before being immersed in the boric acid aqueous solution. Analytically, SEM(scanning electron microscopy) and Raman measurements were employed to confirm whether the electrospinning and carbonization of PAN mats proceeded successfully. Then, XPS(X-ray photoelectron spectroscopy) peak analysis showed whether the intended nitrogen-doped carbon nanofiber surface was formed and boron was properly adsorbed on nanofibers. Those results demonstrated that the carbonized nanofibers prepared from electrospun PAN mats could be feasible adsorbents for boron recovery in seawater.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.41 no.1
• /
• pp.41-48
• /
• 2017

Fine polymeric fibers have been gaining interest from the energy harvesting/storage, tissue, and bioengineering industries because of advantages such as the small diameter, high porosity, permeability, and similarities to a natural extracellular matrix. Electrospinning is one of the most popular methods used to fabricate polymeric fibers because it is not as limited in regards to the materials selection, and it does not require expensive or complex equipment. However, electrospun fibers have a severe aerodynamic instability because the small diameter fibers are able to pass through the atmospheric layer when there is a high electric field. As a result, electrospun fibrous mats have serious difficulties with controlling its shape and geometric properties. In this study, a hybrid nano/microfibrous mat is presented that is fabricated using electrospinning with two different solvent-based PCL solutions. This provides control of the fiber diameter, mat porosity, and mechanical properties. Various hybrid fibrous mats were fabricated after an experimental investigation of the effects of solvent on fiber diameter. It was then demonstrated that the mechanical properties and porosity of the fabricated various hybrid mats could be successfully controlled.

• Applied Chemistry for Engineering
• /
• v.24 no.4
• /
• pp.416-422
• /
• 2013

In order to incorporate silver ions into the alginate, silver-alginate was prepared with aqueous solutions of silver nitrate. In the study, the silver-alginate was prepared by blending with poly vinylpyrrolidone solutions and the electrospinning was performed by using this blend solution. Antibacterial properties of silver-alginate/PVP solutions were estimated for Escherichia coli and Staphylococcus aureus by the colony counting test. Electrospinning conditions of silver-alginate/PVP solution were the tip-to-collector distance of 22 cm, the flow rate of the solution at 0.01 mL/min, and the voltage at 26 kV. The form and size of silver-alginate/PVP nanofibers were estimated by SEM and Image J. The average diameter of the electrospun SA5P15 fibers was 124 nm and showed a narrow diameter distribution. The reduction of bacteria for SA5P15 exhibited 99.9% after 24 h.

• Journal of Radiation Industry
• /
• v.5 no.4
• /
• pp.365-370
• /
• 2011

Electrospun nanofibers prepared with synthetic biodegradable polymer have some limitations in regulating adhesion, proliferation, and spreading of cells because of their surface hydrophobicity and absence of cell-interaction. In this study, we functionalized the electrospun poly(L-lactide-co-${\varepsilon}$-caprolactone) (PLCL) nanofibers with acrylic acid (AAc) to modulate their surface hydrophilicity using electron-beam irradiation method and then measured grafting ratio of AAc, water contact angle, and ATR-FTIR of AAc-grafted nanofibers. A grafting ratio of AAc on the nanofibers was increased as irradiation dose and AAc concentration were increased. AAc-grafted nanofibers also have higher wettability than non-modified nanofibers. In conclusion, those surface-modified nanofibers may be an essential candidate to regulate cell attachment in tissue engineering applications.