• Polymer(Korea)
• /
• v.32 no.4
• /
• pp.359-365
• /
• 2008

We have fabricated a novel thermo-responsive nanofibrous surfaces by grafting PIPAAm by electron beam irradiation onto poly(3-hydroxybutyrate-co-3-hydroxyvalerate)(PHBV) nanofibrous mats. The electrospun PHBV nanofiber structures revealed randomly aligned fibers with average diameter of 400 nm. Increased atomic percent of nitrogen was observed on the PIPAAm-grafted PHBV mats after electron beam irradiation determined by ESCA. The amounts of PIPAAm-grafted onto PHBV films were $6.49{\mu}g/cm^2$ determined by ATR-FTIR. The PIPAAm-grafted surfaces exhibited decreasing contact angles by lowering the temperature from 37 to $20^{\circ}C$, while ungrafted PHBV surfaces had negligible contact angle change. This result indicates that PIPAAm surfaces, which are hydrophobic at the higher temperature, became markedly more hydrophilic in response to a temperature reduction due to spontaneous hydration of the surface-grafted PIPAAm. Thermo-responsive nanofibers showed good tissue compatibility. Cultured cells were well detached and recovered from the surfaces by changing culture temperature from 37 to $20^{\circ}C$.

• Polymer(Korea)
• /
• v.32 no.2
• /
• pp.131-137
• /
• 2008

We have fabricated polystyrene (PS) nanofibrous scaffold for hepatocyte culture by electrospinning method and subsequently coated with specific ligand of Poly[N-p-vinylbenzyl-O-$\beta$-D-galactopyranocyl-($1{\rightarrow}4$)-D-gluconamide](PVLA) to enhance hepatocytes attachment. Rat hepatocytes behavior on the PVLA-coated and non-coated PS nanofibrous matrices have been investigated. Electrospun PS nanofiber structures revealed randomly aligned fibers with average diameter of 500 nm. It is observed that PS nanofibrous matrix could incorporate many cells into the interior of the matrix probably due to the suitable pore size. Cell viabilities cultured on PVLA-coated PS nanofibrous mats were maintained for 3 weeks, while it was decreased rapidly on PVLA-coated PS dishes. High hepatic functions especially for albumin secretion and ammonia removal were maintained at least for 2 weeks on nanofibrous mats but rapidly decreased on flat PS dishes. These results indicate that nanofibrous structure enabled 3-D culture with high level of cell-cell contact results in providing cell-cell communications and subsequent long-term maintenance of specific cell functions.

• Applied Chemistry for Engineering
• /
• v.23 no.1
• /
• pp.47-52
• /
• 2012

Porous carbon nanofibers were prepared as a gas sensor electrode to study the $CO_2$ sensing property based on effects of porosity and introduced amine functional groups. Electrospun fibers were obtained by using electrospinning method with polyacrylonitrile precursor and they were treated by the thermal treatment and chemical activation. Amine functional groups were introduced by the liquid state treatment using diethylenetriamine. The specific surface area increased up to $2000m^2/g$ by the chemical activation. The Introduced amine functional group was identified using FT-IR spectroscopy. $CO_2$ gas sensing property was improved as four folds via introduced amine functional groups on the activated carbon nanofiber. In conclusion, the gas sensing property was improved based on the developed porosity by the chemical activation and the chemical attraction of $CO_2$ gas by introduced functional groups.

• Applied Chemistry for Engineering
• /
• v.19 no.4
• /
• pp.413-420
• /
• 2008

Over the past decade, there have been significant advancement in the field of electrospinning area. This study has focused on preparing yarn using polycarbonate (PC) nanofibers including modified multi-walled carbon nanotube (mMWNT) by solution electrospinning process using the mixture of solvents consisting of tretrahydronfuran (THF) and N,N-dimethylformamide (DMF). In order to enhance the dispersion, MWNT was chemically modified. TEM analysis for the prepared PC/mMWNT nanofibers reveals that mMWNT was well-dispersed into the PC nanofiber matrix. Also with increasing contents of mMWNT, thermal stability of PC/mMWNT nanofibers was improved than that of PC nanofibers. Moreover when 3 to 5 wt% of mMWNT was added, the nanofibers showed good electrical properties expecting antistatic effect, ranging 109.1~109.5 ${\Omega}$. It was confirmed that the multi-filament fibers using PC/mMWNT had $60{\sim}100{\mu}m$ in diameter and 4~5 cm in length.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.22 no.6
• /
• pp.274-278
• /
• 2012

$TiO_2$ can be used optically and is applied on many areas such as gas sensor, solar cell and photocatalysis. Electrospun nanofibers have received great interest for development and utilization in some novel applications, such as chemical sensors, dye-sensitized solar cell and photo catalysis. In this study, pure $TiO_2$ and Ga-doped $TiO_2$ nanofibers synthesized by a modified electrospinning method. The Ga doped $TiO_2$ solution is prepared by mixing poly vinyl pyrrolidone, ethyl alcohol, and titanium (IV) isopropoxide. By electrospinning these sols, nanofibers were fabricated. These fibers are heat-treated at $800^{\circ}C$ in air. The prepared pure $TiO_2$ and Ga-doped $TiO_2$ nanofibers samples were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Raman spectroscopy.

• Polymer(Korea)
• /
• v.36 no.1
• /
• pp.47-52
• /
• 2012

Abstract: In this study, PAN/$TiO_2$ fiber mats were fabricated from polyacrylonitrile (PAN) and titanium(IV) butoxide ($Ti(OBu)_4$) by an electrospinning method with various solution concentrations, applied voltages and solution flow rates. The fiber mats were irradiated with an electron beam to induce structural crosslinking and enhance photocatalytic activity. As a result, uniform and bead-free fibers without pits or cracks on surface were obtained at 5 wt% of $Ti(OBu)_4$ solution with 15 kV and 0.02 mL/min flow rate. The PAN/$TiO_2$ fiber mats were irradiated with an electron beam of 1.14 MeV acceleration voltage, 4 mA of current and $1{\times}10^4kGy$. Electron beam irradiation was enhanced the photocatalytic activity of PAN/$TiO_2$ nano fiber mat. The photocatalytic activity of the PAN/$TiO_2$ fiber mat was analyzed by degradation of methylene blue and volatile organic compounds.