• Journal of Surface Science and Engineering
• /
• v.42 no.5
• /
• pp.191-196
• /
• 2009

Nanocrystalline Cu thin films were electrodeposited from sulfate baths and investigated systematically the influences of $Cu^{2+}$ concentration and additives on current efficiency, residual stress, surface morphology, and XRD patterns of electrodeposited Cu film. Current efficiency was nearly 100% at from 0.2M to 1.0 M $Cu^{2+}$ concentration. but it was linearly increased with $Cu^{2+}$ concentration at less than 0.2M. The residual stress was observed in range of 7.9 to 18.4 MPa and tensile stress mode. Dendritic and powdered form was obtained at below 0.1 M. As increased with $Cu^{2+}$ concentration in solution, the main peak in the XRD pattern shifted (111) and (220) from (200). In the other hand, all about 100% current efficiency observed in all additive concentration systems, and residual stress observed in range of 20.4 to 26.3 MPa tensile stress. The condition 5(Ultra make-up - 10 ml/l, Ulta A - 0.5ml/l, Ultr B - 0.5 ml/l) was good surface morphology, and fcc(111) peak in XRD patterns increased with increasing additive concentration.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.12
• /
• pp.2214-2218
• /
• 2007

The effects of bath temperature on electrochemical behavior, alloy composition, crystallographic structure, morphology and the magnetic properties of electrodeposited Co-Pt-W(P) films were investigated. Electrochemical studies show that alloy electrodeposition has been shifted to more positive potentials and the critical time for nucleation decreased as electrolyte temperature increased. As the temperature increased from 40 oC to 80 oC, tungsten content in the deposit increased, while phosphorus content decreased. The films deposited at T = 40 oC exhibited soft magnetic properties. However, electrodeposited at T = 70 oC, the films exhibited hard magnetic properties. It is also demonstrated that higher temperature more than 70 oC could weaken hard magnetic properties. XRD results indicated that the deposits obtained at 50 oC-70 oC showed enhancement of [00.1] P.O. (preferred orientation) with the bath temperature, which resulted in the stronger perpendicular magnetic anisotropy.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 1999.11a
• /
• pp.28-31
• /
• 1999

Carbon fiber/epoxy composites using electrodeposited monomeric and polymeric coupling agents were compared with the dipping and the untreated cases. Treating conditions such as time, concentration and temperature were optimized. Four-fibers embedded micro-composites were prepared for fragmentation test. Interfacial properties of four-fiber composites with different surface treatments were investigated with simultaneous acoustic emission (AE) monitoring. The microfailure mechanisms occurring from fiber break, matrix and interlayer crackings were examined by AE parameters and an optical microscope. It was found that interfacial shear strength (IFSS) of electrodeposited carbon fibers was much higher than the other cases under dry and wet conditions. Well separated and different-shaped AE groups occurs for the untreated and ED treated case, respectively.

• Journal of the Korean Chemical Society
• /
• v.51 no.1
• /
• pp.14-20
• /
• 2007

The anodic dissolution of electrodeposited iron group elements (Fe, Co, Ni) were studied in phthalate buffer solution. The pH dependence of the corrosion potential, the corrosion current and Tafel slope was measured for each element. Based on the electrochemical parameters including Tafel slopes, we proposed the redox mechanism of the corrosion and the passivation. The adsorption of various phthalate species on the electrodeposited iron group elements seemed to be affected the corrosion mechanisms.

• Journal of Surface Science and Engineering
• /
• v.49 no.5
• /
• pp.401-407
• /
• 2016

In this work, effect of zincate treatment of AZ91 Mg alloy on the following electrodeposition of copper was examined in a non-cyanide bath containing pyrophosphate ions in view of surface morphology and adhesion of the electrodeposited copper layer. Without zincate treatment, the electrodeposited copper layer showed very porous structure and poor adhesion. On the other hand, the copper layer electrodeposited on the zincate-treated surface showed dense structure and good adhesion. The dissolution rate of AZ91 Mg alloy after the zincate treatment appeared to decrease about 40 times in the copper pyrophosphate bath, as compared to that of the surface without zincate treatment. The porous morphology and poor adhesion of a copper layer on the AZ91 Mg alloy surface without zincate treatment were attributed to small number of nucleation sites of copper because of rapid dissolution of the magnesium substrate in the pyrophosphate bath. Based on the experimental results, it is concluded that the zincate treatment to form a conducting and protecting layer on the AZ91 Mg alloy surface is essential for successful electrodeposition of a copper layer on AZ91 Mg alloy with good adhesion and dense structure in the copper pyrophosphate bath.

• Journal of the Korean Electrochemical Society
• /
• v.13 no.2
• /
• pp.132-137
• /
• 2010

This study is concerned the electrocatalytic generation of oxygen gas at electrochemically deposited manganese oxide electrode in KOH solution. Manganese oxide nanoparticles electrodeposited onto relatively substrate, e.g glassy carbon, Au, Ti electrode. MnOx is electrodeposited in nanorod structure which cover the overall surface of the substrate. The $\gamma$-MnOOH that is kind of manganese oxide species plays a significant role as a catalytic mediator, which promote 4-electron reduction process. Modified electrodes with electrodeposited manganese oxide structures resulted in significant decrease in the anodic polarization compared with the unmodified electrodes in alkaline media.

• Journal of Surface Science and Engineering
• /
• v.53 no.5
• /
• pp.232-240
• /
• 2020

Cu₂O films as a photocathode for photoelectrochemical water splitting were potentiostatically deposited on FTO glasses. The morphology and composition of the electrodeposited Cu₂O films were adjusted by the applied potentials. The potential-dependent grain size of Cu₂O films was characterized by XRD and SEM analysis. Photoelectrochemical properties of the fabricated Cu₂O photocathodes were investigated with photocurrents as a function of potentials under 1 sun condition of 100mW/㎠. Photocurrents of the electrodeposited Cu₂O films were controlled with the tailored surface morphologies of Cu₂O photocathodes.

• Journal of Surface Science and Engineering
• /
• v.39 no.1
• /
• pp.13-17
• /
• 2006

The effects of an organic additive, naphthalene trisulfonic acid (NTSA), contained in the nickel sulfamate bath on the surface properties of the electrodeposited nickel layer were investigated through electrochemical technique, x-ray diffraction analysis, and microscopic observation. The addition of NTSA facilitated the oxidation process of electrodeposited nickel layer during anodic scan and also increased the hardness and internal stress of the nickel film as the applied current density became higher. It seems that NTSA modulated the deposit structure during electrodeposition and so induced higher distribution of (110) orientation with respect to (200). With the increase of the NTSA in the bath, nickel layer was formed in small grain size, which resulted in enhanced surface evenness and brightness.

• Journal of Surface Science and Engineering
• /
• v.52 no.1
• /
• pp.37-42
• /
• 2019

Electrodeposited zinc layer is widely used as a sacrificial anode for a corrosion protection of steel. In this study, we modified the surface of electrodeposited zinc to have a hydrophobicity, which shows various advanced functionalities, such as anti-corrosion, anti-biofouling, anti-icing and self-cleaning, due to its repellency to liquids. Superhydrophobicity was realized on electrodeposited zinc layer with a hydrothermal treatment, creating nanostructures on the surface, and following Teflon coating. The superhydrophobic surface shows a great repellency to water with high surface tension, while liquid droplets with low surface tension easily adhered on the superhydrophobic surface. However, immiscible lubricant-impregnated superhydrophobic surface shows a great repellency to various liquids, regardless of their surface tension. Therefore, it is expected that the lubricant-impregnated surface can be an alternative of superhydrophobic surface, which have a drawback for some liquids with a low surface tension.

• Korean Journal of Metals and Materials
• /
• v.46 no.7
• /
• pp.420-426
• /
• 2008

By using electrodeposition, we developed a new method to produce Ni/Invar bimetal sheets, which have been used for the present study to investigate the texture evolution during annealing. The grains of electrodeposited Ni were columnar, while those of electrodeposited Fe-Ni alloy were nanocrystalline. These different parts of the bimetal underwent different evolution of textures and microstructures during annealing. In the nanocrystalline Invar, the as-deposited textures were of fiber-type characterized by strong <100>//ND and weak <111>//ND components, and the occurrence of grain growth resulted in the strong development of the <111>//ND fiber texture with the minor <100> // ND components. On the other hand, in the columnar-structured Ni part, the as-deposited <110>//ND fiber texture transformed to the <112>//ND fiber texture due to recrystallization occurring above $550^{\circ}C$. The development of microtextures which took place during annealing in the Ni/Invar interfacial regions was investigated by using the OIM analysis, and discussed in terms of the effect of atomic diffusion across the interfaces.