• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2004년도 춘계학술대회 논문집
• /
• pp.171-176
• /
• 2004

Electro chemical corrosion tests were conducted on two structural steels, SS400 and SM490A, in various solutions with different pH values, All materials showed typical active corrosion behaviors in the solutions, and corrosion potential and current density were measured from the slopes obtained from the Tafel curves using linear polarization method. Corrosion potential increased in the acidic region and then decreased depending on the pH values of the solutions. All materials showed the fast corrosion rate in artificial acid rain(pH=4.7), but the slower corrosion rate was observed in NaOH solution(pH=12.0) for SS400 and in distilled water(pH=7.0) for SM490A, respectively, which is thought to come from the difference in chemical composition of two alloys. Generally homogeneous corrosion occurred in acid rain condition, and almost no corrosion was observed in distilled water in both alloys. NaOH solution produced more corrosion than distilled water, and more corrosion had progressed in SS400 than in SM490A in $3.5\%$ NaCl solution.

• 대한기계학회논문집A
• /
• 제24권3호
• /
• pp.603-612
• /
• 2000

Corrosion characteristics on the 12Cr alloy steel of turbine blade was electro-chemically investigated in 3.5wt% NaCI and 12.7wt% Na2S04 solution, respectively. Electro-chemical polarization test, Huey test and Oxalic acid etching test were previously conducted to estimate corrosion susceptibility of the material. And, using the horizontal corrosion fatigue tester, corrosion fatigue characteristics of 12Cr alloy steel in distilled water, 3.5wt% NaCI solution, and 12.7wt%(1M) Na2S04 solution were also fracture-mechanically estimated and compared their results. Parameter considered was room temperature, 60'C and 90'C. Corrosion fatigue crack length was measured by DC potential difference method.Obtained results are as follows,1) 12Cr alloy steel showed high corrosion rate in 3.5wt% NaCI solution and Na2S04 solution at high tempratue.2) Intergranular corrosion sensitivity of 12 Cr alloy was smaller than austenitic stainless steel.3) Corrosion fatigue crack growth rate in 3.5wt% NaCI and 12.7wt%(IM) Na2S04 solution is entirely higher than in the distilled water, and also increased with the temperature increase.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2014년도 춘계 학술논문 발표대회
• /
• pp.178-179
• /
• 2014

Corrosion is very serious problem in RC structure under ocean environment. There is no enough experiment information using the reinforced geo polymer concrete applied by electo chemical protection system. Three condition, such as tidal zone, submerged zone and crack were simulated to geo polymer specimen. Corrosion rate and natural electrode potential were measured through accelerated test. Anti corrosion property of geo polymer was better than OPC regardless of specimen condition and applied time.

• Journal of Mechanical Science and Technology
• /
• 제18권1호
• /
• pp.114-121
• /
• 2004

In order to investigate the corrosion fatigue characteristics in the weld of multi-pass welded A 106 Gr B steel pipe, corrosion fatigue tests were performed under the various stress ratios and 3.5 wt% NaCl solution at room temperature. The corrosion fatigue characteristic curves were represented using crack closure concept. The obtained results are as follows : when the load frequency is 1.0 Hz, the crack opening point is transited in the region of $K_{max}$=20∼32 MPaㆍ $m^{1}$2/. In the low stress intensity factor range, the crack opening point is higher than that in air. However, in the high stress intensity factor range, it is lower than that in air. In the cases of 0.1 Hz and 0.01 Hz, the crack opening point gradually decreases to $K_{min}$ with $K_{max}$ increase.rease.

• 한국해안해양공학회지
• /
• 제19권4호
• /
• pp.320-328
• /
• 2007

해양콘크리트구조물의 내구성은 일반적으로 해수의 침식 작용과 콘크리트 내부로 침투하는 염분의 확산에 따른 부식에 의해 크게 피해를 입으며, 이러한 내구성 저하는 해양콘크리트구조물의 과다한 유지 관리비를 초래하게 된다. 따라서 해양구조물의 내구성 증진을 위하여 고내구성 재료의 사용이 검토되고 있다. 본 연구에서는, 광물질 혼화재(실리카흄, 플라이애쉬, 고로슬래그미분말)와 표면처리 철근(스테인리스 봉강, 에폭시 코팅) 그리고 부식억제제를 사용한 해양콘크리트의 부식저항 특성을 전기화학적기법을 이용하여 비교 검토하였다. 또한 고내구성 재료사용에 따른 내구성 증진효과를 정량적으로 제안하였다.

• Journal of Advanced Marine Engineering and Technology
• /
• 제23권6호
• /
• pp.806-813
• /
• 1999

The effect of Post-Weld Heat Treatment(PWHT) of SS400 Steel was investigated with parameters such as micro vickers hardness corrosion potential polarization behaviors galvanic current Al anode generating current Al anode weight loss etc. Hardness of each parts(HAZ, BM, WM)by PWHT is lower than that of each parts by Non Post-Weld Heat Treatment(NPWHT) However hardness of WM of HAZ part was the highest among those three parts and HAZ area were also acted as cathode without any case of heat treatment. Potential difference between each three parts by PWHT was also smaller compared to NPWHT. Therefore it is suggested that Corrosion resistance property is increased by PWHT. However both Al anode generating current and anode weight loss was also decreased by PWHT compared to NPWHT when SS400 steel is cathodically protected by Al anode.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2017년도 춘계 학술논문 발표대회
• /
• pp.105-106
• /
• 2017

The metal spray method, one of the surface anti-corrosion methods to prevent the corrosion of the steel material, does little effects on the material, while it can be used on a wider surface. However, metal spraying is used only in a limited environment, and research on the case of using with concrete is lacking. The purpose of this study was to observe the corrosion behavior of steels with metal spray coatings in concrete using electrochemical methods And to evaluate the performance of the method according to the type of metal used in the metal spray. As a result, the Al metal spray coating showed the best performance, because Aluminum is oxidized in the cement mortar and forms alumina oxide film.

• 대한화학회지
• /
• 제55권6호
• /
• pp.1000-1006
• /
• 2011

A systematic study of Knoevenagel reaction and Nazarov cyclization was made on variety of less reactive carbonyl compounds such as ${\beta}$-ketoesters, 1,3-diketones and cyclic active methylene compounds using $Yb(OTf)_3$ as the catalyst. Recycling study confirms reusability of the catalyst without much loss of activity.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2008년도 추계학술대회 초록집
• /
• pp.149-149
• /
• 2008

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.412-412
• /
• 2008

ENIG(Electroless Nickel Immersion Gold)is a surface treatment method that is used most widely at fine pitch's SMT and BGA packaging process. ENIG has good diffusion barrier of Ni against solder and good wettability due to Au finish. But when the discoloration occurred on the Au finish of ENIG, some key characteristics related to the quality and reliability of PCB such as bondability, solderability and electrical flowing of packaging process could be deteriorated. In this paper, we have performed the water dip test ($88^{\circ}C$ purified water) which accelerates the galvanic corrosion of Ni diffused from the Ni-P layer. That is, the excessive oxidation of the Ni layer could result in non-wetting of the solder because the flux may not be able to remove excessive oxides. Though Au discoloration have been reported to be caused by Ni oxides in many literature, it is still open to verify and discuss The microstructures and chemical compositions have been investigated using FE-SEM, TEM, FIB, EDS and XPS. As a result, authors have found that the Au discoloration in ENIG type is severely caused by the oxidation of the Ni and the mechanism of Au discoloration can be confirmed through the experiment result of water dip test.