• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2009.05b
• /
• pp.53-56
• /
• 2009

This study reviewed the characteristics of concrete made of performance improving mixture materials based on KOH as a means to resolve the problems of initial quality reduction that result in concretes with blast furnace slag powder. Summarizing the results, first as the characteristics of fresh concrete, liquidity was found to reduce in general with increased BS substitution ratio. Objective range of liquidity was not satisfied in all mixes according to the use of performance improving mixture materials. Air capacity was satisfied to the objective range in all mixes. As the characteristics of hardened concrete, while compressive strength showed a decreasing trend with increasing BS substitution ratio at early age, increasing trend was shown by the plain with increasing BS substitution ratio at later age. On the other hand, K1 and K2 were only effective among mixture materials at early age, but K1F30 showed excellent strength at both early and later ages.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.10a
• /
• pp.293-296
• /
• 1999

Blast Furnace Slag Powder is potential hydration material, then that is well known to evidently inferior early strength, in fact because of feeble solidify. So this experience is that Blast Furnace Slag Powder as 4000, 6000, 8000$\textrm{cm}^2$/g of blain as 15, 35% of replacement ratio, SO3 is maxed as 0.5, 1.0% of binder ratio for intention to increase of strength.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1990.10a
• /
• pp.101-106
• /
• 1990

To estimate the concrete strength at fresh state is very important problem in quality control. So, this study is designed for analyzing the quality control application of practical use Re-Mi-Con with the early estimation method of concrete strength using the test of solution heat of hydrochloric acid.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.3
• /
• pp.90-97
• /
• 2009

The purpose of the study was to examine basic property at the time of applying cast ('CS' below) and high fineness fine particle cement ('FC' below) as a stimulant to 20% substitution cement mortar of ground granulated blast-furnace slag ('BS' below) to settle a problem that early strength of BS mortar is lowered. The results were as follows. First of all, as a characteristic of fresh mortar, liquidity was reduced as much as BS substitution rate was increased. When substituting CS for BS 20%, it didn't have a large effect regardless of substitution rate. When substituting FC, it was reduced as much as substitution was increased. In the event of compressive strength, it was reduced as much as BS substitution was increased in early age. In age 28, it was somewhat increased by reflection of potential hydraulicity. With regard to improvement of early compressive/bending strength of BS 20% substitution mortar, when substituting CS, in early age, they were a little increased as much as addition rate was increased. When substituting FC, in early and 28 age, they were largely increased as much as substitution rate was increased. To settle a problem that early strength of BS 20% substitution mortar was lowered, CS substitution has a little effect and FC 25% substitution was similar to plain with only OPC. Therefore, when substituting FC 25%, it is expected that its quality will be improved.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2005.11a
• /
• pp.75-78
• /
• 2005

This raper investigates the effect of curing temperature on strength development of concrete incorporating cement kiln dust(CKD) and blast furnace slag (BS) quantitatively. Estimation of compressive strength of concrete was conducted using equivalent age equation and rate constant model. An increasing curing temperature results in an increase in strength at early age, but with the elapse of age, strength development at high curing temperature decreases compared with that at low curing temperature. Especially, the use of 35 has a remarkable strength development at early age and even at later age, high strength is maintained due to accelerated pozzolanic activity resulting from high temperature. Whereas, at low curing temperature, the use of BS leads to a decrease in compressive strength. Accordingly, much attention should be paid to prevent strength loss at low temperature. Based on the strength development estimation using equivalent age equation, good agreements between measured strength and calculated strength are obtained.

• Journal of the Korea Concrete Institute
• /
• v.13 no.2
• /
• pp.139-145
• /
• 2001

One of ways to make high-strength concrete is for the mix contain particles graded down to the finest size : this is achieved by the use of fly ash, silica fume which fills the spaces between the cement particle and between the aggregate and the cement particles. And, the mix needs a sufficient workability. This is achieved by the use of a superplasticizer. This study is to investigate frost resistance of high-strength concrete at early age, with ratio of tensile strength and recovery of compressive strength, when high-strength concrete is placed in cold climates. According to this study, it is necessary to ensure 4 % of air content, 5 kgf/$\textrm{cm}^2$ of tensile strength, at least, for frost resistance of high-strength concrete at early age.

• Journal of the Korea Concrete Institute
• /
• v.28 no.3
• /
• pp.309-316
• /
• 2016

In this study, performance of hardening accelerator types which promote setting and hardening of cement has been reviewed in order to develop early age strength of concrete with compressive strength of 21~27 MPa after examination of strength development of the concrete at early age according to curing temperature and unit cement(binder) content. As results, soluble mineral salt showed better hardening acceleration effect than organic salt in the scope of this study. Also, hydration reaction accelerating effect of $C_3S$ by Soluble mineral salt is effective on development of early age compressive strength and it was shown that the Pt's hydration reaction accelerating effect was the best. Construction duration reduction can be expected by securing compressive strength for prevention of early aged freezing damage in 25hour-curing time under curing temperature at $15^{\circ}C$. Also, it was shown that compressive strength of specimen cured at $5^{\circ}C$ was similar with plain specimen cured at $10^{\circ}C$. Therefore, it is expected that fuel costs and carbon dioxide can be reduced when the same construction duration is considered.

• Nuclear Engineering and Technology
• /
• v.44 no.5
• /
• pp.523-534
• /
• 2012

The objective of this study was to experimentally investigate the effect of heat curing methods on the temperature history and strength development of slab concrete exposed to $-10^{\circ}C$. The goal was to determine proper heat curing methods for the protection of nuclear power plant structures against early-age frost damage under adverse (cold) conditions. Two types of methods were studied: heat insulation alone and in combination with a heating cable. For heat curing with heat insulation alone, either sawdust or a double layer bubble sheet (2-BS) was applied. For curing with a combination of heat insulation and a heating cable, an embedded heating cable was used with either a sawdust cover, a 2-BS cover, or a quadruple layer bubble sheet (4-BS) cover. Seven different slab specimens with dimensions of $1200{\times}600{\times}200$ mm and a design strength of 27 MPa were fabricated and cured at $-10^{\circ}C$ for 7 d. The application of sawdust and 2-BS allowed the concrete temperature to fall below $0^{\circ}C$ within 40 h after exposure to $-10^{\circ}C$, and then, the temperature dropped to $-10^{\circ}C$ and remained there for 7 d owing to insufficient thermal resistance. However, the combination of a heating cable plus sawdust or 2-BS maintained the concrete temperature around $5^{\circ}C$ for 7 d. Moreover, the combination of the heating cable and 4-BS maintained the concrete temperature around $10^{\circ}C$ for 7 d. This was due to the continuous heat supply from the heating cable and the prevention of heat loss by the 4-BS. For maturity development, which is an index of early-age frost damage, the application of heat insulation materials alone did not allow the concrete to meet the minimum maturity required to protect against early-age frost damage after 7 d, owing to poor thermal resistance. However, the combination of the heating cable and the heat insulating materials allowed the concrete to attain the minimum maturity level after just 3 d. In the case of strength development, the heat insulation materials alone were insufficient to achieve the minimum 7-d strength required to prevent early-age frost damage. However, the combination of a heating cable and heat insulating materials met both the minimum 7-d strength and the 28-d design strength owing to the heat supply and thermal resistance. Therefore, it is believed that by combining a heating cable and 4-BS, concrete exposed to $-10^{\circ}C$ can be effectively protected from early-age frost damage and can attain the required 28-d compressive strength.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.609-612
• /
• 2008

Ultra Super Early Strength Cement is a material that satisfies these requirements. early hydration heat however, is significant over regular concrete, thus discretion is advised for thermal cracks in accordance with heat generation when constructing a large-scale structures. In addition, the negative point that it is difficult to achieve required strength in a short period of time following rubbing process while retaining workability, the cement is being used conditionally for engineering material and Ultra Super Early Strength Cement for maintenance material for construction doesn't exist. Magnesia Phosphate Cement, which is currently under studies in overseas uses no extra admixture and has strong points of Ultra Super Early Strength as well as favorable construction-ability and adhesive stability to the prototype concrete. These factors stem recognition that it could be used as maintenance material for construction of diverse applicability. In order to provide necessary data to increase practicality of the magnesia phosphate cement for Ultra Super Early Strength Mortar, the study carried out simulate experiment on member of framework to review field applicability.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.95-101
• /
• 1999

This study was performed to evaluate the characteristics of workability and strength of the concrete containing mineral admixtures such as flyash, blast furnace slag, zeolite powder. As a result, considering their workability and strength, the optimum replacement ratio of them to plain concrete were obtained for each ternary admixture. This increased compressive strength was ascribed to both the closer parkinof fine particles and pozzolan reactivity of powders. This work showed that could be effectively utilized as a blending material without any decrease in the strength of early hydration stage. On the other hand, we found that the compressive strength at early ages ternary ordinary and high strength concrete untill 7 days was small, but that ternary concrete at 28days was highly increased about 31% and 15% extent.