• Nuclear Engineering and Technology
• /
• v.45 no.5
• /
• pp.689-694
• /
• 2013

A duplex stainless steel sheet with 1 wt.% gadolinium was fabricated for a neutron absorbing material with high strength, excellent corrosion resistance, and low cost as well as high neutron absorption capability. The microstructure of the as-cast specimen has typical duplex phases including 31% ferrite and 69% austenite. Main alloy elements like chromium (Cr), nickel (Ni), and gadolinium (Gd) are relatively uniformly distributed in the matrix. Gadolinium rich precipitates were present in the grains and at the grain boundaries. The solution treatment at $1070^{\circ}$ for 50 minutes followed by the hot-rolling above $950^{\circ}$ after keeping the sheet at $1200^{\circ}$ for 1.5 hours are important points of the optimum condition to produce a 6 mm-thick plate without cracking.

• Journal of Ocean Engineering and Technology
• /
• v.23 no.4
• /
• pp.52-57
• /
• 2009

The effect of aging treatment on the microstructure and mechanical properties of super duplex stainless steel with W was investigated. The phase was precipitated mainly at the early stage of aging and a lower aging temperature under $750^{\circ}C$, but the phase was formed after long-term aging treatment between $600^{\circ}C$ and $900^{\circ}C$. The volume fraction of the phase increased with aging temperature up to $750^{\circ}C$ and then decreased up to $900^{\circ}C$. With an increase in the aging time, the volume fraction phase at the early stage of aging increased slightly, and then increased rapidly beyond a certain time. The rapid increase in the tensile strength and hardness and decrease in the elongation and impact toughness were measured with aging temperatures up to $750^{\circ}C$. On the other hand, the tensile strength and hardness decreased slightly, and the elongation and Charpy impact toughness were unchanged with aging temperatures over $750^{\circ}C$. The tensile strength and hardness increased rapidly at the early stage of aging, and then increased slowly beyond a certain time. The elongation and Charpy impact toughness decreased rapidly at the early stage of aging, and then remained unchanged beyond a certain time. The phase that formed at the early stage of aging and the lower aging temperature had a considerable effect on the elongation and Charpy impact toughness of the super duplex stainless steel with W.

• Journal of the Korean Society for Heat Treatment
• /
• v.26 no.6
• /
• pp.293-299
• /
• 2013

A specimen of weld metal was prepared by GTA welding with weld wire of super duplex stainless steel. Aging treatment was conducted for the sample at the temperature range of 700 to $900^{\circ}C$ for 5 to 300 minutes. The effect of volume fraction of ${\sigma}$-phase to intergranular corrosion of weld metal has been investigated and the results were derived as follows. The volume fraction of ${\sigma}$ phase tends to increase with an increase of aging temperature and time and intergranular corrosion of weld metal was increased by an increase of ${\sigma}$ phase. Degree of sensitization representing intergranular corrosion was found to tend to increase with an increase of aging time at 700 to $800^{\circ}C$, while it decreased by an increase of aging time at $900^{\circ}C$.

• Journal of the Korean Society for Heat Treatment
• /
• v.14 no.4
• /
• pp.205-211
• /
• 2001

The characteristics of super duplex stainless steel were investigated on its fibrous structure and dispersed structure. These structures consist of various volume fractions and distributions of the austenite phase that were obtained by changing the heat treatment temperature and cycle. The fibrous structure had higher austenite volume fraction than dispersed structure on the same temperature. As the austenite volume fraction increased in both structures, tensile strength and elongation increased, but hardness decreased. Fatigue life of fibrous structure parallel to rolling direction was shorter than that of perpendicular to rolling direction. Fatigue life of dispersed structure was longer than parallel fibrous structure, and shorter than perpendicular fibrous structure. Fatigue crack propagation rate of fibrous structure was faster than that of dispersed structure.

• Journal of Power System Engineering
• /
• v.18 no.2
• /
• pp.70-76
• /
• 2014

A specimen of weld metal was prepared by GTA welding with weld wire of super duplex stainless steel. Aging treatment was conducted for the sample at the temperature range of 700 to $900^{\circ}C$ for 5 to 300 minutes. The effect of aging temperature and time to pitting corrosion of weld metal has been investigated and the results were derived as follows. The volume fraction of ${\sigma}$ phase tends to increase with an increase of aging temperature and time. Pitting potential Ep representing pitting corrosion was found to tend to decrease with an increase of aging time at 700 to $900^{\circ}C$. And most of the pits formed near the ${\sigma}$-phase in the ferrite and seemed to propagated to austenite.

• Journal of Power System Engineering
• /
• v.17 no.6
• /
• pp.122-129
• /
• 2013

The microstructure and deformation behavior in 22Cr-0.2N micro-duplex stainless steels with various Ni and Mn contents were compared using by OM, TEM, and XRD. The 22Cr-0.2N duplex stainless steel plates were fabricated and hot rolled, followed by annealing treatment at the temperature range of $1,000-1,100^{\circ}C$. All the samples showed the common strain hardening behaviour during the tensile test at a room temperature. The steels tested at the temperatures of $-30^{\circ}C$ or $-50^{\circ}C$ showed a distinct inflection point in the stress-strain curves, which should be resulted from the formation of strain-induced martensite(SIM) of austenite phase. This was confirmed by TEM observations. The onset strain of a inflection point in a stress-strain curve should be depended up the value of $M_d30$. With the decrease of the tensile test temperature, the inflection point appeared earlier, and the strength and fracture strain were higher. The tensile behaviour was discussed from the point of austenite stability of the micro-duplex stainless steels with the different Ni and Mn content.

• Journal of the Korean institute of surface engineering
• /
• v.31 no.6
• /
• pp.334-344
• /
• 1998

Yew coating pmccss t.o form a surface layer ol CrN phasc on mild steel (A81 1020!, AlSI Hi3, 1Cr-0.5Mo steel (ASTM A213 and Nickrl-base superalloy (Inconel 718) was developed. Surlaces of various alloys t,n.ateii by chromizing for the formation ol Cr diffusion layer was subsequently trcaled by plasma nitriding in order t.o form the hard CrS coating layer on the surfaces. This duplex plasma surface tri-atments of chromizing and plasma nitriding have induced a lormation of a duplex-lrcated surfacr hyer of approximat~ls 70-80 $\mu\textrm{m}$thickncss with a iargcly improved microiiardnrss up to approxiniateW 1500Hv(50gf). The main cause for the lage improvment in the surface hardncss is altribilted to [.he fact that CrN and $Fe_xN$ phases are created successfully by ccliromizins and plasma nilriding treatment. High tenipera1,urc wear resislance of the duplex-treated mild steel and HI3 steels at $600^{\circ}C$ was examined. Comparing the duplex-treated specimens with the specimens treated only by chromizing, the rcsults shovmi that, thc wear volume of the duplex-treated mild skcl and 1113 stcel aSt.er a wear test, at $600^{\circ}C$ were reduced hy a Iactor of 8 and 3, respectively. Characteristics of the CrS phase by duplrx treatment were compared with $CrN_x$,/TEX> film by ion plating and the wear behaviors of CrN film lormed by two different nroccsses arc nea.riy identical.

• Journal of Advanced Marine Engineering and Technology
• /
• v.27 no.6
• /
• pp.704-713
• /
• 2003

The effect of partial substitution of tungsten for molybdenum on the microstructure and corrosion resistance in 22Cr-5Ni-3Mo duplex stainless steel(DSS) aging heat treated in a temperature range of 600~$1000^{\circ}C$ has been investigated. Electrochemical tests were carried out for the evaluation of corrosion resistance. Aging treatment had hardly influenced the general corrosion resistance. With the increase of aging time, the pitting corrosion resistance of the DSS had decreased, After aging for 2min at 700~$900^{\circ}C$, the pitting potential of the 3Mo steel decreased remarkably, while that of the W-substituted steel hardly changed. During aging. the intermetallic $\sigma$ and secondary austenite ($\gamma_2$) phases were precipitated. and the pitting corrosion and intergranular corrosion resistance were significantly decreased after aging at 700~$750^{\circ}C$ for 10 h, which could be caused by the $\gamma_2$ formation. The ${\gamma}$$_2$ phase could affect the depletion of molybdenum and chromium in the $\gamma_2/\alpha and \gamma_2/\sigma$ boundaries.

• Corrosion Science and Technology
• /
• v.16 no.6
• /
• pp.278-284
• /
• 2017

The effects of TIG welding and post-treatment procedures on the microstructure and the pitting corrosion resistance of welded lean duplex stainless steel S82441 were investigated. Autogenous TIG welding was used with different amounts of heat input and shielding gases such as Ar, and mixtures of $Ar-N_2$ and Ar-He. The addition of 5% to 15% of nitrogen to argon practically did not affect the level of the pitting corrosion resistance. However, the application of gas mixtures (50% Ar + 50% He) resulted in a significant decrease in pitting corrosion resistance. We found that increased current (200 A and 250 A) led to lower values of CPT of welds compared with welds obtained with 50 A, 100 A and 150 A. In addition, the removal of the weld surface layer (0.2 ~ 0.3 mm thickness) in most cases not only resulted in a significant increase in resistance to the pitting corrosion but also post-treatment of weld, implying that corrosion resistance depended on factors such as surface roughness or the presence of undesirable oxides.

• Corrosion Science and Technology
• /
• v.13 no.2
• /
• pp.48-55
• /
• 2014

Influence of annealing temperature on the microstructure and resistance to pitting corrosion of the hyper duplex stainless steel was investigated in acid and neutral chloride environments. The pitting corrosion resistance is strongly dependent on the microstructure, especially the presence of chromium nitrides ($Cr_2N$), elemental partitioning behavior and volume fraction of ferrite phase and austenite phase. Precipitation of deleterious chromium nitrides reduces the resistance to pitting corrosion due to the formation of Cr-depleted zone. The difference of PREN (Pitting Resistance Equivalent Number) values between the ferrite and austenite phases was the smallest when solution heat-treated at $1060^{\circ}C$. Based on the results of electrochemical tests and critical crevice temperature tests, the optimal annealing temperature is determined as $1060^{\circ}C$.