• The Journal of the Korean dental association
• /
• v.42 no.9 s.424
• /
• pp.632-637
• /
• 2004

• Restorative Dentistry and Endodontics
• /
• v.38 no.4
• /
• pp.241-247
• /
• 2013

Objectives: The aim of this study was to determine the effect of epigallocatechin gallate (EGCG) on the shear bond strength of composite resin to bleached enamel. Materials and Methods: Ninety enamel surfaces of maxillary incisors were randomly divided into 9 groups as follows: G1: control (no bleaching); G2: bleaching; G3: bleaching and storage for seven days; G4 - 6: bleaching and application of 600, 800 and 1,000 ${\mu}mol$ of EGCG-containing solution for 10 minutes, respectively; G7 - 9: bleaching and application of 600, 800 and 1,000 ${\mu}mol$ of EGCG-containing solution for 20 minutes, respectively. The specimens were bleached with 30% hydrogen peroxide gel and a composite resin cylinder was bonded on each specimen using a bonding agent. Shear bond strength of the samples were measured in MPa. Data was analyzed using the two-way ANOVA and Tukey HSD tests (${\alpha}$ = 0.05). Results: The maximum and minimum mean shear bond strength values were observed in G1 and G2, respectively. Time and concentration of EGCG showed no significant effects on bond strength of the groups (p > 0.05). Multiple comparison of groups did not reveal any significant differences between the groups except for G2 and all the other groups (p < 0.05). Conclusions: There is a significant decrease in bond strength of composite resin to enamel immediately after bleaching. A delay of one week before bonding and the use of EGCG increased bond strength of composite resin to bleached enamel.

• Journal of dental hygiene science
• /
• v.9 no.2
• /
• pp.189-195
• /
• 2009

Two diketones, 1,2-phenylpropanedione (PD) and diacetyl (DA) were investigated as new visible light photosensitizers for dental composite resin of bis-GMA in order to improve the photopolymerization effect. The photopolymerization efficiency of bis-GMA composite resin containing PD and DA was studied by IR absorption spectroscopy. And the results were compared with that of camphorquinone (CQ). Relative photopolymerization efficiency of the photosensitizers increased in the order of DA < CQ < PD. Thus. PO is a new visible light photosensitizer for dental composite resin with higher photopolymerization efficiency than that of CQ.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.05a
• /
• pp.255-258
• /
• 2002

Dental chewing masticator, which is an essential device for evaluating the wear of dental resin and the interfacial failure between the filling resin and enamel of tooth used in conservative dentistry, was developed. This dental chewing masticator mimics the chewing motion and loading by adapting DC motor and rotary cam system. Chewing loading of 49N was imposed by computer-displacement control, loadcell, LM guide, and spring system. Extracted tooth was fixed into a holding jig, and this jig was mounted with rubber pad on the $15^{\circ}$inclined surface to consider the lateral movement of periodontal ligament. A water bath was installed for providing the environment of inside mouth and for circulating the $5^{\circ}C-55^{\circ}C$ water to evaluate the effect of hydrothermal cycling on the damage of resin filled teeth during long-term chewing activity.

• Applied Chemistry for Engineering
• /
• v.16 no.1
• /
• pp.117-122
• /
• 2005

The aim of this study was to evaluate the effect of tertiary amine photo-accelerator on the dental properties of visible light-activated, polymeric, dental restorative composites (PDRC) through the measurement of mechanical and esthetic properties. The surface of barium silicate was hydrophobically treated to improve the interfacial behavior with the acrylic resin matrix. Camphorquinone was adopted as a photo-initiator with 0.5 wt% based on the resin matrix. It was discovered that the dental properties of PDRC were primarily dependent on the chemical structure rather than the added content of photo-accelerator.

• Journal of Technologic Dentistry
• /
• v.43 no.1
• /
• pp.13-18
• /
• 2021

Purpose: This study aimed to compare the flexural properties and perform the Weibull analysis of photo-curing three-dimensional (3D) printing resin. Methods: Photo-curing temporary resin (3D polymer) was used as a printing resin. Specimens (65 × 10 × 3.3 ㎣) were prepared following the ISO 20975-1 guidelines and according to the different printing orientations using a digital light processing 3D printer (D2 120; Dentium). The flexural strength (FS), flexural modulus, and work of fracture (WOF) were measured using a universal testing machine (Instron 3344; Instron) at a crosshead speed of 5 mm/min. Results: In this study, the 0° orientation exhibited higher FS and WOF than the 45° orientation. Significant differences were found among the printing orientations (p<0.05). Specimens printed at the 0° orientation were the most accurate. In the Weibull analysis, 0° showed the greatest Weibull modulus (m), which represents a higher reliability. Conclusion: 3D printing should be selected and used by considering flexural properties, size accuracy, and reliability.

• The Journal of Korean Academy of Prosthodontics
• /
• v.40 no.1
• /
• pp.42-52
• /
• 2002

The purpose of this study was to evaluate the bond strength of reline resin to pressure injection type thermoplastic denture base resin. The denture base resins used in this study were $Hi-polycarbonate^{(R)}$(High Dental Co., Japan), Acetal $dental^{(R)}$(Pressingdental s.r.1., Repubblica di San Marine) of thermoplastic resin and Acron $MC^{(R)}$(GC Dental Industrial Co., Japan) of heat cured resin. The reline resins used were Lucitone $199^{(R)}$(Dentsply international Inc., USA), Tokuso $rebase^{(R)}$(Tokuyama Corp., Japan), and $Lightdon-U^{(R)}$(Dreve-Dentamid-Gmbh, Germany). The reline resins are representative of heat-cured, self-cured, and light-cured resin respectively Bond strength was examined by use of a three-point transverse flexural strength test. The results were as follows 1. The bond strength of Lucitone 199 to Acron MC was the highest. 2. The bond strengths of Lucitone 199 and Tokuso rebase to Hi-polycarbonate resulted in a value of approximately one half that of Lucitone 199 to Acron MC and there were no significant differences between these and the bond strength of Tokuso rebase to Acron MC(p<0.05) 3. The bond strengths of reline resins to Acetal dental were lower than those of reline resins to Hi-polycarbonate. 4. For all base resins Lightdon-U showed lower bond strength than the other reline resins.

• The Journal of the Korean dental association
• /
• v.57 no.12
• /
• pp.747-756
• /
• 2019

This paper reviews the adaptation accuracy and mechanical properties of currently used denture processing systems with base resin materials and introduces the latest research on the development of antimicrobial denture base resins. Poly(methyl methacrylate) has been successfully used as a dental denture base resin material by the compress-molding method and heat polymerization for a long time, but recently, new processing techniques, injection molding-methods or fluid-resin technique are also used for fabricating denture base. However, studies indicated that there was no difference between the injectionmolding and the conventional compression-molding method in terms of adaption accuracy of denture base. The fluid-resin fabrication and one injection-molding systems exhibited better adaptation accuracy than the other processing methods. Resin denture bases in the oral cavity may undergo midline fractures due to flexural fatigue from repeated masticatory loading. For those patients, impact resistant denture base resins are recommended to prevent denture fracture during service. Thermoplastic denture base resins can be helpful for patients suffering from allergic reaction to resin monomers with a soft-fit, however, thermoplastic resins with low stiffness can irritate gum tissues and accelerate abnormal alveolar ridge resorption. Moreover, due to low chemical durability in oral cavity, those should be used for a limited period of time.

• Journal of Technologic Dentistry
• /
• v.39 no.1
• /
• pp.17-24
• /
• 2017

Purpose: The purpose of this study was to evaluate the internal fitness of the resin coping that was fabricated by the traditional and Digital manufacturing methods through 3-dimensional analysis. Methods: maxillary right second molar was chosen implant master model. Custom-built impression trays were manufactured. After screwing the pick-up impression coping onto the master cast, impressions were made with silicone impression. The Working model was then made with type IV stone. The coping was fabricated: SLAC group (n=8), APPC group (n=8), LAPC group (n=8) Resin coping data was measured by using a three-dimensional evaluation program. Internal fitness was calculated by RMS (Root Mean Square).It measures mean and Standard Deviation (SD). Results: Three groups are measured $47.11{\pm}(3.08){\mu}m$ total RMS of SLAC group, $48.35({\pm}1.55{\mu}m)$ for total RMS of LAPC group, $43.45{\pm}2.09{\mu}m$ for total RMS of APPC group. Measured value is gradually increased. Followed by autopolymerized pattern resin; Stereolithography resin, Light-activated pattern resin But there were no differences stastically(P>0.321). Conclusion: Evaluation of internal fitness on Resin copings was fabricated by three-ways methods showed that no differences statistically significant and clinically acceptable results.

• Journal of Korean society of Dental Hygiene
• /
• v.19 no.2
• /
• pp.173-181
• /
• 2019

Objectives: The resin infiltration technique is a promising alternative therapy for arresting the early dental caries. However, there are very few reports on the safety and biocompatibility of this technique. We evaluated various properties of resin infiltrant (RI) based on a triethylene glycol dimethacrylate (TEGDMA).The water sorption (Wsp) and water solubility (Wsl) was assessed. Additionally, the cytotoxicity of RI against both animal and human fibroblast cell lines was investigated. Methods: The RI of the $Icon^{(R)}$, the first product developed for resin infiltration, is mainly composed of TEGDMA in the resin matrix. The Wsp and Wsl for the RI were measured in accordance with ISO 4049 specifications. Fourier-transform infrared spectroscopy (FTIR) was used for analyzing the polymerization before and after curing of RI. The cytotoxicity of RI against the mouse fibroblasts (L929) and human gingival fibroblasts (hTERT-hNOF) was evaluated using MTT [3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide] assay and the data were analyzed using one-way analysis of variance. Results: Wsp and Wsl of the RI specimens were $53.37{\mu}g/mm^3$ and $10.6{\mu}g/mm^3$, respectively. FTIR analysis revealed a slightly higher degree of curing with longer irradiation time. The degree of conversion for RI was high (80.9%) after 40 seconds of light curing. There was a significant decrease in the viability of L929 and hTERT-hNOF cells at RI extraction solution concentrations above 50%, respectively, compared to that in the negative control (p< 0.05). Conclusions: Even though the RI exhibited positive effect on the early prevention of dental caries, the clinicians should also consider the toxicity of RI on periodontal tissues.