• 대한치과보철학회지
• /
• 제40권4호
• /
• pp.344-351
• /
• 2002

The purpose of this study is to compare tensile bond strength between Cr-Co alloy and three denture base resins after surface treatment. Following the manufacturer's instructions, 180 bonded specimens were made from three denture base resins (Lucitone 199. Paladent 20. POSS resin) and three surface treatment methods (sandblasting. metal primer. silicoating) 20 samples were made in each group and a half was ther-mocycled 1000 times between $5^{\circ}C$ and $55^{\circ}C$. The tensile bond strength was measured using an Instron with 5mm/min crosshead speed. Data was analyzed with one-way ANOVA, T-test and Duncan test. The results were as follows : 1. Samples with metal primer coating had significantly high tensile bond strength than the other surface treated groups (p<.05). Significantly low tensile bond strength was shown in sand blasted groups (p<.05). 2. No significant difference was observed in metal primer coating groups before and after ther-mocycling (p>.05) 3. Tensile bond strength was decreased in silicoated samples after thermocycling (p<.05). 4. Of the surface treated groups with metal primer, Lucitone 199 had the greatest bond strength and POSS resin and Paladent 20 were followed (p<.05). 5. Of the surface treated groups with silicoating, POSS resin and Lucitone 199 had greater bond strength than Paladent 20 (p<.05).

• 대한치과보철학회지
• /
• 제40권1호
• /
• pp.53-67
• /
• 2002

This study was aimed to analyze the stress distribution of implant and supporting tissue in single tooth implant restoration using Branemark $system^{(R)}$(Nobel Biocare, Gothenberg, Sweden) and Bicon system(Bicon Dental Implants, Boston, MA). Two dimensional finite element analysis model was made at mandibular first premolar area As a crown materials porcelain, ceromer, ADA type III gold alloy were used. Tests have been performed at 25Kgf vertical load on central fossa of crown portion and at 10Kgf load with $45^{\circ}$ lateral direction on cusp inclination. The displacement and stresses of implant and supporting structures were analyzed to investigate the influence of the crown material and the type of implant systems by finite element analysis. The results were obtained as follows : 1. The type of crown material influenced the stress distribution of superstructure, but did not influence that of the supporting alveolar bone. 2. The stress distribution of ceromer and type III gold alloy and porcelain is similar. 3. Stress under lateral load was about twice higher than that of vertical load in all occlusal restorative materials. 4. In Bicon system, stress concentration is similar in supporting bone area but CerOne system generated about 1.5times eater stress more in superstructure material. 5. In Branemark models, if severe occlusal overload is loaded in superstvucture. gold screw or abutment will be fractured or loosened to buffer the occlusal overload but in Bicon models such buffering effect is not expected, so in Bicon model, load can be concentrated in alveolar bone area.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2018년도 춘계학술대회 논문집
• /
• pp.25-25
• /
• 2018

Electron beam melting (EBM) is one of powder based additive manufacturing technology used to produce parts for high geometrical complexity and directly with three-dimensional computer aided design (CAD) model. It is kind of the most promising methods with additive manufacturing for a wide range of medical applications, such as orthopedic, dental implant, and etc. This research has been investigated the microstructure and mechanical properties of as fabricated and hot iso-static pressing (HIP) processed specimens, which are made by an Arcam A1 EBM system. The Ti-6Al-4V titanium alloy powder was used as a material for the 3 dimensional printing specimens. Mechanical properties were conducted with EBM manufacturing and computer numerical control (CNC) machining specimens, respectively. Surface morphological analysis was conducted by scanning electron microscopy (SEM) for their surface, dissected plan, and fractured surface after tensile test. The mechanical properties were included tensile stress-strain and nano-indentation test as a analysis level between nano and macro. As following highlighted results, the stress-strain curves on elastic region were almost similar between as fabricated and HIP processed while the ductile (plastic deformed region) properties were higher with HIP than that of as fabricated processed.

• 구강회복응용과학지
• /
• 제25권1호
• /
• pp.1-12
• /
• 2009

이 논문의 목적은 시멘트 층 내의 응력분포에 대해 금관의 물성과 시멘트의 물성 및 교합력의 방향이 미치는 영향을 이차원 유한요소분석으로 조사하는 것이다. Chamfer 변연을 가지는 23개의 하악 제1대구치 모델을 상정하였다. 금관의 재질은 제 3형 금합금, Ni-Cr 합금, 세라믹, 복합레진 등 4가지이며, 시멘트의 재질은 인산 아연 시멘트와 글라스 아이오노머 시멘트 등 2가지이다. 치축과 평행하게 또는 경사지게 하여 1N 단위로 금관에 하중을 가했다. 시멘트층의 응력은 금관 변연이 다른 곳보다 더 높았다. 치축에 평행한 하중이 치축에 경사진 하중보다 더 높은 응력을 발생시켰다. 경도가 더 큰 금관은 시멘트 층 내에서 더 높은 응력을 나타냈으며, 더 높은 응력은 더 큰 Young's modulus을 나타냈다.

• 한국표면공학회지
• /
• 제38권3호
• /
• pp.126-135
• /
• 2005

SKD 11 steel has been widely used for tools, metallic mold and die for press working because of its favorable mechanical properties such as high toughness and creep strength as well as excellent oxidation resistance. The ion nitrided tool steel containing Mo results in improvement of corrosion resistance, strength at high temperature and pitting resistance, especially in $Cl^-$ contained environment. But the Mo addition causes a disadvantage such as lower oxidation resistance at elevated temperature. In this study, several effects of ion-disadvantage on the oxidation characteristics for SKD 11 steel with various oxidation temperature were investigated. SKD 11 steels were manufactured by using vacuum furnace and solutionized for 1 hr at $1,050^{\circ}C$. Steel surface was ion nitrided at $500^{\circ}C$ for 1 hr and 5 hr by ion nitriding equipment. ion nitrided specimen were investigated by SEM, OM and hardness tester. Oxidation was carried out by using muffle furnace in air at $500^{\circ}C,\;700^{\circ}C\;and\;900^{\circ}C$ for 1hr, respectively. Oxidation behavior of the ion nitrided specimen was investigated by SEM, EDX and surface roughness tester. The conclusions of this study are as follows: It was found that plasma nitriding for 5 hr at $500^{\circ}C$, compared with ion nitriding for 1 hr at $500^{\circ}C$, had a thick nitrided layer and produced a layer with good wear, corrosion resistance and hardness as nitriding time increased. Nitrided SKD 11 alloy for 1hr showed that wear resistance and hardness decreased, whereas surface roughness increased, compared with nitrided SKD 11 alloy for 5 hr. The oxidation surface at $900^{\circ}C$ showed a good corrosion resistance.

• 대한치과보철학회지
• /
• 제38권2호
• /
• pp.169-177
• /
• 2000

The purpose of this study was to compare the retention of complete cast crown over amalgam ores, composite resin cores, and cast gold cores when cemented with three different luting agents. Eighteen core specimens each of amalgam(Bestaloy, Dong Myung, Seoul, Korea), composite resin (Z100, 3M Dental product, st. Paul, Minn) and type IV gold alloy (Ba-4, Heesung Engelhard Corp., Korea) were made in a customized milling stainless steel die. A wax pattern with a loop attached to occlusal surface was made for each core and a type II gold alloy casting was fabricated. The castings which had clinically acceptable marginal fit were used as test samples. The following luting cements were used to cement cast crowns on each core material : (1) zinc phosphate cement (Confi-dental Products Co., USA) (2) glass-ionomer cement (Fuji Plus, GC Industrial Corp., Tokyo, Japan) (3) resin cement (Panavia 21, Kuraray Co., USA). All cements were mixed according to manufacturers' instructions. A static load of 5kg was then applied for 10 minutes on the crowns. All specimens were stored in saline solution for 24 hours at $37^{\circ}C$ and thermocycled for 500 cycles. After storage and cycling, the tensile bond strengths were measured by using a universal testing machine (Instron Corp., Canton, Mass.) at a crosshead speed of 0.5mm/min. The results were as follows 1. The retentive strength of resin cement was the highest of alt three types of cement for resin core (p<0.05). 2. There was no statistical difference among the retentive strengths of three cements for amalgam core (p>0.05). 3. The retentive strength of resin cement was higher than that of zinc phosphate for cast core, but there was no difference between the retentive strength of glass ionomer cement and those of rein and zinc phosphate cement. 4. The retentive strength of the zinc phosphate cement for amalgam core was the highest of all type of cores.

• 대한의용생체공학회:의공학회지
• /
• 제25권5호
• /
• pp.383-389
• /
• 2004

본 연구에서는 치과용 티타늄(CP-Ti)과 Ti-25wt%Pd를 인산염계 실리카$.$알루미나 주형재로 주조 후 SEM/EDS, XRD, XPS를 이용하여 주조시 생성되는 표면반응생성물을 조사하였다. Ti-25wt%Pd는 CP-Ti에 비하여 융점이 현저이 감소하여 주조체의 표면반응이 상대적으로 적게 발생하였다. 또한 인산염계 실리카$.$알루미나 주형재를 소성한 결과 주형재는 $SiO_2$, $Al_2$ $O_3$, P$_2$ $O_{5}$, $Mg_3$(P $O_4$)$_2$, AlP $O_4$, $Mg_2$ $SiO_4$, MgAl$_2$ $O_4$의 성분들로 구성되어 있었으며, 표면반응생성물은 CP-Ti 주조체의 경우 $Ti_{5}$Si$_3$ 와 Ti $O_2$로, Ti-25wt%Pd 주조체의 경우 Ti $O_2$ 와 $SiO_{x}$ 로 구성되어 있었다.

• 대한치과보철학회지
• /
• 제38권4호
• /
• pp.427-437
• /
• 2000

Recently the 2nd generation laboratory composite resins were introduced. Although the mechanical properties of these composite resins have been improved, there were some disadvantages such as discoloration, low abrasion resistance and debonding between metal and resin. The purpose of this study was to evaluate the tensile bond strength between non-pecious dental alloy(verabond) and four veneering reinforced composite resins ; Targis(Ivoclar Co., U.S.A.), Artglass(Kulzer CO., Germany), Sculpture(Jeneric Pentron Co., U.S.A.), and Estonia(Kurary Co., Japan). All test metal specimens were polished with #1,000 SiC paper, and sandblasted with $250{\mu}m$ aluminum oxide. After then. according to manufacturer's instructions metal adhesive primer and veneering resins were applied. All test specimens were divided into two groups. One group was dried in a desiccator at $25^{\circ}C$ for 3 days, the other group was subjected to thermal cycling($2,000{\times}$) in water($5/55^{\circ}C$). Tensile bond strength was measured using Instron Universal Testing machine and the fractured surface was examined under the naked eyes and scanning electron microscope. Within the limitations imposed in this study, the following conclusions can be drawn: 1. In no-thermal cycling groups, there were no significant differences between Estenia and VMK68 but there were significant differences between Targis, Artglass, Sculpture and VMK68(p<0.05). 2. In no-thermal cycling resin groups, the highest tensile bond strength was observed in Estenia and there were significant differences between Estenia and the other resins(p<0.05). 3. Before and after thermal cycling, there were significant differences in tensile bond strength of Targis and Artglass(p<0.05). The tensile bond strength of Artglass was decreased and that of Targis was increased. 4. In no-thermal cycling groups, Artglass showed mixed fracture modes(95%), but after thermal cycling, Artglass showed adhesive fracture modes(75%).

• Journal of Periodontal and Implant Science
• /
• 제36권4호
• /
• pp.849-861
• /
• 2006

타이타늄은 기계적 특성이 우수하고 생체적합성이 뛰어나 의료용 장비의 주 재료로 사용되고 있으며 타이타늄 보다 기계적 특성이 더 우수한 타이타늄 합금들(주로 Ti-6Al-4V와 Ti-6Al-7Nb 합금)도 개발되어 치과와 의료용 임플란트로 사용되고 있다. 그러나 타이타늄 합금 성분들 중 알루미늄 (aluminum)과 바나디움(vanadium)은 인체에 노출되면 세포손상과 신경계에 문제를 일으킬 수 있다. 따라서 인체에 독성이 없으면서 기계적 성질과 생체적합성이 우수한 타이타늄 합금의 개발이 필요하다. 최근 인체에 독성이 없는 성분들이 함유된 새로운 ${\beta}$ - 형태의 타이타늄 합금들이 개발되고 있는데, ${\beta}$ - 타이타늄 합금은 그 기계적 성질이 기존의 ${\alpha}+{\beta}$ 타이타늄 합금에 비해 우수하다고 알려져 있다. 최근 새로운 ${\beta}$ - 타이타늄 합금이 전남대학교 부설 타이타늄 연구소에서 개발되었다. 이 연구는 새로 개발된 ${\beta}$ - 타이타늄 합금의 생채 적합성을 세포 증식도, 알카리 인산 분해 효소 활성과 유전자 증폭을 통해 알아보고자 하였다. 그 결과는 다음과 같다; 1. Titanium-6aluminum-4vanadium (Ti-6Al-4V) 합금 표면애서의 세포 증식율은 Titanium-Titanium8Tantalum-3Niobium (Ti-8Ta-3Nb) 합금과 순수 타이타늄 표면에 비해 유의하게 낮았다(p<0.00l). Ti-8Ta-3Nb 합금 표면에서의 증식도는 순수 타이타늄 표면과 유사하였다. 2. Ti-8Ta-3Nb 합금과 순수 타이타늄에서 배양된 세포이 알카리 인산 분해 효소의 활성도는 Ti-6Al-4V 합금에서의 것보다 유의하게 높았다 (p<0.001). 3. 유전자 증폭 분석 결과, Ti-8Ta-3Nb 합금과 순수 타이타늄에서 collagen type I과 bone sialoprotein mRNA 가 유사한 수준으로 발현되었다. 이상의 결과는 생체 적합성 측면에서 Ti-8Ta-3Nb 합금과 순수 타이타늄의 차이가 없음을 보여주며 따라서 Ti-8Ta-3Nb 합금이 의학 및 치의학 영역에서 새로운 임프란트 재료로 사용될 수 있음을 의미한다.

• 대한치과보철학회지
• /
• 제37권1호
• /
• pp.51-70
• /
• 1999

Dental porcelain is one of the materials of choice for restoration where esthetics is of concern, but has a considerable potentials of wear. The wear of enamel is variable when opposed by different porcelain systems and surface conditions, and the exposed dentine and opaque porcelain due to clinical failure is expected to have high potentials of wear. The purpose of this study was to investigate the wear effects of self-glazed, polished incisal porcelain. polished dentine and opaque porcelain against human enamel in the laboratory by use of a pin-on-disk type wear tester. 4 types of dental porcelain($Vita-{\Omega}$, Ceramco-II, Vintage powder $Vita-{\alpha}$ of In-Ceram system) and type IV gold alloy as cotrol group were used for test specimens. Intact buccal cusps of maxillary premolar were used for enamel specimens, and the cusp converged to a point and was devoid of visible abrasion, caries, decalcification. The upper part was the cusp of a maxillary premolar and the lower part was a porcelain specimen. The enamel wear was deter-mined by weighing the cusp before and after each test. Surface profilometer was used to quantitate wear of the porcelain specimens. Vicker's hardness tester was used to evaluate the surface hardness of test specimens. The SEM was used to evaluate the wear surfaces. The results were as follows : 1 Self-glazed porcelain produced more enamel wear than polished porcelain, especially the enamel wear of $Vita-{\alpha}$ self-glazed porcelain was 3.2 times more than that of other groups. 2. Opaque porcelain produced least porcelain wear, $Vita-{\alpha}$ self-glazed porcelain produce greatest porcelain wear, but there was no statistically significant difference between the groups(p>0.05). 3. The enamel wear of dentine porcelain was 3.8 times more than that of polished inisal porcelain(p<0.05), and the enamel wear of opaque porcelain was 1.9 times more than that of polished inisal porcelain, but there was no statistically significant difference between the groups(p>0.05) 4. Overglazed porcelain produced less enamel wear than self-glazed porcelain, and more enamel wear than polished porcelain, but there was no statistically significant difference between the groups(P>0.05). 5. The hardness number of $Vita-{\Omega}$ dentine and Ceramco-II opaque porcelain was larger, but that of Vintage dentine and $Vita-{\alpha}$ self-glazed porcelain was similar to other groups. 6. Examination of SEM photographs revealed that overglazed porcelain had smoother surface than self-glazed porcelain, and self-glazed porcelain had smoother surface than polished porcelain. Much polishing scratches and larger porosities were observed on the opaque porcelain specimen, and much polishing scratchess and small porosities were observed on the dentine porcelain specimen.