• Macromolecular Research
• /
• v.17 no.5
• /
• pp.339-345
• /
• 2009

The core/shell type structure of the highly crosslinked poly(glycidylmetharylate-co-divinylbenzene) microspheres prepared in the precipitation polymerization in acetonitrile was thoroughly verified by means of swelling, $^1H$ NMR, XPS, TEM and TGA measurements. In the XPS measurement, the higher the GMA content, the higher the oxygen content was observed, implying that the higher content of GMA is observed in the particle surface. The further verification of the core/shell structure of the poly(GMA-co-DVB) particles was carried out using $^1H$ NMR and TEM techniques, resulting in the poly(GMA-co-DVB) particles with the GMA rich-phase and DVB rich-phase. In overall, the poly(GMA-co-DVB) microspheres consist of a highly crosslinked DVB rich-phase in the core and slightly or non-crosslinked GMA rich-phase in the shell part due to the different reaction ratios between two monomers and self-crosslinking density of DVB.

• Journal of the Korean Applied Science and Technology
• /
• v.20 no.4
• /
• pp.332-340
• /
• 2003

Crosslinked poly(methyl methacrylate) particles from 2.4 to $8.1{\mu}m$ in diameter were prepared by homogenized suspension polymerization. The effect of polymerization parameters such as homogenizing speed, homogenizing time and stabilizer concentration on the particle size were examined. Optical diffusion films were prepared with the crosslinked poly(methyl methacrylate) particles. The effect of film thickness, particle size, and particle size distribution on transmittance and haze of optical diffusion film was examined. Transmittance of optical diffusion film increased with increasing particle size and decreasing film thickness. Haze increased with increasing film thickness and decreasing particle size. We also found the existence of an optimum ratio for optical performance when the mixture of small particle and large particle was used.

• Macromolecular Research
• /
• v.12 no.2
• /
• pp.233-239
• /
• 2004

We prepared thermally robust fully crosslinked poly(methyl methacrylate-co-divinyl benzene) ［poly(MMA-co-DVB)］microspheres successfully by precipitation polymerization in the absence of a stabilizing agent. The DVB concentration plays a pivotal role not only in the formation of the individually stable microspheres but also in the polymerization characteristics, including the particle size, the uniformity of size, the polymerization yield, and the thermal properties. The number-average diameter of the microspheres increased linearly, from 0.72 to 2.15 $\mu\textrm{m}$, and the particle size distribution became narrower, by elevating the uniformity from 1.35 to 1.12, as the DVB concentration increased from 20 to 75 mol%. In addition, the yield of the polymerization increased, from 73.4 to 98.6%, as the DVB concentration increased. Since the prepared particles possess fully crosslinked microstructures, no glass transition temperatures were observed, but all the samples prepared with DVB concentrations ranging from 20 to 75 mol% possess enhanced thermal properties. Based on the DSC and TGA data, the thermal stability of the mesospheres prepared by the precipitation polymerization is significantly improved as a result of crosslinking with DVB.

• Journal of Environmental Health Sciences
• /
• v.24 no.3
• /
• pp.11-17
• /
• 1998

Chitin is known as biodegradable natural polymer. In spite of various application of chitin derivatives from waste marine sources, commercial use of chitin has been limited due to high resistance to chemicals and the absense of proper solvents. We chitin prepared through the decalcification, bleaching and deproteination from Protunus trituberculatus shells by change of Hackman's method. Also, Microcrystalline chitin made by hydrolysis that was reduce made of resistance solvents used by dilute hydrochloric acid, ultrasonic and hydrogen peroxide. Crosslinked chitin derivatives were preparaed from chitin with crosslink agents(epichlorohydrin, 1,3-dichloropropanol) follwed by crosslinkage at 6C position. The effects of these parameters on chitin dervatives were invastigated by IR, DSC, XRD, BET, PSA and SEM. SEM analysis showed that both chitin and crosslinked chitin had a particle shaped morphology.

• Macromolecular Research
• /
• v.12 no.5
• /
• pp.534-539
• /
• 2004

Two biopolymers, silk fibroin (SF) and chitosan, were conjugated by tyrosinase (EC 1.14.18.1), a polyphenolic oxidase, to improve their physicochemical properties, such as their thermal properties and morphological stabilities in organic solvents. The crosslinking between SF and chitosan took place mainly through Michael addition reactions. A main reaction between the amino groups in chitosan and o-quinone, the oxidation product of the tyrosyl residue in SF, was confirmed by UV spectroscopy. Measurements of viscosity and light scattering indicated that the crosslinked SF/chitosan conjugate was compact: it had a smaller particle size because of tight bonding forces between the SF and chitosan molecular chains. Thermal decomposition of SF/chitosan conjugates crosslinked by tyrosinase occurred at higher temperatures. The adhesiveness of the SF/chitosan conjugates decreased steadily as the crosslinking reaction progressed. We propose that this new crosslinking method be used for the preparation of silk fibroin/chitosan conjugates using tyrosinase. We expect that SF/chitosan conjugates crosslinked by tyrosinase can be used preferentially in biomedical applications because of its unique properties and non-toxicity.

• Polymer(Korea)
• /
• v.38 no.6
• /
• pp.767-773
• /
• 2014

Rheological and electrical properties of polystyrene (PS)/carbon nanotube (CNT) nanocomposites via coagulated precipitation were investigated. Chemical modification and surfactant wrapping of CNT to improve the dispersion of CNTs may reduce the intrinsic properties of pristine CNT. To avoid this problem, PS and CNTs were dissolved and dispersed in dimethylformamide and then PS/CNT nanocomposites were prepared by the coagulated precipitation of CNT-dispersed PS solution in water. The coagulated precipitation method was highly effective enhancing the electrical conductivity of nanocomposites. Furthermore, the effect of adding poly(styrene-co-divinylbenzene) crosslinked particles to PS matrix on the rheological and electrical properties was investigated. With the addition of the crosslinked particles, the electrical percolation threshold of CNT reduced to 0.25 wt% and electrical conductivity increased further. It is speculated that CNTs in the volume occupied by crosslinked particles helped electrical pathway formation.

• Polymer(Korea)
• /
• v.35 no.1
• /
• pp.66-71
• /
• 2011

With the synthesis of hyper crosslinked polymer particle (HCPP), having microporous structure with hydroxyl functional group, synthesized via polymerization reaction consists of three stepssuspension polymerization, hyper crosslinking by Friedel-Craft catalysis and hydrolysis reaction, the effects of the ratio of each monomer, hyper crosslinking conditions and $CO_2$ supercritical drying on the variations of surface morphology, pore size & distribution and BET surface area of HCPP have been investigated. It was observed that the formation of surface crack or fracture of HCPP was intimately related with the degree of hyper crosslinking reaction between microphase separated domains. And the value of BET surface area of HCPP increased with the increase of reaction temperature, time and the amounts of solvent used in hyper crosslinking step. Moreover, $CO_2$ supercritical drying was proven to be a very effective method for removing stabilizer, unreacted monomers and oligomers from HCPP but needed to add methanol as a co-solvent for efficient removing of residual catalyst.

• Elastomers and Composites
• /
• v.37 no.1
• /
• pp.39-48
• /
• 2002

Linear and crosslinked polyurethane dispersions were synthesized with 2,4-toluene diisocyanate, dimethylol propionic acid, polyoxypropylene glycol and polyoxypropylene glycerin. The structures of these polyurethanes were characterized by $^1H-NMR$ and FT-IR and the properties were measured with DSC, TGA, Instron and AFM etc. In case of linear polyurethane dispersion, the particle size, viscosity and glass transition temperature of polyurethanes increased with higher molecular weight of polyol and the degree of crosslinking. The crosslinked polyurethanes which contains more than 15% of polyoxypropyleneglycerin didn't from dispersion, when mixtures by polyoxypropyleneglycol and polyoxypropyleneglycerin were used as polyols. Thus, we synthesized crosslinked polyurethanes with 5%, 8%, 13% and 15% weight percents of polyoxypropylene glycerin as polyol mixtures.

• Economic and Environmental Geology
• /
• v.55 no.4
• /
• pp.367-376
• /
• 2022

One of biopolymer, β-glucan (BG) chains were crosslinked by citric acid under the heating condition for the adsorption of Pb and Cu ions in the aqueous solution. The variation of functional groups on BG itself and crosslinked β-glucan (CBG) with their surface adsorption characteristics were investigated by FTIR and SEM-EDX. Adsorption kinetic results showed that adsorption of Pb and Cu onto the CBG followed the pseudo-second-order kinetic model and intra-particle diffusion model. The Langmuir adsorption model was depicted better adsorption characteristics than the Freundlich model. The adsorption capacities of Pb and Cu onto the CBG estimated by the Langmuir model were 59.70 and 23.44 mg/g, respectively. This study suggested that CBG may act as an eco-friendly adsorbent for the adsorption of Pb and Cu in the aqueous solution.

• Proceeding of EDISON Challenge
• /
• 2017.03a
• /
• pp.39-45
• /
• 2017

We present a Brownian dynamics simulation study on the diffusion of a neutral tracer particle confined in a regularly crosslinked polymer network, especially, when the tracer size is comparable to the mesh size of the network. Polymer networks with different mesh sizes are prepared and compressed to the extent that the total polymer densities become the same. Irrespective of the network mesh size, the tracer diffusion in the networks is slowed down, showing the subdiffusion on intermediate time scales followed by the normal diffusion at long times. However, the confinement effect on the tracer diffusion becomes more significant when network strands are tightly stretched with smaller mesh size. The time scales of dynamic transitions are analyzed in terms of the probability distribution of time-correlated particle displacements.