• Computers and Concrete
• /
• v.11 no.1
• /
• pp.21-37
• /
• 2013

High-performance concrete (HPC) usually has higher paste and lower coarse aggregate volumes than normal concrete. The lower aggregate content of HPC can affect the shear capacity of concrete members due to the formation of smooth fractured surfaces and the subsequent development of weak interface shear transfer. Therefore, an experimental investigation was conducted to study the shear strength and cracking behavior of full-scale reinforced beams made with low-cement-content high-performance concrete (LcHPC) as well as conventional HPC. A total of fourteen flexural reinforced concrete (RC) beams without shear reinforcements were tested under a two-point load until shear failure occurred. The primary design variables included the cement content, the shear span to effective depth ratio (a/d), and the tensile steel ratio (${\rho}_w$). The results indicate that LcHPC beams show comparable behaviors in crack and ultimate shear strength as compared with conventional HPC beams. Overall, the shear strength of LcHPC beams was found to be larger than that of corresponding HPC beams, particularly for an a/d value of 1.5. In addition, the crack and ultimate shear strength increased as a/d decreased or ${\rho}_w$ increased for both LcHPC beams and HPC beams. This investigation established that LcHPC is recommendable for structural concrete applications.

• The Journal of the Korea Contents Association
• /
• v.16 no.10
• /
• pp.467-476
• /
• 2016

With the development of information technology, Small office Home office(SOHO) is picking up. SOHO generally uses Wi-Fi. The wireless LAN environment using 802.11 protocol is easily affected by DoS attacks. To deal with these threats, there is Wireless Intrusion Detection System(WIDS). However, legacy products of WIDS cannot be easily used by SOHO because they are expensive and require management burden. In this paper, Smart WIDS for SOHO is proposed and implemented on Raspberry Pi2. And, it provides the interface for attack detection notice to android smart phone. Smart WIDS detects Masquerading DoS and Resource Depletion DoS based on IEEE 802.11 so that we notice the attempt of cracking Pre-shared Key(PSK), Man-In-The-Middle(MITM), and service failure.

• Resources Recycling
• /
• v.24 no.3
• /
• pp.66-75
• /
• 2015

The flexural performance of amorphous steel fibers having environmental and economy benefits due to relatively short manufacturing process were evaluated as well as that of hooked steel fibers by varing fiber length and volume fraction. Fiber lengths were 10 mm, 20 mm, 30 mm and fiber volume fractions were varied from 0.3% to 1.2%. Test results with flexural performance showed that mixing design needs to be careful because of relatively high volume of amorphous steel fiber compared to hooked steel fibers. High flexural strength was obtained from both longer fiber length and higher volume fraction. Residual strength and toughness of amorphous steel fiber were similar to that of hooked steel fiber, even though rapid dropping of applied load right after concrete matrix breaking. It can be judged that relatively high ability of energy dissipation around first cracking area relatively overcome rapid dropping of loading.

• International Journal of Highway Engineering
• /
• v.7 no.4 s.26
• /
• pp.69-77
• /
• 2005

Joint spacing is a potent influence in increasing the long term performance of jointed concrete pavement slabs through the control of tensile stress, sealant failure and Load Transfer Efficiency (LTE). Internal Joint Spacing is an empirical and fixed method therefore this study will present the optimum joint spacing considerations depending on various climactic conditions. Calculating the optimum joint spacing eliminates random cracking due to the effect of the environmental loads such as the early behavior of drying shrinkage and heat hydration. Optimum joint spacing is calculated so as not to cause pavement distress by the deterioration of LTE by long term pavement movement. This study shows that the provisional joint spacing is 6-8m. Pavement Distress Prediction Models show that pavement distress has no effect on joint spacing of 8m.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.9 no.1
• /
• pp.40-46
• /
• 1985

Some problems such as toughness decrement and stess relief cracking (SRC), many occur when post weld heat treatment (PWHT) is applied to remove residual stress adn hydrogen. In this paper PWHT was carried out under the stress of 0, 98, 196 and 294 MPa (0, 10, 20 and 30kgf/mm$^{2}$ each) to simulate residual stress in HAZ of Cr-Mo steel. The effect of applied stress during PWHT on fracture toughness was evaluated by COD fracture toughness test, micro-hardnes test and observation of SEM. The experimental results are as follows; (1) Fracture toughness of weld HAZ was improved by PWHT, but it decreased as heat treated under the stress. (2)Hardness ratio under the stress of 294MPa (30kg/mm$^{2}$) was lower and fracture toughness was decreased than that of the no stress. (3) Applied stress in weld HAZ during PWHT assisted precipitation of over saturated alloying elements in the structure, so fracture surface at the stress of 294MPa (30kg/mm$_{2}$) appeared the grain boundary failure possibly one of the reasons for PWHT embrittlenment.

• The Journal of Korean Academy of Prosthodontics
• /
• v.46 no.3
• /
• pp.298-306
• /
• 2008

STATEMENT OF PROBLEM: Effect of surface treatment of ceramic under loading does not appear to have been investigated. PURPOSE: The aim of this study was to investigate the effect of surface treatment of esthetic ceramic, which is performed to increase the bonding strength, on the fracture stress under controlled cyclic loading condition. MATERIAL AND METHODS: Sixty 1.0 mm-thick specimens were made from Mark II Vitablocs (Vita Zahnfabrik, Germany) and divided into 3 groups: polished (control), sandblasted, and etched. Specimens of each group were bonded to a dentin analog material base including micro-channels to facilitate the flow of water to the bonding interface. Bonded ceramics were cyclically loaded with a flat-end piston in the water (500,000 cycles, 15Hz). Following completion of cyclic loading, specimens were examined for subsurface crack formation and subsequent stress was determined and loaded to next specimen by the staircase method according to the crack existence. RESULTS: There were significant differences of mean fatigue limit in the sandblasted (222.86 ${\pm}$ 23.42 N) and etched group (222.86 ${\pm}$ 14.16 N) when compared to polished group (251.43 ${\pm}$ 10.6 N) (P<.05; Wald-type pair-wise comparison and post hoc Bonferroni test). Of cracked specimens, surface treated group showed longer crack propagation after 24 hours. All failures originated from the radial cracking without cone crack. Fracture resistance of this study was very low and comparable to failure load in the oral cavity. CONCLUSION: Well controlled cyclic loading could induce clinically relevant cracks and fracture resistance of Mark II ceramic was relatively low applicable only to anterior restorations. Surface treatment of inner surface of feldspathic porcelain in the matsicatory area could influence lifetime of restorations.

• Journal of the Korean Ceramic Society
• /
• v.42 no.8 s.279
• /
• pp.554-560
• /
• 2005

The engineering ceramic needs the properties of high strength, hardness, corrosion-resistance and heat-resistance in order to withstand thermal shock or applied nonuniform stresses without failure. The densely coated porous ceramics can be used for machine component, electromagnetic component, bio-system component and energy-system component by their high-performances from superior coating properties and light-weight characteristics due to the structure including pore by itself. In this study we controlled the porosity of silica and alumina, $8.2\~25.4\%$ and $23.4\~36.0\%$, respectively, by the control of sintering temperature and starting powder size. We made bilayer structures, consisting of a transparent glass coating layer bonded to a thick substrate of different porous ceramics by a thin layer of epoxy adhesive, facilitated observations of crack initiation and propagation. The elastic modulus mismatch could be controlled using different porous ceramics as the substrate layer. Then we applied 150 N force using WC sphere with a radius of 3.18 mm by Hertzian indentation. As a result, the crack initiation in the coating layer was delayed at lower porosity in the substrate layer, and the damage in the coating layer was relatively smaller at the bilayer structure coated on higher elastic substrate.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.1
• /
• pp.10-18
• /
• 2016

RC(Reinfored Concrete) structures exposed to carbonation in urban city have durability degradation with extended service life and cracks in concrete causes a local accelerated carbonation. In the present work, crack effect on carbonation depth is investigated and the service life of RC structure is evaluated considering cracks from early age and time-dependent cracks based on the previous field investigation. DFP(Durability Failure Probability), safety index, and the related service life are calculated considering the time to crack width reaches to maximum crack width(0.3mm). The results with time effect on crack width show lower DFP and longer service life, which seems to be reasonable compared with conservative results from crack effect from initial stage. Furthermore, crack effect is evaluated to be insignificant on DFP and service life. The technique with time-dependent crack effect on carbonation can be effectively used for RC structure containing cracking in use.

• Computers and Concrete
• /
• v.22 no.1
• /
• pp.27-37
• /
• 2018

Reinforced concrete structures are widely used in civil engineering projects around the world in different designs. Due to the great evolution in computational equipment and numerical methods, structural analysis has become more and more reliable, and in turn more closely approximates reality. Thus among the many numerical methods used to carry out these types of analyses, the finite element method has been highlighted as an optimized tool option, combined with the non-linear and linear analysis techniques of structures. In this paper, the behavior of reinforced concrete beams was analyzed in two different configurations: i) with welding and ii) conventionally lashed stirrups using annealed wire. The structures were subjected to normal and tangential forces up to the limit of their bending resistance capacities to observe the cracking process and growth of the concrete structure. This study was undertaken to evaluate the effectiveness of welded wire fabric as shear reinforcement in concrete prismatic beams under static loading conditions. Experimental analysis was carried out in order compare the maximum load of both configurations, the experimental load-time profile applied in the first configuration was used to reproduce the same loading conditions in the numerical simulations. Thus, comparisons between the numerical and experimental results of the welded frame beam show that the proposed model can estimate the concrete strength and failure behavior accurately.

• Journal of the Korea Concrete Institute
• /
• v.25 no.6
• /
• pp.641-648
• /
• 2013

Current design codes regulate the minimum torsional reinforcement requirement for reinforced concrete members to prevent their brittle failure. The minimum torsional reinforcement ratio specified in the current national code and ACI318-11, however, have problems in the minimum longitudinal reinforcement ratio for torsion, the equilibrium condition in space truss model, and a marginal strength, etc. Thus, in order to overcome such shortcomings, this study presents a rational equation for minimum torsional reinforcement ratio that can provide a sufficient margin of safety in design. The minimum torsional reinforcement ratio proposed in this study was compared to the test results available in literature, and it was confirmed that it gave a proper margin of safety for all specimens studied in this paper.