• Journal of the Korean Society of Industry Convergence
• /
• v.27 no.4_2
• /
• pp.973-980
• /
• 2024

Dependence of dynamic fracture path on loading velocity was observed from experimental results based on the three point bending fracture in cast iron. In this study, 3D and 2D numerical simulations are used to evaluate singular stress fields near crack tip and fracture mechanics parameters. Moving finite element technique, 2D and 3D Delauney automatic mesh generation and contact-noncontact evaluation is introduced into the numerical method. Dynamic fracture thoughness is decreased with increase of impact loading velocity. Fracture mode-ratio corresponds to initial kink angle of fracture path. The numerical result shows that the maximum hoop stress criterion cannot be applied to dynamic fracture of cast iron.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1997.04a
• /
• pp.69-73
• /
• 1997

Microwave Plasma assisted CVD (Chemical Vapor Deposition) and DC Plasma CVD were used to prepare thin and thick diamond film, respectively. Diamond coated silicon nitride and fiee standing diamond thick film were eroded by silicon carbide particles. The velocity of the solid particle was about 220m/sec. Phase transformation and the other crack formation were investigated by using Raman spectroscopy and microscopy.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.10a
• /
• pp.167-170
• /
• 2004

In order to investigate the impact behaviors of 3-D braided glass/epoxy composites, the energy profiles and damage area were compared to the laminates of similar volume fraction and composition. The energy profiles showed different characteristics from each other which indicates they have distict energy absorption mechanisms. The image analysis on the damage projections visualized the crack propagation paths along the fiber direction.

• Structural Engineering and Mechanics
• /
• v.60 no.2
• /
• pp.225-235
• /
• 2016

Fluid impact tests on plates containing mesh reinforcement and polypropylene fibers were modeled and simulated using explicit finite element analysis software, LS-DYNA. The scabbing dimensions obtained by the experiments and the simulations were compared and crack formations were matched. The objective was to test the accuracy and fidelity of the model and to confirm that damage caused by fluid impact on the plates can be estimated with a reasonable accuracy over a wide range of impact velocity.

• Proceedings of the Korean Nuclear Society Conference
• /
• 2005.10a
• /
• pp.324-325
• /
• 2005

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1995.04a
• /
• pp.578-584
• /
• 1995

This investigation evaluates dynamic fracture characteristics of two alloy steels (STD-11 and STS-3 and a gray cast iron (GG-30). The dynamic crack initiation fracture toughness and some of the dynamic fracturing characteristics were evaluated by using the instrumented Charpy impact testing procedures. It was found from experimental results that inertia force strongly depends on impact velocity. The duration of inertia force was constant regardless of impact velocities in steel specimens.

• Journal of Mechanical Science and Technology
• /
• v.16 no.2
• /
• pp.165-174
• /
• 2002

In the present study, interfacial cracks between an isotropic and orthotropic material, subjected to static far field tensile loading are analyzed using the technique of photoelasticity. The fracture parameters are extracted from the full-field isochromatic data and the same are compared with that obtained using boundary collocation method. Dynamic photoelasticity combined with high-speed digital photography is employed for capturing the isochromatics in the case of propagating interfacial cracks. The normalized stress intensity factors for static cracks are greate. when ${\alpha}$: 90$^{\circ}$(fibers perpendicular to the interface) than when ${\alpha}$=0$^{\circ}$(fibers parallel to the interface), and those when ${\alpha}$=90$^{\circ}$are similar to ones of isotropic material. The dynamic stress intensity factors for interfacial propagating cracks are greater when ${\alpha}$=0$^{\circ}$ than ${\alpha}$=90$^{\circ}$. For the velocity ranges (0.1 < C/C$\sub$s1/<0.7) observed in this study, the complex dynamic stress intensity factor │K$\sub$D/│increases with crack speed c, however, the rate of increase of │K$\sub$D/│with crack speed is not as drastic as that reported for homogeneous materials.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.7 no.4
• /
• pp.191-199
• /
• 2003

The inelastic response of many structural steel and reinforced concrete structures subject to extreme loadings can be characterized by elastoplastic behaviors. Although excursion beyond the elastic range is usually not permitted under normal conditions of service, the extent of permanent damage a structure may sustain when subjected to extreme conditions, such as severe blast or earthquake loading, is frequently of interest to the engineer. A blast is usually the result of an explosion defined as a "sudden expansion". This paper discusses the basic concept that defines blast loadings on structures and corresponding elastoplastic structural response (displacement, velocity, and acceleration) and try to explain a crack propagation of concrete in sudden expansion. According to nonlinear finite element analysis, the crack forms of static and dynamic states displayed different in RC structural members. This paper also provides useful data for the dynamic fracture analysis of RC frame structures.

• Nuclear Engineering and Technology
• /
• v.50 no.7
• /
• pp.1138-1147
• /
• 2018

Delayed hydride cracking (DHC) is an important failure mechanism for Zircaloy tubes in the demanding environment of nuclear reactors. The threshold stress intensity factor, $K_{IH}$, and critical hydride length, $l_C$, are important parameters to evaluate DHC. Theoretical models of them are developed for Zircaloy tubes undergoing non-homogenous temperature loading, with new stress distributions ahead of the crack tip and thermal stresses involved. A new stress distribution in the plastic zone ahead of the crack tip is proposed according to the fracture mechanics theory of second-order estimate of plastic zone size. The developed models with fewer fitting parameters are validated with the experimental results for $K_{IH}$ and $l_C$. The research results for radial cracking cases indicate that a better agreement for $K_{IH}$ can be achieved; the negative axial thermal stresses can lessen $K_{IH}$ and enlarge the critical hydride length, so its effect should be considered in the safety evaluation and constraint design for fuel rods; the critical hydride length $l_C$ changes slightly in a certain range of stress intensity factors, which interprets the phenomenon that the DHC velocity varies slowly in the steady crack growth stage. Besides, the sensitivity analysis of model parameters demonstrates that an increase in yield strength of zircaloy will result in a decrease in the critical hydride length $l_C$, and $K_{IH}$ will firstly decrease and then have a trend to increase with the yield strength of Zircaloy; higher fracture strength of hydrided zircaloy will lead to very high values of threshold stress intensity factor and critical hydride length at higher temperatures, which might be the main mechanism of crack arrest for some Zircaloy materials.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.10
• /
• pp.1869-1876
• /
• 1992

The effect of particle property on FOD(foreign object damage) and strength degradation in structural ceramics especially, silicon carbide was investigated by accelerating a spherical particle having different material and different size. The damage induced showed significant differences in their patterns with increase of impact velocity. Also percussion cone was formed at the back part of specimen when particle size became large and its impact velocity exceeded a critical value. The extent of ring cracks was linearly related to particle size, however the impact of steel particle produced larger ring cracks than that of SiC particle. Increasing impact velocity the residual strength showed different degradation behaviors according to particle and its size. In the region the impact site represents nearly elastic deformation behavior, the residual strength was dependent upon the depth of cone crack regardless of particle size. However in elastic- plastic deformation region, the radial cracks led to rapid drop in residual strength.