• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 1996년도 춘계학술발표회논문집(3)
• /
• pp.92-97
• /
• 1996

The fatigue crack propagation behavior in SA106 Gr.C main steam pipe weld joint was investigated in air environment. Crack growth rate tests were conducted on base metal and weld metal at load ratio of 0.1 and 0.3 and at frequency of 10Hz. The fatigue crack growth rates of the base metal and the weld metal were above the ASME reference line and the fatigue crack propagation rate of the weld metal was higher than those of the base metal. Fatigue crack growth rate increased with increasing the load ratio and the effect of the load ratio was more significant in the weld metal. The post weld heat treatment increased the fatigue crack growth rates of the base metal by reducing compressive residual stress and decreased those of the weld metal by reducing weld defects.

• Corrosion Science and Technology
• /
• 제2권2호
• /
• pp.93-97
• /
• 2003

Fatigue crack growth test or low alloy steel was performed in high temperature water. Test parameters were dissolved oxygen content. loading frequency and R-ratio ($P_{min}/P_{max}$). Since the sulfur content or the steel was low, there were no environmentally assisted cracks (EAC) in low dissolved oxygen(DO) water. At high DO, the crack growth rate at R = 0.5 tests was much increased due to environmental effects and the crack growth rate depended on loading frequency and maximized at a critical frequency. On the other hand, R = 0.7 test results showed an anomalous decrease of the crack growth rate as much different behavior from the R = 0.5. The main reason of the decrease may be related to the crack tip closure effect. All the data could be qualitatively understood by effects of oxide rupture and anion activity at crack tip.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2003년도 춘계학술대회 논문집
• /
• pp.1349-1353
• /
• 2003

Previous researches for fiber reinforced composite material(FRCM) have been evaluated the fatigue delamination behavior using the traditional fracture mechanics parameters. Therefore. previous researches for FRCM have not generally been firmed yet. Because delamination growth behavior in FRCM should be consider relationship between delamination area, A$\sub$D/ and crack length, a instead of traditional fracture mechanics parameters. Especially, in case of delamination behavior for FRCM without crack should be considering equivalent crack, i.e., pseudo crack, a$\sub$p/, using the fracture behavior of FRCM with crack. The major purpose of this study was to evaluate the delamination for FRCM without crack. The details of the studies are as follow : 1) Relationship between crack growth rate, da/dN and stress intensity factor, ΔK in FRCM containing a saw-cut and circular hole with crack. 2) Propose of PSEUDO CRACK MODEL for the delamination in FRCM without crack. 3) Analysis of crack propagation energy, E$\sub$crack/ using a total energy, E$\sub$total/ and delamination growth energy, E$\sub$del/.

• 대한기계학회논문집A
• /
• 제35권4호
• /
• pp.375-381
• /
• 2011

본 연구의 주목적은 마그네슘합금의 피로균열성장거동을 지배하는 파라미터들의 확률론적 특성을 규명하는 것이다. 피로균열전파실험은 AZ31 마그네슘합금의 CT 시편을 이용하여 통계적으로 수행하였으며, 시편두께, 하중비, 최대하중 등의 여러 가지 실험조건으로 실온에서 진행하였다. 이 실험을 통하여 획득한 통계적 피로 데이터를 이용하여 피로거동 파라미터의 확률적 변동성 해석과 함께 확률분포 적합성을 고찰하였다. 균열성장속도계수는 확률적으로 매우 큰 변동성을 나타내는 파라미터로 밝혀졌으며, 반면에 균열성장속도지수는 매우 작은 변동성을 나타냄으로써 재료상수로 볼 수 있을 것이다. 피로거동 파라미터인 균열성장속도계수와 균열성장속도지수에 가장 적합한 확률분포는 3-파라미터 Weibull 분포이며, 2-파라미터 Weibull 분포는 균열성장속도계수의 경우에만 양호한 적합성을 나타낸다는 것을 규명하였다.

• 한국해양공학회지
• /
• 제10권1호
• /
• pp.53-64
• /
• 1996

In this paper, rotating bending fatigue tests have been carried out to investigate the growth behabiors of surface fatigue crack initiated from a small artificial surface defect, that might exist in real structures, on 2024-T3 and 6:4 brass. The test results are analysed in the viewpoints of both strength of materials and fracture mechanics, it can be concluded as follows. The effect of a small artificial surface defect upon the fatigue strength is very large. The sensitivity of 2024-T3 on the defect is higher than that of 6:4 brass. The growth behavior of the surface fatigue crack of 2024-T3 is different from that of 6:4 brass. The growth rate of the surface fatigue crack of 2024-T3 is considerably rapid in the early stage of the fatigue life and apt to decrease in the later stage. It was impossible to establish a unifying approach in the analysis of crack growth begabior of 2024-T3 and 6:4 brass using the maximum stress intensity factor because of their dependence on stress level. But if the elastic strain and cyclic total strain intensity factor range were applied to obtain the growth rate of surface fatigue cracks of the materials, the data were found to be nearly coincided.

• 대한기계학회논문집
• /
• 제17권9호
• /
• pp.2145-2152
• /
• 1993

The objective of this paper is to examine the detection limit, growth characteristics and notch curvature radius in short crack problem. Measurement techniques such as ultrasonic method and back-face strain compliance method were adopted. The fatigue crack growth rate of the short crack is slower than that of a long crack for a notched specimen. The characteristic of crack growth and crack closure is same as the case of a delay of crack growth caused by constant amplitude load for an ideal crack or single peak overload for a fatigue crack. The short crack is detected effectively by ultrasonic method. A short surface crack occurs in the middle of specimen thickness and is transient to a through crack depth is larger than the notch curvature radius.

• 한국정밀공학회지
• /
• 제8권2호
• /
• pp.27-35
• /
• 1991

We propose the crack growth rate equation which applied over three regions (threshold region, stable region, unstable region) of fatigue crack propagation. Constant stress amplitude fatigue tests are conducted for four materials under three stress ratios of R=0.05, R=0.2 and R=0.4. Materials which have different mechanical properties i.e. stainless steel, low carbon steel, medium carbon steel and aluminum alloy are used. The fatigue crack growth rate equation is given by $da/dN={\beta} (1-R)^{\delta}\({\DELTA}K-{\DELTA}K_t)^{\alpha} / (K_{cf}-K_{max})$${\alpha}, {\beta}$ , and ${\delta}$ are constants, and ${\Delta}K_t$ is stress intensity factor range at low ${\Delta}K$ region. The constants are obtained from nonlinear least square method. $K_{ef}$is critical fatigue stress intensity factor. The relation between half crack length and number of cycles obtained by integrating the crack growth rate equation is in agreement with the experimental data. It is also experimented with constant maximum stress and decreasing stress ratios, and the fatigue growth rate of each material is in accord with the proposed equation.

• 한국구조물진단유지관리공학회 논문집
• /
• 제15권2호
• /
• pp.179-188
• /
• 2011

강부재의 피로가 주요원인이 되어 구조물이 붕괴되거나 교체되는 사례를 찾아보기 어렵다. 이처럼 사실상 피로에 대해서는 손상을 허용하고 있지만, 발견되는 피로균열에 대한 직접적인 상태평가는 이루어지지 않고 있다. 피로균열에 대한 진전 비진전성의 판단 및 균열진전속도의 평가가 이루어져야만, 합리적인 보수 보강 공법의 선정과 시행시기가 결정될 수 있을 것이다. 본 연구에서는 측정되는 COD(Crack Opening Displacement)를 통한 피로균열진전속도 평가법을 검토하기 위하여, 2종류의 관통 균열 시험편과 면외거셋 용접이음 시험편의 균열진전시험을 실시하였다. 그리고 실용적인 COD의 측정을 위해 변형률 게이지를 이용하는 방법에 대해 검토하였다. 그 결과, COD 측정을 통한 균열진전속도의 합리적인 평가법을 제안하였고, 변형률 게이지를 이용한 성공적인 COD 측정을 실험적으로 증명하였다.

• 대한조선학회지
• /
• 제21권1호
• /
• pp.43-47
• /
• 1984

The purpose of this paper is to investigate theoretically the effect of residual stress due to welding in stress intensity factor of a plate containing the Model I Crack in different crack size and location, and on fatigue crack growth rate. The initiation of crack is found to be possible only in the region of tensile residual stress. The most dangerous crack has the values of d/b and a/b equal to about 0.6 and 1.0, respectively, where d/b is the ratio of distance from the crack to welding bead and the width of tensile residual stress region and a/b is the ratio of crack length and tensile residual stress region. The crack perpendicular to and on the line of welding bead and with a/b equal to about 0.6 has maximum stress intensity factor. The theoretical fatigue crack growth rate under residual stress and applied stress, which is obtained from Forman's Law by stress superposition, is relatively in good agreement with Glinka's[8] experimental value. The fatigue crack growth is shown to be retarded due to residual stress distribution.

• 대한기계학회논문집A
• /
• 제21권10호
• /
• pp.1674-1682
• /
• 1997

Fatigue tests were performed to investigate the effect of ceramic coatings as in TiN and TiCN on fatigue crack growth properties of ceramic coated 1Cr-1Mo-0.25V steel with different coating thickness in laboratory air conditions. The experimental results are described with respect to a Paris equation, da/dN=C(.DELTA.K)$^{m}$ , where the crack growth rate of coated specimens provided as similar growth rate as that of the uncoated specimen regardless of coating thickness. Furthermore, it was observed that the type of coating layer had virtually no effect on crack growth rate in the full region of stress intensity factor range. And it was also appeared that the final crack length of TiCN coated specimens was short compared to that of TiN coated, and the substrate specimens, in which it was inferred due to lowering the toughness of coated material from high hardness of TiCN coating layer itself.