• Progress in Superconductivity
• /
• 제7권2호
• /
• pp.152-157
• /
• 2006

New precursor solution with dichloroacetic acid (DCA) was developed for fabricating high $J_c$ REBCO film. DCA based-precursor solution was coated on $LaAlO_3$(001) substrate by dip coating method. Processing parameters such as oxygen partial pressure, water vapor, ramping rate and pyrolysis temperature were controlled in order to obtain a good epitaxial film. The film with thickness of 0.5 micrometer was obtained by single coating and no crack was observed at calcined films. Oxygen partial pressure was controlled in the range of $100{\sim}1,000$ ppm and conversion heat treatment was carried out at the temperature range of $705-765^{\circ}C$. A critical transition temperature ($T_c$) of 90 K and a critical transport current density ($J_c$) of $>0.5\;MA/cm^2$ (77 K and self-field) were obtained for the GdBCO film. It is thought that fluorine-free MOD solution using DCA is promising precursor solution for fabricating high quality REBCO films.

• 한국표면공학회지
• /
• 제44권1호
• /
• pp.7-12
• /
• 2011

The effect of organic additives, polyethylene glycol (PEG), on the trivalent chromium electroplating was analysed in the view point of current efficiency, solution stability and metallurgical structure. It was measured that PEG-containing trivalent chromium solution had about 10% higher current efficiency than pure solution and controlled the micro-crack density of electrodeposits. PEG exhibited profound effect on the solution stability by reducing the consumption rate of formic acid which acts as a complexant to lower the activation energy required for electrochemical reduction of trivalent chromium ions. It was also revealed that the formation of chromium carbide layer was facilitated in the presence of polyethylene glycol, which meant easier electrochemical codeposition of chromium and carbon, not single chromium deposition. Trivalent chromium layer formed from PEG-containing solution was amorphous with local nano-crystalline particles, which were prominently developed on the entire surface after non-oxidative heat treatment.

• Journal of Biosystems Engineering
• /
• 제26권1호
• /
• pp.47-56
• /
• 2001

In order to prevent the possibility of mixing of metal powder during food grinding processing with the metal roll mill this study was conducted to develope the materials of ceramics roll as a substitute of gray cast iron mill. Since the ceramics is brittle material and can be broken easily by a crack, it was needed to develope engineering ceramics roll materials with high elastic modulus and fracture toughness. Adding 0∼50 wt% Al$_2$O$_3$as densification additives to porcelain body material and forming the ceramics an different condition, mechanical properties were evaluated. The material structure’s densification process was analyzed by SEM and XRD. The evaluation of the mechanical properties of ceramics roll materials were compared and analyzed by non-destructive test using Young’s modulus and destructive test using 3-point bending strength and fracture toughness. The results showed several correlative results. Porcelain body material with 40 wt% Al$_2$O$_3$content heated at 1,200$\^{C}$ for 5h was high bulk density of 2.77, Young’s modulus of 118.4Gpa, 3-point bending strength of 137 MPa and fracture toughness of 2.88 MPa$.$m$\^$$\sfrac{1}{2}$/ . After analyzing the relationship between non-destructive test and destructive test, the coefficient of determination was more than 0.9. Therefore, the evaluation of non-destructive test by ultrasonic was turned out to be feasible in evaluating the mechanical properties of ceramics.

• 수산해양기술연구
• /
• 제43권4호
• /
• pp.362-369
• /
• 2007

This paper was studied on the characteristics of acid resistance and thermal shock for epoxy coatings in the strong acidic environment. The exhaust gas system, such as a air preheater, desulfurization equipment, for industrial boiler is damaged by dew point corrosion. To protect the acid corrosion, the coating using nonmetal was applied. The electrochemical polarization test, acid resistance and thermal shock test for epoxy coatings were carried out. And the acid resistance and thermal shock characteristics, aspect, and electrochemical anti-corrosion characteristics for epoxy coatings in the strong acidic environment were considered. The main results are as followings: As the epoxy glass flake coating by acidic thermal shock was damaged to the crack, blistering and elution etc., the current density of epoxy glass flake coating is high. But the damage of epoxy metal complex coating by acidic thermal shock was not occurred. Therefore the characteristics of acid resistance and thermal shock for epoxy metal complex coating is better than those for epoxy glass flake coating.

• 한국전기전자재료학회논문지
• /
• 제16권11호
• /
• pp.1041-1046
• /
• 2003

In order to improve the surface uniformity and the conduction properties of the fabricated YBCO thick films, a system that applies alternating field vertically to the EPD field has been developed for the first time and applied to the electrophoretic deposition process. The applied alternating electric field, so called Shaky Alternating Assisted Field, caused a force to be exerted on each YBCO particle and resulted in a shaking of the particle in the direction of applied electric field, accomplishing a uniform particle orientation. The usual commercial electrical power was used for the vertically applied alternating voltage and the induced electric field was 25-120 V/cm at 60Hz. The thick film fabricated by the method developed in this paper showed better surface uniformity without crack and porosity and improved film characteristics such as critical temperature (Tc,zero = 90 K) and critical current density (2354 A/$\textrm{cm}^2$), Therefore, it is expected that the shaky-aligned electrophoretic deposition method can be used to fabricate superconductor films through a simpler process and at less expense.

• 한국세라믹학회지
• /
• 제40권1호
• /
• pp.104-108
• /
• 2003

스크래칭 시험(scratching test)을 이용하여 단결정 실리콘의 수직하중에 대한 마찰계수, AE(Acoustic Emission) 신호와 긁힌 자취의 미세균열을 관찰하고 그 결정구조를 분석하였다. 스크래칭 시험은 하중인가속도(loading rate)를 100N/min으로 하고 스크래칭 속도(scratching speed)를 1, 3, 6, 10mm/min의 4가지로 하여 최대 30N이 될 때까지 행하였다. 그 결과, 수직하중 또는 스크래칭 속도가 증가할 때 마찰계수, AE, 균열밀도는 증가하는 경향을 나타내었다. 스크래칭, 자취에 대한 마이크로 라만 분광법을 이용한 결정구조 분석결과, 스크래칭 속도가 느린 조건에서 압력인가에 따른 실리콘의 다이아몬드 구조에서 다른 고압상의 구조로의 상전이 현상을 관찰할 수 있었다.

• Journal of Welding and Joining
• /
• 제14권4호
• /
• pp.43-52
• /
• 1996

The plasma sprayed Cr$_{2}$C$_{2}$-NiCr coatings are widely used as wear-resistant and corrosion-resistant materials. The mechanical properties of the plasma sprayed Cr$_{2}$C$_{2}$-NiCr coatings were examined in this study. The distribution of the residual stress with the coating thickness was also examined by X-ray diffraction method. The pore in the coatings could be classified into two types ; one is the intrinsic pore originated from the spraying powder, the other is the extrinsic pore formed during spraying. During the tensile adhesion test, the fracture occurred at the interface of top coat and substrate or top coat and bond coat depending on the existence of bond coat. It was found that the compressive residual stress near the interface decreased with the increase of the top coat thickness. The tensile adhesion strength of the coating without bond coat was higher than that with bond coat, because the coating with bond coat has higher horizontal crack density near the interface between bond coat and top coat.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 춘계학술발표대회 개요집
• /
• pp.370-376
• /
• 2005

Magnesium alloys are becoming important material for light weight car body, due to their low specific density but high specific strength. However they have a poor weldability, caused high oxidization tendency and low vapor temperature. In this study, the welding performance of magnesium alloys was investigated for automobile application. The materials were rolled magnesium alloy sheet contains Al and Zn such as AZ3l , AZ6l and AZ9l. Three types of welding process were studied, that were GTAW, Laser beam welding and FSW. To evaluate the weldability, we examined the appearance of welding bead. Also we checked bead shape and internal defects such as crack and porosity on cross section of welding bead. The mechanical property was measured for welded specimen by tensile test. For determination of the strength change by welding process, the hardness profile across the welding center was measured. For the results, the tensile properties of welded specimen were decreased obviously on all welding process. For the fusion welding process such as GTAW and laser beam welding, the surface of the welding bead was covered with oxidized magnesium dust but it was removed by simple cleaning work as wipe-out with tissue. Also under cut, that caused vaporization of base metal was occurred. for the friction stir welding, there was no oxidation, under-cut or internal defects. However it had poor weld performance, the reason was cleavage fracture occurred at plastic deformation zone. For welding of magnesium alloy, the laser beam welding process was recommended.

• 한국표면공학회지
• /
• 제48권6호
• /
• pp.354-359
• /
• 2015

Stainless steel has poor corrosion resistance in marine environment due to the breakdown of a passive film caused by chloride. It suffers electrochemical corrosion like pitting corrosion, crevice corrosion, and stress corrosion crack (SCC) in marine environment. In general, it indicates that the passive film of $Al_2O_3$ has better corrosion resistance than that of $Cr_2O_3$ in seawater. This paper investigated the damage behavior 304 stainless steel and hot-dip aluminized 304 stainless steel in seawater solution. Various electrochemical experiments were carried out including potential measurement, potentiodynaimic experiment, Tafel analysis and galvanostatic experiment. As a result of anodic polarization experiment, higher pitting damage depth was indicated at 304 stainless steel than hot-dip aluminized 304 stainless steel. In addition, relatively higher corrosion current density was shown at hot-dip aluminized stainless steel as a result of Tafel analysis.

• 한국표면공학회지
• /
• 제44권2호
• /
• pp.68-73
• /
• 2011

A Ni-W thin-film was synthesized by electrodeposition, and its corrosion resistance and electrical surface conductivity were investigated. Amount of tungsten in the Ni-W thin-film increased linearly with current density during the electrodeposition, and crack-free and low-crystalline Ni-21 at.%W coating layer was obtained. Corrosion resistances of the Ni-W thin-films were examined with an anodic polarization method and a storage test in a strong sulfuric acid solution. As a result, the Ni-21 at.%W thin-film exhibited the greatest corrosion resistance, and maintained the electrical surface conductivity even after the severe corrosion test, which could be applicable as a surface treatment for advanced metallic bipolar plates in fuel cell or redox flow battery systems.