• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.318-319
• /
• 2006

The thermal dissipation performance of sintered heat pipes is usually determined by the capillarity and permeability of the Cu powder wicks. Since the capillary provided by the Cu powder is usually large enough to draw water from the condenser end to the evaporator end, the permeability has become the controlling factor. In this study, Cu powders with different particle sizes and shapes were loosely sintered, and their permeabilities were compared. The results show that more complicated shapes, finer particle sizes, lower porosities, and rougher pore surfaces give lower permeability and thermal dissipation.

• 소성∙가공
• /
• 제4권2호
• /
• pp.123-130
• /
• 1995

The present study is concerned with the hydrostatic extrusion process for the copper-clad aluminum rod through metallurgical joining. The rigid viscoplastic finite element analyses are performed for the steady state extrusion process of the bimetal rod. An algorithm for finding the interface profile of the bimetal rod by tracking a particle path in Eulerian domain is presented. The distributions of the effective strain rate, equivalent stress and hardness are examined for the several extrusion ratios. Experiments are also carried out for the copper-clad aluminum rod at room temperature. It is found out that the finite element predictions are generally in good agreement with the experimental observations. The detail comparisons of the extrusion loads predicted by the element method with those by experiments are given.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.511-512
• /
• 2006

Tungsten coatings with different interlayers onto the oxygen-free copper substrates were fabricated by atmosphere plasma spraying. The effects of different interlayers of NiCrAl, NiAl and W/Cu on bonding strength were studied. SEM, EDS and XRD were used to investigate the photographs and compositions of these coatings. The tungsten coatings with different initial particle sizes resulted in different microstructures. Oxidation was not detected in the tungsten coating, but in the interlayer, it was found by both XRD and EDS. The tungsten coating deposited directly onto the copper substrate presented higher bonding strength than those with different interlayers.

• 농업생명과학연구
• /
• 제44권4호
• /
• pp.29-43
• /
• 2010

The numerical analysis by using CFX 11.0 commercial code was done for proper design of the heat exchanger. The present experimental studies were also conducted to investigate the effects of circulating solid particles on the characteristics of fluid flow, heat transfer and cleaning effect in the fluidized bed vertical shell and tube type heat exchanger with counterflow, at which a variety of solid particles such as glass ($3mm{\Phi}$), aluminum ($2{\sim}3mm{\Phi}$), steel ($2{\sim}2.5mm{\Phi}$), copper ($2.5mm{\Phi}$) and sand ($2{\sim}4mm{\Phi}$) were used in the fluidized bed with a smooth tube. Seven different solid particles have the same volume, and the effects of various parameters such as water flow rates, particle diameter, materials and geometry were investigated. The present experimental and numerical results showed that the flow velocity range for collision of particles to the tube wall was higher with heavier density solid particles, and the increase in heat transfer was in the order of sand, copper, steel, aluminum, and glass. This behavior might be attributed to the parameters such as surface roughness or particle heat capacity.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2005년도 봄학술 발표회 논문집(II)
• /
• pp.97-100
• /
• 2005

The purpose of this study is to research the basic property of mortar as the grading distribution of copper slag used as fine aggregate and the results are as follows. The compressive strength of mortar as the size of largest diameter of copper slag granule is the highest when the largest size is in 2.5-5mm, and flow of mortar is in proportion to the size. As the largest size of copper slag particle is under 2.5mm(Type 1) the compressive strength and flow is higher as the big granules is more included than small ones. As the largest size of copper slag granule is under 5mm(Type 2) the compressive strength and flow is similar to situation of Type 1, except compressive strength is higher as the percent of the size of granule in $2.5\~5mm$ is under 35$\%$. F.M.(Fine Modulus), compressive strength and flow is relative each other except the batch with 2.5$\∼$5mm granule size of copper slag.

• Journal of Electrochemical Science and Technology
• /
• 제11권1호
• /
• pp.60-67
• /
• 2020

In this study, copper (II) oxide powder for electroplating was prepared by recovering CuCl₂ from NaClO₃ type etching wastes via recovered non-sintering two step chemical reaction. In case of alkali copper carbonate [mCuCo₃·nCu(OH)₂], first reaction product, CuCo₃ is produced more than Cu(OH)₂ when the reaction molar ratio of sodium carbonate is low, since m is larger than n. As the reaction molar ratio of sodium carbonate increased, m is larger than n and Cu(OH)₂ was produced more than CuCO₃. In the case of m has same values as n, the optimum reaction mole ratio was 1.44 at the reaction temperature of 80℃ based on the theoretical copper content of 57.5 wt. %. The optimum amount of sodium hydroxide was 120 g at 80℃ for production of copper (II) oxide prepared by using basic copper carbonate product of first reaction. At this time, the yield of copper (II) oxide was 96.6 wt.%. Also, the chloride ion concentration was 9.7 mg/L. The properties of produced copper (II) oxide such as mean particle size, dissolution time for sulfuric acid, and repose angle were 19.5 mm, 64 second, and 34.8°, respectively. As a result of the hole filling test, it was found that the copper oxide (II) prepared with 120 g of sodium hydroxide, the optimum amount of basic hydroxide for copper carbonate, has a hole filling of 11.0 mm, which satisfies the general hole filling management range of 15 mm or less.

• Korean Chemical Engineering Research
• /
• 제46권6호
• /
• pp.1069-1074
• /
• 2008

구리 나노입자의 표면에 화학흡착한 octanethiol, decanethiol 및 dodecanethiol의 3D SAMs를 연구하였고, dodecanethiol의 투입량 변화에 따른 구리 나노입자의 산화 안정성을 고찰하였다. 제조 공정은 산소로부터 보호하기 위해 질소 분위기에서 수행하였고, 합성된 입자는 원심분리를 통하여 획득하였다. 구리 전구체는 Copper(II) nitrate, 환원제는 sodium borohydride를 사용하였으며, 반응은 단일상에서 진행하였다. 나노 크기의 구리입자는 TEM 분석을 통하여 확인하였고, 그 크기는 약 3~6 nm였다. FT-IR, XPS와 열중량분석(TGA) 결과 alkanethiol의 thiol기가 구리 표면에 화학흡착 한다는 것과 alkyl기의 사슬이 길수록 alkanethiol의 흡착양이 증가한다는 것을 확인하였고, XRD 패턴으로부터 구리 나노입자의 거대격자회절(superlattice diffraction)을 관측할 수 있었다. 그리고 dodecanethiol의 투입양이 구리의 투입양보다 적을 경우 구리는 $Cu_2O$의 형태로 산화되었으며, 구리보다 1.25배 많이 투입할 경우 더욱 조밀한 SAMs를 형성하였다.

• 한국결정성장학회지
• /
• 제26권3호
• /
• pp.101-108
• /
• 2016

동 제련 과정에서 발생되는 동 슬래그는 국내에서 년간 70만톤 이상이 발생되고 있어 산업부산물의 건설소재로서의 재활용에 대한 관심이 증가되고 있다. 이에 본 연구에서는 동 제련 슬래그의 3가지 유형의 입도형상과 잔골재로 사용된 강사의 대체 치환율 변화를 실험변수로 선정하여, 동 슬래그를 사용한 시멘트 모르타르의 강도 및 공극구조 특성, 황산 침지 저항성 등의 실험을 통해 건설용 골재로서의 사용가능성을 평가하고자 하였다. 실험결과 동 제련 슬래그 입도는 강도에 미치는 영향인자로 확인되었으며 동 제련 슬래그 잔골재 치환율 60 %인 경우가 가장 높은 강도를 보였다. 또한 잔골재를 동 제련 슬래그로 치환함으로 인해 기공크기가 감소되는 것으로 나타났으며, 황산에 대한 저항성도 증가되는 것으로 나타났다.

• 문화기술의 융합
• /
• 제9권6호
• /
• pp.855-859
• /
• 2023

질산구리삼수화물염(copper(II) nitrate trihydrate) 수용액을 공업용 전분(starch)에 함침 시킨 전구체를 이용하여 산화구리(CuO) 나노 입자를 합성하였다. 주사전자현미경(SEM)을 통하여 질산구리삼수화물염 수용액이 함침된 전구체에 대한 구조를 분석하였고, 전구체에 대한 열처리 온도를 증가 시킴에 따라 생성되는 산화구리 입자의 입자 크기와 결정 구조를 X선회절분석법(XRD)과 주사전자현미경(SEM)으로 분석하였다. 분석 결과에 따르면, 전구체에서 유기물질이 완전히 열분해 되어지는 온도는 450-490℃이며, 열처리하는 온도가 증가함에 따라 생성되는 산화구리 입자의 크기와 결정성이 증가하는 것을 확인할 수 있었고, 또한 500-800℃에서 1시간씩 열처리하여 얻은 산화구리 입자의 크기는 100nm-2㎛인 것으로 나타났다. 하소 온도 400℃에서 산화구리 결정상이 형성되고, 800℃까지는 산화구리 단일상만 존재하며, 하소 온도의 증가에 따라 생성되는 입자의 크기가 커지는 것을 확인하였다.

• 한국지반공학회논문집
• /
• 제18권5호
• /
• pp.195-207
• /
• 2002

동제련 과정에서 부산되는 동슬래그는 국내에서 연간 70여만톤에 이르나, 그 활용분야가 제한되어 사용량이 미약하여 그 처리방안이 시급히 요청되고 있는 실정이다. 이에 본 연구는 동슬래그의 입도가 0.15~5mm의 조립상태로 분포하여 환경적으로도 안정된 유리질이라는 점에 착안하여 연약지반개량공법 중의 하나인 모래다짐말뚝의 모래대체재로서의 활용방안을 모색하였다. 실내 물리.역학시험 및 모형토조시험에 의한 동슬래그의 지반공학적 재료특성을 파악하고 현장시험시공을 통해 동슬래그의 모래다짐말뚝의 모래대체재로서의 현장 적용 가능성을 일반모래와 비교.검토하였다. 그 결과 동슬래그의 재료특성이 양호하고 지지력, 침하저감효과 그리고 주변지반 개량효과면에서 동슬래그 또는 동슬래 그다짐말뚝이 우수한 것으로 나타나, 모래다짐말뚝의 모래대체재로 동슬래그를 적용할 경우 천연골재의 고갈에 따른 대체골재원으로서 산업부산물의 재활용이라는 측면에서 경제적.환경적으로 활용가치가 높으리라 판단된다.