• Journal of The Korean Society of Agricultural Engineers
• /
• v.60 no.6
• /
• pp.111-119
• /
• 2018

The air-void is known to be one of the influencing factors for estimating long-term performance of asphalt concrete. Most of all, confirming air void or density of pavement layer is important for quality control of field compaction level of asphalt concrete pavement. In this study, a non-nuclear type non-destructive density gage (NDDG) was used to estimate compacted air-voids of asphalt pavement as a non-destructive test method. Asphalt concrete slab specimens were prepared using 6 types of asphalt mixes in laboratory (lab) for lab NDDG test. Four different base structure materials were used to find out if there were any differences due to the type of base structure materials. The actual air-voids and NDDG air-voids were measured from 6 asphalt concrete slabs. Four sections of field asphalt pavements were tested using the NDDG, and actual air voids were also measured from field cores taken from the site where the NDDG air-void was measured. From lab and field experimental tests, it was found that the air-voids obtained by NDDG were not the same as the actual air-voids measured from the asphalt concrete specimen. However, it was possible to estimate air voids based on the relationship obtained from regression analysis between actual and NDDG air voids. The predicted air-voids based on the NDDG air-voids obtained from 50mm depth were found to be reliable levels with $R^2{\fallingdotseq}0.9$. Therefore, it was concluded that the air-voids obtained from NDDG could be used to estimate actual air-voids in the field asphalt pavement with a relatively high coefficient of determination.

• International Journal of Highway Engineering
• /
• v.20 no.2
• /
• pp.19-25
• /
• 2018

PURPOSES : This purpose of this study is to analyze the effect to autogenous shrinkage of the top-layer material of a two-lift concrete pavement mixing both silica fume and polymer powder. METHODS : The bottom-layer of a two-lift concrete pavement was paved with original portland cement (OPC) with a 20~23 cm thickness. Additionally, the top-layer which is directly exposed to the environment and vehicles was paved with a high-performance concrete (HPC) with a 7~10 cm thickness. These types of pavements can achieve a long service life by reducing joint damage and increasing the abrasion and scaling resistance. In order to integrate the different bottom and top layer materials, autogenous shrinkage tests were performed in this study according to the mixing ratio of silica fume and polymer powder, which are the admixture of the top-layer material. RESULTS : Autogenous shrinkage decreased when polymer powder was used in the mix. Contrary to this, autogenous shrinkage tended to rise with increasing silica fume content. However, the effects were not significant when small amounts of polymer powder were used (3% and 11%). CONCLUSIONS : The durability and compressive strength increase when silica fume is used in the mix. The flexural strength considerably increases and autogenous shrinkage of concrete decreases when polymer powder is used in the mix. As seen from above, the proper use of these materials improves not only durability, but also autogenous shrinkage, leading to better shrinkage crack control in the concrete.

• International Journal of Highway Engineering
• /
• v.14 no.6
• /
• pp.25-35
• /
• 2012

PURPOSES : Hollows are easily made, and bearing capacity can be lowered near underground structures because sublayers of pavement settle for a long time due to difficult compaction at the position. If loadings are applied in this condition, distresses may occur in pavement and, as the result, its lifespan can decrease due to the stress larger than that expected in design phase. Although reinforced slab is installed on side of box culvert to minimize the distresses, length of the reinforced slab is fixed as 6m in Korea without any theoretical consideration. The purpose of this paper is investigating the behavior of concrete pavement according to the cover depth of the box culvert ad the length of the reinforced slab. METHODS : The distresses of concrete pavement slabs were investigated and cover depth was surveyed at position where the box culverts were located in expressways. The concrete pavements including the box culverts were modeled by finite element method and their behaviors according to the soil cover depth were analyzed. Wheel loading was applied after considering self weight of the pavement and temperature gradient of the concrete pavement slab at Yeojoo, Gyeonggi where a test road was located. After installing pavement joint at various positions, behavior of the pavement was analyzed by changing the soil cover depth and length of the reinforced slab. RESULTS : As the result, the tensile stress developed in the pavement slab according to the joint position, cover depth, and reinforced slab length was figured out. CONCLUSIONS : More reasonable and economic design of the concrete pavement including the box culvert is expected by the research results.

• International Journal of Highway Engineering
• /
• v.12 no.3
• /
• pp.1-8
• /
• 2010

This study is performed to evaluate the physical and mechanical characteristics of an acryl polymer concrete that is developed as an overlay material for cement concrete slabs and pavements. Various laboratory tests including viscosity, flow, compressive strength, flexural strength, tensile strength, linear shrinkage, thermal expansion and thermal compatibility tests are performed. It is observed from the laboratory tests that the acryl polymer concrete developed in this study satisfies all the requirements suggested by ACI guideline. In addition to the laboratory tests, an accelerated performance testing (APT) is conducted to validate the performance of the acryl polymer concrete. During the APT, no significant distresses are observed until 15,903,939 cycles of equivalent single axle loading is applied. Finally, a 10mm thick overlay with the acryl polymer concrete is applied on top of an old deteriorated concrete pavement to evaluate field performance. Right after the field construction, skid resistance, noise and roughness are measured. The skid resistance and noise level have been significantly improved while the roughness is increased. Periodic investigation for the field study section will be conducted to evaluate the long-term performance.

• International Journal of Highway Engineering
• /
• v.14 no.2
• /
• pp.11-17
• /
• 2012

This research describes how to predict a model of the tensile strain related to the fatigue cracking performance of several asphalt concrete structures through design of experiments(e.g., Response Surface Methodology) and harmony search(HS) algorithm. The axisymmetric analysis program of finite element method, which is the KICTPAVE, was used to determine the strain level at the interface layer between asphalt layer and lean concrete layer. Once the training database set of various strain levels was constructed under the several condition of layer stiffnesses and thicknesses in the asphalt concrete structures, the data set was trained through the HS algorithm in order to determine the regression coefficients defined based on a response surface methodology. Furthermore, the testing set, which was not used for the training procedure of HS algorithm, was also constructed in order to evaluate whether the regression coefficients of a prediction model can be appropriately applied for other cases in asphalt concrete structures.

• International Journal of Highway Engineering
• /
• v.15 no.1
• /
• pp.23-36
• /
• 2013

PURPOSES: The problem under this circumstance is that the erosion not only drops strength of the steel dowel bar but also comes with volume expansion of the steel dowel bar which can reduce load transferring efficiency of the steel dowel bar. To avoid this erosion problem, alternative dowers bars are developed. METHODS: In this study, the bearing stresses between the FRP tube dowel bar and concrete slab are calculated and compared with its allowable bearing stress to check its structural stability in the concrete pavement. These comparisons are conducted with several cross-sections of FRP tube dowel bars. Comprehensive laboratory tests including the shear load-deflection test on a full-scale specimen and the full-scale accelerated joint concrete pavement test are conducted and the results were compared with those from the steel dowel bar. RESULTS: In all cross-sections of FRP tube dowel bars, computed bearing stresses between the FRP tube dowel bar and concrete slab are less than their allowable stress levels. The pultrusion FRP-tube dowel bar show better performance on direct shear tests on full-scale specimen and static compression tests at full-scale concrete pavement joints than prepreg and filament-winding FRP-tube dowel bar. CONCLUSIONS: The FRP tube dowel bars as alternative dowel bar are invulnerable to erosion that may be caused by moisture from masonry joint or bottom of the pavement system. Also, the pultrusion FRP-tube dowel bar performed very well on the laboratory evaluation.

• International Journal of Highway Engineering
• /
• v.11 no.4
• /
• pp.95-105
• /
• 2009

This study was conducted to investigate the effects of concrete flexural strength and surface smoothness, which were pay factors of concrete pavements, on pavement performance, and to develop the methodologies to determine the proper allowable ranges according to the magnitudes of those pay factors. The concrete flexural strength was analyzed using the AASHTO, power, and linear fatigue failure models, and the surface smoothness was analyzed for the roughness indices of PSI, IRI, and PrI using the AASHTO model. The analysis results showed that the allowable range of the flexural strength should be determined using the rate between the deficiency and strength, and the penalty should be linearly proportional to the strength deficiency rate because the linear relationship between the strength deficiency rate and the reduction in pavement life was observed. As the initial surface smoothness became better, the smoothness deficiency rate should be larger. The penalty due to the surface smoothness deficiency should also be linearly proportional to the smoothness deficiency rate.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.1D
• /
• pp.57-65
• /
• 2008

Joint of concrete pavement contributes to improvement of pavement performance by preventing occurrence of random cracking due to drying shrinkage and temperature changes of concrete slabs at early age. However, saw-cutting operations performed prior to sufficient concrete hardening develop micro-cracking of the concrete near the joints, which may develop to long-term distresses due to repetitious traffic and environmental loadings. To reduce the distresses, the joint crack inducers with heights of 100 mm, 150 mm, and 220 mm and the joint cracking slots with various depth were installed at a test section to investigate occurrence of the joint cracks and their behaviors over 5 months. As the results, higher efficiency of the crack inducing and larger behavior of the joint cracks were observed for the taller joint crack inducer. Higher efficiency of the crack inducing and improvement of the joint performance are warranted by additional investigation and reformation of the joint crack inducer.

• Structural Engineering and Mechanics
• /
• v.90 no.5
• /
• pp.467-480
• /
• 2024

The mechanical properties and durability of concrete pavements may be degraded in extreme situations, resulting in the need for partial repair or total replacement. During the past few decades, there has been a growing body of research on substituting a portion of Portland cement with alternative cementitious materials for improving concrete properties. In this study, two different configurations of powdered and granulated blast furnace slag were implemented, replacing fine aggregates (by 12 wt.%) and Portland cement (by 0, 20, 40, and 60 wt.%) in the making of roller-compacted concrete (RCC) mixes. The specimens were fabricated to investigate the mechanical properties and durability specifications, involving freeze-thaw, salt-scaling, and water absorption resistance. The experimental results indicated that the optimum mechanical properties of RCC mixes could be achieved when 20-40 wt.% of powdered slag was added to concrete mixes containing slag aggregates. Accordingly, the increases in compressive, tensile, and flexural strengths were 45, 50, and 28%, in comparison to the control specimen at the age of 90 days. Also, incorporating 60 wt.% of powdered slag gave rise to the optimum mix plan in terms of freeze-thaw resistance such that a negligible strength degradation was experienced after 300 cycles. In addition, the optimal moisture content of the proposed RCC mixtures was measured to be in the range of 5 to 6.56%. Furthermore, the partial addition of granulated slag was found to be more advantageous than using entirely natural sand in the improvement of the mechanical and durability characteristics of all mixture plans.

• International Journal of Highway Engineering
• /
• v.6 no.4 s.22
• /
• pp.35-43
• /
• 2004

Skid resistance is an important factor that control braking distance and secure safety by preventing slipperiness between tire and pavement surface. Decrease of skid resistance at wet condition may cause fatal traffic accidents. Dirt materials such as sand and do-icings on the road surface also can be a factor for decrease skid resistance. This study makes an investigation into influence of skid resistance between varied cement concrete pavements about surface texturing method(transverse tining, longitudinal tining, exposed aggregate surface texturing method) and wearing condition of pavement surface texture(new constructed pavement's surface, wore pavement's surface) using accelerate concrete pavement wearing tester when remains of dirt material are obtained between tire and road surface on PCC pavement. As dirt material on road surface of concrete pavement, sand, calcium chloride and old oil were used with different amount of each cases.