• Restorative Dentistry and Endodontics
• /
• v.19 no.2
• /
• pp.513-533
• /
• 1994

The smooth surface after polishing of composite resin contributes to the patient's comfort, and appearance and longevity of the restoration. This study was performed for the quantitative analysis of the effects of the various finishing and polishing instruments on the surface roughness and reflectivity of the microfill, and hybrid composite resins. Cylindrical specimens 2mm thick and 10mm in diameter of Silux Plus, Durafill VS ; Z100, Prisma TPH, Brilliant, and Herculite XR composite resin were polymerized under the matrix strip. 18 specimens for each composite resin materials were divided into 6 groups ; 5 experimental groups were abraded with # 600 sand paper to remove resin-rich layer, except control. Thereafter, using diamond bur(Mani Dia-Burs), carbide bur(E. T. carbide set 4159), rubber point(Composite polishing kit), aluminum-oxide disk(Sof-Lex disk), polishing paste(Enhance system) ; each specimen was polished to its best achievable surface according to manufacturer's directions. Final polished surfaces were evaluated for the surface roughness with profilometer(${\alpha}$-step 200, Tencor instruments, USA) and for the reflectivity with image analyser(Omniment Image Analyser, Buehler, USA). The results were as follows. 1. Polishing paste or aluminum-oxide disk finish in the microfill, and hybrid composite resins was as smooth as matrix strip finish on the surface roughness test. 2. Polishing paste or aluminum-oxide disk finish in the microfill ; polishing paste finish in the hybrid composite resins was as reflective as matrix strip finish on the refectivity test. 3. For the polishing paste, there were no significant differences between the composite resin materials on the surface roughness and refectivity tests. 4. For the aluminum-oxide disk, the best result was obtained with the microfill composite resin on the surface roughness and reflectivity test. 5. Diamond bur, carbide bur, and rubber point were inappropriate for the final polishing instruments.

• Advanced Composite Materials
• /
• v.18 no.2
• /
• pp.135-152
• /
• 2009

Liquid molding processes, such as resin transfer molding, involve resin flow through a porous medium inside a mold cavity. Numerical analysis of resin flow and mold filling is a very useful means for optimization of the manufacturing process. However, the numerical analysis is quite time consuming and requires a great deal of effort, since a separate numerical calculation is needed for every set of material properties, part size and injection conditions. The efforts can be appreciably reduced if similarity solutions are used instead of repeated numerical calculations. In this study, the similarity relations for pressure, resin velocity and flow front propagation are proposed to correlate another desired case from the already obtained numerical result. In other words, the model gives a correlation of flow induced variables between two different cases. The model was verified by comparing results obtained by the similarity relation and by independent numerical simulation.

• Proceedings of the KACD Conference
• /
• 2001.11a
• /
• pp.558.1-558
• /
• 2001

Flowable resin composite is a relatively new restorative material. It has been reported that a low viscosity, low modulus intermediate resin applied between the bonding agent and restorative resin act as an "elastic buffer" that can relieve contraction stress. This in-vitro study aimed to evaluate the effect of flowable composite resin as a restorative material on regional tensile bond stredgth to cervical wedge shaped cavity walls. (omitted)

• The Journal of Advanced Prosthodontics
• /
• v.3 no.3
• /
• pp.166-171
• /
• 2011

PURPOSE. The purpose of this study is to evaluate and compare the shear bond strength of the gingiva-colored composite resin and the tooth-colored composite resin to porcelain, metal and zirconia. MATERIALS AND METHODS. Sixty cylindrical specimens were fabricated and divided into the following 6 groups (Group 1-W: tooth-colored composite bonded to porcelain, Group 1-P: gingiva-colored composite bonded to porcelain, Group 2-W: tooth-colored composite bonded to base metal, Group 2-P: gingiva-colored composite bonded to base metal, Group 3-W: tooth-colored composite bonded to zirconia, Group 3-P: gingiva-colored composite bonded to zirconia). The shear bond strength was measured with a universal testing machine after thermocycling and the failure mode was noted. All data were analyzed using the two-way analysis of variance test and the Bonferroni post-hoc test at a significance level of 0.05. RESULTS. The mean shear bond strength values in MPa were 12.39, 13.42, 8.78, 7.98, 4.64 and 3.74 for Group 1-W, 1-P, 2-W, 2-P, 3-W and 3-P, respectively. The difference between the two kinds of composite resin was not significant. The shear bond strength of Group 1 was the highest and that of Group 3 was the lowest. The differences among Group 1, 2 and 3 were all significant (P<.05). CONCLUSION. The shear bond strength of the gingiva-colored composite was not less than that of the tooth-colored composite. Thus, repairing or fabricating ceramic restorations using the gingiva-colored composite resin can be regarded as a practical method. Especially, the prognosis would be fine when applied on porcelain surfaces.

• Restorative Dentistry and Endodontics
• /
• v.18 no.2
• /
• pp.501-506
• /
• 1993

The purpose of this study was to observe the longevity of amalgam and composite resin fillings in Korea. The number of placement of restorations was 760 amalgams and 415 composite resins. The amalgam restorations inserted because of primary caries were 61 % and replacement of amalgam restorations were 39%, and composite restorations inserted because of primary caries were 62 % and replacement of composite restorations were 38 %. The median longevity of failed amalgam restorations was 3 years and the madian longevity of failed composite restorations was 2 years. The main reason of replacement of amalgam and composite resin restorations was secondary caries.

• Journal of the Korean Wood Science and Technology
• /
• v.27 no.2
• /
• pp.23-30
• /
• 1999

This study was carried out to develop the Korean paper(Hanji) sludge-wood fiber composite boards utilizing the relinquished sludges occurring from the making process of Korean classic paper Hanji. The bark of paper mulberry(Broussonetia kazinoki Sieb.) has been used as a raw material since past hundreds and thousands years. Korean paper(Hanji) sludge was divided into two kinds, the one was the white sludge from the first stage and the other was the black sludge occurring from the final stage of Korean paper(Hanji) making. Four levels of the mixed ratio of each white or black sludge to wood fiber(10:90, 20:80, 30:70 and 40:60), three levels of the resin adhesives(PMDI, urea and phenol resin) and three levels of the density(0.60, 0.75 and 0.90) were designed to investigate the physical properties of Korean paper(Hanji) sludge-wood fiber composite boards. From the results and discussion, it could be concluded as follows : 1. In the white sludge-wood fiber composite board, the thickness swelling was not affected by the specific gravity and sludge additive of composite boards, but among the resin adhesives PMDI resin showed the best dimensional stability. Water absorption was superior in urea resin, secondly PMDI resin and very poor in phenol resin. 2. In the black sludge-wood fiber composite board, thickness swelling was superior in PMDI resin but very poor in phenol resin. In water absorption, PMDI and urea resin showed good results, regardless of specific gravity or sludge additive, but phenol resin showed poor results. 3. From the results and discussion of physical properties it is suggested that the white sludge-wood fiber composite boards bonded with PMDI or black sludge-wood fiber composite boards bonded with urea resin were made possibly with similar or better properties. compared with general fiberboard until the addition of 20% sludge into wood fiber.

• Journal of Technologic Dentistry
• /
• v.35 no.4
• /
• pp.313-320
• /
• 2013

Purpose: The purpose of this study was to know the physical properties of UDMA dental composite resins containing two photosensitizers, PD, DA, as a photosensitizer instead of CQ. We want to know Remaining Double Bond(RDB) of UDMA unfilled resin and diametral tensile strength and flexural strength of composite resin containing PD and DA were compared with those of CQ, most widely used photosensitizer for dental composite resins. Methods: The RDB of UDMA studied by FT-IR spectroscopy increased with irradiation time. The composite resins were tested for their physical properties. The dental composite resins were made with UDMA as a monomer, silanized silica as filler, N,N-dimethylaminoethyl methacrylate (DAEM) as amine initiator, and one of the two kinds of new photosensitizers. Results: The relative RDB of UDMA was in the order: DA > CQ > PD but the physical properties of the composite resins show PD and DA with higher results compared with that containing CQ. The reason for the results is that PD and DA serve not only as a photosensitizer but also as a photo-crosslinking agent. Conclusion: PD and DA show as effective photosensizers, suitable for UDMA dental composite resin compare with a higher efficiency than CQ.

• The Journal of Korean Academy of Prosthodontics
• /
• v.37 no.3
• /
• pp.313-327
• /
• 1999

The aim of this study was to compare wear resistance of resin denture teeth opposing various restorative materials. The wear resistance of conventional acrylic resin teeth(Trubyte Biotone) and three high-strength resin teeth(Bioform IPN, Endura, SR-Orthosit-PE) opposing different restorative materials(gold alloys, dental porcelain, composite resin) was compared. Wear tests were conducted with a sliding-induced wear testing apparatus which applied 100,000 strokes to the specimen in a mesio-distal direction under conditions of 100 stroke/min and constant loading of 1Kgf/tooth. Wear resistance of the resin denture teeth was evaluated by the following criteria : 1) wear depth, 2) weight loss, and 3) SEM observation. Results were as follows. 1. When opposed to gold alloys and composite resin, high-strength resin teeth showed superior wear resistance compared to acrylic resin teeth. But, in cases opposing dental porcelain, differences between the wear of the high-strength and acrylic resin teeth were not statistically significant (p<0.05). 2. When comparing wear resistance among high-strength resin teeth, opposing gold alloys, Endura was slightly more resistant and while in cases opposing dental porcelain, SR-Orthosit-PE was showed to be slightly resistant(p<0.05). 3. The wear of high-strength resin teeth was greater by 5 to 7 times when opposing porcelain and 2 to 3 times when opposing composite resin compared to gold alloys(p<0.05). 4. SEM observations of the wear surface showed that wear of resin teeth opposing gold alloys is a fatigue type of wear and wear of resin teeth opposing dental porcelain is fatigue and abrasion type of wear. Trubyte Biotone showed more severe fatigue type of wear than high-strength resin teeth. In conclusion, the use of dental porcelain should seriously be considered as restorative material in cases opposing resin denture teeth and improvement seems to be needed on resin teeth in the areas of wear resistance.

• Journal of Technologic Dentistry
• /
• v.30 no.2
• /
• pp.23-29
• /
• 2008

The purpose of this study is to evaluate possibility of using indirect composite resin instead of porcelain through the measurement of shear bond strength between zirconia core and indirect composite resin under treatment of $Rocatec^{TM}$ system for improving the adhesion of indirect composite resin. 20 cylindrical zirconia core specimens were divided into 2 groups, according to zirconia surface treatment and attached materials: 1) treated with sandblast and attached with indirect composite resin, 2) treated with sandblast + $Rocatec^{TM}$ system and attached with indirect composite resin. The shear bond strength of each experimental group was measured by MTS and the changes of zirconia core surface according to surface treatments were obtained by SEM observation and measurements of surface roughness. The mean shear bond strength values are $0.55\;{\pm}\;0.11MPa$(Group SC) and $1.16\;{\pm}\;0.46MPa$(Group SRC). The mean Ra values for the surface treatments were follows: $0.39\;{\pm}\;0.13$($100{\beta}_{{\mu}m}$ sandblast) and $0.50\;{\pm}\;0.03$($100{\beta}_{{\mu}m}$ sandblast + $Rocatec^{TM}$ system). In the analysis of EDS, Si element was detected in the Group SC. The shear bond strength between zirconia core and indirect composite resin was improved significantly by using $Rocatec^{TM}$ system.

• Restorative Dentistry and Endodontics
• /
• v.25 no.3
• /
• pp.371-380
• /
• 2000

The effect of fiber reinforcing materials on the fracture strength of composite resin was evaluated. Each ten composite resin bars reinforced by glassfiber[Fiber-Splint ML$^{(R)}$(Polydentia SA, Switzerland)], polyethylene fiber [Ribbond$^{(R)}$(Ribbond Inc., U.S.A.)] and polyaramid fiber[Kevlar$^{(R)}$(DuPont, U.S.A.)] were loaded under the 3-point compression technique. Another ten pure composite resin bars without reinforcement were used as a control group. Then mean fracture strength and standard deviation were calculated and a ANOVA and Scheffe test were used in statistics. The results were as follows: 1. Kevlar group showed the highest fracture strength as 175.5MPa (p<0.05). Fiber-Splint ML group showed the lowest fracture strength as 112.7MPa. 2. The mean value of fracture strength in Ribbond group was 136.4MPa, and that of unterated control group was 143.6MPa. No difference was found between the two groups. 3. Ribbond and Kevlar reinforcement groups showed a catastrophic failure, where complete separation of pieces occurs to a unseparated fracture pattern. The use of Kevlar reinforcement fibers with composite resin showed significant increase in the average load failure and the presence of the fibers did prevent the catastrophic crack propagation present in the unreinforced samples. The use of Ribbond reinforcement fibers with composite resin showed no significant increase in the average load failure. However, the presence of the fibers did prevent the catastrophic crack propagation. Because high strength of glassfiber are rapidly degraded on exposure to moisture and humidity. The use of Fiber-Splint ML reinforcement fibers with composite resin showed significant decrease in the average load failure and displayed catastrophic fractures.