A STUDY ON THE SURFACE ROUGHNESS AND REFLECTIVITY AFTER POLISHING OF THE MICROFILL, HYBRID COMPOSITE RESINS

Microfill, Hybrid 복합레진 연마 후 표면조도와 광반사율에 관한 연구

The smooth surface after polishing of composite resin contributes to the patient's comfort, and appearance and longevity of the restoration. This study was performed for the quantitative analysis of the effects of the various finishing and polishing instruments on the surface roughness and reflectivity of the microfill, and hybrid composite resins. Cylindrical specimens 2mm thick and 10mm in diameter of Silux Plus, Durafill VS ; Z100, Prisma TPH, Brilliant, and Herculite XR composite resin were polymerized under the matrix strip. 18 specimens for each composite resin materials were divided into 6 groups ; 5 experimental groups were abraded with # 600 sand paper to remove resin-rich layer, except control. Thereafter, using diamond bur(Mani Dia-Burs), carbide bur(E. T. carbide set 4159), rubber point(Composite polishing kit), aluminum-oxide disk(Sof-Lex disk), polishing paste(Enhance system) ; each specimen was polished to its best achievable surface according to manufacturer's directions. Final polished surfaces were evaluated for the surface roughness with profilometer(${\alpha}$-step 200, Tencor instruments, USA) and for the reflectivity with image analyser(Omniment Image Analyser, Buehler, USA). The results were as follows. 1. Polishing paste or aluminum-oxide disk finish in the microfill, and hybrid composite resins was as smooth as matrix strip finish on the surface roughness test. 2. Polishing paste or aluminum-oxide disk finish in the microfill ; polishing paste finish in the hybrid composite resins was as reflective as matrix strip finish on the refectivity test. 3. For the polishing paste, there were no significant differences between the composite resin materials on the surface roughness and refectivity tests. 4. For the aluminum-oxide disk, the best result was obtained with the microfill composite resin on the surface roughness and reflectivity test. 5. Diamond bur, carbide bur, and rubber point were inappropriate for the final polishing instruments.