• Corrosion Science and Technology
• /
• 제7권1호
• /
• pp.50-60
• /
• 2008

The majority of the described experimental results deal with relatively pure aluminium. Variations were made in the pretreatment of the aluminum substrates and an investigation was performed on the resulting changes in oxide layer composition and chemistry. Subsequently, the bonding behavior of the surfaces was investigated by using model adhesion molecules. These molecules were chosen to represent the bonding functionality of an organic polymer. They were applied onto the pretreated surfaces as a monolayer and the bonding behavior was studied using infrared reflection absorption spectroscopy. A direct and clear relation was found between the hydroxyl fraction on the oxide surfaces and the amount of molecules that subsequently bonded to the surface. Moreover, it was found that most bonds between the oxide surface and organic functional groups are not stable in the presence of water. The best performance was obtained using molecules, which are capable of chemisorption with the oxide surface. Finally, it was found that freshly prepared relatively pure aluminum substrates, which are left in air, rapidly lose their bonding capacity towards organic functional groups. This can be attributed to the adsorption of contamination and water to the oxide surface. In addition the adhesion of a typical epoxy-coated aluminum system was investigated during exposure to water at different temperatures. The coating was found to quite rapidly lose its adhesion upon exposure to water. This rapid loss of adhesion corresponds well with the data where it was demonstrated that the studied epoxy coating only bonds through physisorptive hydrogen bonding, these bonds not being stable in the presence of water. After the initial loss the adhesion of the coating was however found to recover again and even exceeded the adhesion prior to exposure. The improvement could be ascribed to the growth of a thin oxyhydroxide layer on the aluminum substrate, which forms a new, water-stable and stronger bond with the epoxy coating. Two routes for improvement of adhesion are finally decribed including an interphasial polymeric thin layer and a treatment in boiling water of the substrate before coating takes place. The adhesion properties were finely also studied as a function of the Mg content of the alloys. It was shown that an enrichment of Mg in the oxide could take place when Mg containing alloys are heat-treated. It is expected that for these alloys the (hydr)oxide fraction also depends on the pre-treatment and on the distribution of magnesium as compared to the aluminium hydroxides, with a direct impact on adhesive properties.

• 공업화학
• /
• 제16권2호
• /
• pp.250-256
• /
• 2005

자동차 산업에서의 도장 외관은 아주 중요하다. 이러한 도장외관의 향상을 위해서 기본적으로 도막의 내식성과 밀착성이 해결되어야 한다. 도막의 물성의 향상을 위해서 금속의 화성피막은 매우 중요한 요소가 되고 있다. 전착도장 중 음극에서의 pH는 12 정도까지 증가하고, 이 같은 강알카리 조건에서 금속과 화성피막의 용해가 일어난다. 이 같은 현상의 화성피막과 소재사이의 결합력을 감소시키게 된다. 일반적으로 인산염 피막구조는 hopeite 및 phosphphylife 구조를 갖지만 hopeite 피막 구조보다는 phosphophyllite 피막구조가 내식성이 보다 우수하고, 양이온 전착도료에 의한 전착도장에서 강알카리화된 계면에서 피막의 알카리 용해성이 적어 내수밀착성의 향상을 보인다. Ni, Mn 등의 보조금속의 첨가는 P-ratio (phosphophyllite/ hopeite + phosphophyllite)를 증가시키므로 내수 밀착성과 내식성을 향상시키게 됨을 알 수 있었다.

• 접착 및 계면
• /
• 제20권1호
• /
• pp.1-8
• /
• 2019

균일한 단일층(monolayer)의 형성은 박막 두께에서의 특성을 유지하면서 차광, 반사방지 등의 물리적, 화학적 기능을 강화할 수 있는 중요한 수단이다. 이전 연구에서도 여러 코팅 방법으로 단일층을 구현하였으나, 공정이 복잡하고 대면적화 하는데 어려움이 있었다. 이에 본 연구에서는 소량의 용액으로 대면적 코팅이 가능한 로드 (rod) 코팅법을 사용하여, $20cm{\times}20cm$ PET 필름 기판 위에 마이크로미터 크기의 PMMA 비드를 가장 치밀한 형태인 HCP(hexagonal closed packing)가 되도록 코팅을 진행하였다. 끓는점과 증기압이 다른 용매의 사용과 계면활성제의 적용, 플라즈마 처리를 통한 기판 에너지의 변화를 통해 형성되는 단일층의 수준을 관찰하였다. 본 연구를 통해 비드의 메니스커스, 용매와 비드의 인-척력, 표면에너지를 포함한 코팅 조건을 최적화함으로써, 최종적으로 단위면적당 비드가 차지하는 정도인 입자의 커버리지를 초기 대비 약 20% 정도 향상시켰고, 단일층에 영향을 주는 인자들을 확인하였다. 본 결과는 기존에 연구되었던 코팅 방법에 비해 간단하고 빠르게 대면적의 단일층(monolayer)을 형성할 수 있기 때문에, 광학필름과 센서 등 첨단 분야로의 잠재적 응용 가능성이 높다.

• 약학회지
• /
• 제41권3호
• /
• pp.305-311
• /
• 1997

Sustained release-microspheres and immediate release-pellets were prepared to develop a controlled release multiparticulate system containing both water soluble and insoluble dr ug. Pseudoephedrin.HCl (EPD) and terfenadine (TRF) were used as model drugs, respectively. Sustained release-EPD microspheres were prepared by solvent evaporation method using Eudragit RL or RS as a matrix combined with pH-insensitive film coating. Smaller EPD microspheres were obtained when smaller amount of Eudragit as a matrix material or larger amount of magnesium stearate as a dispersing agent was used. However the obtained microspheres did not show syfficient sustained release characteristics. About 97% of EPD was released after 1 hr irrespective of matrix material used. Subsequent coating of the microspheres with pH-insensitive polymer such as Eudragit RS or ethylcelulose (EC) resulted good sustained in 37.5, 73.3 and 92.0% release of encapsulated EPD in distilled water after 1, 3 abd 7 hr, respectively. It corresponds to mean dissolution time (MDT) of 2.3 hr, which is much larger than that of un-coated EPD microspheres (0.0048 hr). Immediate release TRF pellets were prepared by spherically agglomerated crystallization using Eudragit E as an inert matrix and methylene chloride as a liquid binder. Using Eudragit E alone as a matrix resulted in satisfactory physical properties of the pellets such as sphericity, surface texture and flowability, but led to slower release of TRF from pellets than un-modified TRF powder (MDT of 1.70 vs 1.43 hr in pH 1.2 dissolution medium). Introducing propylene glycol or sodium lauryl sulfate as an emulsifier brought about faster release of TRF from pellets (MDT of 1.14 and 0.95 hr, respectively). In conclusion, microencapsulation by solvent evaporation combined with film coating and spherically agglomerated crystallization were successfully utilized to prepare controlled release multiparticulate system composed of sustained release EPD-microspheres and immediate release TRF pellets.

• 폴리머
• /
• 제30권2호
• /
• pp.112-117
• /
• 2006

약물전달 시스템 중의 하나인 삼투압정의 단점을 보완하기 위해 많은 장점을 가지는 유동층 코팅 기술을 이용하여 내부의 삼투염의 양과 반투막 내의 결합제의 종류가 다른 삼투압을 이용하는 과립을 제조하였다. 얻어진 과립은 코팅 단계에 따라 과립의 형태가 상이하였으며, 약물층에 포함된 삼투염의 양이 많을수록 많은 양의 약물을 방출하였다. 이는 과립의 내부와 외부의 삼투압 차이가 커져서 약물을 방출시키는 추진력이 증가하였기 때문으로 사료된다. 또한 반투막의 결합제 종류에 따른 약물의 방출은 결합제의 물에 대한 용해도에 따라 달라짐을 확인할 수 있었다. 반투막 내의 다공의 형성은 SEM과 DSC를 이용하여 확인하였으며, 물에 대한 용해도가 큰 결합제를 사용한 반투막이 더 많은 양의 약물을 방출함을 확인하였다. 이 실험을 통해 삼투압을 이용한 과립의 약물방출은 과립 내부와 외부의 삼투압 차이와 반투막의 다공도에 의해 영향을 받는다는 것을 확인하였다.

• 대한환경공학회지
• /
• 제29권5호
• /
• pp.571-576
• /
• 2007

본 연구에서는 세 가지 다른 방법으로 제조된 망간사에 의한 용존 $Mn^{2+}$의 제거특성을 회분식 및 칼럼실험을 통하여 조사하였다. 실험실 규모에서 망간의 주입농도를 달리하여 망간사 제조시, 모래에 코팅된 망간 코팅량은 주입된 망간 농도에 비례하여 나타났다. 망간사에 의한 용존 망간의 제거는 용액의 pH 증가에 따라 증가하는 양이온형 흡착경향을 따랐다. 흡착을 통한 용존 망간의 제거는 망간사 코팅방법 및 코팅량에 거의 영향을 받지 않고 모든 pH 영역에서 유사하게 나타났다. NaClO를 산화제로써 주입하였을 때 망간사에 의한 용존 망간의 제거는 NaClO 농도에 비례하였다. 이러한 결과는 NaClO 주입농도 증가에 따라 용존 망간이 망간산화물로 산화되고 이때 생성되는 산화망간이 망간사 표면으로의 코팅이 증가되어 나타난 현상으로 여겨진다. 칼럼반응기를 이용한 용존 망간제거 실험에서, NaClO를 주입하지 않은 경우에는 4,100 bed volume 이 후 땅간의 파과가 이루어졌지만, NaClO를 주입하였을 경우에는 파과가 1.6배 지연되어 나타나서 산화제를 사용하는 것이 용존 망간의 제거율을 높이는 것임을 또한 확인할 수 있었다.

• 한국건축시공학회지
• /
• 제15권2호
• /
• pp.143-151
• /
• 2015

실환경에서는 비래염분 뿐만 아니라 자외선, 산성비, 산업공해 부유 물질 등의 여러 가지 복합 열화요소에 노출되어 있어 강재가 발청(發錆)하는 임계 비래염분량을 찾기에 어려움이 있다. 본 연구에서는 비래염분 시뮬레이터를 사용하여 인위적으로 비래염분 부착량을 조절하였으며 강재 마감별 5종을 대상으로 부식촉진 시험을 실시하였다. 그 결과 NC, UC, RLC-1, SS201에 각각 0.58~0.73, 7.89~8.46, 57.95~69.48, $80.73{\sim}89.35mg/dm^2$의 비래염분량을 부착시켰을 때 발청하는 것을 확인할 수 있었으며, 발청 후 부식속도는 각각 1.60, 0.36, 0.97, 0.17로 NC가 가장 빠른 부식속도를 가지는 것으로 평가 되었다.

• 멤브레인
• /
• 제29권5호
• /
• pp.263-275
• /
• 2019

본 연구에서는 종결정 크기, 종결정 코팅양, 수열 용액 숙성시간을 조절함으로써 분리층 두께가 제어된 모데나이트 제올라이트 분리막을 제조하고, 분리층 두께가 투과증발 물 투과유속에 미치는 영향을 90 wt.% 에탄올 수용액에서 고찰하였다. 유성 밀을 이용해 종결정을 분쇄시켜 20~30 nm 크기의 종결정을 제조하였고, 진공여과코팅 중에 종결정 용액의 농도와 통과된 양을 바꿔주면서 코팅양을 조절하였다. 제조된 분리막은 분리층 두께가 얇을수록 더 높은 물 투과유속을 나타내었으며, 약 $4{\mu}m$ 두께를 갖는 분리막의 경우, 760의 높은 물/에탄올 선택도와 $1.0kg/m^2h$의 높은 물 투과유속을 나타내었다. 이는 나노크기 종결정을 사용하여 $4{\mu}m$ 두께로 분리층을 얇게 만들었기 때문으로 판단된다. 따라서 본 연구로부터 종결정의 크기와 진공여과 코팅양, 수열 용액 숙성시간을 조절하는 것은 분리 층의 두께를 효과적으로 조절할 수 있는 방법임을 알았다. 또한, 모데나이트 제올라이트 분리층의 두께를 얇게 하는 것이 분리막의 물 투과유속을 증진시키는 중요한 방법임을 확인하였다.

• 한국세라믹학회지
• /
• 제52권4호
• /
• pp.264-268
• /
• 2015

Cu films were plated in an eco-friendly electroless bath (No-Formaldehyde) on Ni/screen printed Ag pattern/PET substrate. For electroless Cu plating, we used sodium-phosphinate ($NaH_2PO_2{\cdot}H_2O$) as reducing agent instead of Formaldehyde. All processes were carried out in electroless solution of pH 7 to minimize damage to the PET substrate. According to the increase of sodium-phosphinate, the deposition rate, the granule size, and rms roughness of the electroless Cu film increased and the Ni content also increased. The electroless Cu films plated using 0.280 M and 0.575 M solutions of sodium-phosphinate were made with Cu of 94 at.% and 82 at.%, respectively, with Ni and a small amount P. All electroless Cu plated films had typical FCC crystal structures, although the amount of co-deposited Ni changed according to the variation of the sodium-phosphinate contents. From these results, we concluded that a formation of higher purity Cu film without surface damage to the PET is possible by use of sodium-phosphinate at pH 7.

• Journal of Pharmaceutical Investigation
• /
• 제25권1호
• /
• pp.47-54
• /
• 1995

Transdermal patch formulations of estradiol to treat post-menopausal symptoms and prevent osteoporosis in women were developed and evaluated for the permeation characteristics through the excised hairless mouse abdorminal skin and the uterotropic effect on the ovariectomized rabbits. The design of patch formulations was optimized by varying several formulation parameters, such as type of enhancers, amount of enhancers, amount of drug loading and coating thickness. Compared to a commercially available transdermal product, several patch formulations showed the similar skin permeation profiles (following zero-order kinetics), but their skin permeation rates were lasted for the longer period (a week). In one-week uterotropic efficacy test in the ovariectimized rabbits, the selected patch formulations showed the positive effect in atrophy of the urogenital epithelium. The mean values of uterus weight in rabbits after application of patches containing estradiol were much higher than those in control group (containing no drug).