• Journal of Magnetics
• /
• v.5 no.2
• /
• pp.50-54
• /
• 2000

NiMn-pinned spin valve films consisting of a layered glass/NiFe/Co/Cu/Co/NiFe/NiMn/Ta stack were made by do magnetron sputtering. After deposition, the structure was annealed in a series of cycles each including three hours at $220^\circ C, 2\times10^{-6}$ Torr, in a field of 350 Oe, to create an ordered antiferromagnetic structure in the NiMn layer and produce a strong unidirectional pinning field in the pinned magnetic layer, Optimum spin valve properties were obtained after seven annealing cycles, or 21 hours at $220^\circ C$, and were : MR ratio 1%, exchange coupling field 620 Oe, and coercivity of pinned layer 250 Oe. The exchange coupling field remained constant up to an operating temperature of $175^\circ C$, and the blocking temperature was about $380^\circ C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.269-269
• /
• 2010

고주파 마그네트론 동시 스퍼터링법을 이용하여 $TiO_2$ 박막에 탄소를 도핑한 C/$TiO_2$ 박막을 제작하고, 박막의 두께와 탄소 도핑량에 따른 물리적, 광학적 특성을 조사하였다. 스테인레스강을 기판으로 사용하였으며, $TiO_2$ 박막과 기판의 열팽창계수 차이에 의한 크랙을 방지하기 위하여 Ti 박막을 DC 마그네트론 스퍼터링 장치를 이용하여 기판위에 증착시킨 후 실험을 진행하였다. EMP(Essential Macleod Program) 시뮬레이션을 이용하여 막의 층상구조, 두께, 물질변화를 통한 다양한 색상의 칼라를 구현하고 투과율, 반사율 등을 포함한 다양한 광학 특성을 사전 예측하였다. 제작된 박막은 투께 및 밀도에 따라 다양한 색상을 구현하였으며, 박막내의 흡수와 산란효과에 의해 굴절률이 감소하였다. 또한 순수 $TiO_2$ 박막보다 접합력 및 경도가 증가함을 알 수 있었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.05a
• /
• pp.27-30
• /
• 1996

In this paper, we prove through the experiments the possibility that Co-amorphous magnetic films can be used as high sensibility materials. We fabricate amorphous film of Fe$\sub$4.7/Co$\sub$74.3/Si$_2$B$\sub$19/ by using sputtering method at high frequency. Then, we not only measure the magnetic Properties of the annealed samples, but also observe the magnetic domain by using an Kerr effect optical-microscope. As the result, we find that the samples have high sensibility

• Proceedings of the KIEE Conference
• /
• 1999.11d
• /
• pp.929-931
• /
• 1999

BSCCO thin films have been fabricated by co-deposition at an ultralow growth rate using ion beam sputtering(IBS) method. Bi 2212 phase appeared in the temperature range of 750 and $795^{\circ}C$ and single phase of Bi 2201 existed in the lower region than $785^{\circ}C$. Whereas, ozone gas pressure dependance on structural formation was scarcely observed regardless of the pressure variation. And high quality of c-axis oriented Bi 2212 thin film with $T_c$(onset) of about 90 K and $T_c$(zero) of about 45 K is obtained. Only a small amount of CuO in some films was observed as impurity, and no impurity phase such as $CaCuO_2$ was observed in all of the obtained films.

• Korean Journal of Materials Research
• /
• v.5 no.5
• /
• pp.518-524
• /
• 1995

BST 박막을 Pt/Si$O_{2}$/Si 기판위에 co-sputtering 방법으로 형성할 때 열처리 조건이 BST 박막의 결정성과 전기적 특성에 미치는 영향에 관하여 연구하였다. BST 박막의 특성은 급속 열처리나 관상로 열처리과 같은 후열처리 온도보다 증착시의 기판온도에 따라서 민감하게 변화하였고, 기판 온도를 55$0^{\circ}C$로 하여 증착할대 Perovskite상이 가장 안정적으로 성장하여 유전율 1100, 유전손실계수 0.02로 우수한 유전특성을 나타내는 막을 형성할 수 있었다. BST 박막은 기판온도를 증가하면 정합에너지와 표면에너지를 최소로하는 (111) 방향으로 우선방위를 나타내었고 결정립의 조대화 현상으로 누설전류가 증가하였다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.1415-1417
• /
• 2009

High transmittance and low resistance index matched transparent conducting oxide (IMTCO) coated glass was prepared and characterized. IMTCO was deposited by RF magnetron sputtering with the thickness of 15nm and 90nm thick anti-reflection layer was evaporated. To modify surface to hydrophilic, in-situ plasma treatment was also performed. IMTCO coated glass exhibited 96.6% of transmittance in the wavelength range of 400~700nm which is relatively high value compared to commercially available IMTCO glass. The sheet resistance uniformity was measured to be 1.53%.

• Proceedings of the KIEE Conference
• /
• 2000.07c
• /
• pp.1779-1781
• /
• 2000

Pd doped $SnO_2$ thin film sensors were prepared on alumina substrate by rf magnetron sputtering method. The sensitivity of thin film was investigated by varying the heat-treatment temperature, film thickness and gas species. The thin film heat-treated at 600$^{\circ}C$ and film thickness of 5000${\AA}$ showed the highest sensitivity at an operating temperature of 400$^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.309-312
• /
• 1997

The Ce-Cr(-Ta) film are one of the most suitable candidates for perpendicular magnetic media. the control of the preparation conditions, such as Ar gas pressure P$\_$Ar/ substrates temperature T$\_$s/, films thickness $\delta$, deposition speed R$\_$d/, is considered to be important to attain ultra high density recording far perpendicular magnetic recording media. In this study, the Co-Cr thin films and Co-Cr-Ta thin films were deposited on the glass side substrates by using Facing Targets Sputtering apparatus(FTS). Crystallographic characteristics and magnetic characteristics were evaluated by X-ray diffractometry(XRD), Vibrating Sample Magnetometer(VSM) respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.491-492
• /
• 2005

본 연구에서는 $Al_2O_3$, $SiO_2$ 판상체 위에 저굴절 및 고굴절 금속 산화물을 다층 교차 증착하여 Pearl Pigment를 sputtering 공법을 이용하여 증착하였다. Pearl Pigment는 Essential Macleod program 을 이용한 색상과 증착된 pigment의 색상이 파장에 따라 blue, violet, pink, red, orange, yellow, green 등(Wave length 450~623 nm)으로 동일하게 나타났고, 기존의 제품에 비해 색상효과기 뛰어나고, 표면 morphology가 우수하였다. 광학 현미경 및 주사전자현미경(SEM)으로 막 두께, 표면 조직 및 입자 크기를 측정하였고, EDS, XRD를 이용하여 정성 및 정량 분석을 하였다.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.623-626
• /
• 1995

High coercivity thin $Fe_{3}O_{4}$ and ${\gamma}-Fe_{2}O_{3}$ films were deposited on Si substrate under well controlled $O_{2}$ partial pressure by dcreactive magnetron sputtering. The coercivity of as-deposited maggnetite films is below 640 Oe. After cxidizing at $360^{\circ}C$ for 10 minutes, the films transform to maghemite ${\gamma}-Fe_{2}O_{3}$ completely, and the coercivity increases greatly to 2100~4120 Oe, depending on modification of not with minor addition of Co or/and Mn. The orign of coercivity enhancement is attributed mainly to magnetic anisotropy arisen from interfacial stress. The addition of 5 at% Co and 5 at% Mn greatly enhances coercivity and squareness ratio. These films are potential for ultra-high density recording applications.