• Journal of the Korean Ceramic Society
• /
• v.53 no.3
• /
• pp.376-380
• /
• 2016

A composite electrode made of iron oxide nanoparticles/multi-wall carbon nanotube (iNPs/M) delivers high specific capacity and cycle durability. At a rate of $200mAg^{-1}$, the electrode shows a high discharge capacity of ${\sim}664mAhg^{-1}$ after 100 cycles, which is ~ 70% of the theoretical capacity of $Fe_3O_4$. Carbon black, carbon nanotube, and graphene as anode materials have been explored to improve the electrical conductivity and cycle stability in Li ion batteries. Herein, iron oxide nanoparticles on acid treated MWCNTs as a conductive platform are combined to enhance the drawbacks of $Fe_3O_4$ such as low electrical conductivity and volume expansion during the alloying/dealloying process. Enhanced performance was achieved due to a synergistic effect between electrically 3D networks of conductive MWCNTs and the high Li ion storage ability of $Fe_3O_4$ nanoparticles (iNPs).

• Journal of the Korean Ceramic Society
• /
• v.55 no.6
• /
• pp.581-589
• /
• 2018

This work concentrated on the effect of different laser beams on the microstructure and dielectric properties of $BaTiO_3$ nanoparticles at different calcinations times during the gelling preparation step. The nanoparticles were prepared by the sol-gel method. A green (1000 mW, 532 nm) and red laser beam (500 mW, 808 nm), were applied vertically at the center of stirring raw materials. The samples were sintered at $1000^{\circ}C$ for 2, 4, and 6 h. X-ray diffraction (XRD) analysis showed that samples prepared under the green laser have the highest purity. The FT-IR spectra showed that the stretching and bending vibrations of TiO bond without any other bonds, which are compatible to the X-ray diffraction (XRD) results. Samples were characterized by transmission electron microscopy (TEM), Scan electron microscopy (SEM), and UV-Visible spectrophotometer. Characterization showed the samples prepared under the green laser to have the highest particle size (~ 50 nm) and transparency for all sintering durations. Laser beam effects on electrical characterization were studied. BT nanoparticles prepared under the green laser show the higher dielectric constant, which was found to increase with sintering temperature.

• Journal of the Korean Ceramic Society
• /
• v.45 no.9
• /
• pp.512-517
• /
• 2008

In this study, yttrium-doped $SiO_2$ nanoparticles are synthesized using a reverse micelle technique combined with metal alkoxide hydrolysis and condensation. Spherical Y-doped $SiO_2$ nanoparticles with a uniform size distribution are prepared using selfassembly molecules in conjunction with the hydrolysis and condensation of organometallic precursors. The water/surfactant molar ratio influenced the Y-doped $SiO_2$ particles distribution of the core-shell composite particles and the distribution of Y doped $SiO_2$ particles was broadened as the water to surfactant ratio increased. The particle size of Y increase linearly as the $Y(NO_3)_3$ solution concentration increased. The average size of the cluster was found to depend on the micelle size, the nature of the solvent, and the concentration of the reagent. The effects of synthesis parameters, such as the molar ratio of water to surfactant and the molar ratio of water to TEOS, are discussed.

• Transactions of the Korean hydrogen and new energy society
• /
• v.24 no.6
• /
• pp.550-557
• /
• 2013

A glucose hydrothermal method is described for preparing hollow carbon spheres (HCS), which have a regular morphology and a high Brunauer-Emmett-Teller surface area of 28.6 m2/g. Scanning electron microscopy shows that they have thin shells and diameter between 2 and 8 ${\mu}m$. The HCSs were modified for the enhanced room temperature hydrogen storage by employing Ni nanoparticles on their surface. The Ni-decorated HCSs were characterized by X-ray diffraction, transmission electron microscopy coupled with an energy dispersive spectroscope, and an inductively coupled plasma spectrometer, indicating that fine and well-distributed Ni nanoparticles can be accomplished on the HCSs. The hydrogen uptake capacity in HCSs with and without Ni loading was evaluated using a high-pressure microbalance at room temperature under a hydrogen pressure upto 9 MPa. As much as 1.23wt.% of hydrogen can be stored when uniformly distributed Ni nanoparticles are formed on the HCSs, while the hydrogen uptake capacity of as-received HCSs was 0.41 wt.%. For Ni nanoparticle-loaded HCSs, hydrogen molecules could be easily dissociated into atomic hydrogen and then chemically adsorbed by the sorbents, leading to an enhanced capacity for storing hydrogen.

• Journal of Sensor Science and Technology
• /
• v.28 no.4
• /
• pp.256-261
• /
• 2019

In this study, mid-infrared transparent zinc sulfide (ZnS) ceramics were fabricated through hydrothermal synthesis with different molar ratios of S/Zn (S/Zn = 0.8, 1.0, 1.2, 1.4, and 1.6). The ZnS ceramics were sintered at a relatively low temperature of $850^{\circ}C$ to prevent the occurrence of the hexagonal phase featuring optical anisotropy. The phase composition, microstructure, and optical properties of the ZnS ceramics were subsequently investigated by employing X-ray diffraction, scanning electron microscopy, and Fouriertransform infrared spectroscopy. The results obtained indicate that the ZnS nanoparticles feature the cubic phase, without the hexagonal phase. Moreover, with increasing S, the crystallinity and particle size of the ZnS nanoparticles increased. The crystallinity and density of the ZnS ceramics improved when the molar ratio of S was higher than the molar ratio of Zn, thereby enhancing the transmittance. Furthermore, the ZnS ceramic with an S/Zn value of 1.2 was found to exhibit the highest transmittance of approximately 69% owing to the reduced occurrence of the hexagonal phase and a high density of 99.8%.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2008.02a
• /
• pp.346-346
• /
• 2008

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.6
• /
• pp.302-308
• /
• 2013

In this study, we report the synthesis and characteristics of gallium oxide ($Ga_2O_3$) nanoparticles prepared by the polymerized complex method. $Ga_2O_3$ nanoparticles were synthesized using $Ga(NO_3)_3$, ethylene glycol, and citric acid as the starting materials at a low temperature of $500{\sim}800^{\circ}C$. The temperature of the weight reduction by the loss of organic precursor was revealed using TG-DTA analysis. The crystal structural change of $Ga_2O_3$ nanoparticles by the annealing process was investigated by XRD analysis. The morphologies and the size distributions of $Ga_2O_3$ nanoparticles were analyzed using SEM.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.04a
• /
• pp.14.1-14
• /
• 2003

• Applied Chemistry for Engineering
• /
• v.27 no.1
• /
• pp.68-73
• /
• 2016

Silver nanoparticles were prepared by chemical reduction-protection method using 1-decanoic acid and tri-n-octylphosphine as surfactants, and using $NaBH_4$ as a reducing agent. The silver nanoparticles were also studied for their formation, structure, morphology and size using UV-Visible spectroscopy, XRD, TEM and SEM. Further the viscosity of the silver paste and the surface resistance of the silver metal film produced by screen coating onto a PET film were investigated. Well dispersed and quasispherical silver nanoparticles with the size of 10-200 nm were obtained under the optimal molar ratio of $NaBH_4/AgNO_3=1:5$. The surface resistance of silver metal film coated on the PET film made with the silver nanoparticles under the optimal molar ratio showed a minal value of $41{\mu}{\Omega}/cm^2$.

• Ceramist
• /
• v.23 no.2
• /
• pp.200-210
• /
• 2020

Supported catalysts are at the heart of manufacturing essential chemical, agricultural and pharmaceutical products. While the longevity of such systems is critically hinged on the durability of metal nanoparticles, the conventional deposition/dispersion techniques are difficult to enhance the stability of the metal nanoparticles due to the lack of control over the interaction between metal-support. Regarding this matter, ex-solution has begun to be recognized as one of the most promising methodologies to develop thermally and chemically robust nanoparticles. By dissolving desired catalysts as a cation form into a parent oxide, fine and uniformly distributed metal nano-catalysts can be subsequently grown in situ under reductive heat treatment, which is referred to ex-solution. Over the several years, ex-solved analog has resulted in tremendous progress in the chemical-electrochemical applications due to the exceptional robustness coupled with ease synthesis. Herein, we describe the ex-solution process in detail which therein introducing the unique characteristics of ex-solved particles that distinguish them from conventionally dispersed nanoparticles. We then go through the history of science regarding the ex-solution phenomena and summarize several major research achievements which embrace the ex-solved nanoparticles to markedly promote the catalytic performances. In conclusion, we address the remaining challenges and the future perspectives of this rapidly growing field.