• Journal of the Korea Concrete Institute
• /
• v.12 no.3
• /
• pp.3-10
• /
• 2000

In this study, we compared a plain mortar with the CAS-system shrinkage compensation mortar for Ondol that is Korean traditional heating system. The Ondol mortar is necessary to have properties as non-crack, fine flatness and stability for thermal changes. especially, mortar'crack prevention is to be most important property in Ondol mortar. To develope the stable material on the crack-prevention, we used to calcium-sulfo-aluminate(CSA)system in shrinkage compensation mortar. And so, we confirmed the effects of calcium-sulfo-aluminate(CSA) system for mortar's physical properties such as setting time, compressive strength and expansion ratio for crack prevention. The initial and final setting time of the CSA mortar is faster than plain mortar about 2hours. And, Compressive strength increased about 20% that plain mortar. The crack length per unit area, plain mortar is 0.426∼0.481m/m2. The Results of apartment construction field test, the shrinkage compensation mortar is excellent about the crack-reduce effect.

• Journal of Energy Engineering
• /
• v.27 no.1
• /
• pp.33-39
• /
• 2018

In this paper, we reviewed briefly about the barrier materials for the radioactive waste disposal. The primary concept of the radioactive waste disposal is safety. The goal of the radioactive waste management is to assure that the environment is not adversely affected and also public. There are a wide variety of materials are available for the radioactive waste disposal or storage. Among those coal fly ash is one of the significant materials are used as a barrier material. Here we reported, the Calcium sulfo aluminate (CSA) from coal fly ash is effectively suitable for the radioactive waste disposal. This is one of the ways of utilization of waste and manufactured the valuable materials for future indeeds.

• Korean Journal of Metals and Materials
• /
• v.46 no.7
• /
• pp.437-442
• /
• 2008

The synthesis and hydration of Calcium Sulfo Aluminate[$3CaO{\cdot}3Al_2O_3{\cdot}CaSO_4(C_4A_3{\overline{S}})$, CSA cement utilizing secondary steelmaking refining slags is studied for recycling the discarded steel plant wastes to meet the environmental requrations imposed on the steel industry. Raw materials of secondary refining slag, lime sludge, gypsum and bauxite were prepared to be sintered at $1,250^{\circ}C$. The sintered samples were hydrated for 1, 3 and 7 days to evaluate the mineralogical and physico-mechanical properties. The hydration products evaluated with the aid of SEM and XRD analyses confirmed the formation and the continuing growth of ettringite phase with the further hydration times, which plays a role in developing the early strength and the expansion properties of cements. The physico-mechanical properties of hydrated CSA products employing the recycled steelmaking refining slags determined in terms of compressive strength and linear expansion of hydrated products are found to be superior to those of the Ordinary Portland Cement(OPC) or the other commercial CSA cements.

• Resources Recycling
• /
• v.29 no.1
• /
• pp.53-61
• /
• 2020

This study aimed to develop a foam concrete material for a ground repair system that has low strength and low fluidity by using an eco-friendly binder, which substitutes industrial by-products for more than 90% of cement. Basic properties were evaluated after substituting a small amount of calcium sulfo aluminate (CSA) for the binder to improve the sinking depth rate and volume change, commonly found when it had a large amount of industrial by-products. The substitution rates of CSA for the eco-friendly binder used for the foam concrete were 2.5, 5, and 10%. Fresh properties, hardened properties, pore structure, and hydrates were analyzed. Experimental results showed that using only 2.5% of CSA could improve the deep sinking depth which occurred when using an eco-friendly binder. As a result, the weight difference between the upper, middle, and lower parts of cast specimens was improved even after being hardened. The addition of CSA also contributed to the formation of small, uniformly sized closed pores and improved initial strength. However, when the proportion of CSA increased, the long-term strength decreased. However, it satisfied the target strength when 5% or less of CSA was used. The results of this study revealed that it was possible to manufacture foam concrete with low strength and high fluidity for repairing ground satisfying target qualities by adding 2.5% of CSA to the eco-friendly binder containing a large amount of industrial by-products.

• Journal of Environmental Science International
• /
• v.29 no.6
• /
• pp.605-612
• /
• 2020

To improve the initial strength and stability of lightweight-foamed concrete, which shows suitable sound absorption and insulation characteristics, the effect of CO₂-reduced cement on the properties of the concrete was investigated. Various mixing ratios were applied by substituting a certain amount of slag and Calcium Sulfo Aluminate (CSA) in CO₂-reduced Ordinary Portland Cement (OPC) and the physical properties of the samples were examined using the Korean Standard. The kiln temperatures of the CSA were 100-200℃ ; these values are lower than those of OPC and can lead to energy saving. In addition, the low limestone content reduces greenhouse gas emissions by 20 %. Adding a small amount of CSA in OPC content activates Ca-Al-H₂-based hydrates, and the initial compressive strength of the concrete is improved. As the CSA content increased, the thermal conductivity of the concrete decreased by up to 8% compared to plain concrete, thus indicating an improvement in its insulation. Therefore, the settlement stability was improved as the addition of CSA shortened the setting time.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.3 no.3
• /
• pp.199-205
• /
• 2015

The mechanical and thermal properties of high temperature aluminate cementitious thermal storage materials were investigated in this paper. Alumina cement was used as basic binder and the effect of the replacement of fly ash, silica fume, calcium sulfo-aluminate and graphite for alumina cement was investigated. Experiments were performed to measure mechanical properties including compressive strength before and after thermal cycling, and split tensile strength, and to measure thermal properties including thermal conductivity and specific heat. Test results show that the residual compressive strengths of mixtures with alumina cement only, or alumina cement and silica fume were greater than those of the others. Additionally, the specific heat of mixture with graphite was largest in all the mixtures used in the study. The results of this study could be used to provide realistic information for material properties in thermal energy storage concrete in the future.

• Proceedings of the Korean Institute of Resources Recycling Conference
• /
• 2005.10a
• /
• pp.203-207
• /
• 2005

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.397-400
• /
• 2005

This study is a result that, in order to improve the early stage strength of fly ash, the calciumsulfoaluminate in which the generation of ettringite was very active in the early stage was substituted by some amount, and then the effect on the early stage was analyzed. when fly ash was substituted by 30$\%$, the strength dropped by maximum 54 $\%$ in the 3rd day of aging, compared to the cement mixture, but when CSA was substituted by 8 $\%$ in the fly ash amount, the strength improved at the 86 percent level of cement, it is suggested as an economical and effective method to improve the early-stage strength that CSA should be mixed by 8$\%$ compared to the fly ash amount used

• Journal of the Korean Ceramic Society
• /
• v.53 no.2
• /
• pp.215-221
• /
• 2016

In this study, the utilization of the by-products of various industries was examined using raw materials of CSA high-functional cement such as coal bottom ash, red mud, phosphate gypsum, etc. Technology to improve energy efficiency and reduce $CO_2$ was developed as part of the manufacturing process; this technology included lower temperature sintering ($150{\sim}200^{\circ}C$) than is used in the OPC cement manufacturing process, replacement of CSA cement with the main raw material bauxite, and a determination of the optimum mix condition. In order to develop CSA cement, a manufacturing system was established in the Danyang plant of the HANIL Cement Co. Ltd., in Korea. About 4,200 tons of low purity expansion agent CSA cement (about 16%) and about 850 tons of the lime-based expansion agent dead burned lime (about 8%) were produced at a rate of 60 tons per hour at the HANIL Cement rotary kiln. To improve the OPC cement properties, samples of 10%, 13%, and 16% of CSA cement were mixed with the OPC cement and the compressive strength and length variation rate of the green cement were examined. When green cement was mixed with each ratio of CSA cement and OPC cement, the compressive strength was improved by about 30% and the expansibility of the green cement was also improved. When green cement was mixed with 16% of CSA cement, the compressive strength was excellent compared with that of OPC cement. Therefore, this study indicates the possibility of a practical use of low-cost CSA cement employing industrial wastes only.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.3
• /
• pp.125-132
• /
• 2014

Steel fiber is a effective composite for crack resistance and improve structural performance under tensile loading. This study presents an evaluation of crack resistance and structural performance in cement mortar with steel fiber and expansion agent through internal chemical prestressing. For this work, cement mortar samples with 10% replacement of cement binder with CSA (Calcium-Sulfo-Aluminate) expansion agent and 1% volume ratio of steel fiber are prepared. Including basic mechanical properties, initial cracking load and fracture energy are evaluated in cement mortar beam with notch. Initial cracking load and fracture energy in cement mortar with CSA and steel fiber increase by 1.75 and 1.41~1.53 times compared with those in cement mortar with steel fiber. With optimum mix design for steel fiber and CSA expansive agent, the composite with chemical prestressing can be applied to various members and effectively improve crack resistance to external loading.