• The Korean Journal of Ceramics
• /
• 제1권3호
• /
• pp.147-151
• /
• 1995

Porous composite of $Al_2O_3$ and AIN based mullite and SiC can be prepared by alumium reaction synthesis and atmosphere controllied sintering in order to improve the durability of a gas filter body. The porous $Al_2O_3$-AIN-mullite, which has a strength of 168 kg/$\textrm{cm}^2$ and porosity of 51.59%, could be obtained by stmospheric firing at $1600^{\circ}C$ and the porous $Al_2O_3$-AIN-SiC with a porosity of 33% and strength of 977 kg/$\textrm{cm}^2$, could also be prepared. The average pore size has been changed from 0.2$\mu\textrm{m}$ in a reduction atmosphere and to 2$\mu\textrm{m}$ in an air atmosphere, respectively.

• 한국세라믹학회지
• /
• 제28권8호
• /
• pp.593-602
• /
• 1991

Al2O3 and NiO-doped Al2O3 powders were prepared from the ethanol solution of Al (NO3)3$.$9H2O and Ni(NO3)2$.$6H2O by spray pylolysis method using two-fluid nozzle. As a result of spraying test with 0.3 mol/{{{{ iota }} concentration starting solution, mean droplet sizes varied with 8.99∼9.69$\mu\textrm{m}$ and those standard deviation were 4.57∼5.12. As-prepared powders which were synthesized at 1000$^{\circ}C$ have spherical shape, sizes of 0.1∼3.0$\mu\textrm{m}$ and specific surface area of 22.34∼24.20㎡/g. Most powders consisted of {{{{ gamma }}-Al2O3 phase and transforned into ${\alpha}$-A;2O3 phase by calcination at 1100$^{\circ}C$ for 1 hr. NiO-doped Al2O3 sintered bodies had better sinterability than those of pure Al2O3 and 0.3 wt% NiO-doped Al2O3 had near theoretical density and dense microstructure.

• 대한환경공학회지
• /
• 제35권4호
• /
• pp.240-246
• /
• 2013

$SF_6$는 지구온난화지수가 가장 높은 중요한 온실가스이다. 본 연구에서는 마이크로파 조사에 따른 산화알루미늄이 혼합된 실리콘카바이드의 SF6 제거실험을 실시하였다. DRE (Decomposition and Removal Efficiencies)실험은 3,000 ppm의 $SF_6$를 사용하여 GC-TCD를 통하여 분석하였다. 산화알루미늄의 함량이 10~30 wt%까지 $SF_6$의 제거효율은 증가하였으나 산화알루미늄의 함량이 40~50 wt%에서 제거효율이 감소하였다. 특히 $900^{\circ}C$ 이상 에서 SiC-$Al_2O_3$ (20 wt%)와 SiC-$Al_2O_3$ (30 wt%)는 99.99%의 $SF_6$ 제거효율을 보여주었으며 SiC-$Al_2O_3$ (30 wt%)가 $700^{\circ}C$에서 96.72%의 제거효율을 보여주었다. 마이크로파 조사량과 산화알루미늄의 함량을 고려시 SiC-$Al_2O_3$ (30 wt%)가 $SF_6$ 제거에 가장 적절하였다. 본 연구의 결과로 마이크로파에 의한 $SF_6$ 제거시 SiC에 $Al_2O_3$의 함량 조절이 중요할 것으로 사료되어진다.

• 한국세라믹학회지
• /
• 제25권3호
• /
• pp.231-236
• /
• 1988

$Al_2O_3$ 기지에 미치는 2차상의 영향을 알아보기 위하여 SiC 입자를 5~20vol.% 분산시키고 소결조제로서 $TiO_2$ 또는 RY_2O_3$를 2.5wt.%첨가하여 180$0^{\circ}C$, $N_2$분위기 중에서 90분간 상압소결 하였다. SiC함량이 증가함에 따라 소결체의 밀도는 감소하였지만 기계적 물성은 증가하여 $Y_2O_3$를 소결조제로 첨가한 경우, 꺾임강도는 525MPa, 경도는 17.1GPa,파괴인성은 4.1 MPa.$m^{1/2}$ 정도의 최고값을 나타내었고 반면 $TiO_2$를 소결조제로 첨가한 경우 꺾임강도 285MPa , 경도 12.1GPa 정도의 값을 나타냈다. 그리고 이와 같은 기계적 물성의 증진은 주로 SiC의 복합화에 따른 균열의 편향과 $Al_2O_3$ 의 입자성장억제효과에 의한 것으로 밝혀졌다.

• 한국표면공학회지
• /
• 제47권2호
• /
• pp.93-98
• /
• 2014

The $Cr_2AlC$ carbides oxidized at 700, 850 and $1000^{\circ}C$ in air from 70 hours up to 360 days. They oxidized according to the reaction; $Cr_2AlC+O_2{\rightarrow}{\alpha}-Al_2O_3+CO(g)$. The scales consisted primarily of the thin, essentially pure $Al_2O_3$ layer and the underlying Al-dissolved $Cr_7C_3$ layer. They grew via the outward diffusion of Al and carbon, and the inward diffusion of oxygen. The oxidation resistance of $Cr_2AlC$ was excellent due to the formation of the protective $Al_2O_3$ layer. Even when $Cr_2AlC$ oxidized at $1000^{\circ}C$ for 360 days, the ${\alpha}-Al_2O_3$ layer was only about 4 ${\mu}m$-thick.

• 한국세라믹학회지
• /
• 제22권6호
• /
• pp.29-36
• /
• 1985

This study was carried out to research on the optimum condition of $MgAl_2O_4$ spinel synthesis and the chara-ceteristics of its sintered bodies. In this study the used materials-MgO $Al_2O_3$-were prepared from the extragrade chemicals $Mg(OH)_2 Al(OH)_3$ respectively. The tendency to spinel synthesis and sintering condition were discussed about additives of SEM and the characteristics of sintered bodies were measured by TMA etc, The results were as follows ; 1. The addion of $TiO_2$ promoted more effectively the sinterbility than that of $MnO_2$. 2. Residual $\alpha$-$Al_2O_3$ and MgO in theorectical composition samples were disappeared at 1$600^{\circ}C$ 3. When added MnO2 residual $\alpha$-$Al_2O_3$ and MgO were disappeared at 150$0^{\circ}C$ and 1$600^{\circ}C$ respectively. 4, . When added $TiO_2$ residual $\alpha$-$Al_2O_3$ and MgO were disappeared at 150$0^{\circ}C$ and 134$0^{\circ}C$ respectively.

• 한국세라믹학회지
• /
• 제33권4호
• /
• pp.405-410
• /
• 1996

The partial substitution of LiTaO3 with Al2O3 caused the variation of dielectric properties and a lower melting temperature yielding an easier growth of single crystal. The lattice constants and Raman band broadening were measured for the LiTaO3 solid solution in which the cations of Li+ and Ta5+ were partially substituted by Al3+ cation. The LiTaO3 type limit phases were obtained. ; Li1.15Al0.45Ta0.7O3 for cationic excess Li1.15Al0.45Ta0.7O3 for stoichiometry Li0.85Al0.05TaO3 for cationic deficit. The second phase was formed beyond the solubility limit. The limit phase (Li0.85Al0.05TaO3) in the region of cationic deficit showed the lowest Cuire temperature of 61$0^{\circ}C$ and melting point of 152$0^{\circ}C$ compared to the solid solutions in other regions (TMp=1$650^{\circ}C$, Tc=69$0^{\circ}C$ for LiTaO3)

• 한국세라믹학회지
• /
• 제38권12호
• /
• pp.1123-1131
• /
• 2001

재활용 $Al_2$O$_3$분말인 구조재료용 $Al_2$O$_3$세라믹스의 분쇄분말과 폐Al$_2$O$_3$흡착제의 첨가량과 입경에 따른 재생 $Al_2$O$_3$세라믹스의 소결특성을 조사하였다. 1,$650^{\circ}C$에서 5시간 소결한 순수 $Al_2$O$_3$시편을 급랭하여 분쇄한 -40과 +40$\mu$m의 $Al_2$O$_3$분말과 폐Al$_2$O$_3$흡착제를 순수한 $Al_2$O$_3$분말에 10~50wt% 첨가한 후, 재소결하여 재생 $Al_2$O$_3$세라믹스를 제조하였다. 재활용 $Al_2$O$_3$분말의 첨가량과 입경에 관계없이 소결온도가 증가함에 따라 시편의 밀도와 3점곡강도는 증가하였으나, 동일 소결온도에서는 재활용 $Al_2$O$_3$분말의 첨가량이 증가함에 따라 밀도와 3점곡강도는 감소하였다. ~30wt%의 $Al_2$O$_3$분쇄분말(-40$\mu$m), ~20wt%의 $Al_2$O$_3$분쇄분말(+40$\mu$m) 및 10wt%의 폐Al$_2$O$_3$흡착제를 첨가한 시편의 3점곡강도는 200MPa 이상이었다. 재생 $Al_2$O$_3$시편의 치밀화를 위하여 5~20wt%의 폐유리분말을 첨가하여 1200~1$650^{\circ}C$에서 5시간 소결한 시편은 폐유리분말의 첨가량이 증가함에 따라 최대 밀도와 3점곡강도를 나타내는 온도는 감소하였으나, 140$0^{\circ}C$이상에서는 페유리분말을 첨가하지 않은 시편에 비하여 밀도와 3점곡강도가 감소하여 재생 $Al_2$O$_3$세라믹스의 소결성 향상에는 기여하지 못하였다.

• 한국재료학회지
• /
• 제8권12호
• /
• pp.1158-1164
• /
• 1998

깁사이트를 황산수용액에 용해하여 제조된 황산알루미늄 용액에 에틸알코올을 사용하여 결정을 석출시킨 후 여과, 건조를 통하여 수황산알루미늄 결정 [$Al_2(SO_4)_3$ · $nH_2O$]을 제조하였다. XRD분석 결과 수황산알루미늄에 포함된 결정수는 n=18, 16, 12, 0이었으며, TG분석 결과 평균결정수($n_{av}$)는 14.7이었다. 수황산알루미늄을 열처리한 결과 $800^{\circ}C$에서는 무수황산알루미늄, $900^{\circ}C$와 $1000^{\circ}C$에서는 $\gamma-Al_2O_3$, $1200^{\circ}C$에서는 $\alpha-Al_2O_3$의 생성을 확인할 수 있었다. $\gamma-Al_2O_3$에 니켈피착을 위하여 0.025M농도의 황산알루미늄과 황산니켈을 사용하고 $Ni^{+2}$ 이온과 $Al^{+3}$ 이온의 농도비가 0.5인 혼합용액을 제조한 후 $\gamma-Al_2O_3$ 분말을 혼합하여 슬러리를 제조하였다 제조된 혼합슬러리에 우레아와 $NH_4OH$수용액을 첨가하여 pH를 9.0로 조절하고 $80^{\circ}C$에서 니켈피착을 하였으며, 니켈피착의 진행사항은 ORP(oxidation reduction potential), 전도도 그리고 pH값을 측정하여 관찰하였다. 니켈량에 따른 니켈피착 $\gamma-Al_2O_3$의 특성을 조사하기 위하여 피착된 $\gamma-Al_2O_3$를 $900^{\circ}C$에서 열처리하고 비표면적 변화와 열확산도를 측정하였다. 또한 $1250^{\circ}C$에서 니켈피착 $\gamma-Al_2O_3$의 열안정성은 비표면적과 XRD의 결정상변화로 확인하였다 니켈피착 $\gamma-Al_2O_3$의 표면은 XPS분석으로 Ni $2P_{3/2}$의 화학결합에너지의 변화를 확인한 결과 $NiAl_2O_4$, 상의 화학결합에너지가 증가되었다. 본 연구 결과로 니켈피착 $\gamma-Al_2O_3$가 순수 $\gamma-Al_2O_3$에 비하여 열적 안정성을 지닌 것으로 확인 되었다.

• 한국세라믹학회지
• /
• 제35권4호
• /
• pp.311-318
• /
• 1998

The reaction bonded alumina ceramics with reinforced particles which have low shrinkage were pro-duced by blending of SiC or TiC or ZrO2 powders to the mixture of Al metal and Al2O3 powder. The powd-ers were attrition milled isostantically pressed and preheated tio 110$0^{\circ}C$ with a heating rate of $1.5^{\circ}C$/min The specimens were then sintered at the temperature range 1500 to 1$600^{\circ}C$ for 5 hours with a heating rate of 5$^{\circ}C$/min. The specimens showed 5-9% weight gain and 2-9% dimensional expansion through the complete oxidation of Al after preheating up to 11--$^{\circ}C$ the overall dimensional change of the specimens after the reaction sintering at 1500-1$600^{\circ}C$ was 6-12% The maximum densities were 92% theoretical. The fine grain-ed(average grain size :0.4 ${\mu}{\textrm}{m}$) microstructure were observed in the specimen with ZrO2 and SiC. But the microstructure of specimen with TiC was relatively coarse.(average grain size : 2.1 ${\mu}{\textrm}{m}$) The mullite phase was formed by the reaction of Al2O3 and SiO2 in a specimen with SiC. In the TiC contained specimen TiC was oxidized into TiO2 and finally reacted with Al2O3 to form Al2TiO5 during sintering.