• Elastomers and Composites
• /
• 제44권2호
• /
• pp.175-181
• /
• 2009

편광필름용 점착제를 합성하기 위해 아크릴 모노머를 사용하여 용액중합을 수행하였다. 아크릴 모노머는 2-ethylhexyl acrylate, butyl acrylate, acrylic acid를 사용하였으며, 개시제는 benzoyl peroxide, 용매는 ethyl acetate가 사용되었다. 모노머의 비율은 점착제의 유리전이온도 $-40^{\circ}C$에 맞추어 2-ethylhexyl acrylate: butyl acrylate: acrylic acid = 25:50:3.6 이였다. 개시제의 첨가량은 점착제의 젖음성과 초기점착력을 고려하여 모노머 대비 0.09%로 결정하였다. 모노머와 용매의 비율은 젖음성과 투과율을 고려하여 1:1.7로 하였다. 점착제 필름의 투과율은 점도가 낮을수록, 분자량이 작을수록, 분자들 간의 얽힘이 적어져서 굴절율이 낮아지고 투과율이 증가함을 알 수 있었다. 사용가능 기간의 측정에서 모노머와 용매의 비율이 1:1.7일 경우 점도가 200분이 지나도 커다란 변화가 없어 저장안정성이 좋음을 확인할 수 있었다.

• Bulletin of the Korean Chemical Society
• /
• 제23권2호
• /
• pp.320-324
• /
• 2002

Binary cure system is composed of different two cure accelerators, which can cause a synergy effect to delay the scorch time and to increase the cure rate. In this study, binary cure systems between 1,6-bis(N,N'-dibenzylthiocarbamoyldithio)-hexane (DBTH) and benzothiazole sulfenamides were investigated using carbon black-filled natural rubber compounds. N-Cyclohexyl-2-benzothiazole sulfenamide (CBS), N-tert-butyl-2-benzothiazole sulfenamide (TBBS), and 2-(morpholinothio) benzothiazole (MOR) were employed as benzothiazole sulfenamides. The binary cure systems show scorch safty at high temperature. The binary cure systems have faster cure rate and better reversion resistance than the single cure system of the benzothiazole sulfenamides. DBTH is found to be more effective to decrease the viscosity of a compound than the benzothiazole sulfenamides. Physical properties of the vulcanizates with the binary cure system are better than those of the vulcanizates with the single one.

• 한국임상수의학회지
• /
• 제24권2호
• /
• pp.201-207
• /
• 2007

The teat cup liner compounds with improved physical property were developed using tri-polymer blend of natural rubber(NR), ethylene propylene diene monomer rubber(EPDM) and butyl rubber, and the changes of the physical properties of compounds were measured under various conditions such as standard, thermal, alkaline detergent and acid solutions aging conditions. The hardness of the new teat cup liner compound 1 was 50 and that of the compound 2 was 51 under standard condition. The tensile strength and elongation of the new compound 1 were $154kgf/cm^2$ and 675% under the standard condition, respectively. Also, those of the new compound 2 were 180 kgf/cm and 634% under the same condition. Their hardness were increased about $2{\sim}6%$ and the tensile strength and elongation were decreased about 10% under the $25^{\circ}C$ water and detergent solutions. Even though the new teat cup liner compounds exhibited so much decreased tensile properties under the $105^{\circ}C$ thermal aged condition, they sustained more stable aged physical properties including tensile strength and elongation than those of imported teat cup liner materials. Consequently, the new teat cup liner compounds would give prolonged lift cycle if they are used as a teat cup liner product.

• 폴리머
• /
• 제32권6호
• /
• pp.555-560
• /
• 2008

폴리머를 혼입한 폴리머 시멘트 모르타르 및 콘크리트는 인장강도, 휨강도, 접착성, 수밀성, 내마모성 그리고 내약품성 등을 개선시키는데 우수한 효과가 있어 고성능이 요구되어지는 건축 구조물의 외장재, 바닥 마감재, 포장재, 방수재, 장식 코팅재, 그리고 보수재 등의 용도로 많이 사용되고 있다. 또한, 기존의 시멘트 콘크리트의 취약성을 보완하는 측면뿐만 아니라 보다 내구적이고 안정적인 구조재료의 역할을 할 수 있어 다양한 용도의 개발이 이루어지고 있다. 본 연구에서는 폴리머를 건축재료인 시멘트 콘크리트에 적용하기 위한 기초적 실험으로써 폴리머 시멘트 모르타르를 제작하여 그 특성을 파악하고 건축재료로서의 폴리머 이용 가능성을 확인하고자 하였다. 폴리머를 시멘트 모르타르에 혼입하여 적용해 본 결과, 보통 시멘트 모르타르에 비해 폴리머 시멘트 모르타르의 강도와 내구성 증진효과가 높게 나타나는 것을 알 수 있었다.

• Elastomers and Composites
• /
• 제29권5호
• /
• pp.444-452
• /
• 1994

Emulsion graft copolymerizations of vinyl monomers, butyl acrylate(BA), methyl methacrylate(MMA), 2-ethylhexyl acrylate (EHA), glycidyl methacrylate (GMA), 2-hydroxyethyl methacrylate(HEMA), methacrylonitrile(MAN), dimethylaminoethyl methacrylate(DAMA) or 2-vinyl pyridine(VP), onto carboxyl-terminated SBR latex were carried out under different experimental conditions. In case of synthesizing SBR-g-poly(butyl acrylate), the degree of grafting was increased with increasing the amount of emulsifier, polymerization temperature and the amount of initiator. Pull-out strength of resorcinol-formaldehyde-latex(RFL) adhesives formulated with modified latexes was very higher than that of RFL adhesive formulated with ungrafted latex. When the modified latexes with GMA, HEMA, MAN, DAMA or VP were used, the break occurred at cords. Peel strength of RFL adhesives formulated with SBR-g-poly(GMA), SBR-g-poly(HEMA) or SBR-g-poly(VP) was higher by about 1.3 times than that of RFL adhesives formulated with unmodified SBR against nylon cord and was higher by about 2.0 times against polyester cord.

• Journal of Information Display
• /
• 제4권1호
• /
• pp.17-23
• /
• 2003

A thermoset type anisotropic conductive adhesive film (ACAF) comprising epoxy resin and natural butyl rubber (NBR) as the binder, micro-encapsulated imidazole as the curing agent, and Ni/Au coated polymer bead as a conductive particle has been studied. These films have been prepared to respond to requirements such as improved contact resistance, current status less of than 60 ${\mu}m$ and reliability. These films can also be used for connection between the ITO glass for LCD panel and the flexible circuit board. The curing conditions for the connection were 40, 20 and 15 seconds at 150, 170 and 190 $^{\circ}C$, respectively. The initial contact resistance and adhesion strength were 0.5 ${\Omega}/square$ and 0.4 kg/cm under the condition of 30 kgf/$^{cm}^2}$, respectively. After completing one thousand thermal shock cycling tests between -15 $^{\circ}C$ and 100 $^{\circ}C$, the contact resistance was maintained below 0.7 ${\Omega}/square$. Durability against high temperature (80$^{\circ}C$) and high humidity (85 % RH) was also tested to confirm long-term stability (1000 hrs) of the conduction.

• Elastomers and Composites
• /
• 제45권4호
• /
• pp.256-262
• /
• 2010

[ $80\;^{\circ}C$ ] 346 bar 상태의 초임계 이산화탄소 내에서 methyl acrylate, ethyl acrylate, butyl acrylate와 glycidyl methacrylate을 중합하였다. 초임계 이산화탄소 분산매에서의 중합을 위하여 aminopropyltriethoxysilane을 사용하여 glycidyl methacrylate를 monoglycidyl ether terminated PDMS에 결합시킨 glycidyl methacrylate linked poly(dimethylsiloxane)(GMS-PDMS)를 계면활성제로 사용하였다. $CO_2$에서 합성된 Poly(alkyl acrylate)의 수율은 acrylate 단량체의 알킬기가 커질수록 낮아졌다. Poly(glycidyl methacrylate)와 poly(methyl acrylate)는 구형으로 만들어진 반면, poly(ethyl acrylate)와 poly(butyl acrylate)는 점성의 액상으로 합성되었다. Poly(glycidyl methacrylate) 입자의 수평균직경은 2.45 ${\mu}m$이며 입자 직경의 분포는 매우 좁았다. poly(methyl acrylate)의 수평균직경은 0.52 ${\mu}m$이며 입자크기는 bimodal로 분포되었다. 초임계 이산화탄소에서 중합된 poly(glycidyl methacrylate)와 poly(alkyl acrylate)들의 유리전이온도는 통상의 방법으로 중합된 poly(glycidyl methacrylate)와 poly(alkyl acrylate)의 유리전이온도보다 4~9 K 높게 측정되었다.

• Elastomers and Composites
• /
• 제52권4호
• /
• pp.272-279
• /
• 2017

The heterocoagulation of latex is a simple and useful method to fabricate various polymer nanocomposites in which a precise control of the colloid stability is essential. In this work, a multi-layered graphenes (MLGs)/poly(styrene-co-butyl acrylate) (P(S-co-BA)) nanocomposite having an excellent dispersion of MLGs was prepared via the sudden heating heterocoagulation process. The P(S-co-BA) component was obtained by emulsion polymerization. This process can effectively shorten the process and particles growth steps. The colloid stability of these dispersions was controlled by factors such as ionic charge, temperature, and reaction times. The influence of these factors on heterocoagulation was evaluated and the properties of the nanocomposites were investigated. The conductivity of the MLGs/P(S-co-BA) nanocomposites increased from -11.53 to -5.70 S/cm for an increase in MLG content from 0.01 to 5 wt%. Moreover, percolation threshold was observed in the case of 0.01 wt% MLGs.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2012년도 추계 학술논문 발표대회
• /
• pp.261-262
• /
• 2012

The field application through the quality control of self adhesive rubberized asphalt waterproofing sheet was regulated by KS F 4934 of Korea Standard in 2003. However, regulations that different material properties of self-Adhesive waterproofing sheets are difficult on the standard. Therefore, this research was performed for of quality control all affiliations of self-adhesive waterproofing sheet through basic properties test and proposed quality standard revised bill in KS F 4934.

• 대한화학회지
• /
• 제6권2호
• /
• pp.99-103
• /
• 1962

The usefulness of a propionylated paper chromatography to the identification of various insoluble organic antioxidants in rubber vulcanizates was studied. Purified commercial antioxidants and commercially mixed antioxidants could be identified by the propionylated paper chromatography. Antioxidants were identified by the propionylated paper chromatography from acetone extract of pure gum vulcanizates, which were either unaged or aged in Geer-Oven. The $R_f$ values from acetone extracts of vulcanizates were a little lower than those purified samples, but the colours and shapes of the spots support the identification. No spot could be obtained by the method from the aged vulcanizate containing antioxidant 200 (2,6 Di-tert-butyl-p-cresol). This indicates that the antioxidant was converted or decomposed to other compound after aging. It was concluded from the above results that the propionylated paper chromatography is useful to identify the antioxidants from vulcanizates and presents a key for elucidating the mechanism of the inhibition.