• Journal of the Korea Concrete Institute
• /
• v.26 no.4
• /
• pp.421-428
• /
• 2014

This paper describes the experimental results of insulated concrete sandwich wall panels (CSWP) with corrugated glass fiber-reinforced polymer (GFRP) shear connectors under in-plane shear loading. Corrugated GFRP shear connectors were used to improve the thermal property of insulated CSWP and to achieve composite action between the interior and exterior concrete wall panels. Test specimens were consist of three concrete panels with two insulation layers between concrete panels and middle concrete panels was loaded in the direction of gravity. To evaluate the effects of insulation types (extruded polystyrene, XPSS and expanded polystyrene, EPS), shear connector pitch (300 and 400 mm) and width (10 and 15 mm) on in-plane shear behavior of insulted CSWP, failure mode and shear flow-average relative slip relationship of specimens were investigated. Test results indicate that the bond stress between concrete panel and insulation is considerable initially. Especially in case of insulated CSWP without shear connector, initial stiffness of CSWP with XPSS is superior to that of CSWP with EPS. The shear connector's contribution to in-plane shear performance of insulated CSWP depends on the type of insulation.

• Journal of the Korea Concrete Institute
• /
• v.20 no.5
• /
• pp.611-618
• /
• 2008

CFRP (carbon fiber reinforced polymer) tendons can be used as an alternative to solve the corrosion problem of steel tendons. Since CFRP tendons are vulnerable to transverse pressure and stress concentration, the conventional anchorage system used for steel tendons can create an unreliable load carrying capacity and may result in a premature failure. Therefore, it is necessary to develop the anchorage system that is well suited for CFRP tendons. There are many types of anchorage systems for CFRP tendons, which can be classified into three types: wedge-type anchorage, bond-type anchorage, and compression-type anchorage. This paper deals with the compression-type anchorage system manufactured through swaging technology. Based on the previous test results performed by the authors, the dimension of anchorage sleeve, the use and non-use of the insert, and the compression pressure on the sleeve have been selected as the major parameters affecting the performance of the compression-type anchorage. Some anchorage sleeves have been tapered to reduce the stress concentration. Test results revealed that the performance of the anchorage system depends mainly on the dimension and the compression pressure. It has been verified that the tapered sleeve can effectively reduce the stress concentration.

• Journal of the Microelectronics and Packaging Society
• /
• v.22 no.1
• /
• pp.69-74
• /
• 2015

With difficulties during the cleaning of reflow flux residues due to the decrease of the part size and interconnection pitch in the advanced electronic devices, the need for the no-clean solder paste is increasing. In this study, an epoxy curable solder paste was made with SAC305 solder powder and the curable flux of which the main ingredient is epoxy resin and its reflow solderability, flux residue corrosivity and solder joint mechanical properties was investigated with comparison to the commercial rosin type solder paste. The fillet shape of the cured product around the reflowed solder joint revealed that the curing reaction occurred following the fluxing reaction and solder joint formation. The copper plate solderability test result also revealed that the wettability of the epoxy curable solder paste was comparable to those of the commercial rosin type solder pastes. In the highly accelerated temperature and humidity test, the cured product residue of the curable solder paste showed no corrosion of copper plate. From FT-IR analysis, it was considered to be resulted from the formation of tight bond through epoxy curing reaction. Ball shear, ball pull and die shear tests revealed that the adhesive bonding was formed with the solder surface and the increase of die shear strength of about 15~40% was achieved. It was considered that the epoxy curable solder paste could contribute to the improvement of the package reliability as well as the removal of the flux residue cleaning process.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.285-288
• /
• 2008

A model for the effective moment of inertia $I_{\epsilon}$ as expressed in Branson's equation, in which reduction of the flexural rigidity of RC beams due to cracking are aptly taken into accoun,t is presented. However, KCI Code isn`t considered tension stiffening as it is in debonding of reinforcing bar. Therefore, this equation need to set up suitable to our design Code. The experimental work consisted of casting and testing a total of 6 simply supported reinforced concrete beams and a total of 4 continuos reinforced concrete beams under two point concentrated loads. Main parameters are concrete strength, coverage, bond between concrete and reinforcing bars, are known as have an effect on deflection and tension stiffening. Every test beams had the same $250{\times}350$mm rectangular section, with a simply supported clear span of 4,400 mm and a continuos clear span of 6,500 mm. Comparison of the test results with values obtained using the KCI Code equation of the effective moment of inertia showed a noticeable difference.

• Restorative Dentistry and Endodontics
• /
• v.27 no.1
• /
• pp.44-53
• /
• 2002

목적 : 최근 개발된 bonding agent 중 일부는 다양한 함량의 filler를 포함하고 있으며 filler의 첨가는 bonding agent의 기계적인 물성을 향상시킴으로써 접착력의 향상에 기여한다는 주장이 있다. 본 연구에서는 다양한 함량의 filler를 포함한 adhesive를 실험적으로 만들어, filler의 함량이 전단접착강도에 미치는 영향을 살펴보고 임상적으로 가장 적절한 filler의 함량을 알아보고자 하였다. 또 adhesive의 간접인장강도를 측정하여 adhesive의 기계적인 물성과 접착력과의 상관관계를 알아보았다. 방법 : 발거된 건전한 70개의 대구치를 투명 레진에 매몰하고 상아질면을 노출시켰다. 3M사의 Scotchbond Multipurpose의 etchant와 primer를 제조사의 지시대로 적용하고 1$\mu\textrm{m}$크기의 barium glass filler를 0, 5, 10, 15, 20, 30, 45wt% 포함하도록 실험적으로 제작한 adhesive를 도포한 후 레진을 충전하여 시편을 완성하였다. Instron으로 0.5mm/min의 속도에서 전단접착강도를 측정하고 그 단면을 입체현미경으로 관찰하여 파절의 양상을 확인하였다. Filler함량에 따른 adhesive의 후경을 측정하기 위해 상기한 방법으로 시편을 제작하여 주사 전자현미경으로 관찰한 후 Sigmascan을 이용하여 그 후경을 측정하였다. 또, 지름 4mm 높이 6mm의 원통형 시편을 제작하여 Instron로 간접인장강도의 측정을 시행하였다. 얻어진 결과는 Kruskal-Wallis test와 Mann-Whitney test를 시행하여 분석하였으며, 상관관계를 분석을 위해 Pearson Product Moment Correlation Coefficient를 구하였다. 결과 : 1) Filler함유량에 따라 전단접착강도는 유의할 만한 차이를 보였다(p<0.05). 2) Filler함량의 증가에 따라 전단접착강도는 유의하게 증가하여 15% 수준에서 가장 높은 갈(19.9$\pm$1.38Mpa)을 보였으며 20% 이상의 수준에서는 유의하게 감소하였다(p<0.05). 3) Adhesive의 간접인장강도는 20% 수준까지는 증가하는 양상을 보였으나 통계적 유의성은 없었으며(p>0.05), 30% 이상에서는 유의할 만한 감소를 보였다(p<0.05). 4) Adhesive의 후경은 0% 수준에서 5.97$\pm$1.23$\mu\textrm{m}$부터 45%수준에서 73.37$\pm$11.7$\mu\textrm{m}$까지 유의하게 증가하였다(p<0.05). 5) Filler함량에 따른 Adhesive의 간접인장강도와 전단접착강도는 상관관계가 없었다.

• Tunnel and Underground Space
• /
• v.28 no.1
• /
• pp.97-110
• /
• 2018

The application of sprayed waterproofing membrane with high adhesion and ductility is considered to be promising as a measure for repair and reinforcement of a tunnel structure. Therefore, a powder-type and one-component membrane prototype with high tensile and bond strengths was made in this study. Then, its reinforcement effect on a shield segment was evaluated by carrying out a series of full-scale loading tests of segment specimens on which the membrane was sprayed. From the tests, it was confirmed that the initial cracking loads increased by approximately 34% due to cracking retardation by membrane coating. Even though the increase of failure loads were not so high as cracking loads, the strain-softening behaviors were observed from specimens coated by the membrane. Therefore, it is expected that the membrane coated on the inner surface of a lining might be effective in preventing its brittle failure.

• Journal of the Korean Geosynthetics Society
• /
• v.11 no.2
• /
• pp.39-47
• /
• 2012

This paper describes large-scale pullout test results of geosynthetic strip, which can be applied in reinforced earth wall with block-type wall facing. The pullout tests are conducted to evaluate the strain distribution, the induced pullout force and the pullout strength. The maximum pullout force is appeared regardless of reinforcement width and normal stress when end displacement is less than 15 mm. The pullout behavior based on horizontal spacing of reinforcement was similar in relationship between pullout force and end displacement. The strain distribution and pullout force distribution of the geosynthetic strip are concentrated in the front part of reinforcement, and it appeared clearly in higher normal stress condition This means that the pullout behavior of geosynthetic strip is affected by the bond between soil and friction resistance reinforcement according normal stress. Therefore, the pullout resistance design is reasonable when pullout behavior of geosynthetic strip should be evaluated by effective length considering tensile characteristic.

• Journal of the Earthquake Engineering Society of Korea
• /
• v.10 no.1 s.47
• /
• pp.41-49
• /
• 2006

Through the 1982 Urahawa-ohi and the 1995 Kobe earthquakes, a number of bridge columns were observed to develop a flexural-shear failure due to the bond slip as a consequence of premature termination of the column longitudinal reinforcement. Because the seismic behavior of RC bridge piers is largely dependent on the performance of the plastic hinge legion of RC bridge piers, it is desirable that the seismic capacity of RC bridge pier is to evaluate as a curvature ductility. The provision for the lap splice of longitudinal steel was not specified in KHBDS(Korea Highway Bridge Design Specification) before the implementation of 1992 seismic design code, but the lap splice of not more than 50%, longitudinal reinforcement was newly allowed in the 2005 version of the KHBDS. The objective of this research is to investigate the distribution and ductility of the curvature of RC bridge column with the lap splice of longitudinal reinforcement in the plastic hinge legion. Six (6) specimens were made in 600 mm diameter with an aspect ratio of 2.5 or 3.5. These piers were cyclically subjected to the quasi-static loads with the uniform axial load of $P=0.1f_{ck}A_g$. According to the slip failure of longitudinal steels of the lap spliced specimen by cyclic loads, the curvatures of the lower and upper parts of the lap spliced region were bigger and smaller than the corresponding paris of the specimen without a lap splice, respectively. Therefore, the damage of the lap spliced test column was concentrated almost on the lower part of the lap spliced region, that appeared io be failed in flexure.

• Journal of the Korea Concrete Institute
• /
• v.20 no.4
• /
• pp.423-430
• /
• 2008

VES-LMC (very-early strength latex-modified concrete) has been widely used as repair material for bridge deck overlay or rehabilitation, because the overlaid or repaired could be opened to the traffic after 3 hours of curing. Although the field performance of VES-LMC generally indicates that it has an excellent bonding to the substrate and shows a long term performance, little quantitative data or research results have been presented in the literature on structural studies. The purpose of this study was to investigate the flexural behavior, interfacial performance, crack propagation, and strengthen effect of RC beam overlaid or repaired by VES-LMC through the 4-point flexural loading test. Two different types of RC beam were fabricated for repair and rehabilitation types. The test result showed that the strengthen effect, in term of flexural stiffness, increases as the depth of repair or overlay increases. More than 40% of stiffness was improved when the depth of repair was up to steel position. However, there was a little difference between 80 mm and 120 mm repaired beam. This means the repair depth must be considered. The interfacial behavior data showed that the repaired or overlaid beams had a little relative displacement. This means that two materials behave comparatively acting together. However, there were two specimens which had large displacement at the interface, because of poor bond strength. This suggested that interface treatment is one of the most important jobs in composite beams.

• Polymer(Korea)
• /
• v.36 no.4
• /
• pp.413-419
• /
• 2012

Multi-functional urethane acrylate monomers as the curing agent of poly(phenylene ether) (PPE) were synthesized and then the urethane bond formation was checked by FTIR spectrometry and NMR analysis. The synthesized monomers were mixed with PPE and fabricated to dielectric substrates. After forming PPE/monomer composite sheets by a film coater, several sheets were laminated to a test substrate in a vacuum laminator and then its properties depending on the type and the amount of monomers, such as dielectric constant, dielectric loss, and peel strength, were measured. Between the two different hydroxyl acrylates, when the monomer synthesized with 2-hydroxy-3-phenoxypropyl acrylate containing a phenyl group was used as a curing agent, a smaller dielectric loss was obtained and the dielectric constant and loss decreased with a decrease in the amount of the monomer. The peel strength values of the test substrates, however, did not show any specific difference between the cases of two synthesized monomers. As a result, it was obtained the polymer substrate for high frequency application having peel strength of about 10 N, low dielectric constant of 2.54, and low dielectric loss of 0.0027 at 1 GHz.