• Advanced Composite Materials
• /
• v.16 no.4
• /
• pp.377-384
• /
• 2007

'Green' composites were fabricated from poly lactic acid (PLA) and bamboo fibers by using a conventional hot pressing method. The insulating properties of the PLA-bamboo fiber 'green' composites were evaluated by determination of the thermal conductivity, which was measured using a hot-wire method. The thermal conductivity values were compared with theoretical estimations. It was demonstrated that thermal conductivity of PLA-bamboo fiber 'green' composites is smaller than that of conventional composites, such as glass fiber reinforced plastics (GFRPs) and carbon fiber reinforced plastics (CFRPs). The thermal conductivity of PLA-bamboo fiber 'green' composites was significantly influenced by their density, and was in fair agreement with theoretical predictions based on Russell's model. The PLA-bamboo fiber composites have low thermal conductivity comparable with that of woods.

• Journal of the Korean Wood Science and Technology
• /
• v.47 no.3
• /
• pp.336-343
• /
• 2019

Effects of a novel mold inhibitor specifically for bamboo, on the properties of composite products have been confirmed in this study. The mechanical and dimensional stability properties of bamboo fiber-based composites (BFBCs) from different bamboo species were also investigated. The results showed that Burmanica Gamble possessed the highest values of modulus of elasticity (MOE) of 33.2 GPa, modulus of rupture (MOR) of 286.9 MPa, compressive strength of 182.6 MPa and shear strength of 24.0 MPa. By contrast, Phyllostochys heterocycla among all of species showed the lowest MOE of 16.3 GPa, MOR of 170.3 MPa and compressive strength of 128.9 MPa were the lowest among all of species. Moreover, there is a remarkable variation in the swelling and water absorption between the samples with 4 h and 28 h water immersion treatment, especially Phyllostachys iridenscens. Overall, the results suggested that TCIT (Tebuconazole and 3(2H)-isothiazolone) had no significant effect on the mechanical properties compared with the control condition, and it would be utilized as an antimould of BFBCs manufacturing.

• Applied Chemistry for Engineering
• /
• v.29 no.2
• /
• pp.168-175
• /
• 2018

In order to investigate the effect of the chemical treatment of bamboo fiber on physical properties of polypropylene (PP)/bamboo fiber (BF) composites, silane coupling agents such as ${\gamma}$-aminopropyltriethoxysilane (APS), ${\gamma}$-glycidoxypropyl-trimethoxysilane (GPS) and ${\gamma}$-mercaptopropyltrimethoxysilane (MRPS) were applied to BF and alkaline treated BF. Morphological properties of the chemically treated BF were confirmed by optical microscope and SEM measurements, and chemical structure changes were confirmed by FT-IR and EDS. TGA results showed that the thermal stability of silane treated BF increased. Based on the analysis of a universal testing machine and an Izod impact test, the flexural and impact properties of PP/silane treated BF composites showed higher values than those of PP/BF composites. The enhancement of interfacial adhesion properties of the PP/BF composite was checked from SEM images of the fracture of specimens after the tensile test.

• Composites Research
• /
• v.35 no.6
• /
• pp.456-462
• /
• 2022

Since natural fibers are highly flammable, it is not easy to make them flame retardant. In this study, a liquid flame retardant based on phytic acid, APTES, and Thiourea, which are flame retardant candidates derived from nature, was prepared and its performance was verified through flame retardant treatment and flame retardancy evaluation of bamboo fibers. When a liquid flame retardant is used, it is possible to treat a large amount of natural fibers with flame retardant treatment. Nine types of flame-retardant treated bamboo fibers were prepared according to the Taguchi design of experiment method. Thereafter, vertical burning test and microcalorimeter test were performed for flame retardancy evaluation, and the surface of natural fibers before and after flame-retardant treatment was compared using scanning electron microscope. The results show that phytic acid has a significant effect on improving the flame retardancy of natural fibers. Through microstructure analysis, it was assumed that the phytic acid helps flame retardant to uniformly adhere to the surface of natural fibers. If such research results are utilized, it is possible to make a large amount of natural fibers high flammability in an eco-friendly way, which is expected to be advantageous for the application of prototypes.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.4
• /
• pp.355-361
• /
• 2018

In this study, the dimensional stability and mechanical properties of bamboo fiber-based composites (BFBCs) were studied at two pressing manufacturing processes, i.e., hot- and cold- pressing, and were compared with three density parameters (1.0, 1.1, and $1.2kg/m^3$). Width swelling ratio (WSR), thickness swelling ratio (TSR), and water absorption ratio (WAR) were calculated for water immersions of 4 and 28 h. WSR, TSR, and WAR for specimens immersed for 28 h were higher than those for 4 h treatment, which shows that the immersion time has a significant influence on the dimensional stabilities of BFBCs. Moreover, the positive linear relations between density and dimensional were observed at both the pressing ways, indicating that the WSR, TSR, and WAR decreased with an increase in the density of BFBCs. The compressive strength, shear strength, modulus of rupture (MOR), and modulus of elasticity (MOE) were determined. The compressive strength, MOR, and MOE of hot-pressed specimens were significantly higher than those for the cold-pressed specimens, which are also directly proportional to density. Moreover, the samples with the highest density of $1.2kg/m^3$ performed high values on mechanical properties in both the manufacturing methods.