• 열처리공학회지
• /
• 제17권1호
• /
• pp.17-22
• /
• 2004

In the present study, newly developed spark plasma sintering(SPS) technique was introduced to refine the grain size of ${\gamma}$-based TiAl intermetallic compounds. Ti-46Al-1.5Mo and Ti-46Al-1.5Mo-0.2C(at%) prealloyed powders were produced by mechanical milling(MM) in high-energy attritor. The mechanically milled powders were characterized by XRD and SEM for the microstructural evolution as a function of milling time. And then, the MMed powders were sintered by both spark plasma sintering and hot pressing in vacuum (HP). After the sintering process, MM-SPSed specimens were heat-treated in a vacuum furnace (SPS-VHT) and in the SPS equipment(MM-SPS) for microstructural control. It was found from microstrutural observation that the microstructure consisting of equiaxed ${\gamma}$-TiAl with a few hundred nanometer in average size and ${\alpha}_2-Ti_3Al$ particles were formed after both sintering processes. It was also revealed from hardness test and three-point bending test that the effect of grain refinement on the hardness and bending strength is much higher than that of carbon addition. The fully lamellar microstructures, which is less than $80{\mu}m$ in average grain size was obtained by SPS-VHT process, and the fully lamellar microstructure which is less than $100{\mu}m$ in average grain size was obtained by MM-SPS for a relatively shorter heat-treatment time.

• 한국재료학회지
• /
• 제5권6호
• /
• pp.627-632
• /
• 1995

고출력 IC회로의 방열재료 및 전기접점재료로 이용되고 있는 W-Cu복합재료를 기계적합금화법으로 제조하였다. 기계적합금화한 분말을 300MPa로 폭 16mm, 높이 4mm의 원반형으로 제조하였다. 소결은 120$0^{\circ}C$에서 140$0^{\circ}C$까지 수소분위기에서 행하였다. 이렇게 제조된 시편의 절단된 면을 연마하여 SEM으로 관찰하였다. 균질한 W-Cu복합재료를 10시간 기계적합금화를 행한 후에 얻을 수 있었고, 133$0^{\circ}C$에서 1시간 소결한 시편의 경우 거의 99%에 가까운 치밀한 조직을 얻을 수 있었다. 또한 기계적합금화시간이 증가함에 따라서 Fe의 혼입은 직선적으로 증가하였으며, 이로 인한 금속간화합물상의 형성은 W입자 성장을 방해하고 경도를 증가시켰다.

• 한국분말재료학회지
• /
• 제14권4호
• /
• pp.265-271
• /
• 2007

Electromagnetic wave absorbing materials have been developed to reduce electromagnetic interference (EMI) for electronic devices in recent years. In this study, Fe-Si-B-Nb-Cu base amorphous strip was pulverized using a jet mill and an attritor and heat-treated to get flake-shaped nanocrystalline powders, and then the powders were mixed, cast and dried with dielectric $Al_{2}O_{3}$ powders and binders. As a result, the addition of $Al_{2}O_{3}$ powders improved the absorbing properties of the sheets noticeably compared with those of the sheets without dielectric materials. The sheet mixed with 2 wt% $Al_{2}O_{3}$ powder showed the best electromagnetic wave absorption, which was caused by the increase of the permittivity and the electric resistance due to the dielectric materials finely dispersed on the Fe-based powder.

• 자원리싸이클링
• /
• 제3권2호
• /
• pp.9-16
• /
• 1994

본 연구에서는 제철소 전로 dust를 사용하여 일차보고의 기초적인 철분말의 회수에 이어 semi pilot 장치의 혼식 사이클론(wet cyclone)을 사용해서 고순도의 철분말을 회소하여 분말합금용(용접봉용 포함) 원료, 철분법 페수처리용 등으로 그 용도를 개발하고자 하였으며, 이를 통하여 다음과 같은 결론을 얻었다. 1. 광양제철소 EC dust를 vibration mill로 2분 동안 마광한 다음 혼식 사이클론에 분급하여 얻어진 철분말(+200 mesh. underflow)를 다시 아트리터에서 5분 동안 마광한 후 분급실험을 하여 고순도으 철분말(Total Fe 99.76%)을 47.66% 회수할 수 있었다. 2. 전로 dust에서 회수한 철분말은 +65 mesh : 36.16%, 65/100 : 24.43%, 100/200 : 26.68%, 200/270 : 12.64%의 입도분포를 가지고 있었으며, 모두 ${\alpha}$-Fe러 flake형을 보이고 있었다. 3. 재항 CF dust와 광양 EC dust에서 회수한 철분말을 가지고 동이온 제거실험을 한 결과, 철분말에 의해서 동이온이 99%이상 제거됨을 알 수 있었다. 4. 전로 dust를 적당시간 마광하여 혼식 사이클론에 의해 +270mesh(underflow)와 -270 mesh(overflow)로 입도로 분급한 후, -270 mesh 의 입도(산화철)는 폐수처리용 원료로 사용하고, +270mesh 의 입도(철분말)는 분말합금용(용접봉용 포함) 원료로 사용하는 것이 바람직하다.

• 한국재료학회지
• /
• 제11권5호
• /
• pp.345-353
• /
• 2001

본 연구에서는 MA 방법을 사용하여 $Al_3$Nb 금속간화합물의 조성에 Zr을 첨가하여 $Al_3$(Nb$_{1-x}$ )Zr$_{x}$ 합금분말을 제조한 후 이에 따른 상변화 거동 및 미세구조특성을 분석하였다. MA는Al$_3$(Nb$_{1-x}$ )Zr$_{x}$의 조성으로 Al, Nb, Zr 원료분말과 arc meltinly된 $Al_3$Nb, $Al_3$Zr 금속간화합물 분말을 사용하여 300rpm의 회전속도로 20시간 동안 MA하였다. 이때의 정상상태의 원료분말은 약 4$\mu\textrm{m}$의 평균입도와 약 12~18nm의 결정립크기를 가졌으며, arc melting된 분말은 약 2$\mu\textrm{m}$의 평균입도와 약 14nm의 결정립크기를 가지는 분말을 얻을 수 있었다 원료분말과 금속간화합물 분말의 MA 기구는 상이한 거동을 나타내었으며, 분말의 내부변형량은 원료분말이 금속간화합 분말보다 내부변형량이 더 많이 축적되었다. 이는 원료분말의 MA 경우 냉간 압접과 파괴가 반복적으로 진행되었지만 금속간화합물 분말은 취약한 화합물상이어서 냉간압접 보다는 파괴가 지배적으로 진행되었기 때문이다. 원료분말을 MA하였을 경우에는 Al (Nb.Zr)$_2$상이 형성되었으나 금속간화합물 분말로 MA하였을 경우에는 3원계 화합물상이나 비정질상으로 상변태 되지 않고 단지 두 합금상이 분쇄되어 나노복합화 되었다. 후속 열처리에 의해 원료분말인 경우에는 $Al_3$(Nb.Zr)의 화합물상이 쉽게 형성되었으나, 금속간화합물 분말의 경우에는 새로운 상 생성은 얼었고 단지 열처리 전의 분말내부에 쌓여있던 내부변형에너지가 약 60% 정도 감소하였다.