• Journal of the Korean institute of surface engineering
• /
• v.17 no.4
• /
• pp.99-105
• /
• 1984

Integral coloring of aluminum and its alloy with the elecrolytic solution of sulfosallicylic acid and sodium hydroxide was investigated in this study. Addition of hydrogen peroxide and potassium permanganate accelerated the anodizing speed and deepened the color of anodized film. Electron microscopic study was also performed on the surface and cross section.

• Tribology and Lubricants
• /
• v.26 no.1
• /
• pp.68-72
• /
• 2010

A ceramic coating is a surface treatment method that is being used widely in the industrial field, recently. Ni-P plating is also being used widely because of its corrosion resistance and low cost. An anodizing method is applicable to aluminum alloy. An anodizing method generates a thick oxide layer on the surface and then, that heightens hardness and protects the surface. These surface treatments are applied to various mechanical components and treated surfaces relatively move one another. In this study, tribological characteristics of Ni-P plating and TiAlN coating on anodized Al alloy are compared. The counterpart, anodized Al alloy, is worn out abrasively by Ni-P plating and TiAlN coating that have higher hardness. Abrasively worn debris accumulated on the surfaces of Ni-P plating and TiAlN coating, and then transferred layer is formed. This transferred layer affects the amplitude of variation of friction coefficient, which is related to noise and vibration. The amplitude of variation of friction coefficient of Ni-P plating is lower than those of TiAlN coating during the tests.

• Journal of Electrochemical Science and Technology
• /
• v.12 no.2
• /
• pp.188-203
• /
• 2021

The specific benefits of the modified films formed on preliminary anodized aluminum, including the versatility of their potential applications impose the need for evaluation of the exploitation reliability of these films. In this aspect, the durability of Cu and Ni modified anodized aluminum oxide (AAO) films on the low-doped AA1050 alloy was assessed through extended exposure to a 3.5% NaCl model corrosive medium. The electrochemical measurements by means of electrochemical impedance spectroscopy (EIS) and potentiodynamic scanning (PDS) after 24 and 720 hours of exposure have revealed that the obtained films do not change their obvious barrier properties. In addition, supplemental analyses of the coatings were performed, in order to elucidate the impact of the AC-deposition of Cu and Ni inside the pores. The scanning electron microscopy (SEM) images have shown that the surface topology is not affected and resembles the typical surface of an etched metal. The subsequent energy dispersive X-ray spectroscopy (EDX) tests have revealed a predominance of Cu in the combined AAO-Cu/Ni layers, whereas additional X-ray photoelectron (XPS) analyses showed that both metals form oxides with different oxidation states due to alterations in the deposition conditions, promoted by the application of AC-polarization of the samples.

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.22 no.12
• /
• pp.1069-1077
• /
• 2011

In this paper, a design and fabrication of a miniaturized 2.5 GHz 8 W power amplifier using selectively anodized aluminum oxide(SAAO) substrate are presented. The process of SAAO substrate is recently proposed and patented by Wavenics Inc. which uses aluminum as wafer. The selected active device is a commercially available GaN HEMT chip of TriQuint company, which is recently released. The optimum impedances for power amplifier design were extracted using the custom tuning jig composed of tunable passive components. The class-F power amplifier are designed based on EM co-simulation of impedance matching circuit. The matching circuit is realized in SAAO substrate. For integration and matching in the small package module, spiral inductors and single layer capacitors are used. The fabricated power amplifier with $4.4{\times}4.4\;mm^2$ shows the efficiency above 40 % and harmonic suppression above 30 dBc for the second(2nd) and the third(3rd) harmonic at the output power of 8 W.

• Bulletin of the Korean Chemical Society
• /
• v.24 no.7
• /
• pp.975-980
• /
• 2003

The electrochemical properties and the mechanism of formation of anodic oxide films on Mg alloys containing 0-15 mass% Al, when anodized in NaOH solution, were investigated by focusing on the effects of anodizing potential, Al content, and anodizing time. The intensity ratio of Mg(OH)₂ in the XRD analysis decreased with increasing applied potential, while that of MgO increased. Mg(OH)₂ was barely detected at 80 V, while MgO was readily detected. The anti-corrosion properties of anodized specimens at each constant potential were better than those of non-anodized specimens. The specimen anodized at an applied potential of 3 V had the best anti-corrosion property. The intensity ratio of the β phase increased with aluminum content in Mg-Al alloys. During anodizing, the active dissolution reaction occurred preferentially in β phase until about 4 min, and then the current density increased gradually until 7 min. The dissolution reaction progressed in α phase, which had a lower Al content. In the anodic polarization test in 0.017 mol·$dm^{-3}$ NaCl and 0.1 mol·$dm^{-3}$ Na₂SO₄ at 298 K, the current density of Mg-15 mass% Al alloy anodized for 10 min increased, since the anodic film that forms on the α phase is a non-compacted film. The anodic film on the α phase at 30 min was a compact film as compared with that at 10 min.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.1
• /
• pp.83-89
• /
• 2012

Due to the potential importance and usefulness, usage of highly ordered nanoporous anodized aluminum oxide can be broadened in industry, when highly ordered anodized aluminum oxide can be placed on a substrate with controlled thickness. Here we report a facile route to highly ordered nanoporous alumina with the thickness of hundreds-of-nanometer on a silicon wafer substrate. Hexagonally or tetragonally ordered nanoporous alumina could be prepared by way of thermal imprinting, dry etching, and anodization. Adoption of reusable polymer soft molds enabled the control of the thickness of the highly ordered porous alumina. It also increased reproducibility of imprinting process and reduced the expense for mold production and pattern generation. As nanoporous alumina templates are mechanically and thermally stable, we expect that the simple and costeffective fabrication through our method would be highly applicable in electronics industry.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2008.12a
• /
• pp.293.1-293.1
• /
• 2008

• Korean Journal of Materials Research
• /
• v.11 no.4
• /
• pp.329-334
• /
• 2001

Microstructures of barrier-type oxide layers on aluminum was studied by XRD, TEM and RBS. Fer formation of oxide layer. aluminum was anodized in a boric acid solution. The thickness of the oxide film subjected to applied voltage increased linearly at ratio of 1.54nm/V. For oxide layer anodized at 300V, amorphous structure of oxide layer was not transformed after heat treatment at 50$0^{\circ}C$ , while for oxide layers anodized at higher voltages the amorphous structure crystallized into a ${\gamma}$-alumina without any heat treatment. It was also found that the amorphous structure of oxide layer formed at 100V transformed into crystalline structure by electron irradiation. The structure was identified as ${\gamma}$-alumina.

• Korean Journal of Materials Research
• /
• v.17 no.5
• /
• pp.244-249
• /
• 2007

The properties of anodized films on aluminum 6061 alloy in single electrolyte of sulfuric acid and mixed electrolyte of sulfuric-boric acid and sulfuric-boric-nitric acid have been studied. Polarization tests in NaC solution were used to investigate the corrosion performance. Characteristics of film formation and surface morphology were examined by optical microscopy, FE-SEM and EDS. The results obtained have indicated that oxide films growth have been promoted by nitric acid and anodized films in mixed electrolyte have superior corrosion resistance. In case of anodic films formed in mixed electrolyte, some grooves and numerous crazings were also observed at the surface.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.242-242
• /
• 2009

Fabrication of Anodic aluminum oxide under DC vias condition has been studied. When bias and time of anodic aluminum oxide process change, the hole distance and diameter size change. Comparison of fabricated AAO between AC vias and DC vias condition has been studied in this experiment. The first and second anodization of one aluminum is done by using DC and AC power supplier. And first and second anodization of another aluminum is done by DC power supplier. The size of the aluminum is $1cm{\times}3cm$, and second anodic aluminum oxide process takes about 45min. It is found that the hexagonal shape appears on the surface of the AAO. AC power source can fabricate aao which have a nano hole array. We can see that the hole on the surface of the AC vias has a better rounded hole than DC vias AAO. we need more data so we can get characteristic about AC power generated AAO.