• Proceedings of the Korean Magnestics Society Conference
• /
• 1994.03a
• /
• pp.38-39
• /
• 1994

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2005.04a
• /
• pp.7-7
• /
• 2005

• Proceedings of the Korean Magnestics Society Conference
• /
• 1998.10a
• /
• pp.78-79
• /
• 1998

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.11a
• /
• pp.34-34
• /
• 2002

• Proceedings of the KSME Conference
• /
• 2003.11a
• /
• pp.1804-1809
• /
• 2003

The purpose of this study is to clarify the bulk/sheet forming characteristics of bulk amorphous alloys in the supercooled liquid state. The temperature dependences of Newtonian viscosities of amorphous materials are obtained based on the previous experimental works. Finite element analyses for compression forming and sheet deep drawing of amorphous materials are performed. Effects of friction coefficients and temperature are examined and formability of amorphous material is explained in detail.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.10a
• /
• pp.203-206
• /
• 2004

Copper-based bulk amorphous alloy composite was synthesized by using the copper-coated $Cu_{54}Ni_{6}Zr_{22}Ti_{18}$ amorphous powder which was obtained by argon gas atomization. The amorphous powder having a super-cooled liquid region of 53 K was coated by crystalline copper by electroless coating. The consolidation was carried out by manufacturing performs and by the subsequent warm extrusion at 743 K. During the compression test at the room temperature, the composite containing a large fraction of crystalline copper displayed a larger plastic strain after yielding. FEM simulation revealed change in fracture modes in the composites depending on the amount of crystalline copper in the composites.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.271-272
• /
• 2012

Bulk Metallic Glasses (BMGs or amorphous alloy) exhibit high strength and good corrosion resistance. Applications of thin films and micro parts of BMGs have been used a lot since its inception in the research of BMGs. However, Application and fabrication of BMGs are limited to make structural materials. Thin films of BMGs which is sputtered on the surface of structural materials by sputtering process is used to improve limits about application of BMGs. In order to investigate the difference of properties between designed alloys and thin films, we identified that thin films deposited on the surface that have the characteristic of the amorphous films and the composition of designed alloys. Zr-Cu (Cu=30, 35, 38, 40, 50 at.%) and Zr-Cu-Al (Al=10 at.% fixed, Cu=26, 30, 34, 38 at.%) alloys were fabricated with Zr (99.7% purity), Cu (99.997% purity), and Al (99.99% purity) as melting 5 times by arc melting method before rods 2mm in diameter was manufactured. In order to analyze GFA (Glass Forming Ability), rods were observed by Optical Microscopy and SEM and $T_g$, $T_x$, ($T_x$ is crystallization temperature and $T_g$ is the glass transition temperature) and Tm were measured by DTA and DSC. Powder was manufactured by Gas Atomizer and target was sintered using powder in large supercooled liquid region ($=T_x-T_g$) by SPS(Spark Plasma Sintering). Amorphous foil was prepared by RSP process with 5 gram alloy button. The composition of the foil and sputtered thin film was analyzed by EDS and EPMA. In the result of DSC curve, binary alloys ($Zr_{62}Cu_{38}$, $Zr_{60}Cu_{40}$, $Zr_{50}Cu_{50}$) and ternary alloys ($Zr_{64}Al_{10}Cu_{26}$, $Zr_{56}Al_{10}Cu_{34}$, $Zr_{52}Al_{10}Cu_{38}$) have $T_g$ except for $Zr_{70}Cu_{30}$ and $Zr_{60}Al_{10}Cu_{30}$. The compositions with $T_g$ made into powders. Figure shows XRD data of thin film showed similar hollow peak.

• Korean Journal of Materials Research
• /
• v.4 no.4
• /
• pp.416-427
• /
• 1994

The changes of crystallinity and microstructure and the $Si_{1-x}Ge_x/Sio_2$ interfaces of $Si_{1-x}Ge_x$ alloys deposited on amorphous $SiO_{2}$ were studied as a function of deposition temperature. The crystallinity, microstructure, and compositional uniformity of $Si_{1-x}Ge_x$ alloys deposited on the SiOl at different temperature were investigated by X-ray diffraction and transmission electron microscopy. And $Si_{1-x}Ge_x/Sio_2$ interface were investigated by high-resolution transmission electron microscopy. The $Si_{0.7}Ge_{0.3}/Sio_2$ films were deposited on amorphous $SiO_{2}$ at $300^{\circ}C,400^{\circ}C,500^{\circ}C,600^{\circ}C,$ and $700^{\circ}C$ by Si-MBE. In the film deposited at $300^{\circ}C$, only amorphous phase were observed. In the film deposited at $400^{\circ}C$, both amorphous and polycrystalline films were observed. Both phases were deposited simultaneously, but, at initial film growth, amorphous phase prevailed over polycrystalline phase. As the film thickness increased, the fraction of polycrystalline phase increased. At $500^{\circ}C$, thin amorphous layer was observed at lOnm from $SiO_{2}$ surface. In the films deposited at higher than $600^{\circ}C$, only crystalline phase were observed. Polycrystalline films had columnar structure. Compositional uniformity for deposited films were good regardless of deposition temperature. The interfaces of $Si_{1-x}Ge_x/Sio_2$ were flat, whatever polycrystal or amorphous was deposited on $SiO_{2}$.

• Journal of Powder Materials
• /
• v.14 no.1 s.60
• /
• pp.50-55
• /
• 2007

The hydrogen sorption speeds of $Zr_{57}V_{36}Ti_7$ amorphous alloy and its crystallized alloys were evaluated at room temperature. $Zr_{57}V_{36}Ti_7$ amorphous alloy was prepared by ball milling. The hydrogen sorption rate of the partially crystallized alloy was higher than that of amorphous. The enhanced sorption rate of partially crystallized alloy was explained in terms of grain refinement that has been known to promote the diffusion into metallic bulk of the gases. The grain refinement could be obtained by crystallization of amorphous phase resulting in the observed increase in sorption property.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.784-785
• /
• 2006

Co-based amorphous powder was produced by a new atomization process "Spinning Water Atomization Process (SWAP)", having rapid super-cooling rate. The composition of the alloys was ($(Co_{0.95}Fe_{0.05})_{1-x}Cr_x$)$_{75}Si_{15}B_{10}$ (x=0, 0.025, 0.05, 0.075). The powders became the amorphous state even if particle size was up to about $500{\mu}m$. The coercive force of powders was about 0.35 - 0.7 Oe. Furthermore, Co-based amorphous powder cores with glass binders were made by cold-pressing and sintering methods. The initial permeability of the core in the frequency range up to 100 kHz was about 110, and the core loss at 100 kHz for Bm = 0.1 T was $350kW/m^3$.