• International Journal of Highway Engineering
• /
• v.17 no.2
• /
• pp.1-11
• /
• 2015

PURPOSES : This study set out to investigate the fundamental properties of alkali-activated concrete (AAC) using modified slag as the pavement maintenance material. METHODS: The material properties of modified slag based alkali-activated concrete (MSAAC) were analyzed and evaluated against those of alkali-activated slag concrete (AASC). Several mix formulations were considered, including one MSACC and four AASCs. The main variables considered in the study were slump, air content, compressive strength, rapid chloride permeability test, scaling resistance, freeze-thaw test, XRD, SEM, and EDS. RESULTS: MSAAC exhibits a compressive strength in excess of 21 MPa six hours after curing. Also, the charge passed of the MSACC was found to be less than 2000 coulombs after seven days and about 1000 coulombs after 28 days. The weight loss determined from a scaling test did not exceed $1kg/cm^2$ in the case of the MSACC, but that of the AASCs had already exceeded $1kg/cm^2$ at the 10th cycle. Based on the results of the freeze-thaw test, the relative dynamic modulus of every mix was found to be in excess of 90%. An energy dispersive spectroscopy(EDS) analysis found that the weight rate percentage of the calcium and aluminum in the MSAAC mix is twice that of the AASC mixes. CONCLUSIONS : It was found that the MSAAC mix exhibits significantly better performance than AASC mixes, based on various fundamental properties.

• KIEAE Journal
• /
• v.6 no.1
• /
• pp.11-16
• /
• 2006

This paper deals with the experimental for manufacturing the lightweight buildng materials with portland cement, fly ash, slag, lime, gypsum, and aluminum powder system. Aluminum powder was added an aerating agent. Specific gravity range of lightweight concrete specimens were 0.6~0.9g/cm3. These specimens properties studied by means of specific gravity, compressive strength, absorption coefficient, transmission loss and scanning electron microscopy. Cellular concrete with maximum compressive strength was 41kgf/cm2 by obtained Al=0.05wt.%. Moreover, the aeration lightweight concrete showed excellent sound absorption properties.

• Journal of the Korea Concrete Institute
• /
• v.28 no.2
• /
• pp.205-212
• /
• 2016

This research investigates the influence of ground granulated blast furnace slag (GGBFS) composition on the alkali-activated slag cement (AASC). Aluminum oxide ($Al_2O_3$) was added to GGBFS binder between 2% and 16% by weight. The alkaline activators KOH (potassium hydroxide) was used and the water to binder ratio of 0.50. The strength development results indicate that increasing the amount of $Al_2O_3$ enhanced hydration. The 2M KOH + 16% $Al_2O_3$ and 4M KOH + 16% $Al_2O_3$ specimens had the highest strength, with an average of 30.8 MPa and 45.2 MPa, after curing for 28days. The strength at 28days of 2M KOH + 16% $Al_2O_3$ was 46% higher than that of 2M KOH (without $Al_2O_3$). Also, the strength at 28days of 4M KOH + 16% $Al_2O_3$ was 44% higher than that of 4M KOH (without $Al_2O_3$). Increase the $Al_2O_3$ contents of the binder results in the strength development at all curing ages. The incorporation of AASC tended to increases the ultrasonic pulse velocity (UPV) due to the similar effects of strength, but increasing the amount of $Al_2O_3$ adversely decreases the water absorption and porosity. Higher addition of $Al_2O_3$ in the specimens increases the Al/Ca and Al/Si in the hydrated products. SEM and EDX analyses show that the formation of much denser microstructures with $Al_2O_3$ addition.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.1
• /
• pp.47-56
• /
• 2017

In this study, the higher temperature thermal property of the fly ash-blast furnace slag system Geopolymer including alumina aggregate was investigated whether that Geopolymer will be or not useful as thermal-resistant construction materials. Under every mixing conditions, the crack on the surface of hardened body was not observed up to $800^{\circ}C$ and it corresponded with fact that level of changes was not significant before and after heating process. Residual compressive strength is most high when mixing Blast-Furnace Slag ratio is 60 wt% until temperature reaches $800^{\circ}C$. The major hydrates of hardened body of Geopolymer; amorphous halo pattern between $20{\sim}35^{\circ}$ (2theta) and mullite ($3Al_2O_3{\cdot}2SiO_2$) and quartz ($SiO_2$) was found during the experiment. Amorphous halo pattern was a aluminosilicate gel generated by geopolymeric polycondensation and it was found that the halo pattern of aluminosilicate gel was preserved up to $800^{\circ}C$. The patterns of aluminosilicate gel disappeared from $1,000^{\circ}C$ and crystal phases like gehlenite, calcium silicate, calcium aluminum oxide, microcline was observed with the increase of exposure temperature.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.6
• /
• pp.26-33
• /
• 2012

This paper reported on the effect of blended activator on the physical properties of alkali-activated slag mortar. Five different activators(caustic alkalis) were used: sodium hydroxide(NaOH, A Case), calsium hydroxide($Ca(OH)_2$, B Case), magnesium hydroxide($Mg(OH)_2$, C Case), aluminum hydroxide($Al(OH)_3$, D Case), and potassium hydroxide(KOH, E Case). We blended five caustic alkalis with sodium carbonate($Na_2CO_3$). The dosage of five caustic alkalis was 3M and sodium carbonate was 1M, 2M and 3M. The result of flow and setting time was decrease as the dosage of sodium carbonate increase. But the compressive strength was increase as the dosage of sodium carbonate increase. It was shown that there is a good effect of blended caustic alkalis with sodium carbonate in alkali-activated slag mortar.

• Journal of the Korea Institute of Building Construction
• /
• v.21 no.4
• /
• pp.281-291
• /
• 2021

To reduce the environmental load of the construction industry, there is a need to minimize construction and demolition by strengthening the eco-friendliness of building materials and extending the durable lifespan. Therefore, while many Hanok roof finishing methods have been proposed to address these problems, the current trend is to use the existing method due to issues such as economic feasibility, weight, and durability. The manufacturing method of clay roof tiles used as roofing materials for Hanok buildings is optimized by using a mixture of 64.5% Gyeongju clay, 15.0% kaolin, 15.0% FNS(Ferro Nickel Slag), and 5.5% MAS(Magnesia Aluminum Silicate) under optimal conditions. The results of the experiment involving firing at 1,125℃ showed that flexural strength of 12,102N, which is higher than the standard of KS F 3510, an absorption rate of 6.08%, a volume specific gravity of 2.15g/cm³, and the freeze-thaw properties were satisfied. A method for securing stable quality was studied.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.6
• /
• pp.507-515
• /
• 2017

This study is to develop a high quality lightweight foamed concrete that can be applied in the field using EXFG by cracking reducing agent combined with FGD and ALS. First, to increase the volume of foam, the flow and density of the mixture was increased and decreased, respectively. At this time, the effect of substitution ratio of EXFG on fluidity was negligible. The fraction of foam was the highest at EXFG 1%, and the settlement was found to be prevented by the expansion reaction at EXFG 1%. At this time, the ratio of foam was 65%. In the compressive strength, the strengths were similar or decreased when the substitution ratio of EXFG was more than 1%. The apparent density satisfied the KS 0.5 type at the bubble contents was 65%. In case of EXFG substitution, dry shrinkage was decreased by about 10%. As the substitution ratio of EXFG increased, the thermal conductivity increased proportionally.

• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.177-184
• /
• 2015

In order to use the high-volume slag cement as a construction materials, a proper activator which can improve the latent hydraulic reactivity is required. The dissolved aluminum silicon ions from ground granulated blast furnace slag (GGBFS) react with sulfate ions to form ettringite. The proper formation of ettringite can increase the early-age strength of high-volume GGBFS (80%) cement. The aim of this study is to investigate the hydration properties with sulfate activators (sodium sulfate, anhydrite). In this paper, the effects of $Na_2SO_4$ and $CaSO_4$ on setting, compressive strength, hydration, micro-structure were investigated in high-volume GGBFS cement and compared with those of without activator. Test results indicate that equivalent $SO_3$ content of 3~5% improve the early-age hydration properties such as compressive strength, heat evolution rate, micro-pore structure in high-volume GGBFS cement.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.189-190
• /
• 2016

Lightweight concrete is currently used at apartment buildings or housing construction sites causes some uneconomical problems due to excessive cracks and subsidences. So, it is in the situation that it is necessary to set up countermeasures against such subsidences. Therefore, in this study, it is intended to analyze the prevention of a subsidence inducing the expansion of the aluminum components depending on the changes of substitution rate and bubble mixing ratio by using the bubble-based Leavening Agent that Aluminum slag as an industrial by-product is substituted into some desulfurized plaster. As the results, it was found that the blending ratios, such as, the substitution ratio of bubble-based leavening agent (1%) and the bubble mixing ratio (65%) are appropriate while the flow property, subsidence depth and compression strength are considered.

• Journal of the Mineralogical Society of Korea
• /
• v.26 no.4
• /
• pp.229-244
• /
• 2013

Arsenic contamination may be brought about by a variety of natural and anthropogenic causes. Among diverse naturally-occurring chemical speciations of arsenic, trivalent (As(III), arsenite) and pentavalent (As(V), arsenate) forms have been reported to be the most predominant ones. It has been well known that the behavior of arsenic is chiefly affected by aluminum, iron, and manganese oxides. For this reason, this study was initiated to evaluate the applicability of manganese slag (Mn-slag) containing high level of Mn, Si, and Ca as an efficient sorbent of arsenic. The main properties of Mn-slag as a sorbent were investigated and the sorption of each arsenic species onto Mn-slag was characterized from the aspects of equilibrium as well as kinetics. The specific surface area and point of zero salt effect (PZSE) of Mn-slag were measured to be $4.04m^2/g$ and 7.73, respectively. The results of equilibrium experiments conducted at pH 4, 7 and 10 suggest that the sorbed amount of As(V) was relatively higher than that of As(III), indicating the higher affinity of As(V) onto Mn-slag. As a result of combined effect of pH-dependent chemical speciations of arsenic as well as charge characteristics of Mn-slag surface, the sorption maxima were observed at pH 4 for As(V) and pH 7 for As(III). The sorption of both arsenic species reached equilibrium within 3 h and fitting of the experimental results to various kinetic models shows that the pseudo-second-order and parabolic models are most appropriate to simulate the system of this study.