• Nuclear Engineering and Technology
• /
• v.27 no.4
• /
• pp.453-462
• /
• 1995

In connection with the safe storage of high level nuclear waste, effect of $H_2O$$_2$ on the corrosion behavior of 304L stainless steel was examined. Open circuit potentials and polarization curves were measured with and without $H_2O$$_2$. The experimental results show that $H_2O$$_2$ increased corrosion potential and decreased pitting potential. The passive range, therefore, decreased as $H_2O$$_2$ concentration increased, indicating that pitting resistance was decreased by the existence of $H_2O$$_2$ in the electrolyte. These effect of $H_2O$$_2$ on corrosion of 304L stainless steel are considered to be similar to those of ${\gamma}$-irradiation. To compare the effects of $H_2O$$_2$ with those of $O_2$, cathodic and anodic polarization curves ore made in three types of electrolyte such as aerated, deaerated, and stirred electrolyte. The experimental results show that the effects of $H_2O$$_2$ on the corrosion behavior were tory similar to those of $O_2$ such as increase of corrosion potential, decrease of pitting resistance, and increase of repassivation potential. In acid and alkaline media, the corrosion potential shifts by $H_2O$$_2$ were restricted by the large current density of proton reduction and by the le Chatelier's principle respectively.y.

• Korean Journal of Materials Research
• /
• v.18 no.6
• /
• pp.334-338
• /
• 2008

The purpose of this study is to characterize various electrolytes on electrochemical mechanical planarization (ECMP). The ECMP system was modified from conventional CMP system to measure the potentiodynamic curve and removal rate of Cu. The potentiodynamic curves were measured in static and dynamic states in investigated electrolytes using a potentiostat for the evaluation of the polishing behavior on ECMP. KOH (alkaline) and $NaNO_3$ (salt) were selected as electrolytes which have high conductivity. In static and dynamic states, the corrosion potential decreased and the corrosion current increased as a function of the electrolyte concentration. But, the electrochemical reaction was prevented by mechanical polishing effect in the dynamic state. The static etch and removal rate were measured as functions of concentration and applied voltage. When $NaNO_3$ was used, the dissolution was much faster than that of KOH. It was concluded that the removal rate was strongly depended on electrochemical dissolution. The removal rate increased up to 350 nm/min in $NaNO_3$ based electrolyte.

• Journal of Korean Association for Spatial Structures
• /
• v.23 no.3
• /
• pp.87-94
• /
• 2023

Chloride is one of the most common threats to reinforced concrete (RC) durability. Alkaline environment of concrete makes a passive layer on the surface of reinforcement bars that prevents the bar from corrosion. However, when the chloride concentration amount at the reinforcement bar reaches a certain level, deterioration of the passive protection layer occurs, causing corrosion and ultimately reducing the structure's safety and durability. Therefore, understanding the chloride diffusion and its prediction are important to evaluate the safety and durability of RC structure. In this study, the chloride diffusion coefficient is predicted by machine learning techniques. Various machine learning techniques such as multiple linear regression, decision tree, random forest, support vector machine, artificial neural networks, extreme gradient boosting annd k-nearest neighbor were used and accuracy of there models were compared. In order to evaluate the accuracy, root mean square error (RMSE), mean square error (MSE), mean absolute error (MAE) and coefficient of determination (R2) were used as prediction performance indices. The k-fold cross-validation procedure was used to estimate the performance of machine learning models when making predictions on data not used during training. Grid search was applied to hyperparameter optimization. It has been shown from numerical simulation that ensemble learning methods such as random forest and extreme gradient boosting successfully predicted the chloride diffusion coefficient and artificial neural networks also provided accurate result.

• Journal of the Korea Concrete Institute
• /
• v.16 no.4 s.82
• /
• pp.529-539
• /
• 2004

The corrosion of steel rebars has been the major cause of reinforced concrete deterioration. FRP(Fiber-reinforced polymer) rebar has emerged as one of the most promising and affordable solutions to the corrosion problems of steel reinforcement in structural concrete. However, FRP rebar is prone to deteriorate due to other degradation mechanisms than those for steel. The high alkalinity of concrete, for instance, is a possible degradation source. Therefore, the USA, Japan, Canada, UK. etc are using environmental reduction factor. Although difference design guidelines were drawn in many, including USA, Japan, Canada, UK etc, recommendations and coefficients that could take into account the long-term behavior of FRP reinforcement were not well defined. This study focuses on recommendation of environmental reduction factor of FRP rebar. Environment reduction factor were decided using durability test result. FRP rebars were subjected to twelve type of exposure conditions including alkaline solution, acid solution, salt solution and deionized water etc. The water absorption behavior was observed by means of simple gravimetric measurements and durability properties were investigated by performing tensile, compressive and short beam tests. Based on the experimental result, environmental reduction factor of hybrid FRP rebar(A), and (C) and CFRP rebar was decided as 0.85. Also, hybrid FRP rebar(B) and GFRP rebar were decided as 0.7 for the environmental reduction factor

• Journal of Periodontal and Implant Science
• /
• v.43 no.4
• /
• pp.198-205
• /
• 2013

Purpose: The aim of this study was to evaluate the surface properties and biological response of an anodized titanium surface by cell proliferation and alkaline phosphatase activity analysis. Methods: Commercial pure titanium (Ti) disks were prepared. The samples were divided into an untreated machined Ti group and anodized Ti group. The anodization of cp-Ti was formed using a constant voltage of 270 V for 60 seconds. The surface properties were evaluated using scanning electron microscopy, X-ray photoelectron spectroscopy, and an image analyzing microscope. The surface roughness was evaluated by atomic force microscopy and a profilometer. The contact angle and surface energy were analyzed. Cell adhesion, cell proliferation, and alkaline phosphatase activity were evaluated using mouse $MC_3T_3-E_1$ cells. Results: The anodized Ti group had a more porous and thicker layer on its surface. The surface roughness of the two groups measured by the profilometer showed no significant difference (P>0.001). The anodized Ti dioxide ($TiO_2$) surface exhibited better corrosion resistance and showed a significantly lower contact angle than the machined Ti surface (P>0.001). Although there was no significant difference in the cell viability between the two groups (P>0.001), the anodized $TiO_2$ surface showed significantly enhanced alkaline phosphatase activity (P<0.001). Conclusions: These results suggest that the surface modification of Ti by anodic oxidation improved the osteogenic response of the osteoblast cells.

• Corrosion Science and Technology
• /
• v.11 no.3
• /
• pp.96-102
• /
• 2012

Outer diameter stress corrosion cracking (ODSCC) has occurred for Alloy 600 (Ni 75 wt%, Cr 15 wt%, Fe 10 wt%) as a heat exchanger tube of the steam generator (SG) in nuclear power plants (NPP) during long term operation. Among many causes for SCC, lead (Pb) is known to be one of the most deleterious species in the secondary system. In the present work, the oxide formed on Alloy 600 was characterized as a function of the PbO content in 0.1 M NaOH at $315^{\circ}C$ by using an electrochemical impedance spectroscopy (EIS), a transmission electron microscopy (TEM), equipped with an energy dispersive x-ray spectroscopy (EDS). The oxide property was analyzed in view of SCC susceptibility.

• Journal of the Korean Electrochemical Society
• /
• v.6 no.4
• /
• pp.242-249
• /
• 2003

Zn electrode was widely used as an anode material in alkaline battery systems in highly concentrated KOH electrolyte, however it was well known that its cycle life is significantly shortened by growth of dendrite due to the high dissolution of $Zn(OH)_2$ and rapid electrochemical reaction. In this study when by the additives such as $Ca(OH)_2$, Citrate, tartrate and Gluconate were added to $40\%$ KOH electrolyte at solution temperature of $25^{\circ}C$ and the amount of $5wt\%\;Pb_3O_4$ was mixed to Zn electrode and then the effect of $Pb_3O_4$ and additives on the electrochemical behavior of Zn electrode was investigated by Potentiodynamic Polarization Curves, Cyclic Voltammetry, Accelerated Life Cycle lest, and SEM image analyses. The addition of $Pb_3O_4$ reduced the corrosion rate of Zn electrode. The corrosion potential of Zn electrode with $Pb_3O_4$ was higher or lower than that of pure Zn electrode however was not influenced practically to the open circuit voltage. And the addition of 4 type additives had an important role in improving both cycle life in accelerated cycle life test and corrosion resistance. Furthermore the additive of Tartrate indicated comparatively a good effect to corrosion resistance as well as charging-discharging property Improvement among those four type additives.

• Applied Chemistry for Engineering
• /
• v.16 no.2
• /
• pp.250-256
• /
• 2005

Coating appearance is the most important problem in automotive industry. To increase the coating appearance quality, the corrosion resistance and the coating adhesion on metal substrates must be basically solved. The phosphating film made by the pretreatment of metal substrate is important factor to increase the coating adhesion. During the cathodic electrodeposition, the pH at the cathode surface increases up to about 12. In such a highly alkaline condition, the dissolution of metal substrate and phosphate film occurs. These phenomena result in the decrease of the bonding strength between the phosphating film and the substrate. Generally, the structure of zinc phosphating film is hopeite or phosphophyllite. It has been known that the phosphophyllite film contains better corrosion resistance and paint adhesion for hot water immersion test because of the decrease of dissolving amount of both metal substrate and phosphating film during the cathodic electrodeposition. It is found that the addition of Ni and Mn composition increase P-ratio and then can improve the paint adhesion on metal surface and the corrosion resistance.

• Proceedings of the Korea Technical Association of the Pulp and Paper Industry Conference
• /
• 2006.06a
• /
• pp.67-71
• /
• 2006

Strong oxidizing biocides are commonly used to control biofilm formation in alkaline papermaking systems. However, paper streams contain many substances that react with or consume oxidizers (e.g., fiber and starch, Therefore, to achieve effective microbiological control, the oxidizer must be overfed to overcome the effect of these substances. When dosed in this manner, the oxidizer can cause many unwanted reactions and adverse side effects, including the consumption of costly papermaking additives increased corrosion rates, and reduced felt life. Some oxidizers also contribute to the formation of halogenated organic compounds. When used for biofilm control, strong oxidizers can cause more problems than they remedy. A patented biocide that effectively controls biofilm without the adverse side effects associated with strong oxidizing biocides is available from Hercules. $Spectrum^{(R)}$ XD3899 Ammonium Bromide Technology, which can be described as a mild oxidizer, is currently used on more than 300 machines globally and has resulted in numerous production and/or machine efficiency records since its introduction in 2001.

• Journal of Electrochemical Science and Technology
• /
• v.14 no.3
• /
• pp.243-251
• /
• 2023

Developing oxygen evolution reaction (OER) electrocatalysts is essential to accomplish viable CO₂ and water electrolysis. Herein, we report the fabrication and OER performance of Ni-foam (NF)-immobilized Ni₆ nanoclusters (NCs) (Ni₆/NF) prepared by a dip-coating process. The Ni₆/NF electrode exhibited a high current density of 500 mA/cm² for the OER at an overpotential as low as 0.39 V. Ni₆/NF exhibited high durability in an alkaline solution without corrosion. Electrokinetic studies revealed that OER can be easily initiated on Ni6 NC with fast electron-transfer rates. Finally, we demonstrated stable CO₂-to-CO electroreduction using an NC-based zero-gap CO₂ electrolyzer operated at a current density of 100 mA/cm² and a full-cell potential of 2.0 V for 12 h.