• Journal of the Korean Wood Science and Technology
• /
• v.26 no.1
• /
• pp.14-18
• /
• 1998

A low density polyethylene(LDPE) was examined as an additive in phenol-formaldehyde(PF) resin adhesive for bonding radiata pine plywood. The LDPE was supplied by the commercial manufacturer. The LDPE was compared to a commercial filler commonly used in structural plywood adhesives in the United States. The adhesive mixes were made by following the recommended procedure of Georgia-Pacific Resins Inc.. using plywood-type PF resin. A total of 48 three-ply plywoods. 6.3 mm nominal thickness and 30 by 30 em in size, were made at two press times (4 and 5 min). two press temperatures (150 and $160^{\circ}C$) and 30 minute assembly times for four adhesive mixing types. Evaluations of the LDPE addition were carried out by performance tension shear tests after two cycle boil aging tests on plywood per the U.S. Product Standard PS I-83. After accelerated-aging tests. plywoods were exhibited no delamination. The test results included tension shear strength and estimated wood failure values. The plywood test results support the use of polyethylene as an additive in plywood adhesives.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.6
• /
• pp.446-453
• /
• 2015

PURPOSE. To compare the push-out bond strength of feldspar and zirconia-based ceramic inlays bonded to dentin with different resin cements following simulated aging. MATERIALS AND METHODS. Occlusal cavities in 80 extracted molars were restored in 2 groups (n=40) with CAD/CAM feldspar (Vitablocs Trilux forte) (FP) and zirconia-based (Ceramill Zi) (ZR) ceramic inlays. The fabricated inlays were luted in 2 subgroups (n=20) with either etch-and-bond (RelyX Ultimate Clicker) (EB) or self-adhesive (RelyX Unicem Aplicap) (SA) resin cement. Ten inlays in each subgroup were subjected to 3,500 thermal cycles and 24,000 loading cycles, while the other 10 served as control. Horizontal 3 mm thick specimens were cut out of the restored teeth for push out bond strength testing. Bond strength data were statistically analyzed using 1-way ANOVA and Tukey's comparisons at ${\alpha}=.05$. The mode of ceramic-cement-dentin bond failure for each specimen was also assessed. RESULTS. No statistically significant differences were noticed between FP and ZR bond strength to dentin in all subgroups (ANOVA, P=.05113). No differences were noticed between EB and SA (Tukey's, P>.05) bonded to either type of ceramics. Both adhesive and mixed modes of bond failure were dominant for non-aged inlays. Simulated aging had no significant effect on bond strength values (Tukey's, P>.05) of all ceramic-cement combinations although the adhesive mode of bond failure became more common (60-80%) in aged inlays. CONCLUSION. The suggested cement-ceramic combinations offer comparable bonding performance to dentin substrate either before or after simulated aging that seems to have no adverse effect on the achieved bond.

• The korean journal of orthodontics
• /
• v.31 no.2 s.85
• /
• pp.261-270
• /
• 2001

The purpose of this study was to evaluate the clinical usefulness of plasma arc light which can reduce the curing time dramatically compared by shear bond strengths and failure patterns of the brackets bonded with visible light in direct bracket bonding. Some kinds of brackets were bonded with the Transbond$^{\circledR}$ to the human premolars which were embedded in the resin blocks according to the various conditions. After bonding, the shear bond strength was tested by Instron universal testing machine and in addition , the amount of residual adhesive remaining on the tooth after debonding was measured by the stereoscope and assessed with adhesive remnant index(ARI). The results were as follows : 1. When plasma arc light was used for bonding the brackets, the shear bond strength was clinically sufficient in both metal and ceramic brackets, but resin brackets showed significantly lower bond strength but which was clinically useful. 2. When metal brackets were bonded using visible light, there was no significant difference in shear bond strength due to the light-curing time and the bond strength was clinically sufficient. 3. When the adhesive failure patterns of brackets bonded with plasma arc light were observed by using the adhesive remnant index, the bond failure of the metal and resin bracket occurred more frequently at bracket-adhesive interface but the failure of the ceramic bracket occurred more frequently at enamel-adhesive interface. 4. There was no statistically significant difference of the shear bond strength and adhesive failure pattern between metal bracket bonded for 2 seconds by curing with plasma arc light and 10 seconds by curing with visible light. 6. When metal brackets were bonded using plasma arc light, the shear bond strength decreased as the distance from the light source increased. The above results suggest that plasma arc light can be clinically useful for bonding the brackets without fear of the decrease of the shear bond strength.

• Restorative Dentistry and Endodontics
• /
• v.30 no.6
• /
• pp.493-504
• /
• 2005

This study was performed to investigate the compatibility between 4 dentin adhesives and 4 resin luting cements. Dentin adhesives used in this study were All-Bond 2 (Bisco Inc., Schaumbrug, IL, USA), Clearfil SE-Bond (Kuraray Medical Inc, Osaka, Japan), Prompt L-Pop (3M Dental Products, St. Paul, MN, USA), One-Up Bond F (Tokuyama corp., Tokyo, Japan) Resin luting cements used in this study were Choice (Bisco Inc., Schaumbrug, IL, USA), Panavia F (Kuraray Medical Inc, Osaka, Japan), RelyX ARC (3M Dental Products, St. Paul, MN, USA) Bistite II DC (Tokuyama corp., Tokyo, Japan). Combination of each dentin adhesive and corresponding resin cement was made to 16 experimental groups. Flat dentin surfaces was created on mid-coronal dentin of extracted mandibular third molars, then dentin surface was polished with 320-grit silicon carbide abrasive papers. Indirect resin composite block (Tescera, Bisco) was fabricated. Its surface for bonding to tooth was polished with silicon carbide abrasive papers Each dentin adhesive was treated on tooth surface and resin composite overlay were luted with each resin cement. Each bonded specimen was poured in epoxy resin and sectioned occluso-gingivally into 1.0mm thick slab, then further sectioned into $1.0{\times}1.0mm^2$ composite-dentin beams. Microtensile bond strength was tested at a crosshead speed of 1.0mm/min. The data were analysed by one-way ANOVA and Duncan's multiple comparison tests The results of this study were as follows, 2-step self-etching dentin adhesive which has additional bonding resin is more comparison than tests. self-etching dentin adhesive.

• Restorative Dentistry and Endodontics
• /
• v.20 no.1
• /
• pp.1-16
• /
• 1995

The purpose of this study was to investigate the effect of dentin bonding agents on the bond strength of composite resin restorations in case of applying the dentin bonding agents to acid etched enamel surfaces. Freshly extracted 364 bovine anterior teeth were selected as a adherents. 320 enamel specimens were divided into two groups(unetched group (1) and etched group (2) for testing the shear bond strength, 40 specimens were used for the hardness testing, and 4 specimens of rest were to observe the resin-tag formation into etched enamel surfaces. All surfaces of enamel specimens were polished with 320~1500 SiC paper under continuous running water. In Group (1), 100 enamel specimens were polished and unetched. 220 polished enamel specimens in Group (2) were etched with 37 % phosphoric acid solution for 60 seconds, washed with water for 20 seconds, and dried with a light air pressure for 60 seconds. Three kinds of dentin bonding agents(Gluma, Prisma, Scotchbond 2) were evaluated the effect on the bond strength to conditioned enamel surfaces. Shear bond strengths were measured on the three cases such as a coating of primer only, a coating of sealer only, and a sequential coating of primer and sealer to acid etched enamel surfaces were compared with the bond strengths measured by the coating of enamel bonding agent followed by the bonding of composite resin (Photo clearfil bright, Kuraray, Japan) to unetched and acid etched enamel surfaces. In addition, the hardness tested on the adhesive fractured surface between composite resin enamel as a mean of evaluation of a factor whether the mechanical bond strengths were affected and the penetration of dentin bonding agents into etched enamel surfaces was also observed. Bond strengths were measured using the method of shear bond strength by a universal testing machine (Instron-4467, USA), statistical test were applied to the results using a one way analysis variance(ANOVA), and hardness was measured by the Vicker's Hardness Tester(MHT-i, Matsuzawa, Japan) and the penetration of the resins were observed by the SEM (Hitachi, S-2300, Japan). The following conclusions were drawn; 1. Enamel bonding agent showed to affect the improvement of bond strength of composite resin to enamel surface both unetched and etched. 2. Dentin bonding agents could be resulted in increase of bond strength to unetched enamel surface, but there were no statistical significances. 3. Bond strengths to etched enamel surface were significantly decreased with a coating of dentin primer only. 4. Coating of sealer only and coating of primer and sealer noticed the similar bond strengths of composite resin to etched enamel using the enamel bonding agents. 5. The applying method proved to be more effective than the kinds of dentin bonding agents on the bond strength of composite resin to etched enamel than the kind of dentin. 6. Vicker's hardness numbers of dentin bonding agents were lower than that of composite resin, but the degree of penetration of dentin bonding agents into etched enamel surfaces was excellent.

• Restorative Dentistry and Endodontics
• /
• v.27 no.3
• /
• pp.257-269
• /
• 2002

Objective : The purpose of this study was to evaluate the resin infiltration into dentin of one-bottle adhesive systems and self-etching primer bonded to Class V cavities using confocal laser scanning microscope(CLSM). Material and Methods : Forty Class V cavities were prepared from freshly extracted caries-free Human teeth. These teeth were divided into two groups based on the presence of cervical abrasion: Group I, cervical abrasion : Group II, wedge-shaped cavity preparation. Resin-dentin interfaces were produced with two one-bottle dentin bonding systems-ONE COAT BOND(OCB; Coltene$^R$) and Syntac$^R$SPrint$^{TM}$(SS; VIVADENT)-, one self-etching priming system-CLEARFIL$^{TM}$ SE BOND (SB : KURARAY)- and one multi-step dentin bonding system-Scotchbond$^{TM}$Multi-Purpose (SBMP, 3M Dental Products)-as control according to manufacturers' instructions. Cavities were restored with Spectrum$^{R}$(Dentsply). Specimens were immersed in saline for 24 hours and sectioned longitudinally with a low-speed diamond disc. The resin-dentin interfaces were microscopically observed using CLSM. The quality of resin-infiltrated dentin layers were evaluated by five dentists using 0~4 scale. Results : Confocal laser scanning microscopal investigations using primer labeled with rhodamine B showed that the penetration of the primer occurred along the cavity margins. Statistical analysis using one-way ANOVA followed by Duncan's Multiple Range test revealed that the primer penetration of the group 2(wedge-shaped cavity preparation) was more effective than group 1(cervical abrasion) and that of the gingival interfaces was more effective than the occlusal interfaces. In the one-bottle dentin bonding systems, the resin penetration score of OCB was compatible to SBMP, but those of SS and self-etching priming system, SB were lower than SBMP.

• Restorative Dentistry and Endodontics
• /
• v.24 no.4
• /
• pp.546-553
• /
• 1999

In Older to evaluate the effectiveness of 'One-bottle dentin adhesive system', the shear bond strengths of two fourth generation dentin adhesive systems and two One-bottle systems to the occlusal dentin of the freshly extracted third molars were measured by the regulation of the ISO TR 11405. The fourth generation dentin adhesive systems used in this study were Scotchbond Multi-Purpose Plus and All-Bond 2, and the One-bottle systems were Single Bond and One-Step. The effects of the thickness of hybrid layer and adhesive layer, the diameter of resin tag and the ratio between the diameter of resin tag and that of dentinal tubule were analyzed as the contributing factors of the shear bond strength of dentin bonding systems from the Scanning Electron Microscopic images. The results were as follows: 1. The shear bond strengths of Scotchbond Multi-Purpose, All-Bond 2, and Single Bond were 16.98${\pm}$3.40 MPa, 15.10${\pm}$2.77 MPa and 15.05${\pm}$3.18 MPa, respectively. There were no statistical differences(p>0.05). 2. But, the shear bond strength of One-Step were significantly lower than those of the other groups (11.81${\pm}$1.95 MPa, p<0.05). 3. The thicknesses of hybrid layer and adhesive layer of One-Step were significantly thinner than those of the other groups(p<0.05). The differences of the diameter of resin tag(p=0.0685) and the ratio between the diameter of resin tag and that of dentinal tubule(p=0.2401) were not significant among all the material groups. 4. The thickness of hybrid layer and adhesive layer might be considered as contributing factors of the she at bond strengths of dentin bonding systems, but the diameter of resin tag and the ratio between the diameter of resin tag and that of dentinal tubule might not.

• Journal of the Korean Wood Science and Technology
• /
• v.45 no.4
• /
• pp.409-418
• /
• 2017

This work attempted to manufacture glued-laminated timber (Glulam) bonded with melamine-urea-formaldehyde (MUF) resin adhesives at various melamine contents from 20% to 50% under high frequency (HF) heating for a very short time. Two preparation methods were employed to prepare MUF resin adhesives with different melamine contents: one-batch method of synthesizing MUF resins in a single batch, and two-batch method of mixing urea-formaldehyde (UF) resin with melamine-formaldehyde (MF) resin that had been synthesized separately. As the melamine content increased, the gelation time and peak temperature of MUF resins decreased. The adhesion performance of plywood showed that the one-batch MUF resin adhesive with 50% melamine content only satisfied the standard requirement of water resistance. Thus, the one-batch MUF resin adhesive with 50% melamine content was applied for bonding wood lamina from four softwood species such as Japanese larch, Korean red pine, Korean pine and Japanese cedar to manufacture Glulam under HF heating. All Glulam samples bonded with the one-batch MUF resin adhesives with 50% melamine content except those from Korean Red Pine satisfied the requirement in water soaking or boiling water delamination test as an exterior grade Glulam. The presence of rosin in Korean Red Pine was believed to be responsible for its poor adhesion. These results showed that the one-batch MUF resin adhesives with 50% melamine content provided acceptable water resistance with exterior grade Glulam manufactured under HF heating.

• Restorative Dentistry and Endodontics
• /
• v.12 no.1
• /
• pp.95-105
• /
• 1986

For the purpose of obtaining a basic data in selecting a suitable material with clinical care, this study was designed to measure the shear stress and to examine the fracture pattern of various dentin bonding restorative materials using 43 extracted bicuspids. The following results were obtained. 1. In dentin, Silux/Scotchbond group showed the highest value ($34.5{\pm}14.7kg/cm^2$) and Fuji Ionomer Type II group and Heliosit/Dentin-Adhesit group showed almost same bond strength in the next place. Durafill/Dentin-Adhesive group showed an infinitesimal value. ($3.1{\pm}1.4kg/cm^2$) 2. Every group showed no difference in bond strength between upper and lower teeth. Between buccal and lingual surfaces. Fuji Ionomer Type II and Durafill/Dentin-Adhesive groups showed too. But, in Silux/Scotchbond and Heliosit/Dentin-Adhesit groups, it was shown that the bond strength in lingual was stronger than in buccal. 3. There was resin fracture with cohesive fracture of bonding agent in Enamel group. In dentin, adhesive-cohesive fracture and adhesive fracture were shown. 4. The stronger bond strength was, the more frequently cohesive fracture occurred. Dentin-Adhesit group showed specific shining appearance as if varnish became hard.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.3
• /
• pp.213-220
• /
• 2018

In order to use Pitch pine (Pinus rigida Miller) as the material of the structural glued laminated timber, the effect of the amount of resin exudation due to storage time after the planning and the knot of the lamina were evaluated on the bonding properties of the glued board with resorcinol resin. For Pitch pine that was dried at high temperature ($120{\sim}95^{\circ}C$) and low temperature ($65{\sim}50^{\circ}C$), the flat sawn(tangential section) showed higher amount of resin exudation than the quarter sawn(radial section). And the low temperature drying wood showed higher resin exudation than the high temperature drying wood. The low and high temperature drying wood showed the highest amount of resin exudation on the 3rd day and 7th day, respectively and they were gradually decreased. However, there were no significant differences from 15 to 90 days. Adhesion performances were low until 2~3 days with high exudation of resin, but there were no significant differences after 15 days. Both high temperature and low temperature drying woods satisfied the Korean standard regardless of the storage time. The adhesive strengths of the laminating parts including knots were higher than those of KS criteria, but the wood failures were not satisfied the KS standard. Adhesive performances according to the laminating combinations (quarter sawn + quarter sawn, flat sawn + flat sawn, quarter sawn + flat sawn) were better than those of KS criteria in all laminating combinations in both high temperature and low temperature drying woods.