The depth and patterns of demineralization according to the difference in concentration and application time of phosphoric acid were observed through the transmission electron microscope, and shear bond strengths to the acid -conditioned dentin were then measured and compared with the TEM results. To investigate the influence of polymer addition into the phosphoric acid and the effect of difference in concentration and application time of the acid, the specimens were randomly divided into 9 groups. Among the specimens, the exposed dentin surfaces were acid-conditioned with 10% polymer-thickened phosphoric acid(All Bond 2, Bisco, U.S.A.) and aqueous 10%, 20%, 30%, 40% phosphoric acid for 20 seconds, The rest of the specimens were acid-conditioned with 10% phosphoric acid for 15s, 30s, 60s, 120s respectively. The specimens were immersed in 4% glutaraldehyde in 0.1M sodium cacodylate buffer and postfixed with 1 % osmium tetroxide without decalcification and then observed under a JEOL Transmission Electron Microscope(JEM 1200 EX II, Japan). After the specimens were acid-conditioned as the above, primer and adhesive resin were applied to blot-dried dentin and shear bond strengths were then measured and analysed. The results were as follows : 1. The intertubular demineralization depth of 4.0-$5.0{\mu}m$ in 10% polymer-thickened phosphoric acid gels was similar or slightly deeper than that of 4.0-$4.5{\mu}m$ in aqueous 10% phosphoric acid solution. 2. The intertubular demineralization depth of aqueous 20%, 30% and 40% phosphoric acid solution was 6.5-$7.0{\mu}m$, 6.5-$7.5{\mu}m$ and 9.0-$15.0{\mu}m$ respectively. It showed that the depth of dentin demineralization is partly related to the concentration of phosphoric acid solution. 3. The intertubular demineralization depth of aqueous 10% phosphoric acid solution in application time for 15s, 30s, 60s and 120s was 2.5-$3.0{\mu}m$, 4.0-$6.0{\mu}m$, 6.5-$7.0{\mu}m$ and 8.5-$14.0{\mu}m$ respectively. It showed that the depth of dentin demineralization is directly related to the application time of phosphoric acid solution. 4. The partially demineralized dentin layer between demineralized collagen layer and unaffected dentin was showed to a width of 0.5-$1.0{\mu}m$ in lower concentration groups treated with aqueous 10% phosphoric acid for 20s, 60s, 120s and 20% phosphoric acid for 20s. 5. The demineralization effect at the border of intertubular-peritubular junction was less evident than that in the peritubular and intertubular dentin. The collagen fibers in the intertubular dentin had a random orientation, whereas those that lined the tubules were circumferentially aligned. The cross-linkage of dentinal collagen in demineralized collagen layer was clearly seen. 6. A statistically significant difference of bond strengths according to the difference in phosphoric acid concentration did not exist among the groups treated with 10%, 20%, 30% and 40% acid solution (P>0.05). However, bond strengths to the treated dentin with 10% phosphoric acid solution for 30s were significantly higher than that for 120s (P<0.05).
주요 조림수종으로 도입 식재된 리기다소나무의 고부가가치 이용을 위한 구조용 집성재 이용 가능성을 검토하고, 이에 적합한 기술을 개발하기 위하여 본 연구를 수행하였다. 국산 리기다소나무 제재목의 기계응력등급은 대부분 E7에서 E9등급으로 집성재 제조에는 다소 불량한 것으로 나타났다. 반면 단일수종 및 혼합수종 구조용 집성재 제조에 필수적인 리기다소나무 및 낙엽소 판재의 접착성을 평가한 결과 전단접착력, 목파율, 침지 및 삶음박리율 모두 KS기준 이상으로 나타났다. 리기다소나무 단일수종 집성재의 휨성능을 측정해본 결과 휨강도는 KS의 집성재 강도등급에 따른 휨성능 합격기준을 만족한 반면 휨 탄성계수는 기준에 다소 못 미치는 결과를 나타내었다. 그러나 낙엽송 층재와의 혼합구성을 통해 리기다소나무 집성재의 휨성능(휨강도와 휨탄성계수)을 20% 향상시킬 수 있었으며, 층재 구성방법에 있어서는 판재의 탄성계수가 높고 품질이 우수한 낙엽송 층재를 외층에 배치하는 방법이 보다 효과적인 것으로 확인되었다. 결론적으로 리기다소나무의 부가가치 증진을 위한 구조용 집성재 이용은 그 가능성이 매우 컸다.
The changes of microstructures, morphology of sclerotic dentin and bonding aspects generated by an adhesive resin was investigated. Incisors and premolars showing natural cervical abrasions were collected and conditioned with 10 % phosphoric acid or 10 % maleic acid. The sclerotic dentin specimens were then rinsed and blot-dried and applied with dentin adhesive (All Bond 2) to the conditioned dentin surface. To examine the morphologic change of the sclerotic dentin specimen after etching and bonding procedure, the treated specimens were examined by SEM. To analyze the chemical composition of sclerotic dentin and crystals occluding dentinal tubules, the sclerotic dentin specimen was powdered and examined with X-ray Diffractometer. To investigate the Ca/P weight percent ratio within the dentinal tubules, the sclerotic dentin specimen was fractured perpendicularly to the long axis of the tooth from the center of cervical abrasion lesion and then examined with EDX(Energy Dispersive X-ray) microanalyzer. The results were as follows : 1. The increased width of peritubular dentin and the depositions of the irregular amorphous materials within the dentinal tubules were showed in the sclerotic dentin specimens. 2. After the treatment of sclerotic dentin specimen with 10 % phosphoric acid or 10 % maleic acid, the lateral side of tubules rather than cross-sectional tubule openings was showed exclusively at the incisal and gingival incline of the specimens. 3. After the treatment of sclerotic dentin specimen with 10 % phosphoric acid or 10 % maleic acid, the hybrid layer was not formed evidently and the resin tag was not formed or shortly penetrated into the tubules with the thinner diameter. 4. According to the results of XRD analysis of the sclerotic dentin specimen, Hydroxyapatite and Octacalcium phosphate were predominent, however, Whitlockite crystals were rare. 5. The mean Ca/P weight percent ratio analysed from 5 fractured sclerotic dentin specimens was $2.322{\pm}0.170$ at the intertubular dentin, $1.826{\pm}0.051$ within the dentinal tubule.
이 논문의 목적은 복합레진과 컴포머에서, 중합수축의 양과 이로 인하여 야기되는 교두변위와의 상관관계를 알아보기 위함이다. 수복재료로서 Dyract AP, Compoglass F, Z100, Surefil, Pyramid, Synergy Compact, Heliomolar와 Heliomolar HB가 사용되었으며, 접착제로서는 SE Bond 가 사용되었다. 수복재료의 중합수축의 양을 측정하기 위하여, 자체 제작한 linometer를 사용하여, 60초간 일어나는 선수축량을 측정하였다. 한 수복재료 당 10회 측정하였으며, one way ANOVA와 사후검정방법으로 Tukey Test를 이용하여 $95\%$ 신뢰수준에서 각 수복재료의 중합수축량의 차이를 비교하였다. 치아에서 일어나는 교두변위의 양을 측정하기 위하여 사람의 상악소구치에 표준화된 MOD 와동을 형성하고(깊이 3mm, 넓이 3.5mm), 접착제를 도포한 후 광조사 시킨 후, 수복재료로 충전하였다 치아를 자체 제작한 교두변위 측정장치에 위치시키고, 광조사 시키고, 이 때 발생하는 교두의 변위를 10분간 측정하였다. 한 수복재료 당 15회를 측정하였으며 one way ANOVA와 사후검정방법으로 Tykey Test를 이용하여 $95\%$ 신뢰수준에서 각 수복재료의 교두변위 량의 차이를 비교하였다. 중합수축의 양과 교두변위의 양의 상관관계를 회귀분석법을 이용하여 분석하였다. 중합수축의 양은 Heliomolar, Surefil < Heliomolar HB < Z100, Synergy Compact < Dyract AP, Pyramid, Compoglass F (p < 0.05), 교두변위의 양은 Heliomolar, Surefil, Z100, Heliomolar HB, Synergycompact < Compoglass F < Pyramid, Dyract AP (p < 0.05) 였다. 중합수축의 양과 교두변위는 높은 상관관계를 나타내었다 (p < 0.001).
카제인은 우유 속에 약 3% 함유되어 있으면서, 우유에 함유된 전체 단백질의 약 80%를 차지한다. 카제인에 수산화칼슘 및 수산화나트륨 수용액을 섞으면 고결력이 발생하며, 이러한 고결방식은 목재나 건조한 환경에 적용하는 것이 일반적이다. 본 연구에서는 지하수위가 존재하는 토사의 고결을 위해 물에 약한 카제인 고결제의 구성성분을 조절하거나 새로운 성분을 추가하여 내수성을 향상시키고자 하였다. 이를 위해 낙동강모래에 고결제로 가장 많이 사용되는 시멘트뿐 아니라 위스콘신대학에서 제시한 표준 카제인 고결제를 비롯한 다양한 카제인 고결모래 공시체를 제작하였다. 6 종류의 카제인 고결모래 중에서 표준 카제인 고결제에 수산화칼슘을 30% 증가시키고 수산화나트륨을 50% 감소시킨 것이 가장 우수한 강도와 내구성을 나타내었다. 이렇게 개선된 카제인 고결제를 1-4% 혼합하여 만든 공시체의 일축압축강도와 반복건습으로 인한 내구성지수를 시멘트 고결모래 공시체와 비교하였다. 그 결과, 카제인비 4%인 고결모래 공시체의 입축압축강도와 내구성지수는 6,253kPa 및 92%로 일축압축강도 1,500kPa 및 내구성지수 62%인 시멘트비 8%인 고결모래 공시체보다 우수한 것으로 나타났다. 또한, 카제인이 3% 이상 함유된 고결모래 공시체는 반복적인 건습 작용에도 80% 이상의 양호한 내구성을 유지하였다.
본 연구는 최근 심미보철물 제작에 널리 사용되는 지르코니아의 저온열화가 수복물의 안정성 및 내구성에 영향을 미치는 여부를 확인하기 위하여 전단결합강도를 측정하였다. 디스크 형태의 시편을 각각 7개씩 제작한 후 전장도재를 축성하여, ISO 13356 규격에 의거한 조건으로 고압증기 멸균기에 저온열화의 정도를 조절하기 위하여 3, 5, 10시간 동안 수열처리를 진행하였다. 제한된 조건하에 시행된 실험을 통해 전단결합강도를 확인하였으며, 측정 후 파절양상을 관찰 하였다. 저온열화 처리 전후의 시편에 대한 전단결합강도의 변화는 각 실험군별 유의한 차이가 있었다(p<0.05). 10시간을 저온열화 처리한 시편이 가장 낮은 전단결합강도로 나타났으며, 처리시간이 길어질수록 전단결합강도가 낮아지는 경향을 보였다. 파절 양상으로 저온열화 처리를 하지 않은 시편에서 응집성 파절을 보였으며, 저온열화 처리가 길어질수록 혼합형 파절 경향으로 전환되었다. 결론적으로 본 연구는 저온열화 현상이 진행될수록 지르코니아 코어와 전장도재 간의 결합강도가 낮아지는 경향을 확인하였다. 본 실험결과를 토대로 치과용 지르코니아를 이용한 보철물 제작과정과 환자에게 장착 후 안정적인 사용을 위하여 저온열화 현상에 대한 주의가 필요할 것으로 생각된다.
Kim Min-Ho;Yang Jae-Ho;Lee Sun-Hyung;Chung Hun-Young;Chang Ik-Tae
대한치과보철학회지
/
제39권3호
/
pp.260-272
/
2001
All-ceramic restorations have had a more limited life expectancy than metal ceramic restorations because of their low strength. Their relatively lower strength and resistance to fracture have restricted the use of all-ceramic crowns to anterior applications where occlusal loads are lower. But there has been increasing interest in all-ceramic restorations because patients are primarily concerned with improved esthetics. Many efforts have been made to in prove the mechanical properties of dental ceramics. This study was designed to elucidate the influence of the luting agent on the strength of the Empress 2 crown (staining technique) cemented on human teeth. Seventy extracted human permanent molar teeth were chosen. Teeth were prepared for Empress 2 crowns with milling machine on a surveyor. A dental bur was placed in the mandrel that was positioned so that the long axis of the bur was perpendicular to the surveyor base. Dimensions of the Empress 2 crown preparation were $6^{\circ}$ taper on each side, $1.5{\pm}0.1mm$ shoulder margin, and 4mm crown height. The luting cements used in this study were as follow: 1. Uncemented 2. Zinc phosphate cements (Confi-Dental) 3. Conventional glass ionomer cement : Fuji 1 (GC) 4. Resin-modified glass ionomer cements : Fuji plus (GC) 5. Adhesive cements : Panavia F (Kuralay), Variolink II (Vivadent), Choice (Bisco). Fracture test using Instron. The crowns were loaded in compressive force to evaluate the effect of these cements on the breaking strength of these all-ceramic crowns. A steel ball with a diameter of 4mm was placed on the occlusal surface and load was applied to the steel ball by a cylindrical bolt with a crosshead speed of 0.5mm per minute until fracture occurred. The fractured surface was examined using Scanning Electron Microscopic Image (SEM) to discover the correlation between fracture strength and bonding capacity. Within the limitation of this in vitro study design, the results were as follows : 1. fomentations significantly increased the fracture resistance of Empress ceramic crowns compared to control. Uncemented (206.9 N): ZPC (812.9 N): Fuji 1 (879.5 N): Fuji Plus (937.7 N): Choice (1105.4 N): Variolink II (1221.1 N): Panavia F (1445.2 N). 2. Resin luting agent, treated by a silane bond enhancing agents, yielded a significant increase in fracture resistance. In some of the Panavia F group, a fracture extended into dentin. 3. According to SEM images of fractured Empress crowns, the stronger the bond at both interfaces(crown and die), the more fracture strength was acquired.
본 연구는 도재 수복물에 부착된 단결정 세라믹 브라켓의 전단접착강도와 파절양상에 열순환과 도재 수복물의 종류가 어떤 영향을 미치는지 알아보기 위해 시행되었다. 도재전장관에 사용되는 재료들 중 Ceramco 3, Empress II, Zi-ceram/Vintage ZR 세 가지를 선택하여 각 20개씩 총 60개의 시편을 원반형태(두께 2 mm, 직경 12 mm)로 제작하였다. 동일한 접착 술식으로 세라믹 브라켓을 부착한 후 열순환을 시행한 실험군과 시행하지 않은 대조군, 두 군으로 나누어 전단접착강도와 파절양상을 평가하였다. 열순환을 하지 않은 대조군의 전단접착강도는 Ceramco 3는 $7.06\;{\pm}\;1.76\;MPa$, Empress II는 $7.55\;{\pm}\;2.38\;MPa$ 그리고 Zi-ceram/Vintage ZR은 $7.19\;{\pm}\;1.38\;MPa$로 추천되는 전단접착 강도(6 - 8 MPa)에 적합한 강도를 보였으나 열순환을 시행한 실험군은 전단접착강도가 유의하게 감소하였으며(p < 0.05) 열순환 후의 전단접착강도는 Ceramco 3는 $4.88\;{\pm}\;1.00\;MPa$, Empress II는 $5.46\;{\pm}\;1.35\;MPa$ 그리고 Zi-ceram/Vintage ZR은 $4.84\;{\pm}\;1.01\;MPa$로 임상적으로 추천되는 것보다 다소 낮은 값을 보였다. 도재의 종류에 따른 전단접착강도에는 유의한 차이가 없었다. 파절양상은 대조군에서는 모두 브라켓 기저부와 접착제 사이에서 파절이 일어났으며, 실험군에서는 2개의 시편(Ceramco 3과 Zi-ceram/Vintage ZR군에서 각 1개)만이 접착제내 파절을 보였으며 28개의 시편은 브라켓 기저부와 접착제 사이에서 파절이 일어났다. 이상의 연구 결과에서 보았을 때 도재 수복물의 종류에 따른 차이는 없었으나 열순환에 의해 전단접착강도가 약화되므로 실제 임상에서 고려되어야 할 것이다.
The purpose of this study was to investigate the bonding of resin- based root canal sealer, AH26 when the sealer was applied as a thin layer between dentine and gutta-percha surface. In this study forty non-caries extracted human molars and resin-based root canal sealer(AH 26, DeTrey/Dentsply, Germany) were used. Disks of gutta-percha, 6mm in diameter.6mm thick (Diadent/Dentsply, Korea) for thermoplastic obturation were used and dentin surfaces were treated with 2% NaOCl(Group 1) or 2%NaOCl+17% EDTA(Group 3). Disks of gutta-Percha, 6mm in diameter.6mm thick (Diadent/Dentsply, Korea) for conventional obturation were used and dentin surface were treated with 2% NaOCl(Group 2) or 2%NaOCl+17% EDTA(Group 4). Enamel was removed by a horizontal section 1mm below the deepest portion of the central occlusal groove by using a watercooled low speed diamond saw. A second horizontal section was done around cementoenamel junction. Exposed dentin surface was cut to approximately $8{\times}8{\;}mm$ rectangular shape and was ground against 320, 400, 600 grade silicon carbide abrasive paper serially. After grinding, the dentine surface were soaked in a solution of 2% NaOCl for 30 minutes and twenty of specimens were treated with 17% EDTA solution for 1 minute. The treated specimens were washed and dried, Root canal sealer, AH26 was prepared according to the manufacture's instructions The Gutta-percha and dentin surface were coated with a thin layer of the freshly mixed seal or. The specimens were left overnight at room temperature. After their initial set, they were transferred to an incubator at $37$^{\circ}C$ for 72 h. After 72 hours, resin blocks were made. The resin block was serially sectioned vertically into stick of $1{\cdot}1mm$. Twenty sticks were prepared from each group. After that, tensile bond strength f3r each stick was measured with Microtensile Tester Failure patterns of the specimens at the interface between gutta-percha and dentin were observed under the SEM(x1000) and Stereomicroscope (LEICA M42O, Meyer Inst., TX U.S.A) at 1.25 x25 magnification. The results were statistically analysed by using a One-way ANOVA and Tukey's test. The results were as follows; 1. Tensile bond strengths($mean{\pm}SD$) were expressed with ascending order as follows: Group 1, $3.09{\pm}$ 1.05Mpa : Group 2, $6.23{\pm}1.16MPa$ : Group 3, $7.12{\pm}1.07MPa$ : Group 4, $10.32{\pm}2.06MPa$. 2. Tensile bond strengths of the group 2 and 4 used disks of gutta-percha for conventional obturation were significantly higher than that of the group 1 and 3 used fir thermoplastic obturation. (p < 0.05). 3. Tensile bond strengths of the group 3 and 4 treated with 2% NaOC1+17% EDTA were significantly higher than that of the group 1 and 2 treated with 2% NaOCl. (p < 0.05). 4. In analysis of failure patterns at the interface between sealer and gutta-percha, there were observed 49 (61%)cases of adhesive failure patterns and 31 (39%) cases of mixed failures patterns.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.