• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 추계 학술발표회 논문집
• /
• pp.501-504
• /
• 2006

Recycled aggregate mortar contains plenty of calcium hydroxide to improve the strength of blast furnace slag, although the surface mortar made of recycled aggregate deteriorates adhesion to cement paste and blast furnace slag has a low initial strength. Therefore, this study assumes that the combination with both recycled aggregate and blast furnace slag will produce a better performance. The results of the experiment show that dry mortar made of recycled aggregate provides with higher strength than wet mortar does at the 3-day and 7-day age, while lower at the 28-day age. It indicates that a large amount of cement mortar made of dry recycled aggregate has deteriorated adhesion strength. The mixes with 30% and 50% of blast furnace slag and 50% and 75% of recycled aggregate provide with much better strength at the 7-day age, although they usually have latent hydraulic property at the 28-day age. It indicates that calcium hydroxide($Ca(OH){_2}$) in recycled aggregate has affected ground granulated blast furnace slag.

• Korean Chemical Engineering Research
• /
• 제48권2호
• /
• pp.193-197
• /
• 2010

현재 포장 공정에서 사용되고 있는 stretch wrapping 공정은 초기 포장기의 장치 구비 등의 가격문제와 사용 후 폐기되는 포장재의 처리문제가 심각하다. 이에 대해 미끄럼 방지 접착제(Slip-resistant adhesive)를 사용하여 물류를 고정하여 운반하는 방식은 간단한 접착제의 도입으로 폐기물 발생이 없고 공정이 간단하며 비용이 매우 낮은 장점을 지닌다. 본 연구에서는 다습한 환경에서 polyethylene 필름 상에 미끄럼 방지 접착제를 적용했을 경우 접착력이 저하되는 것을 peel test를 통해 확인하고 적절한 첨가제의 선정 및 도입을 통해 접착력을 개선하는 연구를 수행하였다. 이를 통해서 maltodextrin의 첨가 시에 내습성에 대한 개선으로 인해 미끄럼 방지 접착력의 저하가 억제되었으며 10 wt% 도입 시에 최적의 성능을 나타내었다.

• 대한소아치과학회지
• /
• 제51권2호
• /
• pp.165-175
• /
• 2024

This study aimed to investigate the effects of blood contamination on the Vickers hardness and the surface morphology of premixed MTA and compare them with the effects on conventional MTA. The Vickers microhardness of Endocem MTA Premixed Regular (EP) and ProRoot MTA (PM) was assessed after immersion in fetal bovine serum (FBS) and saline. Stem cells from human exfoliated deciduous teeth (SHED) were seeded on MTA after immersion in FBS, saline, and deionized water (DW). Cell adhesion patterns and surface morphology were visualized via scanning electron microscopy (SEM). The surface microhardness of EP and PM in FBS was lower than in saline. However, short-term exposure of PM to FBS did not reduce the microhardness compared to saline. Angular crystals formed in water, while rounded crystals with more air voids appeared in FBS. Favorable SHED attachment occurred in all groups. Overall, the surface hardness of EP and PM decreased after FBS exposure, although PM was less influenced. We suggest minimizing the amount of bleeding when using MTA clinically; nevertheless, PM remains an option with more expected blood contamination than EP. In summary, exposure to FBS decreased mechanical performance but allowed cell adhesion for both MTAs, with PM being more resistant to these changes.

• Corrosion Science and Technology
• /
• 제5권1호
• /
• pp.27-32
• /
• 2006

One of the critical issues in the coating specification is the allowable limit of surface contaminant(s) - such as soluble salt(s), grit dust, and rust - after grit blasting. Yet, there is no universally accepted data supporting the relationship between the long-term coating performance and the amount of various surface contaminants allowed after grit blasting. In this study, it was attempted to prepare epoxy coatings applied on grit-blasted steel substrate dosed with controlled amount of surface contaminants - such as soluble salt(s), grit dust, and rust. Then, coating samples were subjected to 4,200 hours of cyclic test(NORSOK M-501), which were then evaluated in terms of resistance to rust creepage, blistering, chalking, rusting, cracking and adhesion strength. Additional investigations on the possible damage at the paint/steel interface were carried out using an Electrochemical Impedance Spectroscopy(EIS) and observations of under-film-corrosion. Test results suggested that the current industrial specifications were well matched with the allowable degree of rust, whereas the allowable amount of soluble salt and grit dust after grit blasting showed a certain deviation from the specifications currently employed for fabrication of marine vessels and offshore facilities.

• 패션비즈니스
• /
• 제17권2호
• /
• pp.63-81
• /
• 2013

A Study using compare and analyze about differences among three patterns(shape and size of pattern, fitting and amount of air gap and so on) through 3D simulation. This study use 3D simulation program, DC Suite version 3.0. The results are as a follows: The results of estimation about total appearance, the pattern of Bunka is best of all pattern about total fitting and silhouette of front and back side. The pattern of armstrong and on&on stand low in estimation. As the total fitting, the pattern of Bunka is 4.40, the pattern of Armstrong is 2.60 and the pattern of On&on is 1.60. The result show better pattern of Bunka than pattern of Armstrong and On&on. When we examine about space between body and cloth, the pattern of Bunka is best. The pattern of Armstrong don't have problems about back side but front side have some problem of getting loose. Because it only have a waist dart so dart size is too big. The pattern of On&on have so much space because it don't have a waist dart. On the amount of air gap, the pattern of Bunka squash up body so it have the amount of air gap 0.08 at bust circumference and underbust circumference. Next is the pattern of Armstrong, amount of air gap is 0.14 at bust circumference and 0.23 at underbust circumference. The pattern of On&on's amount of air gap is 0.30 at bust circumference and 0.37 at underbust circumference. So the pattern of Bunka is bodice block of the best closing adhesion and the On&on is a loose-fitting pattern.

• 폴리머
• /
• 제33권4호
• /
• pp.290-296
• /
• 2009

본 연구에서는 에폭시(DGEBA)/폴리아미드/MPD/2E4MZ-CN 반응성 블렌드의 경화 촉진제 함량에 따른 블렌드계의 형태학적 특징 및 기계적 물성에 대해 고찰하였다. 본 블렌드계의 경화거동은 DSC, 기계적 강도는 UTM, 형태학적 특징 변화는 SEM을사용하여 관찰하였다. 이미다졸(2E4MZ-CN) 경화촉진제의 함량을 $0{\sim}3\;phr$까지 조절 하였으며, 경화 반응 온도는 $170^{\circ}C$에서 30분간 유지하였다. 경화 촉진제의 함량이 증가함에 따라 최대 발열 온도가 미세하게 감소하는 경향을 보였으며, 이는 에폭시와의 상용성이 우수한 폴리아미드에 의해 경화 반응이 거의 방해받지 않았음을 보여 준다. 폴리아미드 함량이 20 phr인 조건에서 에폭시 블렌드계는 co-continuous한 분산상을 보이며, 이 조건에서 경화 촉진제의 첨가에 의해 더욱 균일한 co-continuous한 분산상이 나타났다. 상압 플라즈마 표면처리에 의해 표면장력이 증가되어 집착력이 향상되었으며, 경화 촉진제의 함량이 2 phr에서 가장 우수한 집착력을 보여 20% 이상의 집착력 향상 효과가 있었다. 이것은 경화 촉진제에 의한 블렌드계의 형태학적 조절을 고려하면 구조용 접착제에서 보다 향상된 집착력과 연신율을 동시에 기대할 수 있음을 보여 준다.

• 공업화학
• /
• 제16권2호
• /
• pp.250-256
• /
• 2005

자동차 산업에서의 도장 외관은 아주 중요하다. 이러한 도장외관의 향상을 위해서 기본적으로 도막의 내식성과 밀착성이 해결되어야 한다. 도막의 물성의 향상을 위해서 금속의 화성피막은 매우 중요한 요소가 되고 있다. 전착도장 중 음극에서의 pH는 12 정도까지 증가하고, 이 같은 강알카리 조건에서 금속과 화성피막의 용해가 일어난다. 이 같은 현상의 화성피막과 소재사이의 결합력을 감소시키게 된다. 일반적으로 인산염 피막구조는 hopeite 및 phosphphylife 구조를 갖지만 hopeite 피막 구조보다는 phosphophyllite 피막구조가 내식성이 보다 우수하고, 양이온 전착도료에 의한 전착도장에서 강알카리화된 계면에서 피막의 알카리 용해성이 적어 내수밀착성의 향상을 보인다. Ni, Mn 등의 보조금속의 첨가는 P-ratio (phosphophyllite/ hopeite + phosphophyllite)를 증가시키므로 내수 밀착성과 내식성을 향상시키게 됨을 알 수 있었다.

• 접착 및 계면
• /
• 제24권1호
• /
• pp.26-35
• /
• 2023

일반적으로 유기 용매를 이용한 코팅제는 제조 과정에서 발암성 물질인 휘발성 유기화합물 (Volatile Organic Compounds, VOC)을 배출하게 되어 환경적인 문제로 사용이 규제되고 있다. 게다가 기존의 화석 연료 자원이 한정적이라 에너지 자원 고갈을 야기시킨다는 문제가 있다. 따라서 본 연구에서는 바이오매스 물질인 isosorbide의 함량을 달리하여 광경화형 바이오매스계 우레탄 아크릴레이트 올리고머를 합성하여 코팅제의 물성 평가를 진행하였다. Isosorbide 함량이 증가할수록 점도, 유리전이온도, 인장강도, 내오염성, 연필경도 등이 증가하였고 신율 및 굴곡성은 낮게 측정되었으며, 부착력은 BOI-3가 가장 좋은 결과를 나타내었다. 올리고머의 isosorbide 함량을 20% 로 고정하고 polycaprolactone diol(PCL)과 Ecoprol H1000(Ecoprol)의 함량비에 따라 광경화형 바이오매스계 우레탄 아크릴레이트 올리고머를 합성하여 코팅제의 물성 평가를 진행하였다. PCL/Ecoprol의 함량비가 증가할수록 유리전이온도, 신율 및 굴곡성은 증가하였지만 인장강도와 연필경도는 감소하였으며, PCL 첨가로 인한 표면 결합력 향상으로 부착력과 내오염성이 크게 증진한 것을 확인할 수 있었다. 합성된 올리고머의 필름은 모두 변색 없이 투명한 결과를 나타내었다.

• 접착 및 계면
• /
• 제17권3호
• /
• pp.110-116
• /
• 2016

야간 우천시 수막에 의한 차선의 재귀반사 효율 감소로 운전자의 시인성이 저하되고 있으며 이로 인해 많은 사고가 발생한다. 시인성을 높이기 위해 메틸메타크릴레이트의 현탁중합 시 소수성으로 표면이 개질된 $SrAl_2O_4:Eu^{2+}$,$Dy^{3+}$ 축광 물질을 도입하고 이를 캡슐화하였다. 표면 개질에 사용된 물질과 라디칼 개시제의 종류, 사용된 축광 물질의 양, 그리고 캡슐의 입도가 캡슐 내부의 축광 물질 함량($W_{TGA}$)에 미치는 영향을 TGA를 사용하여 분석하였다. 그 결과 축광 물질의 함량은 7~81 wt%까지 넓은 분포를 나타내었으며, 이러한 결과는 현탁중합이 넓은 함량 범위의 축광 물질을 캡슐화하는데 적합한 것을 의미한다. 축광 물질의 함량이 낮은 경우에는 캡슐의 입도가 감소함에 따라 $W_{TGA}$이 증가하였으나, 축광 물질의 함량이 높을 때에는 캡슐의 입도에 별 영향을 받지 않았다. 축광 캡슐 중 지름 $425{\sim}710{\mu}m$의 축광 캡슐을 활용하여 형광 차선 시편을 제작하였으며 LED램프를 20 min 동안 조사한 후 광원을 제거하였을 때, 100 s 동안 약 $300mcd/m^2$ 이상의 휘도를 유지했다. 이러한 결과로 미루어 보아 제조된 축광 캡슐은 차선 위의 유리 비드를 대체하기에 충분한 가능성을 가짐을 알 수 있었다.

• Journal of the Korean Association of Oral and Maxillofacial Surgeons
• /
• 제29권4호
• /
• pp.212-218
• /
• 2003

Matrix metalloproteinases (MMPs) play an important role in the normal morphogenesis, maintenance, and repair of matrix and also have important functions in pathologic conditions characterized by excessive degradation of extracellular matrix, such as rheumatoid arthritis, osteoarthritis, periodontitis and in tumor invasion and metastasis. In this study, expression of MMP-1 and -2 mRNA in retrodiscal tissue of the temporomandibular joint (TMJ) was examined and compared with magnetic resonance imaging (MRI) and surgical findings. MMP mRNAs in the retrodiscal tissue samples were detected by reverse transcription - polymerase chain reaction. TMJ internal derangement (ID) was categorized as normal disc position, disc displacement with reduction, early stage of disc displacement without reduction (DDsR) and late stage of DDsR. TMJ osteoarthrosis (OA) was classified with normal, mild and advanced OA. The amount of synovial fluid collection was divided into not detected, small, large and extremely large amount on MR T2-weighted imaging. Perforation and adhesion were examined during open surgery of the TMJ. Six out of 37 samples were excluded because of little amount of extracted total mRNA. MMP-2 mRNA was detected whole joints, and so the MMP-2 mRNA seems to be expressed normally in retrodiscal tissue. However, MMP-1 mRNA was expressed in 8 of 31 joints. Frequencies of MMP-1 mRNA expression according to the TMJ IDs, amount of synovial fluid and surgical findings made no significant difference. MMP-1 mRNA was detected more frequently in OA groups (7/16 joints, 43.8%) than in normal bony structure group (1/15 joints, 6.7%). Expression of MMP-1 mRNA in retrodiscal tissue might be related with OA of the TMJ.