• Bulletin of the Korean Chemical Society
• /
• v.35 no.5
• /
• pp.1379-1384
• /
• 2014

${\alpha}-Fe_2O_3$ spherical particles having an average diameter of ca. 420 nm and ${\alpha}-Fe_2O_3$ fine particles (< 10 ${\mu}m$ particle size) were prepared to examine as catalysts for CO oxidation. Kinetic studies on the catalytic reactions were performed in a flow reactor using an on-line gas chromatography system operated at 1 atm. The apparent activation energies and the partial orders with respect to CO and $O_2$ were determined from the rates of CO disappearance in the reaction stage showing a constant catalytic activity. In the temperature range of $150-275^{\circ}C$, the apparent activation energies were calculated to be 13.7 kcal/mol on the ${\alpha}-Fe_2O_3$ spherical submicron clusters and 15.0 kcal/mol on the ${\alpha}-Fe_2O_3$ fine powder. The Pco and $Po_2$ dependencies of rate were investigated at various partial pressures of CO and $O_2$ at $250^{\circ}C$. Zero-order kinetics were observed for $O_2$ on both the catalysts, but the reaction order for CO was observed as first-order on the ${\alpha}-Fe_2O_3$ fine powder and 0.75-order on the ${\alpha}-Fe_2O_3$ spherical submicron clusters. The catalytic processes including the inhibition process by $CO_2$ on the ${\alpha}-Fe_2O_3$ spherical submicron powder are discussed according to the kinetic results. The catalysts were characterized using XRD (X-ray powder diffraction), FE-SEM (field emission-scanning electron microscopy), HR-TEM (high resolution-transmission electron microscopy), and $N_2$ sorption measurements.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.2
• /
• pp.121-126
• /
• 2000

The effect of electroless Ni and Cu plating on $LaNi_5$, $AB_5$ type hydrogen storage alloy was investigated by the various electrochemical techniques such as constant current charge-discharge test, cyclic voltammeoy, and a.c. impedance spectroscopy. Scanning electron microscopy and X-ray diffraction test were conducted for phenomenological logical analyses. Cyclic Voltammetry results show that activation characteristics, cycle life and reaction ,rate were improved through electroless Ni and Cu plating. Compared with bare $LaNi_5$ the charge transfer resistance of electrode was greatly reduced as charge-discharge cycle increases. Therefore, electroless Ni and Cu plating on $LaNi_5$ alloy tends to accelerate the early activation, increasing the cyclic lift of electrode.

• Journal of Energy Engineering
• /
• v.21 no.4
• /
• pp.373-377
• /
• 2012

Among the fossil fuels, the brown coal is a great deal of resources. However, it is hardly used due to the high moisture content and low calorific value. It has both the week points such as spontaneous combustion and high volatile content and the strong points such as the low-sulfur and low ash content. If we overcome these week points, the using amount of brown coal would be increased. Also, it is well known that biomass is one of the important primary renewable energy sources because of carbon neutral energy. Furthermore, the utilization of biomass has been more and more concerned with the depletion of fossil fuel sources as well as the global warming issues. Combustion and thermal decomposition of biomass is one of the more promising techniques among all alternatives proposed for the production of energy from biomass. In this study, combustion of brown coals and mushroom waste was done. Mass change of samples and emission of hydrocarbon components were measured. As the results, we obtained combustion rate constant. Also activation energy was calculated in char combustion step. Hydrocarbon components were more generated in low oxygen concentration than high. Emission amount of hydrocarbon components in mushroom waste was significantly increased comparing to brown coal.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.12
• /
• pp.2565-2573
• /
• 2002

A basic research was performed to ensure the usefulness of Small Punch-creep(SP-creep) test for residual life evaluation of heat resistant components effectively. This paper presents analytical results of initial stress and strain distributions in SP specimen caused by constant loading for SP-creep test and its experimental correlations with uniaxial creep(Ten-creep) test on 9Cr1MoVNb steel. It was shown that the initial maximum equivalent stress, ${\sigma}_{eq{\cdot}max}$ from FE analysis was correlated with steady-state equivalent creep strain rate, ${\epsilon}_{qf-ss'}$ rupture time, $t_r$, activation energy, Q and Larson-Miller Parameter, LMP during SP-creep deformation. The simple correlation laws, ${\sigma}_{sp}-{\sigma}_{TEN}$, $P_{sp}-{\sigma}_{TEN}\; and\; Q_{sp}-Q_{TEN}$ adopted to established a quantitative correlation between SP-creep and Ten-creep test data. Especially, the activation energy obtained from SP-creep test is linearly related to that from Ten-creep test at $650^{\circ}C$ as follows : $Q_{SP-P}\;{\risingdotseq}\;1.37 \;Q_{TEN},\; Q_{SP-{\sigma}}{\risingdotseq}1.53\; Q_{TEN}$.

• Journal of the Korean Society for Heat Treatment
• /
• v.13 no.6
• /
• pp.383-390
• /
• 2000

The static creep behaviour of AlSl 420F stainless steel was investigated over the temperature range of $540{\sim}585^{\circ}C$ and the stress range of $13{\sim}19kg/mm^2$ (127.4~186.2MPa). Constant stress creep tests were carried out in the experiment. Measured stress exponent, n, for the creep deformation of the alloy under the given conditions was found to vary at the range of 9.59, 9.15, 8.78, and 8.53 for the temperature of 540, 555, 570, and $585^{\circ}C$ respectively. The activation energy, Qc, for the creep deformation was 106.42, 102.58,97.81, and 94.58 kcal/mole for the stress of 13, 15, 17, and $19kg/mm^2$, respectively. Lason-Miller parameter, P, for the crept specimens for AlSl 420F stainless steel was measured as $P=T(log\;t_T+21)$. The empirical static creep rate obtained by the regression analysis was as follows. $${\varepsilon}={\exp}[(3.79{\times}10^{-2}{\sigma}+2.722)T-3.0747{\sigma}+28.109]{\times}{\sigma}^{(-2.367{\times}10^{-2}T+22.33)}{\exp}\left[-\frac{(-2.015{\sigma}+132.580){\times}10^3}{RT}\right]$$ The failure plane were observed, intergranular fracture was dominated by r (round) type crack over the experimental range.

• The Korean Journal of Physiology and Pharmacology
• /
• v.10 no.2
• /
• pp.71-77
• /
• 2006

The goal of this study was to analyze the effects of genistein, a widely used tyrosine kinase inhibitor, on cloned Shaw-type $K^+$ currents, Kv3.1 which were stably expressed in Chinese hamster ovary (CHO) cells, using the whole-cell configuration of patch-clamp techniques. In whole-cell recordings, genistein at external concentrations from 10 to $100{\mu}M$ accelerated the rate of inactivation of Kv3.1 currents, thereby concentration-dependently reducing the current at the end of depolarizing pulse with an $IC_{50}$ value of $15.71{\pm}0.67{\mu}M$ and a Hill coefficient of $3.28{\pm}0.35$ (n=5). The time constant of activation at a 300 ms depolarizing test pulses from -80 mV to +40 mV was $1.01{\pm}0.04$ ms and $0.90{\pm}0.05$ ms (n=9) under control conditions and in the presence of $20{\mu}M$ genistein, respectively, indicating that the activation kinetics was not significantly modified by genistein. Genistein $(20{\mu}M)$ slowed the deactivation of the tail current elicited upon repolarization to -40 mV, thus inducing a crossover phenomenon. These results suggest that drug unbinding is required before Kv3.1 channels can close. Genistein-induced block was voltage-dependent, increasing in the voltage range $(-20\'mV{\sim}0\'mV)$ for channel opening, suggesting an open channel interaction. Genistein $(20{\mu}M)$ produced use-dependent block of Kv3.1 at a stimulation frequency of 1 Hz. The voltage dependence of steady-state inactivation of Kv3.1 was not changed by $20{\mu}M$ genistein. Our results indicate that genistein blocks directly Kv3.1 currents in concentration-, voltage-, time-dependent manners and the action of genistein on Kv3.1 is independent of tyrosine kinase inhibition.

• Korean Journal of Materials Research
• /
• v.18 no.1
• /
• pp.45-50
• /
• 2008

Microstructural evolution and the intermetallic compound (IMC) growth kinetics in an Au stud bump were studied via isothermal aging at 120, 150, and $180^{\circ}C$ for 300hrs. The $AlAu_4$ phase was observed in an Al pad/Au stud interface, and its thickness was kept constant during the aging treatment. AuSn, $AuSn_2,\;and\;AuSn_4$ phases formed at interface between the Au stud and Sn. $AuSn_2,\;AuSn_2/AuSn_4$, and AuSn phases dominantly grew as the aging time increased at $120^{\circ}C,\;150^{\circ}C,\;and\;180^{\circ}C$, respectively, while $(Au,Cu)_6Sn_5/Cu_3Sn$ phases formed at Sn/Cu interface with a negligible growth rate. Kirkendall voids formed at $AlAu_4/Au$, Au/Au-Sn IMC, and $Cu_3Sn/Cu$ interfaces and propagated continuously as the time increased. The apparent activation energy for the overall growth of the Au-Sn IMC was estimated to be 1.04 eV.

• Korean Chemical Engineering Research
• /
• v.51 no.3
• /
• pp.308-312
• /
• 2013

Active carbons with high specific surface area and micro pore structure were prepared from the coconut shell char using the chemical activation method of NaOH. The preparation process has been optimized through the analysis of experimental variables such as activating chemical agents to char ratio and the flow rate of gas during carbonization. The active carbons with the surface area (2,481 $m^2/g$) and mean pore size (2.32 nm) were obtained by chemical activation with NaOH. The electrochemical performances of hybrid capacitor were investigated using $LiMn_2O_4$, $LiCoO_2$ as the positive electrode and prepared active carbon as the negative electrode. The electrochemical behaviors of hybrid capacitor using organic electrolytes ($LiPF_6$, $TEABF_4$) were characterized by constant current charge/discharge, cyclic voltammetry, cycle and leakage tests. The hybrid capacitor using $LiMn_2O_4$/AC electrodes had better capacitance than other hybrid systems and was able to deliver a specific energy as high as 131 Wh/kg at a specific power of 1,448 W/kg.

• Korean Journal of Food Science and Technology
• /
• v.18 no.6
• /
• pp.497-502
• /
• 1986

Soaking of soybeans is usually considered necessary as a part of further processing. However the soaking process causes the loss of soluble solids from soybean. The temperature effect on the leaching rate of soluble solids during soaking of soybeans were determined at temperatures ranging from $10^{\circ}-50^{\circ}C$. Soaking temperature and time were found to greatly influence the content of soluble solids. Solid leaching rate constant was increased with temperature ranging from 10 - 33 mg/min. Overall mass transfer coefficient of $66.7\;mg/m^2{\cdot}h$ at $20^{\circ}C$ for Saeal variety was higher as compared with other variety (Kwanggyo, Tanyob), and activation energy was found to be 4026 cal/mole. Z-values to reach different degree of leaching showed the descending tendency with increase of solid leaching.

• Polymer(Korea)
• /
• v.24 no.1
• /
• pp.16-22
• /
• 2000

Poly(butylene terephthalate- co-oxybenzoate)(PBOT) containing mesogenic oxybenzoate units in the main chain was synthesized through ester exchange reaction by melt mixing of poly(butylene terephthalate)(PBT) and p-acetoxybenzoic acid (ABA). From the kinetics of the copolymerization reaction, the activation energies and the rate constants of homopolymerization and copolymerization, k$_{h}$ and k$_{c}$, could be determined. From the reaction conditions of different compositions, 4/6, 5/5, and 6/4 of PBT/ABA, at 250, 260, and 27$0^{\circ}C$, it was revealed that copolymerization between PBT and ABA proceeds on a pseudo-second order reaction if the ABA content and its conversion are low. In this case, the ratio of rate constants of homopolymerization to copolymerization was in the range from 1.08 to 3.17, indicating that the copolymer with more notable block character was obtained at the higher mole fraction of ABA and at higher temperature.e.e.