Electrochemical Characteristics of $LaNi_5$ Electrode Fabricated by Ni and Cu Electroless Plating Techniques

Ni 및 Cu무전해 도금법에 의해 제조한 $LaNi_5$ 전극의 전기화학적 특성

The effect of electroless Ni and Cu plating on $LaNi_5$, $AB_5$ type hydrogen storage alloy was investigated by the various electrochemical techniques such as constant current charge-discharge test, cyclic voltammeoy, and a.c. impedance spectroscopy. Scanning electron microscopy and X-ray diffraction test were conducted for phenomenological logical analyses. Cyclic Voltammetry results show that activation characteristics, cycle life and reaction ,rate were improved through electroless Ni and Cu plating. Compared with bare $LaNi_5$ the charge transfer resistance of electrode was greatly reduced as charge-discharge cycle increases. Therefore, electroless Ni and Cu plating on $LaNi_5$ alloy tends to accelerate the early activation, increasing the cyclic lift of electrode.

[ $AB_5$ ] 수소저장합금인 $LaNi_5$, 합금분말에 Ni 및 Cu 무전해 도금의 영향을 전기 화학적 실험을 통하여 고찰하였다. 전기 화학적 실험은 정전류 충$\cdot$방전 실험, 순환전류전위 실험, 교류 임피던스 실험 등을 실시하여 도금하지 않은 $LaNi_5$ 전극과 Ni 및 Cu 무전해 도금한 전극간의 특성을 비교 연구하였다. 현상학적인 분석으로는 SEM을 이용하여 분말상의 미세조직을 관찰하였으며 X-선 회절시험을 실시하였다 무전해 도금을 실시하여 Ni 및 Cu박막이 피복된 수소저장 합금은 활성화 특성파 싸이클 수명 등의 특성이 개선되었으며 도금하지 않은 전극에 비하여 반응속도가 증가하였다. 또한 충$\cdot$방전이 반복됨에 따라 전극과 전해질 계면에서의 전하이동저항이 현저하게 감소하였다. 따라서 본 연구에서 실시한 $LaNi_5$, 활물질에 Ni및 Cu 무전해 도금을 실시하면 초기 활성화반응을 촉진시키며 $LaNi_5$활물질이 전해질과의 직접 접촉을 피하게 되어 전극의 수명을 증가시키는 것을 알 수 있었다.