• Corrosion Science and Technology
• /
• 제21권5호
• /
• pp.418-421
• /
• 2022

Stir-accelerated corrosion test of a high chromium cast iron was attempted in 0.1 mol dm^-3 H₂SO₄ + 0.05 mol dm^-3 HCl + 10 wt% SiC solution for 48 h at room temperature or at 45 ℃. The high chromium cast iron was composed of 2.8 wt% C and 27 wt% Cr and balanced with Fe. The high chromium cast iron was positioned into a 500 mL beaker with stirring of the solution at 1050 rpm using a magnetic hot plate. The corrosion rate was increased by agitating the solution. In addition, the corroded depth of the high chromium cast iron surface was increased by agitating the solution. The surface morphology of the high chromium cast iron after the stir-accelerated corrosion test revealed that a dendritic austenite phase partially remained in the corroded region after agitating the solution, indicating that solution movement during agitating could accelerate the corrosion rate of the high chromium cast iron.

• 한국강구조학회 논문집
• /
• 제20권2호
• /
• pp.313-321
• /
• 2008

최근 일본에서 하로식 트러스교의 콘크리트 상판을 관통하는 사재가 콘크리트 상판의 상부 또는 하부에서 심한 부식손상 에 의해 파단 된 사례가 보고되었다. 이는 도장막의 노화에 따른 콘크리트와의 경계부에 있어 사재의 국부부식에 기인한 것으로 추정되고 있다. 그러므로 이와 같이 콘크리트와 강재의 경계부에 있어서의 국부 부식손상 대책수립 및 이를 기점으로 발생될 수 있는 피로손상에 대한 검토가 필요하다. 본 실험에서는 인장시험편에 부분적으로 콘크리트 블록을 설치한 콘크리트-강재의 모델시험체에 대한 부식환경촉진실험을 실시하여, 경계부의 부식감소량을 측정하였으며, 부식실험 후의 모델시험체를 이용한 피로실험을 실시하였다. 부식촉진실험의 조건으로는 실제대기환경에의 적용성이 검토된 S6사이클(JIS K5621)을 사용하였으며, 부식촉진실험기간은 150일, 300일, 450일, 600일로 각 5개의 모델시험체를 사용하였다. 부식촉진실험결과를 근거로 실험기간에 따른 최대 및 평균 부식깊이를 정량화하였으며, 부식실험 후의 부식 손상된 모델시험체의 피로실험결과를 근거로 실험기간의 증가에 따른 피로강도 감소량을 명확히 하였다.

• 한국자기학회지
• /
• 제3권3호
• /
• pp.221-228
• /
• 1993

고밀도기록용 박막재료로서의 충족조건은 높은 보자력, 높은 포화자화, 생산성, 그리고 화학적 안정성으로써 수직자기기록매체 CoCrMo 자성박막을 RF 스퍼터링 방법으로 제조한 후, 부식 특성을 전기화학적 측정, acceleration corrosion test 및 부식후 박막의 표면분석을 통하여 조사 하였다. CoCrMo 박막의 부식특성은 스퍼터링 조건에 따라서 다르게 나타났으며, Mo의 함량이 증가 할수록 내식성은 향상되었다. 전기화학부식실험 결과 박막의 Mo 함량이 증가할수록 뚜렷한 활성- 불활성 전이를 나타내었으며 부동태전류밀도의 감소를 나타내었다. Accelerated corrosion test에 서 CoCrMo 박막의 부식은 전기화학반응에 의하여 일어났으며 Mo첨가에 따라 부식이 일어난 곳의 수는 감소하였다. AES분석결과 부식 장소에는 많은 양의 $Cl_{-}$ 이온이 존재하였고, Cr의 고갈이 부식의 원인이었다.

• 공업화학
• /
• 제20권2호
• /
• pp.177-185
• /
• 2009

자동차용 써모스타트 하우징 피팅부상의 침전물(스케일)에 대한 고장분석을 실시하였다. 에너지분산형분석기와 전자현미분석기를 이용하여 침전물이 부동액의 주요 첨가제 성분임을 확인하였다. 자세한 유기성분 분석을 위해 열분해 기체크로마토그래피/질량분석을 수행한 결과, 침전물의 주성분이 벤조산이며, 소량의 아세토페논, 벤젠 및 페닐계 화합물 등으로 이루어져 있음을 확인하였다. 더불어 침전물 생성 원인은 알루미늄 하우징과 고무호스 사이에 존재하는 틈새 공간에 부동액 성분의 침전에 따른 틈새부식에 기인한 것으로 판단된다. 이런 결과를 바탕으로 하여 써모스타트 하우징상의 침전물 생성과 틈새부식을 재현할 수 있는 가속시험기법을 개발하였다. 가속인자(온도, 습도)를 변화시키면서 실제 가동조건을 묘사하였다. 가속시험에서 얻은 침전물을 성분 분석을 통해 완벽히 재현되었음을 확인하였다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2014년도 춘계 학술논문 발표대회
• /
• pp.178-179
• /
• 2014

Corrosion is very serious problem in RC structure under ocean environment. There is no enough experiment information using the reinforced geo polymer concrete applied by electo chemical protection system. Three condition, such as tidal zone, submerged zone and crack were simulated to geo polymer specimen. Corrosion rate and natural electrode potential were measured through accelerated test. Anti corrosion property of geo polymer was better than OPC regardless of specimen condition and applied time.

• Corrosion Science and Technology
• /
• 제15권1호
• /
• pp.28-37
• /
• 2016

Due to the increased construction of offshore concrete structures and the use of de-icing salts for the purpose of snow removal, the needs for the development of anti-corrosive concrete are increasing. To solve these problems, an evaluation of the mechanical and durability properties for concrete were conducted by mixing modified-sulfur as 0 %, 5 %, 10 %, 15 % cement weight ratio. Both strengths and the properties affecting durability such as water absorption coefficient, chloride ion permeability, accelerated carbonation resistance, rapid freezing and thawing, and chemical resistance were evaluated. All evaluations performed were according to the test specifications associated KS. The results indicate that mixing of modified-sulfur lowed chloride ion permeability and improved chemical resistance.

• 한국자기학회지
• /
• 제9권4호
• /
• pp.210-216
• /
• 1999

본 연구에서는 e-beam evaporator를 사용하여 제조한 CoCrTa/CrNi 박막시편의 자성층 두께에 따른 부식특성과 열처리에 따른 부식특성의 변화를 알아보았다. Potentiodynamic scan을 이용하여 알아본 결과, 자성층 두께가 증가함에 따라 부식전위가 낮아지고, 부동태 전류밀도가 감소함을 알 수 있었다. XRD를 이용한 분석결과에 따르면, 이것은 자성층 두께가 증가함에 따라 (100)면보다 수소과전압이 큰 (0002)면으로 우선 성장했기 때문이다. 열처리에 따른 CoCrTa(400$\AA$) 자성박막의 부식특성 변화를 potentiodynamic scan과 accelerated corrosion chamber test를 이용하여 알아본 결과, 열처리후 박막시편의 내부식성이 우수해짐을 알 수 있었다. 이것은 열처리에 의해 자성층위에 Cr 산화물층이 형성되고, 이 산화물층이 자성층의 보호막으로 작용했기 때문이다.

• Corrosion Science and Technology
• /
• 제16권6호
• /
• pp.298-304
• /
• 2017

Coil spring steels from the automobile suspension part after field exposure for 10 years and those after anti-corrosion validation test in proving ground of 5,000 ~ 10,000 km were examined for corrosion damages. Partial loss of paint, accumulation of corrosion product, and cracking of paint and superficial material were observed. The surface and subsurface region of spring steels had compressive residual stress and high hardness by shot peening. The surface hardness values of the specimens were 620 ~ 670 Hv. They were 60 ~ 80 Hv higher than those of the samples taken from the middle part of the spring. The maximum compressive stress was -916 ~ -1208 MPa measured at depth of about $100{\mu}m$. Electrochemical impedance spectroscopy showed that the resistances of charge transfer and the paint layer of the spring steels ranged from several tens to millions ${\Omega}{\cdot}cm^2$. The resistance of the field samples was much higher than that of the proving ground samples used in this study, implying that the proving ground test condition would be more corrosive than the field environment.

• Journal of Welding and Joining
• /
• 제15권1호
• /
• pp.46-54
• /
• 1997

The object of this paper is to evaluate SCC(stress corrosion cracking) susceptibility for parent metal and bond line region of weld joints which have the various weld heat input condtions in TMCP(thermo-mechanical control process) steel by SP-SSRT(small punch-slow strain rate test) method. And the SCC test results of TMCP steel are compared with those of the conventional HT50 steel which has te almost same tensile strength level like TMCP steel. The loading rate used was $3\times10^{-4}$mm/min and the corrosive environment was synthetic sea water. According to the test results, in the case of parent metal, TMCP steel showed higher SCC susceptibility than HT50 steel because of the high plastic strain level of ferrite microstructure obtained by accelerated cooling. And in the case of bond line, the both TMCP steel and HT50 steel showed low load-displacement behaviors and higher SCC susceptibility above 0.6. These results may be caused by theembrittled martensite structure on HT50 steel and by the coarsened grain and the proeutectoid ferrite structure obtained by the impart of accelerated cooling effect on TMCP steel.

• 한국환경과학회지
• /
• 제27권6호
• /
• pp.467-475
• /
• 2018

The lifetime of the electrode is one of the most important factors on the stability of the electrode. Since the lifetime of the DSA (Dimensionally stable anode) electrode is long, an accelerated lifetime test is required to reduce the test time. Beacuse there is no basis or standard method for accelerated lifetime testing, many researchers use different methods. Therefore, there is a need for basis and methods for accelerated lifetime testing that other researchers can follow. We designed a reactor system for accelerated lifetime testing and planned specific methods. Reactor system was circulating batch reactor. Reactor volume and cooling water tank were 12.5 L and 100 L, respectively. Electrode size was $2cm{\times}3cm$ (real electrolysis area, $5cm^2$). In order to maintain the harsh conditions, accelerated lifetime test was carried out in a high current density ($0.6A/cm^2$) and low electrolyte concentration (NaCl, 0.068 mol/L). Maintaining a constant temperature was an important operation parameter for exact accelerated lifetime test. As the accelerated lifetime test progressed, the active component of electrode surface was consumed and desorption occurred. At the point of 5 V rise, corrosion of the surface of the base material(titanium) also started.