Tribological Properties of the Monolithic CrZrN Coatings and CrZrN/CrZrSiN Multilayer Coatings (CrZrN 코팅과 CrZrN/CrZrSiN 다층 코팅 합성과 박막의 기계적 특성)

  • Kim, Hoe-Geun;Lee, Sang-Yul
    • Proceedings of the Korean Institute of Surface Engineering Conference
    • /
    • 2015.11a
    • /
    • pp.198-198
    • /
    • 2015
  • 최근 CrZrN 코팅을 기반으로한 다양한 박막의 합성을 통해 코팅의 경도, 내마모성 등의 기계적 물성을 향상시키는 연구가 활발히 진행되고 있다. 본 연구에서는 높은 경도, 낮은 마찰계수을 나타내는 CrZrN 코팅과 이 박막의 고온 특성을 향상 하기 위한 CrZrN/CrZrSiN 다층 코팅 박막을 합성하고 그 특성을 분석하였다.

  • PDF

Characteristic of Zr(Si)N film as a diffusion barrier between Cu metal and Si substrate (Cu 금속과 Si 기판 사이에서 확산방지막으로 사용하기 위한 Zr(Si)N 박막의 특성)

  • 김좌연;조병철;채상훈;김헌창;박경순
    • Journal of the Korean Crystal Growth and Crystal Technology
    • /
    • v.12 no.6
    • /
    • pp.283-287
    • /
    • 2002
  • We have studied Zr(Si)N film as a diffusion barrier between Cu metal and Si substrate for application of interconnection metal in ULSI circuits. Zr(Si)N film was deposited with reactive DC magnetron sputtering system using $Ar/N_2$mixed gas. The value of the resistivity was the lowest for the ZrN film using 29 : 1 of Ar : $N_2$reactant gas ratio at room temperature and decreased with increasing of Si substrate temperature. As the value of ZrN film resistivity was decreased, the direction of crystal growth was toward to (002) plane. The barrier property of ZrN film added with Si was improved. But Si was added too much in ZrN film, the barrier property was degraded. The adhesive property was improved with increasing of Si in ZrN. For the analysis of the film, XRD, Optical microscopy, Scretch tester, so on were used.

Effect of composition on the structural and thermal properties of TiZrN thin film (TiZrN 박막의 조성이 구조적 특성 및 열적 특성에 미치는 영향)

  • Choi, Byoung Su;Um, Ji Hun;Seok, Min Jun;Lee, Byeong Woo;Kim, Jin Kon;Cho, Hyun
    • Journal of the Korean Crystal Growth and Crystal Technology
    • /
    • v.31 no.1
    • /
    • pp.37-42
    • /
    • 2021
  • The effect of chemical composition on the structural and thermal properties of TiZrN thin films was studied. As the Zr fraction in the deposited TixZr1-xN (x = 0.87, 0.82, 0.7, 0.6, and 0.28) increased, microstructural changes consisted of reduction in the grain size and a gradual transition from columnar structure to granular structure were observed. In addition, it was also confirmed that a gradual crystal phase transition from TiN to TiZrN has occurred as the Zr fraction increased up to 0.4. After heat treatment at 900℃, Ti0.82Zr0.18N and Ti0.7Zr0.3N layers were converted to a form in which rutile phase TiO2 and TiZrO4 oxides coexist, while Ti0.6Zr0.4N layer was converted to TiZrO4 oxide. Among the five compositions of TiZrN films, the Ti0.6Zr0.4N showed the best high temperature stability and produced a significant enhancement in the thermal oxidation resistance of Inconel 617 through suppressing the surface diffusion of Cr caused by thermal oxidation of the Inconel 617 substrate.

Influence of Bilayer Periods on the Mechanical Properties of CrZrN/CrZrSiN Multilayer Coatings (이중층 주기가 CrZrN/CrZrSiN 다층 코팅의 기계적 특성에 미치는 영향)

  • Kim, Hoe-Geun;Ra, Jeong-Hyeon;Bae, Gi-Tae;Lee, Sang-Yul
    • Proceedings of the Korean Institute of Surface Engineering Conference
    • /
    • 2015.11a
    • /
    • pp.293-293
    • /
    • 2015
  • 최근 다층 코팅의 합성을 통해 코팅의 경도, 내마모성 등의 기계적 물성을 향상시키는 연구가 활발히 진행되고 있다. 본 연구에서는 높은 경도, 낮은 마찰계수, 우수한 고온 특성을 함께 나타내기 위해 CrZrN/CrZrSiN 다층 코팅을 설계하였고, 이중층 주기를 조절하여 CrZrN/CrZrSiN 다층 코팅의 물성변화를 확인하였다.

  • PDF

Influence of N2 partial pressure on the characteristics of Cr-Zr-N coatings synthesized using a Cr-Zr segment target

  • Kim, Gwang-Seok;Kim, Yeong-Su;Lee, Sang-Yul
    • Proceedings of the Korean Institute of Surface Engineering Conference
    • /
    • 2008.11a
    • /
    • pp.1-1
    • /
    • 2008
  • 본 연구에서는 비대칭 마그네트론 스퍼터링법을 이용하여 Cr-Zr-N 박막을 합성하였다. Cr-Zr-N 박막의 합성을 위해 사용된 타겟은 Cr 과 Zr의 segments(Cr:Zr= 50:50 vol.%)로 구성된 단일 타겟을 사용하였고, 공정조건 중 질소분압을 변화시켜 Cr-Zr-N 박막을 합성하였다. 또한 질소분압 변화에 따른 박막의 물리적, 기계적, 화학적 특성들의 변화를 분석하였으며, 기 발표된 Cr 타겟과 Zr 타겟을 이용하여 합성된 Cr-Zr-N 박막의 특성들과 비교하였다.

  • PDF

Microstructure, Mechanical, Oxidation and Corrosion Properties of Zr-Al-N Coatings Synthesized by the Hybrid Coating System (하이브리드 코팅 시스템에 의해 합성된 Zr-Al-N 박막의 미세구조와 기계적 특성, 산화 특성, 부식특성)

  • Choi, Hasong;Jang, Jaeho;An, Eunsol;Kim, Kwang Ho
    • Journal of the Korean institute of surface engineering
    • /
    • v.46 no.6
    • /
    • pp.242-247
    • /
    • 2013
  • Zr-Al-N coatings were synthesized by the hybrid coating system combining arc ion plating and DC magnetron sputtering from a Zr and an Al target in argon-nitrogen atmosphere, respectively. By changing the power applied on the Al cathodes, the Zr-Al-N coatings with various Al contents were deposited. The microstructure and chemical compositions of the Zr-Al-N coatings were studied by X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM). With increasing of Al content in the coatings, the solid solution (Zr, Al)N crystallites were observed in the Zr-Al-N coatings. The nanohardness of the Zr-Al-N coatings exhibited a maximum value of 42 GPa for the Zr-Al (7.9 at.%)-N, and decreased with further increase in Al content in the coatings. The oxidation and corrosion behavior of the Zr-Al-N coatings revealed better properties compared than those of ZrN coatings due to the formation of a solid solution.

Oxidation of CrAlN and CrZrN Films (CrAlN과 CrZrN의 산화)

  • Kim, Min-Jeong;Kim, Seul-Gi;Lee, Sang-Yul;Lee, Dong-Bok
    • Proceedings of the Korean Institute of Surface Engineering Conference
    • /
    • 2011.05a
    • /
    • pp.33-35
    • /
    • 2011
  • Films of CrAlN and CrZrN were deposited on a steel substrate by closed field unbalanced magnetron sputtering, and their oxidation behaviors were investigated. CrAlN films consisted of dense, polycrystalline CrN and AlN fine columns. The formed oxides consisted primarily of crystalline $Cr_2O_3$ incorporated with $Al_2O_3$. The oxide layers were thin and compact so as to make CrAlN films more protective than CrN films. In case of CrZrN films, Zr atoms were dissolved in the CrN phase. Zr atoms advantageously refined the columnar structure, reduced the surface roughness, and increased the micro-hardness. However, the addition of Zr did not increased oxidation resistance, mainly because Zr was not a protective element. All the deposited films displayed relatively good oxidation resistance, owing to the formation of the highly protective $Cr_2O_3$ on their surface. The $Cr_{40}Zr_9N$ and $Cr_{31}Zr_{16}N$ films oxidized to $Cr_2O_3$ as the major phase and ${\alpha}-ZrO_2$ as the minor one, whereas the CrN film oxidized to $Cr_2O_3$.

  • PDF

Surface Characteristics of TiN and ZrN Film Coated STD 61 by Sputtering (스퍼터링법으로 TiN 및 ZrN 피막 코팅된 STD 61의 표면특성)

  • Eun, Sang-Won;Choe, Han-Cheol
    • Journal of the Korean institute of surface engineering
    • /
    • v.43 no.6
    • /
    • pp.260-265
    • /
    • 2010
  • STD 61 steel has been widely used for tools, metallic mold and die for press working because of its favorable mechanical properties such as high toughness, and creep strength as well as excellent oxidation resistance. The STD 61 tool steel coated with TiN and ZrN by sputtering results in improvement of wear and corrosion resistance. In this study, surface characteristics of TiN and ZrN film coated STD 61 by sputtering were studied by using FE-SEM, EDS, XRD, and XRR and nanoindentation tests. From the results of surface characteristics of coated specimen, the ZrN coated surface showed finer granular than that of TiN coated surface. The coated layer structures of ZrN and TiN were grown to (111) and (200) preferred orientation. From the results of XRR test for surface roughness, density and growth rate of coating film, surface roughness and growth rate of ZrN coated film revealed lower values those of TiN coated film, whereas density of ZrN coated film showed higher values than that of TiN coated film. From the nanohardness and elastic modulus test, nanohardness value and elastic modulus of ZrN coated film became higher than those of TiN coated film.

Machanical and electrochemical properties of CrZrN coatings as a function of $N_2$ partial pressure synthesized using a Cr-Zr segment target

  • Kim, Yeong-Su;Lee, Ha-Na;Lee, Sang-Yul
    • Proceedings of the Korean Institute of Surface Engineering Conference
    • /
    • 2009.10a
    • /
    • pp.138-138
    • /
    • 2009
  • Cr과 Zr의 segments(Cr:Zr= 50:50 vol.%)로 구성되어진 단일타겟을 이용하여 CrZrN 박막을 합성하였다. CrZrN 박막은 비대칭 마그테트론 스퍼터링법을 이용하였으며, 공정조건 중 질소분압을 변화시켜 CrZrN 박막을 합성하였다. 질소분압 변화에 따른 CrZrN 박막의 기계적, 화학적 특성들의 변화를 분석하였다.

  • PDF

Phase Analysis and Fracture Toughness of $Si_3N_4$-Zr(Y)$O_2$ Composites after Heat Treatment ($Si_3N_4$-Zr(Y)$O_2$ 복합체의 열처리에 따른 상분석 및 파괴인성)

  • 김재룡;김종희
    • Journal of the Korean Ceramic Society
    • /
    • v.28 no.1
    • /
    • pp.53-59
    • /
    • 1991
  • The reaction product between Si3N4 and ZrO2 has been studied by heat treatment of Si3N4-Zr(Y)O2 composite in high vacuum(<10-5 torr) and in air at $700^{\circ}C$. ZrN was formed after heat treatment in vacuum and easily oxidized after heat treatment in air. The amount of ZrN is related to the Y2O3 content dissolved in ZrO2. After the heat treatment in air the toughness increased and the spalling due to the oxidation of ZrN in specimen surface was observed. As a result, it is suggested that the formation of ZrN phase in Si3N4-ZrO2 composite enhance the toughness of the composite in an oxidation conditon.

  • PDF