• Proceedings of the KIEE Conference
• /
• 1994.07b
• /
• pp.1454-1456
• /
• 1994

$Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramic thin films were fabricated from an alkoxide-based solution by Sol-Gel method. $Pb(Zr_{0.52}Ti_{0.48})O_3$ ceramic thin films were formed by spin coating method on $Pt/SiO_2/Si$ substrate at 3000rpm for 30 seconds. The coating process was repeated 6 times and then heat-treated at temperature between 500 - $800[^{\circ}C]$ for 1 hour. The final thickness of the thin films were about 4800[A]. The 100% ferroelectric perovskite phases precipitated under the heat treated at $700[^{\circ}C]$ for 1 hour. $Pb(Zr_{0.52}Ti_{0.48})O_3$ thin films heat-treated at $700[^{\circ}C]$ for 1 hour showed good dielectric constant (812) property.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1913-1915
• /
• 1999

The ${\beta}-SiC+ZrB_2$ ceramic composites were hot-press sintered and annealed by adding 1, 2, 3wt% $Al_2O_3+Y_2O_3$(6 : 4wt%) powder as a liquid forming additives at $1950^{\circ}C$ for 4h. In this microstructures, no reactions were observed between $\beta$-SiC and $ZrB_2$, and the relative density is over 90.79% of the theoretical density and the porosity decreased with increasing $Al_2O_3+Y_2O_3$ contents. Phase analysis of the composites by XRD revealed of $\alpha$-SiC(6H, 4H), $ZrB_2$, $Al_2O_3$ and $\beta$-SiC(15R). Flexural strength showed the highest of 315.46MPa for composites added with 3wt% $Al_2O_3+Y_2O_3$ additives at room temperature. Owing to crack deflection and crack bridging of fracture toughness mechanism, the fracture toughness showed the highest of $5.5328MPa{\cdot}m^{1/2}$ for composites added with 2wt% $Al_2O_3+Y_2O_3$ additives at room temperature.

• Korean Chemical Engineering Research
• /
• v.47 no.1
• /
• pp.17-23
• /
• 2009

The catalytic behavior of $Ni/Ce_XZr_{(1-X)}O_2$ loaded on the alumina coated honeycomb monolith was studied for the autothermal reforming reaction of methane. Among the catalysts with the different Ce/Zr ratios, the $Ni/Ce_{0.80}Zr_{0.20}O_2$ Catalyst showed the highest conversion of methane. By investigating the effect of Ni content on the $Ni/Ce_{0.80}Zr_{0.20}O_2$ catalysts, the catalyst loaded with 15wt% Ni had the highest activity. Also, $H_2$ yield was increased as $H_2O/CH_4$ ratio increased. Methane conversion was improved as $O_2/CH_4$ ratio was increased, whereas the yield of $H_2$ was decreased. Among the catalysts tested for 30 hours, $Ni(15wt%)/Ce_{0.80}Zr_{0.20}O_2$ showed the excellent conversion(${\geq}99%$) of methane and the stability at the condition of $GHSV=30,000h^{-1}$, feed ratio S/C/O=2/1/0.5 and reaction temperature $800^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.22 no.5
• /
• pp.220-226
• /
• 2012

Pure zirconia and $x$ mol% calcia partially stabilized zirconia ($x$ = 1.5, 3, and 8) nanopowders were synthesized by hydrothermal method with various reaction temperatures for 24 hrs. The precipitated precursor of pure zirconia and $x$ mol% calcia doped zirconia was prepared by adding $NH_4OH$ to starting solutions; resulting sample was then put into an autoclave reactor. The optimal experimental conditions, such as reaction temperatures and times and amounts of stabilizer CaO, were carefully studied. The synthesized $ZrO_2$ and $x$ mol% CaO-$ZrO_2$ ($x$ = 1.5, 3, and 8) powders were characterized by XRD, SEM, TG-DTA, and Raman spectroscopy. When the hydrothermal temperature was as low as $160^{\circ}C$, pure $ZrO_2$ and $x$ mol% CaO-$ZrO_2$ ($x$ = 1.5 and 3) powders were identified as a mixture of monoclinic and tetragonal phases. However, a stable tetragonal phase of zirconia was observed in the 8 mol% calcia doped zirconia nanopowder at hydrothermal temperature above $160^{\circ}C$. To observe the phase transition, the 3 mol% CaO-$ZrO_2$ and 8 mol% CaO-$ZrO_2$ nanopowders were heat treated from 600 to $1000^{\circ}C$ for 2h. The 3 mol% CaO-$ZrO_2$ heat treated at above $1000^{\circ}C$ was found to undergo a complete phase transition from mixture phase to monoclinic phase. However, the 8 mol% calcia doped zirconia appeared in the stable tetragonal phase after heat treatment. The result of this study therefore should be considered as the preparation of 8 mol% CaO-$ZrO_2$ nanopowders via the hydrothermal method.

• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.37-45
• /
• 2003

The dielectric and sintering characteristics of composites made by substituting Ca ion to Ba-site and Zr ion to Ti site in $(Ba{1-x}Ca_x)(Ti{0.96-yZr_ySn_{0.04})O_3$ $(0.15{\leq}x{\leq}0.20,\;0.09{\leq}y{\leq}0.14)$ were investigated. As the content of Ca was more than 15 mol%, composite was formed by precipitating the second phase whose main element was $CaTiO_3$ and the fraction of the second phase was increased. The curie temperature of composites was depended on Ca concentration, $-1.7^{\circ}C$ per mol% and the maximum dielectric constant of composite was decreased by the rate of 200/mol%. The substitution of Zr ion decreased the curie temperature by the rate of $10^{\circ}C$ per mol% and the maximum dielectric constant was decreased by 217/mol% due to the increase of diffuse phase transition. The density and insulation breakdown characteristics were improved by suppressing the abnormal grain growth due to the increase of second phase. We developed the composition of Y5U (EIA standard) condenser which had high breakdown voltage and dielectric constant by controlling diffuse phase transition by the addition of Zr ion into composite.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1916-1918
• /
• 1999

The electrical conductive mechanism and temperature dependence of electrical resistivity of ${\beta}-SiC+ZrB_2$ composites with $Al_2O_3+Y_2O_3$ contents were investigated. The electrical resistivity of hot-pressed composites was measured by the Pauw method from $25^{\circ}C$ to $700^{\circ}C$. The electrical resistivity of the composites showed the PTCR(Positive Temperature Coefficient Resistivity) and follow the electrical conduction model for a homogeneous mixture of two kind of particles with different conductivity. Also, the electrical resistivity versus temperature curves indicate the formation of local chains of $ZrB_2$ particles.

• Journal of the Korean Ceramic Society
• /
• v.41 no.2
• /
• pp.111-117
• /
• 2004

3Y-TZP containing 0.3∼1.2 wt% of $Al_2$O$_3$ was prepared by slip-casting after attrition milling. The specimen was sintered at 1390∼151$0^{\circ}C$ and mechanical characterization and microstructure analysis were conducted. Monoclinic content of the specimen was calculated by XRD. The apparent density of specimen increased with increasing sintering temperature. While above 1470%, the formation of m-ZrO$_2$ degraded the density. The microhardness of specimen decreased with temperature because monoclinic phase increased wit the grain growth. The specimen containing $Al_2$O$_3$ below 0.9 wt% sintered at 143$0^{\circ}C$ showed the highest microhardness of 1360 Hv.

• Journal of Hydrogen and New Energy
• /
• v.17 no.1
• /
• pp.31-38
• /
• 2006

There are two types of metal hydride electrodes as a negative electrode in a Ni-MH battery, $AB_2$ Zr-based Laves phases and $AB_5$ LM(La-rich mischmetal)-based alloys. The $AB_5$ alloy electrodes have characteristic properties such as a large discharge capacity per volume, easiness in activation, long cycle life and a low cost of alloy. However they have a relatively small discharge capacity per weight. The $AB_2$alloy electrodes have a much higher discharge capacity per weight than $AB_5$ alloy electrodes, however they have some disadvantages of poor activation behavior and cycle life. Therefore, in order to improve the discharge capacity of the $AB_5$ alloy electrode the Zr, Ti and V which are the alloying elements of the $AB_2$ alloys were added to the $LaNi_{3.6}Ai_{0.4}Co_{0.7}Mn_{0.3}$ alloy which was chosen as a $AB_5$ alloy with a high capacity. The addition of Zr, Ti and V to $LaNi_{3.6}Ai_{0.4}Co_{0.7}Mn_{0.3}$ alloy improved the activation to be completed in two cycles. The discharge capacities of Zr 0.02, Ti 0.02 and V 0.1 alloys in $LaNi_{3.6}Ai_{0.4}Co_{0.7}Mn_{0.3}M_y$ (M = Zr, Ti, V) were respectively 346, 348 and 366 mAh/g alloy. The alloy electrodes, Zr 0.02, Ti 0.05 and V 0.1 in $LaNi_{3.6}Ai_{0.4}Co_{0.7}Mn_{0.3}M_y$ (M = Zr, Ti, V), have shown good cycle property after 200 cycles. The rate capability of the $LaNi_{3.6}Ai_{0.4}Co_{0.7}Mn_{0.3}M_y$ (M = Zr, Ti, V) alloy electrodes were very good until 0.6 C rate and the alloys, Zr 0.02, Ti 0.05 and V 0.1, have shown the best result as 92 % at 2.4 C rate. The charge retention property of the $LaNi_{3.6}Ai_{0.4}Co_{0.7}Mn_{0.3}M_y$ (M = Zr, Ti, V) alloys was not good and the alloys with M content from 0.02 to 0.05 showed better charge retention properties.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.108-108
• /
• 2000

급증하는 무선통신 정보수요는 특히, 고주파대역 (300NHz-300GHz)에서 사용되는 공진기, 필터, 발진기 등과 같은 소자의 품질향상을 요구하고 있다. 고주파용 유전체 중 ZrTiO4 는 $\alpha$-PbO2 계열의 사방정구조를 갖고 있는 유전체로서 높은 유전율 ($\varepsilon$=40)과 높은 품질계수 (Q=1/tan$\delta$=4700 at 7GHz)를 갖고 있고, Sn 첨가시 0ppm/$^{\circ}C$의 공진주파수 온도계수를 얻을 수 있다고 보고되어 있다. 본 연구에서는 약 110$0^{\circ}C$ 이상에서 안정한 상으로 존재하는 ZrTiO4를 저온에서 증착하여 준안정한 상태로 결정화되게 한후, 유전손실 (tan$\delta$)과 유전율($\varepsilon$)을 측정하였다. 또한 증착온도와 열처리과정에 따른 박막의 us형 (Strain) 정도의 변화를 X-선 회절결과로부터 분석하였으며 이를 측정된 유전특성 값과 비교하였다. ZrTiO4 박막은 DC magnetron reactive sputter로 Zr과 Ti 타겟으로부터 high phosphorous doped Si (100) 기판위에 증착하였다. 압력은 4mTorr로 유지하고 박막의 화학양론적 조성비를 맞추기 위해 각 타겟에 가해지는 power는 Zr/Ti=500W/650W로 고정하고, 반응가스의 비율을 Ar/O2=17sccm/3.5sccm으로 유지하여 박막내에 인입되는 산소량을 제어하였다. 증착 직후와 열처리 후의 박막특성을 비교하기 위해 증착온도를 상온에서부터 $600^{\circ}C$까지 변호시키고 증착후 각각의 시편을 80$0^{\circ}C$ 산소분위기에서 2시간동안 열처리하여 시편을 준비하였다. 박막의 상형성 여부와 결정성변화는 $ heta$-2$\theta$X-선 회절법을 사용하여 조사하였고, EPMA를 이용하여 박막의 조성을 확인하였다. 유전특성의 측정을 위해 백금 상부전극을 증착한 후, impedance analyzer를 이용하여 100kHz 영역에서의 유전손실을 측정하고, 측정된 정전용량과 박막의 두께로부터 유전율을 계산하였다. ZrTiO4 박막은 증착온도 20$0^{\circ}C$ 이상에서 결정성을 보이기 시작했으며, 열처리 이후에는 상온에서 비정질이었던 시편이 $650^{\circ}C$ 이상의 온도에서 결정화되기 시작하였다. 증착온도에 따라 유전손실은 0.038에서 0.017 정도로 감소하는 경향을 나타냈으며, 각각 열처리에 의해서 0.034, 0.005 정도로 다시 감소하였다. 박막의 유전율은 약 35 정도의 값을 나타내었으며 X-선 회절 data로부터 분석한 박막의 변형은 증온도에 따라 7.2%에서 0.04%로 감소하였고 이 이경향은 유전손실은 감소경향과 일치하였다.

• Journal of the Korean Ceramic Society
• /
• v.27 no.6
• /
• pp.824-828
• /
• 1990

Zirconia gel fibers were fabricated by sol-gel processing using zirconium alkoxides and 2, 4-pentanedione. Their phase transformation and microstructural evolution were studied after heat treatments up to 150$0^{\circ}C$. Tetragonal ZrO2 began to form at 50$0^{\circ}C$ and followed by monoclinic, tetragonal phase during subsequent heat treatments at 1000, 150$0^{\circ}C$ for 1hour respectively. During cooling from 150$0^{\circ}C$, cracks were created, propagated along grain boundaries due to the volume change from tetragonal to monoclinic transformation.