The I-V characteristics of $ZnO-Pr_6O_{11}-CoO-Dy_2O_3$ based varistors were investigated in the $Pr_6O_{11}/CoO$ composition ratio range of 0.5/0.5 to 1.0/1.0 and sintering temperature range of 1300 to $1350^{\circ}C$ as the basic study to develop the advanced $Pr_6O_{11}$-based ZnO varistors. All varistors except for $Pr_6O_{11}$/CoO = 0.5/1.0 exhibited the best I-V characteristics at $1350^{\circ}C$. However, the varistors with $Pr_6O_{11}$/CoO= 0.5/1.0 exhibited the best I-V characteristics at $1350^{\circ}C$. The varistors with $Pr_6O_{11}$/CoO= 0.5/1.0 of all varistors exhibited the best I-V characteristics, which the nonlinear exponent is 36.9 and the leakage current is 7.6 ${\mu}A$ Therefore, it was estimated that ZnO-$Pr_6O_{11}-CoO-Dy_2O_3$ ceramics with $Pr_6O_{11}$/CoO= 0.5/1.0 will be usefully used as varistor materials in the future.

• Journal of Sensor Science and Technology
• /
• v.11 no.3
• /
• pp.155-162
• /
• 2002

The sensing properties of carbon monooxide were investigated as a function of mixing ratio and the lamination structure of 3mol% ZnO-doped $SnO_2$ and 3mol% $SnO_2$-doped ZnO. The lamination structures were fabricared monolayer, double layer, and hetero layer of $SnO_2$, Zno, and theirs mixture composition using thick film process. There was no second phase by the reaction of $SnO_2$ and ZnO. The conductance was decreased by the addition of ZnO in $SnO_2$, but it was increased with the addition of $SnO_2$ in ZnO. The conductance was increased with temperature and the inlet of CO. There was no improvement of sensitivity in the structure of mono- and double-layer. The hetero-layer structure, however, of $SnO_2$ 3ZnO-ZnO $3SnO_2$ showed the higher resistivity and the highest sensitivity. Ohmic characteristics was confirmed by the linear properties for I-V measurements.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05a
• /
• pp.92-95
• /
• 2003

전력선 통신용 LC 공진필터에 사용되는 Ni-Zn 페라이트를 제조하기 위해 $Ni_{0.8}Zn_{0.2}Fe_{2}O_{4}$를 기본조성으로 첨가제 $Bi_{2}O_{3}$, CaO와 x (co mol 비)를 변화시켜 전자기적 특성을 조사하였다. $Bi_{2}O_{3}$ CaO가 첨가됨으로써 균일한 입자성장과 입계에 고저항층이 형성되어 주파수 손실이 감소하였으며, $Ni_{0.8-x}Zn_{0.2}Co_{x}Fe_{2}O_{\delta}$의 기본조성에 Co의 함량을 증가시키면 x = 0.05에서 투자율 75, 공진주파수 20MHz의 특성을 나타내고 결정 입자 크기와 같은 구조적 특성에는 영향을 거의 미치지 않지만 전자기적 특성에는 영향을 미친다. 또한, $Ni_{0.75}Zn_{0.2}Co_{0.05}Fe_{2}O_{4.017}$ 조성의 페라이트 코어의 발열량은 큐리온도 이하에서 일어난다.

• Korean Chemical Engineering Research
• /
• v.49 no.6
• /
• pp.720-725
• /
• 2011

Gold catalysts supported on metal-oxides were prepared by co-precipitation using the various metal nitrates and chloroauric acid as precursors, and effect of water addition on the catalytic activity in CO oxidation was investigated. Among the various supported gold catalysts, Au/$Co_{3}O_{4}$ and Au/ZnO catalysts showed the excellent activity for CO oxidation. Water in the reactant gas had a negative effect on the oxidation activity over Au/$Co_{3}O_{4}$ catalysts and a positive effect on that over Au/ZnO, which means the activity depends strongly on the nature of support. It was also confirmed that no significant change in the particle size of gold was observed after reaction both in dry and wet conditions. This fact suggested that the deactivated catalyst due to a carbonate species could be regenerated by water addition in the reactant gas.

• Journal of the Korean Ceramic Society
• /
• v.42 no.3 s.274
• /
• pp.211-217
• /
• 2005

[ $Zn_{1-x}Co_{x}O$ (x=0-0.3) films were grown on Corning 7059 glasses by asymmetrical bipolar pulsed dc magnetron sputtering. The c-axis orientation along (002) plane was enhanced with increasing Co concentration. The $Zn_{1-x}Co_{x}O$ films are grown with fibrous grains of tight dome shape. The transmittance spectra measured from UV-visible showed that sp-d exchange interactions and typical d-d transitions become activated with increasing Co concentration. The electrical resistivity of $Zn_{1-x}Co_{x}O$ films increased with increasing Co concentration, especially it increased greatly at $30at\% Co. X-ray photoelectron spectroscopy and alternating gradient magnetometer analyses indicated that no Co metal cluster is formed and the ferromagnetic properties are exhibited. The low electrical resistivity and room temperature ferromagnetism of $Zn_{1-x}Co_{x}O$ thin films suggested the possibility of the application to Diluted Magnetic Semiconductors (DMSs).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.308-311
• /
• 1999

The varistor characteristics of $ZnO-Pr_6O_11-CoO-Er_2O_3$-based ceramics were investigated. $ZnO-Pr_6O_11-CoO-Er_2O_3$-based ceramics were sintered at $1300^{\circ}C$ and $1350^{\circ}C$in the addition range 0.0~2.0mol% $Er_2O_3$, respectively. $ZnO-Pr_6O_11-CoO-Er_2O_3$-based ceramics, which are added with 0.5mol% $Er_2O_3$ at $1300^{\circ}C$ and l.Omol% $Er_2O_3$ at $1350^{\circ}C$ sintering temperature, exhibited the bestexcellent varistor characteristics, namely, the nonlinear exponent was better 52.78 at $1300^{\circ}C$ thanat 13$1350^{\circ}C$ and the leakage current was better 6.57$\mu\textrm$A at $1350^{\circ}C$ than at $1300^{\circ}C$. Consequently, it is estimated that $ZnO-Pr_6O_11-CoO-Er_2O_3$-based ceramics, which $Er_2O_3$ is added in the range 0.5~l.Omol% will begin to be used as a predominant basic composition of $PR_6O_11$-based ZnO varistors.

• Journal of the Microelectronics and Packaging Society
• /
• v.30 no.4
• /
• pp.79-85
• /
• 2023

A novel low-temperature co-fired ceramic (LTCC) dielectric, composed of (1-4x)Bi_1.5Zn_1.0Nb_1.5O₇-3xBi₂Zn_2/3Nb_4/3O₇-2xLiZnNbO₄ (x=0.03-0.21), was synthesized through reactive liquid phase sintering of Bi_1.5Zn_1.0Nb_1.5O₇-xLi₂CO₃ ceramic at temperatures ranging from 850℃ to 920℃ for 4 hours. During sintering, Li₂CO₃ reacted with Bi_1.5Zn_1.0Nb_1.5O₇, resulting in the formation of Bi₂Zn_2/3Nb_4/3O₇, and LiZnNbO₄. The resulting sintered body exhibited a relative sintering density exceeding 96% of the theoretical density. By altering the initial Li₂CO₃ content (x) and consequently modulating the volume fraction of Bi_1.5Zn_1.0Nb_1.5O₇, Bi₂Zn_2/3Nb_4/3O₇, and LiZnNbO₄ in the final sintered body, a sample with high dielectric constant (ε_r), low dielectric loss (tan δ), and the temperature coefficient of dielectric constant (TCε) characterized by NP0 specification (TCε ≤ ±30 ppm/℃) was achieved. As the Li₂CO₃ content increased from x=0.03 mol to x=0.15 mol, the volume fraction of Bi₂Zn_2/3Nb_4/3O₇ and LiZnNbO₄ in the composite increased, while the volume fraction of Bi_1.5Zn_1.0Nb_1.5O₇ decreased. Consequently, the dielectric constant (εr) of the composite materials varied from 148.38 to 126.99, the dielectric loss (tan δ) shifted from 5.29×10^-4 to 3.31×10^-4, and the temperature coefficient of dielectric constant (TCε) transitioned from -340.35 ppm/℃ to 299.67 ppm/℃. A dielectric exhibiting NP0 characteristics was achieved at x=0.09 for Li₂CO₃, with a dielectric constant (ε_r) of 143.06, a dielectric loss (tan δ) value of 4.31×10^-4, and a temperature coefficient of dielectric constant (TCε) value of -9.98 ppm/℃. Chemical compatibility experiment with Ag electrode revealed that the developed composite material exhibited no reactivity with the Ag electrode during the co-firing process.

• Korean Journal of Materials Research
• /
• v.13 no.8
• /
• pp.519-523
• /
• 2003

We report the synthesis of cubic spinel $ZnCo_2$$O_4$thin films and the tunability of the conduction type by control of the oxygen partial pressure ratio. Zinc cobalt oxide films were grown on$ SiO_2$(200 nm)/Si substrates by reactive magnetron sputtering method using Zn and Co metal targets in a mixed Ar/$O_2$atmosphere. We found from X-ray diffraction measurements that the crystal structure of the zinc cobalt oxide films grown under an oxygen-rich condition (the $O_2$/Ar partial pressure ratio of 9/1) changes from wurtzite-type $Zn_{1-x}$ $Co_{X}$O to spinel-type $ZnCo_2$$O_4$with the increase of the Co/Zn sputtering ratio,$ D_{co}$ $D_{zn}$ . We noted that the above structural change accompanied by the variation of the majority electrical conduction type from n-type (electrons) to p-type (holes). For a fixed $D_{co}$ $D_{zn}$ / of 2.0 yielding homogeneous spinel-type $_2$O$ZnCo_4$films, the type of the majority carriers also varied, depending on the$ O_2$/Ar partial pressure ratio: p-type for an $O_2$-rich and n-type for an Ar-rich atmosphere. The maximum electron and hole concentrations for the Zn $Co_2$ $O_4$films were found to be 1.37${\times}$10$^{20}$ c $m^{-3}$ and 2.41${\times}$10$^{20}$ c $m^{-3}$ , respectively, with a mobility of about 0.2 $\textrm{cm}^2$/Vs and a high conductivity of about 1.8 Ω/$cm^{-1}$ /.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.569-572
• /
• 2003

전력선 통신용 LC 공진필터에 사용되는 Ni-Zn 페라이트를 제조하기 위해 Ni0.8Zn0.2Fe2O4를 기본조성으로 선택하고 x (Co mol 비)를 변화시켜 전자기적 특성을 조사하였다. $Bi_2O_3$ CaO가 첨가됨으로써 균일한 입자성장과 입계에 고저항층이 형성되어 주파수 손실이 감소하였으며, $Ni_{0.8-x}Zn_{0.2}Co_xFe_2O_{\delta}$의 기본조성에 Co의 함량을 증가시키면 x = 0.05에서 투자율 75, 공진주파수 20 MHz의 특성을 나타내고 결정 입자 크기와 같은 구조적 특성에는 영향을 거의 미치지 않지만 자기이방성 변화에 따라 전자기적 특성에는 영향을 미친다. 또한, $Ni_{0.75}Zn_{0.2}Co_{0.05}Fe_2O_{4.017}$ 조성의 페라이트 코어의 발열량은 큐리온도 이하에서 일어난다.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.6
• /
• pp.1993-1997
• /
• 2012

Mg-doped ZnO one-dimensional (1D) nanostrutures were synthesized by using a thermal evaporation technique. The morphology, crystal structure, and sensing properties of the Mg-doped ZnO nanostructures functionalized with Pt to CO gas at $100^{\circ}C$ were examined. The diameters of the 1D nanostructures ranged from 80 to 120 nm and that the lengths were up to a few tens of micrometers. The gas sensors fabricated from multiple networked Mg-doped ZnO nanowires functionalized with Pt showed enhanced electrical response to CO gas. The responses of the nanowires were improved by approximately 70, 69, 111, and 81 times at CO concentrations of 10, 25, 50, and 100 ppm, respectively. Both the response and recovery times of the nanowire sensor for CO gas sensing were not nearly changed by Pt functionalization. It also appeared that the Mg doping concentration did not influence the sensing properties of ZnO nanowires as strongly as Pt-functionalization. In addition, the mechanism for the enhancement in the CO gas sensing properties of Mg-doped ZnO nanowires by Pt functionalization is discussed.